KR20180018395A - 피부 접착재 및 피부 접착재 권회체 - Google Patents
피부 접착재 및 피부 접착재 권회체 Download PDFInfo
- Publication number
- KR20180018395A KR20180018395A KR1020170101012A KR20170101012A KR20180018395A KR 20180018395 A KR20180018395 A KR 20180018395A KR 1020170101012 A KR1020170101012 A KR 1020170101012A KR 20170101012 A KR20170101012 A KR 20170101012A KR 20180018395 A KR20180018395 A KR 20180018395A
- Authority
- KR
- South Korea
- Prior art keywords
- skin
- skin adhesive
- adhesive layer
- acrylic copolymer
- pressure
- Prior art date
Abstract
피부면으로의 양호한 접착성ㆍ피트감과, 접착 시의 땀차기ㆍ소양감을 저감할 수 있는 피부 접착재 및 피부 접착재 권회체를 제공한다.
폴리우레탄엘라스토머 필름의 한쪽의 면에 점착제층이 형성되고, 상기 점착제층의 점착면을 덮어 박리 가능하게 적층된 박리 라이너를 갖는 피부 접착재이며, 상기 폴리우레탄엘라스토머 필름의 두께는 1 내지 9㎛이고, 상기 점착제층은 아크릴계 공중합체와, 실온에서 액상 혹은 페이스트상인 성분을 포함하도록 피부 접착재를 구성한다.
폴리우레탄엘라스토머 필름의 한쪽의 면에 점착제층이 형성되고, 상기 점착제층의 점착면을 덮어 박리 가능하게 적층된 박리 라이너를 갖는 피부 접착재이며, 상기 폴리우레탄엘라스토머 필름의 두께는 1 내지 9㎛이고, 상기 점착제층은 아크릴계 공중합체와, 실온에서 액상 혹은 페이스트상인 성분을 포함하도록 피부 접착재를 구성한다.
Description
본 발명은 피부에 접착하여 사용되는 피부 접착재 및 피부 접착재 권회체에 관한 것이다.
기재 필름의 편면에 점착제층을 형성하여 이루어지는 피부 접착재는, 점착제 층을 통해 피부면에 접착되어 사용된다. 이와 같이 피부 접착재를 피부면에 접착하면, 피부면에 땀차기나 가려움이 발생하고, 때로는 염증을 일으키는 경우도 있다. 이 때문에, 피부 접착재에는 높은 투습성이 요구된다.
또한, 피부면은 불규칙하고 또한 복잡한 표면 형상을 갖고 있기 때문에, 피부 접착재를 구성하는 점착제층이 피부면에 완전히 밀착되는 것이 어렵지만, 피부면에 대하여 강고하게 접착 고정되면 박리 시에 피부 자극이 발생할 가능성이 있어, 접착 시의 양호한 접착성을 가지면서, 접착되어 있는 것을 느끼게 하지 않도록 하는 양호한 피트감과, 박리 시의 피부 자극 저감이라는 절묘한 특성의 밸런스를 갖는 피부 접착재가 요구되고 있다.
본 발명은 상기 현 상황을 감안하여, 피부면으로의 양호한 접착성ㆍ피트감과, 접착 시의 땀차기ㆍ소양감을 저감할 수 있고, 또한 박리 시의 물리적인 피부 자극을 저감할 수 있는 피부 접착재 및 피부 접착재 권회체를 제공하는 것을 목적으로 한다.
본 발명자들은, 상기 목적을 달성하기 위해 예의 검토를 거듭한 결과, 피부 접착재에 있어서, 기재 필름으로서의 폴리우레탄엘라스토머 필름의 두께를 특정한 범위로 제어하고, 점착제층에 실온에서 액상 혹은 페이스트상인 성분을 함유시킴으로써, 상기 과제를 해결할 수 있는 것을 알아내어 본 발명을 완성하기에 이르렀다.
