KR940005741A - 에틸렌 공중합체 조성물 - Google Patents
에틸렌 공중합체 조성물 Download PDFInfo
- Publication number
- KR940005741A KR940005741A KR1019930011092A KR930011092A KR940005741A KR 940005741 A KR940005741 A KR 940005741A KR 1019930011092 A KR1019930011092 A KR 1019930011092A KR 930011092 A KR930011092 A KR 930011092A KR 940005741 A KR940005741 A KR 940005741A
- Authority
- KR
- South Korea
- Prior art keywords
- mfr
- ethylene
- density
- iii
- olefin
- Prior art date
Abstract
밀도, 용융유속(MFR), n-데칸 가용부량이 특정범위내이고, 190℃에서의 멜트텐션(MT)과 MFR이 MF>2.2×MFR-0.84의 관계를 만족하는 에틸렌/α-올레핀 공중합체〔A-1〕와,〔B-1〕고압 라디칼 중합에 의한 저밀도 폴리에틸렌,〔B-2〕결정성 폴리올레핀 및〔B-3〕올레핀 엘라스토머로된 군에서 선택된 하나의 (공)중합체로 구성된 에틸렌 공중합체 조성물.
또한, 에틸렌/α-올레핀 공중합체 조성물과, 고압 라디칼 중합에 의해 얻어진 저밀도 폴리에틸렌〔B-1〕으로 구성되고, 상기 에틸렌/α-올레핀 공중합체 조성물은, 상기 에틸렌/α-올레핀 공중합체〔A-1〕와 유사한 물성을 갖고, 극한점도는 서로 다른, 에틸렌/α-올레핀 공중합체〔A-2〕와,〔A-3〕로 구성돼 있는 에틸렌/α-올레핀 공중합체 조성물에 관한 것이다. 또한 밀도, 용융유속(MFR), n-데칸 가용부량이 특정범위내이고, 190℃에서의 멜트텐션(MT)과 MFR이 MF>2.2×MFR-0.84의 관계를 만족하는 에틸렌/α-올레핀 공중합체〔A-4〕와,〔B-1〕고압 라디칼 중합에 의한 저밀도 폴리에틸렌,〔B-2〕결정성 폴리올레핀 및〔B-3〕올레핀 엘라스토머로된 군에서 선택된 하나의 (공)중합체로 구성된 에틸렌 공중합체 조성물에 관한 것이다.
또한, 에틸렌/α-올레핀 공중합체 조성물과, 고압 라디칼 중합에 의해 얻어진 저밀도 폴리에틸렌〔B-4〕으로 구성되고, 상기 에틸렌/α-올레핀 공중합체 조성물은, 상기 에틸렌/α-올레핀 공중합체〔A-4〕와 유사한 물성을 갖고, 극한점도는 서로 다른, 에틸렌/α-올레핀 공중합체〔A-5〕와,〔A-6〕로 구성돼 있는 에틸렌/α-올레핀 공중합체 조성물에 관한 것이다.
