RU2007103187A - Латекс фторполимера, способ его получения и фторполимер - Google Patents
Латекс фторполимера, способ его получения и фторполимер Download PDFInfo
- Publication number
- RU2007103187A RU2007103187A RU2007103187/04A RU2007103187A RU2007103187A RU 2007103187 A RU2007103187 A RU 2007103187A RU 2007103187/04 A RU2007103187/04 A RU 2007103187/04A RU 2007103187 A RU2007103187 A RU 2007103187A RU 2007103187 A RU2007103187 A RU 2007103187A
- Authority
- RU
- Russia
- Prior art keywords
- mol
- copolymer
- tetrafluoroethylene
- fluoropolymer
- group
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F14/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen
- C08F14/18—Monomers containing fluorine
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L27/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers
- C08L27/02—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers not modified by chemical after-treatment
- C08L27/12—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers not modified by chemical after-treatment containing fluorine atoms
- C08L27/18—Homopolymers or copolymers or tetrafluoroethene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K5/00—Use of organic ingredients
- C08K5/04—Oxygen-containing compounds
- C08K5/09—Carboxylic acids; Metal salts thereof; Anhydrides thereof
- C08K5/095—Carboxylic acids containing halogens
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L71/00—Compositions of polyethers obtained by reactions forming an ether link in the main chain; Compositions of derivatives of such polymers
- C08L71/02—Polyalkylene oxides
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
- Polymerisation Methods In General (AREA)
- Compositions Of Macromolecular Compounds (AREA)
Claims (10)
1. Латекс фторполимера, содержащий фторполимер и фторсодержащий эмульгатор, представленный формулой (1): F(CF2)nO(CF2CF2O)mCF2COOA (где А - атом водорода, щелочной металл или NH4, n - целое число от 3 до 10, и m=0 или целое число от 1 до 3).
2. Латекс фторполимера по п.1, в котором фторполимер является сополимером по меньшей мере одного фтормономера, выбранного из группы, состоящей из тетрафторэтилена, винилиденфторида, гексафторпропилена, CF2=C(ORf)nF2-n, (где Rf - C1-8 перфторалкильная группа или перфтороксиалкиленовая группа, содержащая по меньшей мере одну эфирную связь на молекулу, n=1 или 2, и любая из углеродных цепей может быть линейной цепью, может содержать разветвленную цепь или может иметь циклическую структуру) и хлортрифторэтилена, в случае необходимости, по меньшей мере, с одним мономером, выбранным из группы, состоящей из CH2=CHOR (где R - С1-8 алкильная группа или оксиалкиленовая группа, содержащая по меньшей мере одну эфирную связь, и любая из углеродных цепей может быть линейной цепью, может содержать разветвленную цепь или может иметь циклическую структуру), пропилена и этилена, и, в случае необходимости, самое большее с 10 мол.% мономера, содержащего сшивающую группу.
3. Латекс фторполимера согласно п.1, в которой фторполимер является по меньшей мере одним членом, выбранным из группы, состоящей из полимера тетрафторэтилена, сополимера тетрафторэтилен/хлортрифторэтилена, сополимера тетрафторэтилен/пропилена, сополимера тетрафторэтилен/гексафторпропилена, сополимера винилиденфторид/гексафторпропилена, сополимера тетрафторэтилен/винилиденфторид/гексафторпропилена, сополимера тетрафторэтилен/CF2=CFOCF3, сополимера тетрафторэтилен/CF2=CFOC3F7, сополимера тетрафторэтилен/CF2=CFOCF3/CF2=CFOC3F7, сополимера тетрафторэтилен/CF2=C(OC2F5)2, сополимера тетрафторэтилен/метилвиниловый эфир, сополимера тетрафторэтилен/этилвиниловый эфир, сополимера тетрафторэтилен/н-бутилвиниловый эфир, сополимера тетрафторэтилен/этилвиниловый эфир/н-бутилвиниловый эфир, сополимера винилиденфторид/CF2=CFOC3F7, сополимера этилен/гексафторпропилена и сополимера тетрафторэтилен/пропилен/винилиденфторида.