즉, 본 발명은
폴리우레탄엘라스토머 필름의 한쪽의 면에 점착제층이 형성되고, 상기 점착제층의 점착면을 덮어 박리 가능하게 적층된 박리 라이너를 갖는 피부 접착재이며,
상기 폴리우레탄엘라스토머 필름의 두께는 1 내지 9㎛이고,
상기 점착제층은, 아크릴계 공중합체와, 실온에서 액상 혹은 페이스트상인 성분을 함유하는 점착제를 포함하는 것을 특징으로 하는 피부 접착재에 관한 것이다.
본 발명의 피부 접착재는, 피부면에 대한 양호한 접착성과, 접착 시에 접착되어 있는 것을 느끼게 하지 않도록 하는 양호한 피트감을 가짐과 함께, 접착 시의 땀차기ㆍ소양감을 억제하고, 또한 박리 시의 물리적인 피부 자극을 저감할 수 있는 것이다.
도 1은 실시예 2 내지 5 및 비교예 2 내지 5의 피부 접착재에 대한, 피부로부터의 박리 시의 통증 평가에 사용한 Face Pain Scale를 도시하는 도면.
본 발명에 있어서, 이하에 설명하는 점착제층을 지지하는 기재 필름으로서 기능하는 폴리우레탄엘라스토머 필름의 두께는 1 내지 9㎛인 것이 필요하고, 3 내지 9㎛인 것이 바람직하다. 폴리우레탄엘라스토머 필름의 두께가 1㎛ 미만이면 피부 접착재를 사용할 때, 또는 사용 후 피부면으로부터 박리할 때에, 피부 접착재가 파단되어 버릴 우려가 있다. 한편, 폴리우레탄엘라스토머 필름의 두께가 9㎛를 초과하면, 피부 접착재를 피부면에 접착하고 있는 때에, 피부면의 유연한 움직임에 대하여 당기는 느낌과 같은 위화감이 발생하는 경우가 있다.
또한, 본 발명에서는, 기재 필름으로서 폴리우레탄엘라스토머 필름을 사용하는 것은, 당해 필름이 신축성 및 투습성이 우수하므로, 당해 필름이 신체의 굴곡부의 움직임에 추종할 수 있음과 함께, 피부에 땀이 차서 염증이 생기는 것을 억제할 수 있기 때문이다.
(점착제층)
점착제층은 피부 접착력의 조정이 용이한 것, 피부와 접촉하였을 때에 피부 자극성이 적은 것 등으로부터, 아크릴계 공중합체를 포함하는 것이다.
아크릴계 공중합체로서는 특별히 한정되는 것은 아니지만, 예를 들어 (메트)아크릴산알킬에스테르 단량체 및 알콕시기 함유 에틸렌성 불포화 단량체를 포함하는 단량체 혼합물로부터 얻어지는 아크릴계 공중합체를 사용하는 것이 바람직하다.
(메트)아크릴산알킬에스테르 단량체는, 점착제층에 양호한 피부 접착성을 부여하는 주성분으로 되는 것이며, 특히 알킬기의 탄소수가 6 이상, 나아가 6 내지 18인 장쇄 알킬기를 사용하면 효과적이다. 또한, (메트)아크릴산알킬에스테르 단량체는, 피부에 대한 자극성이 비교적 적어, 장시간의 사용에 의해서도 점착력의 저하가 일어나기 어렵다는 이점을 갖는 것이다.
이와 같은 (메트)아크릴산알킬에스테르 단량체의 구체예로서는, 아크릴산 혹은 메타크릴산의 부틸에스테르, 프로필에스테르, 옥틸에스테르, 노닐에스테르, 데실에스테르, 도데실에스테르, 라우릴에스테르 등을 1종 혹은 2종 이상 병용하여 사용할 수 있다. 또한, 이들 알킬에스테르쇄는 직쇄여도, 분지쇄여도 되는 것은 물론이다.