본 발명의 에틸렌 공중합체 조성물은 열안정성과 성형성이 우수하고, 고투명성, 고기계강도 및 볼록킹 방지성을 갖는 필름을 제조할 수 있다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (8)
- 〔A-1〕하기 물성을 갖는 에틸렌과 탄소수 3∼20 α-올레핀의 에틸렌/α-올레핀 공중합체와, (ⅰ)밀도(d)가 0.880∼0.960g/㎤의 범위내이고, (ⅱ)2.16㎏하중하 190℃에서의 용융유속(MFR)이 0.01∼200g/10분, (ⅲ)시차주사열량(DSC)에 의해 측정한 상기 공중합체의 흡열곡선이 최대 피크를 나타내는 온도(Tm(℃))와 밀도(d)가 하기 관계를 만족하며,Tm<400×d-250(ⅳ)190℃에서의 멜트텐션(MT(g))와 용융유속(MFR)이 하기 관계를 만족하며,MT>2.2×MFR-0.84(ⅴ)190℃에서 용융된 공중합체의 전단응력이 2.4×106dyne/㎤에 달했을때 얻어진 전단속도로 정의되는 후로우인덱스(FI(ℓ/sec)와 용융유속(MFR)이 하기 관계를 만족하며FI>75×MFR(ⅵ)23℃에서 데칸가용부양(W(중량%))과 밀도(d)가 하기 관게를 만족함. MFR≤10g/10분인 경우에, W×80×exp(-100(d-0.88))+0.1 MFR>10g/10분인 경우에, W×80×(MFR-9)-0.26×exp(-100(d-0.88))+0.1〔B-1〕하기물성을 갖는, 고압 라디칼 중합저밀도 폴리에틸렌을 포함하고, (ⅰ)용융유속(MFR)이 0.1∼50g/10분의 범위내이고, (ⅲ)GPC에 의해 측정한 분자량 분포(Mw/Mn, Mw=중량평균분자량, Mn=수평균분자량)와 용융유속(MFR)이 하기 관계를 만족합.Mw/Mn≥7.5×log(MFR)-1.2;상기 에틸렌/α-올레핀 공중합체〔A-1〕와 상기 고압 라디칼 중합 저밀도 폴리에틸〔B-1〕간의 중량비〔A-1〕:〔B-1〕가 99:1∼60:40의 범위내인 것을 특징으로 하는 에틸렌 공중합체 조성물.
- 〔A-1〕하기 물성을 갖는 에틸렌과 탄소수 3∼20 α-올레핀의 에틸렌/α-올레핀 공중합체와, (ⅰ)밀도(d)가 0.880∼0.960g/㎤의 범위내이고, (ⅱ)2.16㎏하중하 190℃에서의 용융유속(MFR)이 0.01∼200g/10분, (ⅲ)시차주사열량(DSC)에 의해 측정한 상기 공중합체의 흡열곡선이 최대 피크를 나타내는 온도(Tm(℃))와 밀도(d)가 하기 관계를 만족하며,Tm<400×d-250(ⅳ)190℃에서의 멜트텐션(MT(g))와 용융유속(MFR)이 하기 관계를 만족하며,MT>2.2×MFR-0.84(ⅴ)190℃에서 용융된 공중합체의 전단응력이 2.4×106dyne/㎤에 달했을때 얻어진 전단속도로 정의되는 후로우인덱스(FI(ℓ/sec)와 용융유속(MFR)이 하기 관계를 만족하며FI>75×MFR(ⅵ)23℃에서 데칸가용부양(W(중량%))과 밀도(d)가 하기 관게를 만족함. MFR≤10g/10분인 경우에, W×80×exp(-100(d-0.88))+0.1 MFR>10g/10분인 경우에, W×80×(MFR-9)-0.26×exp(-100(d-0.88))+0.1〔B-1〕하기중합체군 (B-Ⅰ)2.16g하중하에서 230℃에서의 용융유속(MFR)이 0.1∼100g/10분, 밀도가 0.900g/㎤이상인, 비메탈로센계 촉매를 사용하여 제조한 에틸렌 단독중합체 또는 에틸렌과 탄소수 3∼20의 α-올레핀의 공중합체, (B-Ⅱ)2.16g하중하에서 230℃에서의 용융유속(MFR)이 0.01∼100g/10분, 밀도가 0.900g/㎤이상인, 에틸렌과 탄소수 4∼20의 α-올레핀중에서 선택된 적어도 하나의 올레핀과 프로필렌의 공중합체 또는 프로필렌 단독중합체, (B-Ⅲ) 2.16g 하중하에서 230℃에서의 용융유속(MFR)이 0.01∼100g/10분, 밀도가 0.900g/㎤ 이상인, 에틸렌과 탄소수 4∼20의 α-올레핀의 단독 중합체 또는 탄소수 4∼20의 α-올레핀의 공중합체중에서 선택된 적어도 하나의 결정성폴리올레핀 1∼40중량%를 포함한 것을 특징으로 하는 에틸렌 공중합체 조성물.