4. Латекс фторполимера по п.1, в котором фторполимер является по меньшей мере одним членом, выбранным из группы, состоящей из полимера тетрафторэтилена, сополимера тетрафторэтилен (от 40 до 60 мол.%)/пропилен (от 60 до 40 мол.%), сополимера тетрафторэтилен (от 40 до 70 мол.%)/CF2=CFOCF3 (от 60 до 30 мол.%), сополимера тетрафторэтилен (от 40 до 70 мол.%)/CF2=CFOC3F7 (от 60 до 30 мол.%), сополимера тетрафторэтилен (от 40 до 70 мол.%)/CF2=C(OC2F5)2 (от 60 до 30 мол.%), сополимера тетрафторэтилен (от 70 до 30 мол.%)/метилвиниловый эфир (от 30 до 70 мол.%), сополимера тетрафторэтилен (от 70 до 30 мол.%)/этилвиниловый эфир (от 30 до 70 мол.%), сополимера тетрафторэтилен (от 70 до 30 мол.%)/н-бутилвиниловый эфир (от 30 до 70 мол.%), сополимера тетрафторэтилен (от 60 до 30 мол.%)/этилвиниловый эфир (от 1 до 69 мол.%)/н-бутилвиниловый эфир (от 1 до 69 мол.%), сополимера винилиденфторид (от 40 до 70 мол.%)/CF2=CFOC3F7 (от 60 до 30 мол.%), сополимера этилен (от 40 до 60 мол.%)/гексафторпропилен (от 60 до 40 мол.%), и сополимера тетрафторэтилен (от 30 до 60 мол.%)/пропилен (от 20 до 50 мол.%)/винилиденфторид (от 1 до 40 мол.%).
5. Латекс фторполимера по п.1, в котором фторсодержащим эмульгатором является соединение формулы F(CF2)nOCF2CF2OCF2COOA, (где A - атом водорода, щелочной металл или NH4, и n=3 или 4).
6. Способ получения латекса фторполимера, который включает эмульсионную полимеризацию фтормономера в водной среде, содержащей от 0,001 до 10,0 мас.% фторсодержащего эмульгатора, представленного формулой (1): F(CF2)nO(CF2CF2O)mCF2COOA (где А - атом водорода, щелочной металл или NH4, n - целое число от 3 до 10, и m=0 или целое число от 1 до 3), c получением латекса фторполимера.
7. Способ получения латекса фторполимера по п.6, в котором фтормономер, который является по меньшей мере одним фтормономером, выбранным из группы, состоящей тетрафторэтилена, винилиденфторида, гексафторпропилена, CF2=C(ORf)nF2-n (где Rf - С1-8 перфторалкильная группа или перфтороксиалкиленовая группа, содержащая по меньшей мере одну эфирную связь на молекулу, n=1 или 2, и любая из углеродных цепей может быть линейной цепью, может содержать разветвленную цепь или может иметь циклическую структуру), и хлортрифторэтилена, сополимеризуют, если необходимо, по меньшей мере с одним мономером, выбранным из группы, состоящей из CH2=CHOR (где R - С1-8 алкильная группа или оксиалкиленовая группа, содержащая по меньшей мере одну эфирную связь, и любая из углеродных цепей может быть линейной цепью, может содержать разветвленную цепь или может иметь циклическую структуру), пропилена и этилена, и в случае необходимости сополимеризуют самое большее с 10 мол.% мономера, содержащего сшивающую группу.
8. Способ получения латекса фторполимера по п.6, в котором фторсодержащим эмульгатором является соединение формулы F(CF2)nOCF2CF2OCF2COOA, (где A - атом водорода, щелочной металл или NH4, и n=3 или 4).
9. Латекс фторполимера, который получают концентрированием латекса фторполимера, полученного по способу, определенному в п.6, до концентрации фторполимера по меньшей мере 30 мас.%.
10. Фторполимер, который получают коагуляцией латекса фторполимера, полученного по способу, определенному в п.6.