알콕시기 함유 에틸렌성 불포화 단량체는, 아크릴계 공중합체에 수증기 투과성, 소위 투습성을 부여하는 성분이다. 이와 같은 알콕시기 함유 에틸렌성 불포화 단량체는 특별히 한정되지 않지만, 예를 들어 메톡시폴리에틸렌글리콜아크릴레이트, 에톡시디에틸렌글리콜아크릴레이트, 부톡시디에틸렌글리콜아크릴레이트, 메톡시에틸아크릴레이트, 에톡시에틸아크릴레이트, 부톡시에틸아크릴레이트 등의 탄소수가 1 내지 4인 알콕시기를 갖는 알콕시알킬아크릴레이트를 사용하는 것이 바람직하다.
또한, 본 발명에 있어서의 아크릴계 공중합체는, 카르복실기 함유 에틸렌성 불포화 단량체를 포함하는 단량체 혼합물로부터 얻어지는 아크릴계 공중합체를 사용하는 것이 더 바람직하다. 카르복실기 함유 에틸렌성 불포화 단량체를 포함함으로써, 얻어지는 공중합체의 응집력이 향상되므로, 점착제층의 특성을 조정하는 데 있어서 중요한 단량체가 된다. 이와 같은 단량체의 대표예로서는, 아크릴산, 이타콘산, 크로톤산, 푸마르산, (무수)말레산 등을 들 수 있다. 이들 중, 공중합성이나 취급성 등의 점에서 바람직한 단량체로서는 아크릴산을 들 수 있다.
상기 점착제를 구성하는 아크릴계 공중합체는, 상기 (메트)아크릴산알킬에스테르 단량체와 알콕시기 함유 에틸렌성 불포화 단량체가 공중합함으로써 얻어지는 것이 바람직하고, (메트)아크릴산알킬에스테르 단량체와 알콕시기 함유 에틸렌성 불포화 단량체와 카르복실기 함유 에틸렌성 불포화 단량체가 공중합함으로써 얻어지는 것이 보다 바람직하다.
본 발명의 아크릴계 공중합체는, 상기 각 단량체 이외에, 친수성의 부여 등의 각종 개질을 행하기 위한 개질용 단량체로서, 스티렌이나 아세트산비닐, N-비닐-2-피롤리돈 등의 단량체를 필요에 따라서 적절히 공중합해도 된다.
아크릴계 공중합체에 있어서의 (메트)아크릴산알킬에스테르 단량체의 함유량은, 바람직하게는 40질량% 내지 80질량%, 보다 바람직하게는 50질량% 내지 75질량%의 범위로 한다. (메트)아크릴산알킬에스테르 단량체의 함유량이 상기 범위 내이면, 양호한 피부 접착성을 나타내고, 피부로부터의 박리 시에는 당해 피부에 대하여 점착제 잔류 현상이 발생하지 않아 우수한 박리성을 갖는다.
또한, 아크릴계 공중합체에 있어서의 알콕시기 함유 에틸렌성 불포화 단량체의 함유량은, 바람직하게는 10질량% 내지 60질량%, 보다 바람직하게는 20질량% 내지 60질량%, 더욱 바람직하게는 25질량% 내지 50질량%의 범위로 한다. 알콕시기 함유 에틸렌성 불포화 단량체의 함유량이 상기 범위 내이면, 점착제층에 우수한 투습성을 부여할 수 있다.
또한, 카르복실기 함유 에틸렌성 불포화 단량체를 함유시키는 경우, 상술한 알콕시기 함유 에틸렌성 불포화 단량체의 함유량은, 바람직하게는 10질량% 내지 50질량%, 보다 바람직하게는 20질량% 내지 45질량%의 범위로 한다.
상기 카르복실기 함유 에틸렌성 불포화 단량체의 함유량은, 바람직하게는 1질량% 내지 10질량%이고, 보다 바람직하게는 3질량% 내지 8질량%이다. 카르복실기 함유 에틸렌성 불포화 단량체의 함유량이 상기 범위 내이면, 점착제층에 우수한 응집력을 부여할 수 있어, 점착제 잔류 현상 등을 억제할 수 있음과 함께, 피부 자극성도 억제할 수 있다.
아크릴계 공중합체의 분자량 측정 용매에 대한 가용분의 중량 평균 분자량은 50만 내지 250만, 바람직하게는 60만 내지 200만 정도로 조정하는 것이 바람직한 것이다.