- 〔A-1〕하기 물성을 갖는 에틸렌과 탄소수 3∼20 α-올레핀의 에틸렌/α-올레핀 공중합체 60∼99중량%와, (ⅰ)밀도(d)가 0.880∼0.960g/㎤의 범위내이고, (ⅱ)2.16㎏하중하 190℃에서의 용융유속(MFR)이 0.01∼200g/10분, (ⅲ)시차주사열량(DSC)에 의해 측정한 상기 공중합체의 흡열곡선이 최대 피크를 나타내는 온도(Tm(℃))와 밀도(d)가 하기 관계를 만족하며,Tm<400×d-250(ⅳ)190℃에서의 멜트텐션(MT(g))와 용융유속(MFR)이 하기 관계를 만족하며,MT>2.2×MFR-0.84(ⅴ)190℃에서 용융된 공중합체의 전단응력이 2.4×106dyne/㎤에 달했을때 얻어진 전단속도로 정의되는 후로우인덱스(FI(ℓ/sec)와 용융유속(MFR)이 하기 관계를 만족하며FI>75×MFR(ⅵ)23℃에서 데칸가용부양(W(중량%))과 밀도(d)가 하기 관게를 만족함. MFR≤10g/10분인 경우에, W×80×exp(-100(d-0.88))+0.1 MFR>10g/10분인 경우에, W×80×(MFR-9)-0.26×exp(-100(d-0.88))+0.1〔B-3〕하기물성을 갖는 올레핀계 엘라스토머 1∼40중량%로 구성되고, (ⅰ)밀도(d)가 0.900g/㎤의 범위내이고, (ⅱ)2.16㎏하중하 190℃에서의 용융유속(MFR)이 0.01∼100g/10분,을 갖는 올레핀계 엘라스토머 1∼40중량%를 포함하며, 상기 올레핀게 엘라스토머〔B-3〕대 상기 에틸렌/α-올레핀 공중합체〔A-1〕의 밀도비(〔B-3〕/〔A-1〕)가 1미만인 것을 특징으로 하는 에틸렌 공중합체 조성물.
- 〔Ia〕〔A-1〕에틸렌과 탄소수 3∼20의 α-올레핀의 에틸렌/α-올레핀 공중합체 5∼95중량%와,〔A-3〕에틸렌과 탄소수 3∼20의 α-올레핀의 에틸렌/α-올레핀 공중합체 5∼95중량%로 구성되고, 상기 에틸렌/α-올레핀 공중합체〔A-2〕가 하기 물성을 갖으며, (ⅰ)밀도(d)가 0.880∼0.960g/㎤의 범위내이고, (ⅱ)135℃데칼린중에서 측정한 극한점도〔ηA-2〕가 1.0∼10.0㎗/g (ⅲ)시차주사열량(DSC)에 의해 측정한 상기 공중합체의 흡열곡선이 최대피크를 나타내는 온도(Tm(℃))와 밀도(d)가 하기 관계를 만족하며,tm<400×d-250(ⅳ)190℃에서의 멜트텐션(MT(g))와 용융유속(MFR)이 하기 관계를 만족하며,MT>2.2×MFR-0.84(ⅴ)190℃에서 용융된 공중합체의 전단응력이 2.4×106dyne/㎤에 달했을때 얻어진 전단속도로 정의되는 후로우인덱스(FI(ℓ/sec)와 용융유속(MFR)이 하기 관계를 만족하며FI>75×MFR(ⅵ)실온에서 데칸가용부양(W(중량%))과 밀도(d)가 하기 관계를 만족함.W<×80×exp(-100(d-0.88))+0.1상기 에틸렌/α-올레핀 공중합체〔A-2〕가 하기 물성을 갖으며, (ⅰ)밀도(d)가 0.910∼0.960g/㎤의 범위내이고, (ⅱ)135℃데칼린중에서 측정한 극한점도〔ηA-3〕가 0.5∼2.0㎗/g (ⅲ)시차주사열량(DSC)에 의해 측정한 상기 공중합체의 흡열곡선이 최대피크를 나타내는 