KR950003462A - 내마모성 및 고투자율 합금과 그의 제조방법 - Google Patents
내마모성 및 고투자율 합금과 그의 제조방법 Download PDFInfo
- Publication number
- KR950003462A KR950003462A KR1019940012036A KR19940012036A KR950003462A KR 950003462 A KR950003462 A KR 950003462A KR 1019940012036 A KR1019940012036 A KR 1019940012036A KR 19940012036 A KR19940012036 A KR 19940012036A KR 950003462 A KR950003462 A KR 950003462A
- Authority
- KR
- South Korea
- Prior art keywords
- less
- weight
- alloy
- temperature
- nitrogen
- Prior art date
Abstract
본 발명은 내마모성 및 고투자율성의 자기합금과 그의 제조방법에 관한 것으로써, 더욱 상세하게는 주요성분으로써 니켈(Ni), 니오브(Nb), 질소(N), 산소(O) 및 철(Fe)을 함유하고, 부성분으로써 크롬(Cr), 몰리브덴(Mo), 겔르마늄(Ge), 금(Au), 코발트(Co), 바나듐(V), 텅스텐(W), 구리(Cu), 탄탈(Ta), 망간(Mn), 알루미늄(Al), 규소(Si), 티탄(Ti), 지르큐늄(Zr), 하프늄(Hf), 주석(Sn), 안티몬(Sb), 갈륨(Ga), 인듐(In), 탈륨(Tl), 아연(Zn), 카드뮴(Cd), 회토류원소(rare earth element), 백금족 원소(platinum element), 베릴륨(Be), 은(Ag), 스트론듐(Sr), 바륨(Ba), 불소(B), 인(P) 및 황(S)에서 선택된 최소 1종 원소를 함유하는 자기합금과 그의 제조방법 그리고 자기 기록재생헤드에 관한 것이다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제2도는 79.5% Ni-Fe-0.022%N-0.022%O 합금의 열간가공 온도에 따른 특성변화를 나타낸 그래프이고, 제3도는 79.5% Ni-Fe-5.5%Nb-0.022%N-0.022%O 합금의 냉간가공률에 따른 특성변화를 나타낸 그래프이다.
Claims (11)
- 60~90중량%의 Ni, 0.5~14중량%의 Nb, 0.0003~0.3중량%의 질소와 산소의 혼합물 그리고 잔여분의 철(Fe)로 이루어져 있고, 포화자속밀도가 4000G 이상이고 1KHz에서 3000 이상의 유효 투자율을 갖으며 [110]〈112+[311]〈112〉재결정집합 조직을 갖는 것을 특징으로 하는 내마모성 및 고투자율 합금.
- 60~90중량%의 Ni, 0.5~14중량%의 Nb, 0.0003~0.3중량%의 질소와 산소의 혼합물 그리고 0.001~30중량%의 부성분 및 잔여분의 철(Fe)로 이루어져 있고, 부성분은 Cr, Mo, Ge 및 Au가 각각 7중량% 이하, Co 및 V가 각각 10중량% 이하, W가 15중량% 이하, Cu, Ta 및 Mn이 각각 중량% 이하, Al, Si, Ti, Zr, Hf, Sn, Sb, Ga, In, Tl, Zn, Cd, 회토류원소 및 백금족 원소가 각각 5중량% 이하, Be, Ag, Sr 및 Ba가 각각 3중량% 이하, B가 1중량% 이하, P가 0.7중량% 이하 및 S가 0.1중량% 이하인 성분들 중에서 선택된 최소 1종 원소이며, 포화자속밀도가 4000G 이상이고 1KHz에서 3000 이상의 유효 투자율성을 갖으며 [110]〈112〉+[311]〈112〉재결정집합 조직을 갖는 것을 특징으로 하는 내마모성 및 고투자율 합금.
- 제2항에 있어서, 상기 합금은 0.3중량% 이하의 탄소(C)를 첨가시켜 포화자속밀도 400G 이상이고 1KHz에서 3000 이상의 유효투자율을 갖으며 [110]〈112〉+[311]〈112〉재결정집합 조직을 갖는 내마모성 및 고투자율 합금.
- 60~90중량%의 Ni, 0.5~14중량%의 Nb, 0.0003~0.3중량%의 질소와 산소의 혼합물 그리고 잔여분의 철(Fe)로 이루어져 있는 합금을 900℃ 내지 용융점 이하의 온도에서 열간가공하고 냉각시킨 후, 50% 이상의 가공율에서 냉간가공한 다음, 900℃ 내지 용융점 이하의 온도에서 가열하고, 100℃/초~1℃/시간의 소정의 냉각속도(predetermined cooling rate)로 질서-무질서 격자전이점 이상의 온도를 상온으로 냉각시켜 포화자속밀도 4000G 이상이고 1KHz에서 3000 이상의 유효투자율을 갖으며 [110]〈112〉+[311]〈112〉재결정집합 조직을 갖는 내마모성 및 고투자율 합금의 제조방법.
- 60~90중량%의 Ni, 0.5~14중량%의 Nb, 0.0003~0.3중량%의 질소와 산소의 혼합물 그리고 잔여분의 철(Fe)로 이루어져 있는 합금을 900℃ 내지 용융점 이하의 온도에서 열간가공하고 냉각시킨 후, 50% 이상의 가공율에서 냉간처리한 다음, 900℃ 내지 용융점 이하의 온도에서 가열하고, 100℃/초~1℃/시간의 소정의 냉각속도로 질서-무질서 격자 전이점 이상의 온도를 상온으로 냉각시킨 후, 질서-무질서 격자 전이점 이하의 온도에서 1분 내지 100시간의 소정의 시간동안 가열하고 냉각시켜 포화자속밀도가 4000G 이상이고 1KHz에서 3000 이상의 유효투자율을 갖으며 [110]〈112〉+[311]〈112〉재결정집합 조직을 갖는 내마모성 및 고투자율 합금의 제조방법.