또한, 여기에서 중량 평균 분자량 및 분자량 분포는, 겔 투과 크로마토그래피(GPC)를 사용하여 측정되는 값이며, 측정 샘플을 테트라히드로푸란으로 용해하고, 0.45㎛φ의 멤브레인 필터를 통과하는 가용분에 대하여 행하며, 폴리스티렌 환산으로 산출한다.
본 발명의 점착제층에는, 실온(25℃)에서 액상 혹은 페이스트상인 성분을 포함하는 것이다. 실온에서 액상 혹은 페이스트상인 성분은, 점착제층에 유연성을 부여하여, 당해 점착제가 피부와 접촉한 경우에, 피부 자극성을 저감하기 위한 것이다.
이와 같은 실온에서 액상 혹은 페이스트상인 성분으로서는, 아크릴계 공중합체와 상용하는 것이면 특별히 제한은 없다. 예를 들어, 프탈산, 말레산, 아디프산, 스테아르산이나 각종 지방산과 알킬알코올의 에스테르류, 에틸렌글리콜, 글리세린 등의 다가 알코올의 에스테르류 등을 사용할 수 있다. 보다 구체적으로는, 1가의 알코올의 에스테르로서는, 디부틸프탈레이트, 디-2-에틸헥실프탈레이트, 디부틸아디페이트, 디-2-에틸헥실세바케이트, 디부틸말레에이트, 미리스트산에틸, 미리스트산이소프로필, 팔미트산이소프로필, 스테아르산부틸, 이소스테아르산이소프로필, 라우르산헥실, 락트산세틸, 락트산미리스틸, 프탈산디에틸, 미리스트산옥틸도데실, 올레산옥틸도데실, 디메틸옥탄산헥실데실, 2-에틸헥산산세틸, 2-에틸헥산산이소세틸, 2-에틸헥산산스테아릴, 숙신산디옥틸 등을 들 수 있다. 또한, 2가 이상의 알코올의 에스테르로서는, 디카프릴산프로필렌글리콜, 디카프르산프로필렌글리콜, 디이소스테아르산프로필렌글리콜, 모노카프릴산글리세릴, 트리카프릴산글리세릴, 트리-2-에틸헥산산글리세릴, 트리카프르산글리세릴, 트리라우르산글리세릴, 트리이소스테아르산글리세릴, 트리올레산글리세릴, 트리-2-에틸헥산산트리메틸올프로판 등을 1종 혹은 2종 이상 병용하여 사용할 수 있다. 이와 같은 실온에서 액상 혹은 페이스트상인 성분은 피부 접착재의 다른 요인 등에 의해 적절히 결정할 수 있지만, 아크릴계 공중합체와의 상용성의 관점에서, 카르복실산에스테르, 더욱 바람직하게는 글리세린지방산에스테르, 보다 더욱 바람직하게는 포화 지방산의 글리세린에스테르가 적합하게 사용된다.
또한, 상기 지방산으로서, 카프릴산, 카프르산, 2-에틸헥실산 등의 포화 지방산을 들 수 있고, 이들 단독 혹은 2 이상을 사용할 수 있다. 이들 포화 지방산은 불포화 이중 결합을 갖지 않으므로, 점착제, 즉 점착제층의 산화 열화를 방지할 수 있다.
포화 지방산으로서 상술한 바와 같이 카프릴산 등을 사용한 경우, 각종 포화 지방산과 알코올의 에스테르류로서, 트리카프릴산글리세릴이나 트리카프르산글리세릴, 트리-2-에틸헥산산글리세릴이 얻어진다. 이들 카르복실산에스테르 중에서도, 아크릴계 공중합체와의 상용성 등의 면에서는, 특히 트리카프릴산글리세릴을 사용하는 것이 바람직하다.