온도(Tm(℃))와 밀도(d)가 하기 관계를 만족하며,tm<400×d-250상기 에틸렌/α-올레핀 공중합체 조성물〔Ia〕가 하기 물성을 갖으며, 실온하에서 데칸가용부양(W(중량%))과 밀도(d)가 하기 관계를 만족하며, MFR≤10g/10분인 경우에, W×80×exp(-100(d-0.88))+0.1 MFR>10g/10분인 경우에, W×80×(MFR-9)-0.26×exp(-100(d-0.88))+0.1 상기 에틸렌/α-올레핀 공중합체〔A-2〕대 상기 에틸렌/α-올레핀 공중합체〔A-3〕의(〔A-2〕/〔A-3〕)가 1미만이고, 상기 에틸렌/α-올레핀 공중합체〔A-2〕의 극한점도 대 상기 에틸렌/α-올레핀 공중합체〔A-3〕의 극전점도비〔ηA-2〕/〔ηA-3〕가 1이상이고, (ⅲ)조성물의 밀도가 0.890∼0.955g/㎤의 범위내이고, (ⅳ)하중 2.16㎏하중하 190℃에서의 용융유속(MFR)이 0.01∼100g/10분의 범위내인 에틸렌/α-올레핀 공중합체, 조성물과,〔Ⅱ-a〕〔B-1〕하기물성을 갖는 고압 라디칼 중합저밀도 폴리에틸렌으로 구성되고, (ⅰ)용융유속(MFR)이 0.1∼50g/10분의 범위내, (ⅱ)GPC에 의해 측정한 분자량 분포(Mw/Mn, Mw=중량평균분자량, Mn=수평균분자량)와 용융유속(MFR)이 하기 관계를 만족함.Mw/Mn≥7.5×log(MFR)-1.2상기 에틸렌/α-올레핀 공중합체 조성물〔Ia〕과 상기 고압 라디칼 중합 저밀도 폴리에틸렌〔Ⅱa〕의 중량비〔Ia〕:〔Ⅱa〕가 99:1∼60:40인 것을 특징으로 하는 에틸렌 공중합체 조성물.
- 〔A-4〕하기 물성을 갖는 에틸렌과 탄소수 3∼20 α-올레핀의 에틸렌/α-올레핀 공중합체와, (ⅰ)밀도(d)가 0.880∼0.960g/㎤의 범위내이고, (ⅱ)2.16㎏하중하 190℃에서의 용융유속(MFR)이 0.01∼200g/10분, (ⅲ)시차주사열량(DSC)에 의해 측정한 상기 공중합체의 흡열곡선이 최대 피크를 나타내는 온도(Tm(℃))와 밀도(d)가 하기 관계를 만족하며,Tm<400×d-250(ⅳ)190℃에서의 멜트텐션(MT(g))와 용융유속(MFR)이 하기 관계를 만족하며,MT>2.2×MFR-0.84(ⅴ)23℃에서 데칸가용부양(W(중량%))과 밀도(d)가 하기 관계를 만족함.MFR≤10g/10분인 경우에, W×80×exp(-100(d-0.88))+0.1 MFR>10g/10분인 경우에, W×80×(MFR-9)-0.26×exp(-100(d-0.88))+0.1;〔B-1〕하기물성을 갖는, 고압 라디칼 중합저밀도 폴리에틸렌으로 구성되고, (ⅰ)용융유속(MFR)이 0.1∼50g/10분의 범위내, (ⅱ)GPC에 의해 측정한 분자량 분포(Mw/Mn, Mw=중량평균분자량, Mn=수평균분자량)와 용융유속(MFR)이 하기 관계를 만족함.7.5×log(MFR)-1.2≤Mw/Mn≤×7.5×log(MFR)-12.5상기 에틸렌/α-올레핀 공중합체〔A-4〕와 상기 고압 라디칼 중합 저밀도 폴리에틸〔B-4〕간의 중량비〔A-4〕:〔B-4〕가 99:1∼60:40의 범위내인 것을 특징으로 하는 에틸렌 공중합체 조성물.