- 60~90중량%의 Ni, 0.5~14중량%의 Nb, 0.0003~0.3중량%의 질소와 산소의 혼합물 그리고 0.001~30중량%의 부성분 및 잔여분의 철(Fe)로 이루어져 있고, 부성분은 Cr, Mo, Ge 및 Au가 각각 7중량% 이하, Co 및 V가 각각 10중량% 이하, W가 15중량% 이하, Cu, Ta 및 Mn이 각각 25중량% 이하, Al, Si, Ti, Ar, Hf, Sn, Sb, Ga, In, Tl, Zn, Cd, 회토류원소 및 백금족 원소가 각각 5중량% 이하, Be, Ag, Sr 및 Ba가 각각 3중량% 이하, B가 1중량% 이하, P가 0.7중량% 이하 및 S가 0.1중량% 이하인 성분들 중에서 선택된 최소 1종 원소로써, 이 합금을 900℃ 내지 용융점 이하의 온도에서 열간가공하고 냉각시킨 후, 50% 이상의 가공율에서 냉각 처리한 다음, 900℃ 내지 용융점 이하의 온도에서 열간가공하고, 100℃/초~1℃/시간의 소정의 냉각속도로 질서-무질소 격자 전이점 이상의 온도를 상온으로 냉각시켜 포화자속밀도가 4000G 이상이고 1KHz에서 3000 이상의 유효 투자율성을 갖으며 [110]〈112〉+[311]〈112〉재결정집합 조직을 갖는 내마모성 및 고투자율 합금의 제조방법.
- 제6항에 있어서, 상기 합금에 0.3중량% 이하의 탄소(C)를 첨가시켜 포화자속밀도 4000G 이상이고 1KHz에서 3000 이상의 유효투자율을 갖으며 [110]〈112〉+[311]〈112〉재결정집합 조직을 갖는 내마모성 및 고투자율 합금의 제조방법.
- 60~90중량%의 Ni, 0.5~14중량%의 Nb, 0.0003~0.3중량%의 질소와 산소의 혼합물 그리고 0.001~30중량%의 부성분 및 잔여분의 철(Fe)로 이루어져 있고, 부성분은 Cr, Mo, Ge 및 Au가 각각 7중량% 이하, Co 및 V가 각각 10중량% 이하, W가 15중량% 이하, Cu, Ta 및 Mn이 각각 25중량% 이하, Al, Si, Ti, Zr, Hf, Sn, Sb, Ga, In, Tl, Zn, Cd, 회토류원소 및 백금족 원소가 각각 5중량% 이하, Be, Ag, Sr 및 Ba가 각각 3중량% 이하, B가 1중량% 이하, P가 0.7중량% 이하 및 Ba가 0.1중량% 이하인 성분들 중에서 선택된 최소 1종 원소로써, 이 합금을 900℃ 내지 용융점 이하의 온도에서 열간가공하고 냉각시킨 후, 50% 이상의 가공율에서 냉각 처리한 다음, 900℃ 내지 용융점 이하의 온도에서 열간가공하고, 100℃/초~1℃/시간의 소정의 냉각속도로 질서-무질소 격자 전이점 이상의 온도를 상온으로 냉각시킨 후, 질서-무질소 격자 전이점 이하의 온도에서 1분 내지 100 시간의 소정의 시간동안 가열하고 냉각시켜 포화자속밀도 4000G 이상이고 1KHz에서 3000 이상의 유효투자율을 갖으며 [110]〈112〉+[311]〈112〉재결정집합 조직을 갖는 내마모성 및 고투자율 합금의 제조방법.
- 제8항에 있어서, 상기 합금에 0.3중량% 이하의 탄소(C)를 첨가시켜 포화자속밀도 4000G 이상이고 1KHz에서 3000 이상의 유효투자율을 갖으며 [110]〈112〉+[311]〈112〉재결정집합 조직을 갖는 내마모성 및 고투자율 합금의 제조방법.
- 60~90중량%의 Ni, 0.5~14중량%의 Nb, 0.0003~0.3중량%의 질소와 산소의 혼합물 및 잔여분의 철(Fe)로 이루어져 있고,포화자속밀도 4000G 이상이고 1KHz에서 3000 이상의 유효투자율성을 갖으며 [110]〈112〉+[311]〈112〉재결정집합 조직을 갖는 내마모성 및 고투자율 합금을 이용하여 제조된 자기 기록재생헤드.
- 60~90중량%의 Ni, 0.5~14중량%의 Nb, 0.0003~0.3중량%의 질소와 산소의 혼합물 그리고 0.001~30중량%의 부성분 및 잔여분의 철(Fe)로 이루어져 있고, 부성분은 Cr, Mo, Ge 및 Au가 각각 7중량% 이하, Co 및 V가 각각 10중량% 이하, W가 15중량% 이하, Cu, Ta 및 Mn이 각각 25중량% 이하, Al, Si, Ti, Zr, Hf, Sn, Sb, Ga, In, Tl, Zn, Cd, 회토류원소 및 백금족 원소가 각각 5중량% 이하, Be, Ag, Sr 및 Ba가 각각 3중량% 이하, B가 1중량% 이하, P가 0.7중량% 이하 및 Sa가 0.1중량% 이하인 성분들 중에서 선택된 최소 1종 원소이며, 포화자속밀도가 4000G 이상이고 1KHz에서 3000 이상의 유효투자율을 갖으며 [110]〈112〉+[311]〈112〉재결정집합 조직을 갖는 내마모성 및 고투자율 합금을 이용하여 제조된 자기 기록재생헤드.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.