또한, 아크릴계 공중합체와, 상기 카르복실산에스테르 등의 실온에서 액상 혹은 페이스트상인 성분의 함유 비율은, 예를 들어 아크릴계 공중합체의 100질량부에 대하여 20질량부 내지 100질량부인 것이 바람직하다. 당해 성분의 함유 비율이, 상기 범위에 있음으로써, 점착제층에 충분한 유연성을 부여할 수 있기 때문에, 양호한 피부 접착성을 가짐과 함께, 피부로부터 접착재를 박리할 때의 물리적인 피부 자극을 억제하여, 양호한 박리성을 실현할 수 있다.
본 발명의 피부 접착재를 구성하는 점착제층에는, 적당한 응집력을 부여하기 위해 가교 처리를 실시하는 것이 바람직하다. 가교 처리로서는, 전자선이나 γ선, X선 등의 전리성 방사선의 조사에 의한 물리적 가교와, 가교제에 의한 화학적 가교가 있지만, 취급성이나 재현성 좋게 가교를 실시한다는 관점에서 가교제에 의한 화학적 가교 처리를 실시하는 것이 바람직하다. 예를 들어, 점착제층을 구성하는 재료를 배합한 점착제 조성물에 가교제를 첨가하고, 가열 처리함으로써 가교 처리가 실시된다. 이와 같은 가교제로서는, 이소시아네이트계 가교제, 과산화물계 가교제, 금속 킬레이트계 가교제 등 가교 처리할 때에 사용되는 가교제를 사용할 수 있다.
상기와 같이 하여 가교 처리를 실시한 점착제층은, 가교 정도에 따라서 적당한 피부 접착성과 응집성의 밸런스를 유지하는 것이지만, 아크릴계 공중합체의 분자량이나 분자량 분포도 이들의 조정에 대하여 영향을 주는 것이다.
점착제층의 두께는 특별히 한정되는 것은 아니고, 본 발명의 피부 접착재의 용도나, 접착하는 피부의 적용 개소 등에 따라서 적절하게 설정할 수 있다. 일례로서, 바람직하게는 10 내지 100㎛ 정도로 할 수 있고, 보다 바람직하게는 16 내지 50㎛로 할 수 있고, 더욱 바람직하게는, 20 내지 35㎛ 정도로 할 수 있다. 이에 의해, 피부면에 대하여 적당한 점착력을 부여할 수 있다.
본 발명에 있어서의 피부 접착재는, 점착제층의 표면의 오염을 방지하기 위해, 사용할 때까지 점착제층 표면을 박리 라이너로 피복해 둔다. 이 박리 라이너는, 일반적으로 피부나 피부에 접착하는 점착 테이프에 사용되는 것을 사용할 수 있다. 구체적으로는, 상질지, 글라신지, 파치먼트지 등의 표면에, 실리콘 수지나 불소 수지 등의 박리 성능을 갖는 박리제를 코팅한 것이나, 상질지에 수지를 앵커 코트한 것, 또는 폴리에틸렌 라미네이트한 것 등의 표면에 실리콘 수지나 불소 수지 등의 박리 성능을 갖는 박리제를 코팅한 것을 사용할 수 있다.
또한, 특별히 도시하지 않지만, 본 발명의 피부 접착재는, 상술한 기재 필름의, 점착제층이 형성된 면과 반대측의 면에 있어서, 담지 필름을 박리 가능하게 적층할 수 있다.
담지 필름의 소재로서는, 플라스틱 필름(예를 들어 폴리에틸렌, 폴리프로필렌, 폴리에스테르 및 이들의 적층 복합체 등), 종이(예를 들어 상질지, 크라프트지 등) 등을 바람직한 것으로서 들 수 있다. 이들 중에서도 투명성을 갖는 플라스틱 필름은, 접착 장소를 피부 접착재를 통해 보면서 접착할 수 있기 때문에, 카테터 등의 의료 기구를 고정할 때에는, 그의 유용성이 특히 현저해진다. 담지 필름을 기재 필름의 배면에 박리 가능하게 접합하기 위해서는, 인플레이션 성형, 압출 라미네이트 성형, 적층 성형, 캐스팅 등, 공지의 방법을 사용할 수 있다.