- 〔A-4〕하기 물성을 갖는 에틸렌과 탄소수 3∼20 α-올레핀의 에틸렌/α-올레핀 공중합체60∼99중량%와, (ⅰ)밀도(d)가 0.880∼0.960g/㎤의 범위내이고, (ⅱ)2.16㎏하중하 190℃에서의 용융유속(MFR)이 0.01∼200g/10분, (ⅲ)시차주사열량(DSC)에 의해 측정한 상기 공중합체의 흡열곡선이 최대 피크를 나타내는 온도(Tm(℃))와 밀도(d)가 하기 관계를 만족하며,Tm<400×d-250(ⅳ)190℃에서의 멜트텐션(MT(g))와 용융유속(MFR)이 하기 관계를 만족하며,MT>2.2×MFR-0.84(ⅴ)23℃에서 데칸가용부양(W(중량%))과 밀도(d)가 하기 관계를 만족함.MFR≤10g/10분인 경우에, W×80×exp(-100(d-0.88))+0.1 MFR>10g/10분인 경우에, W×80×(MFR-9)-0.26×exp(-100(d-0.88))+0.1〔B-2〕하기 결정성 폴리올레핀군 (B-I)2.16g하중하에서 190℃에서의 용융유속(MFR)이 0.1∼100g/10분, 밀도가 0.900g/㎤이상인, 비메탈로센계 촉매를 사용하여 제조한 에틸렌 단독중합체 또는 에틸렌과 탄소수 3∼20의 α-올레핀의 공중합체, (B-Ⅱ)2.16g하중하에서 230℃에서의 용융유속(MFR)이 0.01∼100g/10분, 밀도가 0.900g/㎤이상인, 에틸렌과 탄소수 4∼20의 α-올레핀중에서 선택된 적어도 하나의 올레핀과 프로필렌의 공중합체 또는 프로필렌 공중합체, (B-Ⅲ)2.16g 하중하에서 230℃에서의 용융유속(MFR)이 0.01∼100g/10분, 밀도가 0.900g/㎤ 이상인, 에틸렌과 탄소수 4∼20의 α-올레핀의 단독 중합체 또는 탄소수 4∼20의 α-올레핀의 공중합체중에서 선택된 적어도 하나의 결정성폴리올레핀 1∼40중량%를 포함한 것을 특징으로 하는 에틸렌 공중합체 조성물.
- 〔A-4〕하기 물성을 갖는 에틸렌과 탄소수 3∼20 α-올레핀의 에틸렌/α-올레핀 공중합체 60∼99중량%와, (ⅰ)밀도(d)가 0.880∼0.960g/㎤의 범위내이고, (ⅱ)2.16㎏하중하 190℃에서의 용융유속(MFR)이 0.01∼200g/10분, (ⅲ)시차주사열량(DSC)에 의해 측정한 상기 공중합체의 흡열곡선이 최대 피크를 나타내는 온도(Tm(℃))와 밀도(d)가 하기 관계를 만족하며,Tm<400×d-250(ⅳ)190℃에서의 멜트텐션(MT(g))와 용융유속(MFR)이 하기 관계를 만족하며,MT>2.2×MFR-0.84(ⅴ)23℃에서 데칸가용부양(W(중량%))과 밀도(d)가 하기 관계를 만족함.MFR≤10g/10분인 경우에, W×80×exp(-100(d-0.88))+0.1 MFR>10g/10분인 경우에, W×80×(MFR-9)-0.26×exp(-100(d-0.88))+0.1;〔B-3〕하기물성을 갖는 올레핀계 엘라스토머 1∼40중량%로 구성되고, (ⅰ)밀도(d)가 0.900g/㎤의 범위내이고, (ⅱ)2.16㎏하중하 190℃에서의 용융유속(MFR)이 1.01∼100g/10분 상기 올로핀계 엘라스토머 〔B-3〕대 상기 에틸렌/α-올레핀 공중합체〔A-4〕의 밀도비(〔B-3〕/〔A-4〕)가 1미만인 것을 특징으로 하는 에틸렌 공중합체 조성물.
