RU2012135068A - Формовочная композиция - Google Patents

Формовочная композиция Download PDF

Info

Publication number
RU2012135068A
RU2012135068A RU2012135068/04A RU2012135068A RU2012135068A RU 2012135068 A RU2012135068 A RU 2012135068A RU 2012135068/04 A RU2012135068/04 A RU 2012135068/04A RU 2012135068 A RU2012135068 A RU 2012135068A RU 2012135068 A RU2012135068 A RU 2012135068A
Authority
RU
Russia
Prior art keywords
range
molecular weight
copolymer
fractions
ethylene
Prior art date
Application number
RU2012135068/04A
Other languages
English (en)
Other versions
RU2536821C2 (ru
Inventor
Андрей БУРЯК
Альбрехт ДИКС
Магнус ПАЛМЛЕФ
Аннели ПАККАНЕН
Кристиан Пиль
Айодель Олутайо ФИОЛА
Торе Дренг
Янне Мааранен
Александр КРАЕТЕ
Сусана ФИЛИПЕ
Original Assignee
Бореалис Аг
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Бореалис Аг filed Critical Бореалис Аг
Publication of RU2012135068A publication Critical patent/RU2012135068A/ru
Application granted granted Critical
Publication of RU2536821C2 publication Critical patent/RU2536821C2/ru

Abstract

1. Полиэтиленовая формовочная композиция, имеющая мультимодальное молекулярно-массовое распределение, плотность по ISO 1183 при 23°C в диапазоне от 920 до 960 кг/ми ПТРпо ISO 1133 в диапазоне от 0,05 до 10 г/10 мин; при этом указанная полиэтиленовая формовочная композиция содержит по меньшей мере три фракции полимеров этилена, имеющих различные молекулярные массы:A) от 15 до 50 мас.% фракции гомополимера или сополимера этилена с низкой молекулярной массой, со среднемассовой молекулярной массой Mв диапазоне от 15 до 40 кг/моль;B) от 15 до 50 мас.% фракции гомополимера или сополимера этилена со средней молекулярной массой, со среднемассовой молекулярной массой Mв диапазоне от 70 до 200 кг/моль; иC) от 15 до 50 мас.% фракции гомополимера или сополимера этилена с высокой молекулярной массой, со среднемассовой молекулярной массой Mв диапазоне от 220 до 400 кг/моль,при условии, что одна из фракций А, В и С представляет собой гомополимер этилена, а по меньшей мере один из других компонентов представляет собой сополимер этилена с по меньшей мере одним C-Cсомономером;и композиция имеет- твердость по Шору D, измеренную по ASTM D2240-05 (15 с), по меньшей мере 56,0.2. Композиция по п.1, имеющая стойкость к истиранию по Таберу, измеренную по ASTM D4060 с роликом CS-10, менее 8 мг/1000 циклов, предпочтительно менее 7 мг/1000 циклов.3. Композиция по п.1, в которой фракции А, В и С присутствуют в количествах от 20 до 40 мас.%, например 33,3 мас.%, для каждой фракции.4. Композиция по п.1, имеющая модуль упругости при растяжении, измеренный на образцах, полученных прямым прессованием, по меньшей мере 300 МПа;- ударную вязкость по Шарпи (0°C), измеренную на образцах с V-образным надрезом, полученных прямым прессован�

Claims (15)