담지 필름의 두께는, 소재에 따라서도 상이하지만, 통상 15 내지 200㎛ 정도가 바람직하고, 20 내지 100㎛ 정도가 보다 바람직하다.
또한, 특별히 도시하지 않지만, 본 발명의 피부 접착재는, 상술한 바와 같이 담지 필름에 적층한 상태에서 권회시켜, 권회체로 할 수도 있다.
다음에, 본 발명의 피부 접착재의 제조 방법의 일례를 이하에 나타내지만, 전혀 이들에 한정되는 것은 아니다.
처음에, 예를 들어 (메트)아크릴산알킬에스테르 단량체, 알콕시기 함유 에틸렌성 불포화 단량체 및 필요에 따라서 카르복실기 함유 에틸렌성 불포화 단량체를 포함하는 단량체 혼합물을, 유기 용제 중에서 통상의 라디칼 중합에 의해 공중합 반응시켜 아크릴계 공중합체 용액을 제조한다. 다음에, 이 아크릴계 공중합체 용액의 고형분(아크릴계 공중합체) 100질량부에 대하여 20 내지 100질량부의 카르복실산에스테르 등의, 실온에서 액상 혹은 페이스트상인 성분, 나아가 필요에 따라서, 가교제 등을 배합하여 점착제 조성물의 용액을 제조한다.
계속해서, 얻어진 점착제 용액을 박리 라이너의 박리 처리면의 전체면, 또는 부분적으로 도포한다. 부분적으로 도포하는 경우에는, 예를 들어 도트 형상 또는 라인 형상으로 도포하는 것이 바람직하다. 라인 형상의 경우, 예를 들어 직선 형상 도포 또는 물결 형상 도포 등을 들 수 있지만, 기체의 통기로로서 기능하는 공간, 즉 라인간 공간이 확보되어 있으면, 어느 형상이어도 된다. 물결 형상 도포는, 피부에 접착 중인 라인간 공간의 단면적의 경시적인 변화가 적기 때문에 바람직하다. 박리 라이너에 도포된 점착제 용액을 건조한 후, 담지 필름을 적층한 폴리우레탄엘라스토머 필름을 접합하여, 피부 접착재를 얻는다.
[실시예]
이하에 실시예를 들어 본 발명을 더욱 구체적으로 설명하지만, 이들 실시예는 본 발명을 한정하는 것은 아니다. 또한, 이하에서, 「부」 및 「%」는, 각각 「질량부」 및 「질량%」를 의미한다.
(실시예 1)
이소노닐아크릴레이트 65부, 2-메톡시에틸아크릴레이트 30부, 아크릴산 5부를 포함하는 단량체 혼합물을 공중합 반응하여 얻어진 아크릴계 공중합체의 용액에, 아크릴계 공중합체 100부에 대하여, 트리카프릴산글리세릴 60부, 가교제로서의 3관능성 이소시아네이트 화합물 0.04부를 배합하여 균일한 점착제 용액을 제작하였다.
다음에, 이 용액을 편면에 실리콘 박리 처리한 박리 라이너의 박리 처리면에, 건조 후의 두께가 26㎛가 되도록 도포, 건조하여 점착제층을 형성하였다. 이 점착제층을, 두께 8㎛의 폴리우레탄엘라스토머 필름에, 두께 40㎛의 폴리프로필렌 필름(담지 필름)이 박리 가능하게 적층된 적층 필름의 폴리우레탄엘라스토머 필름면에 접합하여, 실시예 1의 피부 접착재를 얻었다.
(비교예 1)
두께 8㎛의 폴리우레탄엘라스토머 필름을 두께 30㎛의 폴리우레탄엘라스토머 필름, 그리고, 건조 후의 점착제층 두께를 30㎛로 변경한 것 이외는 실시예 1과 마찬가지로 하여, 비교예 1의 피부 접착재를 얻었다.