- 〔Ib〕〔A-5〕에틸렌과 탄소수 3∼20의 α-올레핀의 에틸렌/α-올레핀 공중합체 5∼95중량%와,〔A-6〕에틸렌과 탄소수 3∼20의 α-올레핀의 에틸렌/α-올레핀 공중합체 5∼95중량%로 구성되고, 상기 에틸렌/α-올레핀 공중합체〔A-5〕가 하기 물성을 갖으며, (ⅰ)밀도(d)가 0.880∼0.960g/㎤ 이하, (ⅱ)135℃데칼린중에서 측정한 극한점도〔ηA-2〕가 1.0∼10.0㎗/g (ⅲ)시차주사열량(DSC)에 의해 측정한 상기 공중합체의 흡열곡선이 최대피크를 나타내는 온도(Tm(℃))와 밀도(d)가 하기 관계를 만족하며,tm<400×d-250(ⅳ)190℃에서의 멜트텐션(MT(g))와 용융유속(MFR)이 하기 관계를 만족하며,MT≤2.2×MFR-0.84(ⅴ)실온에서 데칸가용부양(W(중량%))과 밀도(d)가 하기 관계를 만족함.W<×80×exp(-100(d-0.88))+0.1상기 에틸렌/α-올레핀 공중합체〔A-2〕가 하기 물성을 갖으며, (ⅰ)밀도(d)가 0.910∼0.960g/㎤의 범위내이고, (ⅱ)135℃데칼린중에서 측정한 극한점도〔ηA-6〕가 0.5∼2.0㎗/g (ⅲ)시차주사열량(DSC)에 의해 측정한 상기 공중합체의 흡열곡선이 최대피크를 나타내는 온도(Tm(℃))와 밀도(d)가 하기 관계를 만족하며,tm<400×d-250(ⅳ)실온하에서 데칸가용부양(W(중량%))과 밀도(d)가 하기 관계를 만족하며, MFR≤10g/10분인 경우에, W×80×exp(-100(d-0.88))+0.1 MFR>10g/10분인 경우에, W×80×(MFR-9)-0.26×exp(-100(d-0.88))+0.1 상기 에틸렌/α-올레핀 공중합체〔Ib〕이 하기물성를 갖으며, (ⅰ)상기 에틸렌/α-올레핀 공중합체〔A-5〕대 상기 에틸렌/α-올레핀 공중합체〔A-6〕의(〔A-5〕/〔A-6〕)가 1미만이고, (ⅱ)상기 에틸렌/α-올레핀 공중합체〔A-5〕의 극한점도 대 상기 에틸렌/α-올레핀 공중합체〔A-6〕의 극한점도비〔ηA-5〕/〔ηA-6〕가 1이상이고, (ⅲ)조성물의 밀도가 0.890∼0.955g/㎤의 범위내이고, (ⅳ)하중 2.16㎏하중하 190℃에서의 용융유속(MFR)이 0.01∼50g/10분의 범위내임,〔Ⅱb〕〔B-4〕하기물성을 갖는 고압 라디칼 중합저밀도 폴리에틸렌으로 구성되고, (ⅰ)용융유속(MFR)이 0.1∼50g/10분의 범위내, (ⅱ)GPC에 의해 측정한 분자량 분포(Mw/Mn, Mw=중량평균분자량, Mn=수평균분자량)와 용융유속(MFR)이 하기 관계를 만족함.7.5×log(MFR)-1.2≤Mw/Mn≤×7.5×log(MFR)+12.5상기 에틸렌/α-올레핀 공중합체〔Ib〕과 상기 고압 라디칼 중합 저밀도 폴리에틸〔Ⅱb〕간의 중량비〔Ia〕:〔Ⅱa〕가 99:1∼60:40인 것을 특징으로 하는 에틸렌 공중합체 조성물.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.