KR910013317A - Fe기 연자성 합금, 그 제조방법 및 이를 이용한 자성코어 - Google Patents

Fe기 연자성 합금, 그 제조방법 및 이를 이용한 자성코어 Download PDF

Info

Publication number
KR910013317A
KR910013317A KR1019900022570A KR900022570A KR910013317A KR 910013317 A KR910013317 A KR 910013317A KR 1019900022570 A KR1019900022570 A KR 1019900022570A KR 900022570 A KR900022570 A KR 900022570A KR 910013317 A KR910013317 A KR 910013317A
Authority
KR
South Korea
Prior art keywords
soft magnetic
magnetic alloy
based soft
element selected
quenching
Prior art date
Application number
KR1019900022570A
Other languages
English (en)
Other versions
KR940006334B1 (ko
Inventor
다까오 사와
유미꼬 다까하시
Original Assignee
아오이 죠이찌
가부시끼가이샤 도시바
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP1339722A external-priority patent/JP2835113B2/ja
Priority claimed from JP2155297A external-priority patent/JPH0448004A/ja
Priority claimed from JP2155298A external-priority patent/JP2877452B2/ja
Priority claimed from JP2155299A external-priority patent/JPH0448005A/ja
Application filed by 아오이 죠이찌, 가부시끼가이샤 도시바 filed Critical 아오이 죠이찌
Publication of KR910013317A publication Critical patent/KR910013317A/ko
Application granted granted Critical
Publication of KR940006334B1 publication Critical patent/KR940006334B1/ko

Abstract

내용 없음.

Description

Fe기 연자성 합금, 그 제조방법 및 이를 이용한 자성코어
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본 발명의 한 실시예에 의한 자성코어의 열처리온도와 자기 특성관계를 종래예와 비교하여 나타낸 그래프.

Claims (16)

  1. 일반식:Fe100-a-b-c-d-e-fXaMbM'cAdSieZf(식중 X는 급냉체 제작시에 응용 가능한 세라믹 재료에서 적어도 한종류의 화합물을 M은 Ti, Zr, Hf, V, Nb, Ta, Cr, Mo 및 W에서 선택된 적어도 한종류의 원소를, M'는 Mn, 백금족원소, Ag, Au, Zn, Al, Ga, In, Sn, Cu, 희토류 원소에서 선택된 적어도 한종류의 원소를, Z은 B,C,P 및 Ge에서 선택된 적어도 한종류의 원소를 나타내며, a,b,c,d,e 및 f는 각각 0.1a5, 0.1b10.0c10.0d40, 5e25.2f20, 12e+f30을 만족하는 수이다. 단 상기 식중의 모든 숫자는 at%를 나타낸다)로 표시되는 조성으로 된 것을 특징으로 하는 미세결정 입자를 가진 Fe기 연자성 합금.
  2. 제1항에 있어서, 미세결정 입자를 합금조성 중에 면적비로 50% 이상 함유하고 있는 것을 특징으로 하는 Fe기 연자성합금.
  3. 제1항에 있어서, 미세결정입자의 평균입자 지름이 50㎚이하인 것을 특징으로 하는 Fe기 연자성 합금.
  4. 제1항에 있어서, 미세결정 입자가 주로 bcc-Fe 고용체로 구성되며 또한 적어도 그 일부가 규칙상인 것을 특징으로 하는 Fe기 연자성합금.
  5. 제1항에 있어서, X로 표시되는 화합물이 750℃-1800℃ 범위의 융점을 가지며 또한 상기 X의 밀도를 DC, X를 제외한 합금조성의 밀도를 Da로 했을 때 0.6DaDC1.3Da를 만족하는 밀도를 가진 것을 특징으로 하는 Fe기 연자성 합금.
  6. 제5항에 있어서, 상기 X로 표시되는 화합물이 CuO, Cu2O, SnO2, Bi2O3, WO3Ta2O5, Nb2O5, MoO3, MnO, GeO2, Ga2O3및 CdO에서 선택된 적어도 한종류의 화합물인 것을 특징으로 하는 Fe기 연자성 합금.
  7. 제1항에 있어서, 일반식이 Fe100-a-b-c-d-e-f-XaMbSieZf로 표시되는 것을 특징으로 하는 Fe기 연자성 합금.
  8. 제1항에 있어서, 일반식이 Fe100-a-b-c-d-e-f-g-hXaMbM"gCuhAdSieZf(식중, M"는 Mn, 백금족원소, Ag, Au, Zn, Al, Ga, In, Sn, 희토류 원소에서 선택된 적어도 한종류의 원소를 나타낸다.
    g 및 h는 각각 0.1h5, g+h10을 만족하는 수이다.
    단, 상기 식중의 모든숫자는 at%를 나타낸다)로 표시되는 것을 특징으로 하는 Fe기 연자성 합금.
  9. 제1항에 있어서, 연자성 합금의 분말을 가진 것을 특징으로 하는 Fe기 연자성 합금.
  10. 용융상태에 Fe기 학금 및 용융상태의 세라믹 재료를 함유하는 용탕을 급냉하는 공정과, 급냉공정으로 얻은 급냉체에 그 급냉체의 결정화 온도부근 또는 그 이상의온도로 열처리하여 합금조직내에 미세 결정입자를 석출시키는 공정을 가진 것을 특징으로 하는 Fe기 연자성 합금의 제조방법.
  11. 제10항에 있어서, 상기 용탕의 조성이 일반식 : Fe100-a-b-c-d-e-fXaMbM'cAdSieZf(식중, X는 급냉체 제작시에 응용 가능한 세라믹 재료에서 적어도 한종류의 화합물을, M은 Ti, Zr, Hf, V, Nb, Ta, Cr, Mo 및 W에서 선택된 적어도 한종류의 원소를, M'는 Mn, 백금족원소, Ag, Au, Zn, Al, Ga, In, Sn, Cu, 희토류 원소에서 선택된 적어도 한종류의 원소를, Z은 B,C,P 및 Ge에서 선택된 적어도 한종류의 원소를 나타낸다.
    a,b,c,d,e 및 f는 각각 0.1a5, 0.1b10.0c10, 0d40, 5e25, 2f20, 12e+f30을 만족하는 수이다. 단, 상기 식중의 모든 숫자는 at%를 나타낸다)를 만족하는 것을 특징으로 하는 Fe기 연자성 합금의 제조방법.
  12. 제10항에 있어서, 상기 열처리를 승온속도 10deg/min으로 측정한 급냉체의 결정화 대책에 비하여 -50℃∼+200℃의 범위의 온도로 실행하는 것을 특징으로 하는 Fe기 연자성 합금의 제조방법.
  13. 제10항에 있어서, 상기 열처리에 의해 평균 입자지름 50㎜ 이하의 상기 미세 결정입자를 면적비로 합금 조직의 50% 이상이 되도록 석출시키는 것을 특징으로 하는 Fe기 연자성 합금의 제조방법.
  14. 제10항에 있어서, 상기 급냉체가 실질적으로 아몰퍼스 상태를 만족하는 것을 특징으로 하는 Fe기 연자성 합금의 제조방법.
  15. 제1항에 있어서, Fe기 연자성 합금의 박대의 권회체 또는 적층체를 가지는 것을 특징으로 하는 자성코어.
  16. 제9항의 Fe기 연자성 합금분말의 압분성형체를 가지는 것을 특징으로 하는 자성코어.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019900022570A 1989-12-28 1990-12-28 Fe기 연자성 합금, 그 제조방법 및 이를 이용한 자성코어 KR940006334B1 (ko)