1. Полиэтиленовая формовочная композиция, имеющая мультимодальное молекулярно-массовое распределение, плотность по ISO 1183 при 23°C в диапазоне от 920 до 960 кг/м3 и ПТР190/2 по ISO 1133 в диапазоне от 0,05 до 10 г/10 мин; при этом указанная полиэтиленовая формовочная композиция содержит по меньшей мере три фракции полимеров этилена, имеющих различные молекулярные массы:
A) от 15 до 50 мас.% фракции гомополимера или сополимера этилена с низкой молекулярной массой, со среднемассовой молекулярной массой Mw в диапазоне от 15 до 40 кг/моль;
B) от 15 до 50 мас.% фракции гомополимера или сополимера этилена со средней молекулярной массой, со среднемассовой молекулярной массой Mw в диапазоне от 70 до 200 кг/моль; и
C) от 15 до 50 мас.% фракции гомополимера или сополимера этилена с высокой молекулярной массой, со среднемассовой молекулярной массой Mw в диапазоне от 220 до 400 кг/моль,
при условии, что одна из фракций А, В и С представляет собой гомополимер этилена, а по меньшей мере один из других компонентов представляет собой сополимер этилена с по меньшей мере одним C3-C10 сомономером;
и композиция имеет
- твердость по Шору D, измеренную по ASTM D2240-05 (15 с), по меньшей мере 56,0.
2. Композиция по п.1, имеющая стойкость к истиранию по Таберу, измеренную по ASTM D4060 с роликом CS-10, менее 8 мг/1000 циклов, предпочтительно менее 7 мг/1000 циклов.
3. Композиция по п.1, в которой фракции А, В и С присутствуют в количествах от 20 до 40 мас.%, например 33,3 мас.%, для каждой фракции.
4. Композиция по п.1, имеющая модуль упругости при растяжении, измеренный на образцах, полученных прямым прессованием, по меньшей мере 300 МПа;
- ударную вязкость по Шарпи (0°C), измеренную на образцах с V-образным надрезом, полученных прямым прессованием, по меньшей мере 90 кДж/м2;
- ударную вязкость по Шарпи (-20°C), измеренную на образцах с V-образным надрезом, полученных прямым прессованием, по меньшей мере 30 кДж/м2;
- и стойкость к растрескиванию под воздействием окружающей среды, измеренную посредством испытания на ползучесть с полным надрезом по ISO/DIS 16770.3 при 50°C и 9 МПа, по меньшей мере 20 ч.
5. Композиция по п.1, в которой Фракция А представляет собой либо фракцию гомополимера, имеющего плотность в диапазоне от 965 до 980 кг/м3, предпочтительно от 970 до 975 кг/м3; либо фракцию сополимера, имеющего плотность в диапазоне от 920 до 930 кг/м3, предпочтительно от 920 до 925 кг/м3.
6. Композиция по п.1, в которой Фракция В представляет собой либо фракцию гомополимера, имеющего плотность в диапазоне от 950 до 965 кг/м3, предпочтительно от 952 до 957 кг/м3; либо фракцию сополимера, имеющего плотность в диапазоне от 910 до 920 кг/м3, предпочтительно от 912 до 917 кг/м3.
7. Композиция по п.1, в которой Фракция C представляет собой либо фракцию гомополимера, имеющего плотность в диапазоне от 935 до 950 кг/м3, предпочтительно от 942 до 947 кг/м3; либо фракцию сополимера, имеющего плотность менее 910 кг/м3.
8. Композиция по п.1, в которой Фракция А представляет собой гомополимер этилена, а фракции В и С представляют собой сополимеры этилена.
9. Композиция по п.1, в которой каждая фракция сополимера имеет содержание сомономера C3-C10 в диапазоне от 1 до 15 мас.%.
10. Композиция по п.1, в которой каждый сополимер включает этилен и гексен.
11. Композиция по п.1, имеющая плотность по ISO 1183 при 23°C в диапазоне от 920 до 940 кг/м3, предпочтительно от 925 до 935 кг/м3.
12. Полиэтиленовая формовочная композиция, имеющая мультимодальное молекулярно-массовое распределение, плотность по ISO 1183 при 23°C в диапазоне от 920 до 960 кг/м3 и ПТР190/2 по ISO 1133 в диапазоне от 0,05 до 10 г/10 мин, при этом указанная полиэтиленовая формовочная композиция включает по меньшей мере три фракции полимера этилена, имеющие различные молекулярные массы:
A) от 15 до 50 мас.% фракции гомополимера или сополимера этилена с низкой молекулярной массой, с ПТР190/2 по ISO 1133 по меньшей мере 50 г/10 мин;
B) от 15 до 50 мас.% фракции гомополимера или сополимера этилена со средней молекулярной массой, с ПТР190/2 менее 10 г/10 мин; и
C) от 15 до 50 мас.% фракции гомополимера или сополимера этилена с высокой молекулярной массой, с ПТР190/2 меньше, чем эта величина у фракции В, и в диапазоне от 0,05 до 5 г/10 мин,
при условии, что одна из фракций А, В и С представляет собой гомополимер этилена, и по меньшей мере один из других компонентов представляет собой сополимер этилена с по меньшей мере одним C3-C10 сомономером;
и композиция имеет
- твердость по Шору D, измеренную по ASTM D2240-05 (15 с), по меньшей мере 56,0.
13. Композиция по любому из предшествующих пп.1-12, в которой каждая фракция получена с использованием катализатора с однотипными активными центрами полимеризации.
14. Изделие, содержащее полиэтиленовую композицию по любому из предшествующих пп.1-13.
15. Способ получения композиции согласно любому из предшествующих пп.1-13, включающий смешивание
A) от 15 до 50 мас.% фракции гомополимера или сополимера этилена с низкой молекулярной массой, со среднемассовой молекулярной массой Mw в диапазоне от 15 до 40 кг/моль;
B) от 15 до 50 мас.% фракции гомополимера или сополимера этилена со средней молекулярной массой, со среднемассовой молекулярной массой Mw в диапазоне от 70 до 200 кг/моль; и
C) от 15 до 50 мас.% фракции гомополимера или сополимера этилена с высокой молекулярной массой, со среднемассовой молекулярной массой Mw в диапазоне от 220 до 400 кг/моль,
при условии, что одна из фракций А, В и С представляет собой гомополимер этилена, а по меньшей мере один из других компонентов представляет собой сополимер этилена с по меньшей мере одним С3-С10 сомономером;
при этом композиция имеет:
- мультимодальное молекулярно-массовое распределение;
- плотность по ISO 1183 при 23°C в диапазоне от 920 до 960 кг/м3;
- ПТР190/2 по ISO 1133 в диапазоне от 0,05 до 10 г/10 мин, и
- твердость по Шору D, измеренную по ASTM D2240-05 (15 с), по меньшей мере 56,0.
RU2012135068/04A 2010-01-29 2011-01-27 Формовочная композиция RU2536821C2 (ru)