(투습도)
실시예 1 및 비교예 1의 각 피부 접착재에 대하여, 구경 38㎜의 유리 용기에 정제수 10mL를 넣고, 유리 용기의 입구를 박리 라이너 및 담지 필름을 박리한 피부 접착재로 덮고, 유리 용기의 입구 부분 외주에 점착 테이프를 감아 밀봉 시일하였다. 이 유리 용기의 중량을 측정한 후, 이것을 온도 40℃, 습도 30%RH의 조건 하에서 24시간 보존하였다. 24시간 보존 후, 유리 용기의 중량을 측정하고, 보존 전후의 중량차로부터, 수증기가 투과한 양을 구하였다. 이 값으로부터 시험편의 1㎡당의 투습량(투습도)을 산출하였다(n=3의 평균값).
(접착 시의 관능 평가)
실시예 1 및 비교예 1의 각 피부 접착재에 대하여, 실험 자원자 5인의 전완부에, 폭 50㎜×길이 50㎜의 직사각 형상으로 재단한 피부 접착재를 박리 라이너를 박리한 후, 점착제층면을 접착하였다. 계속해서, 담지 필름을 박리하고, 이 상태에서, 실온에서 3시간 경과하였을 때의, 접착 개소의 당기는 느낌, 피부 접착재의 단부의 들뜸 상태, 땀차기의 정도를 3단계로 평가하였다. 또한, 피부 접착재를 박리하였을 때의 통증의 정도를 3단계로 평가하였다.
(당기는 느낌)
3 : 당기는 느낌이 없음, 2 : 약간 당기는 느낌이 있음, 1 : 당기는 느낌이 있음
(들뜸 상태)
3 : 들뜸 없음, 2 : 단부에 약간 들뜸 있음, 1 : 절반 이상 들뜸 있음
(통증의 정도)
3 : 아프지 않음, 2 : 약간 통증 있음, 1 : 통증 있음
(땀차기의 정도)
3 : 접착 개소에 땀이 차지 않음, 2 : 접착 개소에 약간 땀이 참, 1 : 접착 개소에 땀이 참
결과를 표 1, 표 2에 나타낸다.
실시예 1의 피부 접착재는, 접착되어 있는 동안, 땀차기도 발생하지 않고, 단부의 들뜸도 보이지 않아 양호한 피부 접착성을 나타냈다. 또한, 실시예 1의 피부 접착재는, 피부의 움직임에 대하여 양호한 추종성을 나타내어, 당기는 느낌이 거의 없고, 접착되어 있는 것을 느끼지 않도록 하는 양호한 피트감이었다. 또한, 실시예 1의 피부 접착재는, 양호한 피부 접착성을 나타내고 있음에도 불구하고, 박리할 때의 점착제 잔류도 없고, 박리 시의 물리적인 피부 자극(통증)이 거의 없는 것이었다.
한편, 비교예 1의 피부 접착재는 접착 중에 당기는 느낌이 있고, 접착되어 있는 것이 느껴지는 것이었다. 또한, 비교예 1의 피부 접착재는 접착 개소에 땀이 차는 경우가 있었다.
(실시예 2)
이소노닐아크릴레이트 65부, 2-메톡시에틸아크릴레이트 30부, 아크릴산 5부를 포함하는 단량체 혼합물을 공중합 반응하여 얻어진 아크릴계 공중합체의 용액에, 아크릴계 공중합체 100부에 대하여, 트리카프릴산글리세릴 60부, 가교제로서의 3관능성 이소시아네이트 화합물 0.13부를 배합하여 균일한 점착제 용액을 제작하였다.
다음에, 이 용액을 편면에 실리콘 박리 처리한 박리 라이너의 박리 처리면에, 건조 후의 두께가 23㎛가 되도록 도포, 건조하여 점착제층을 형성하였다. 이 점착제층을, 두께 8㎛의 폴리우레탄엘라스토머 필름(기재 필름)에, 두께 40㎛의 폴리프로필렌 필름(담지 필름)이 박리 가능하게 적층된 적층 필름의 폴리우레탄엘라스토머 필름면에 접합하여, 실시예 2의 피부 접착재를 얻었다.
(실시예 3 내지 5, 비교예 2 내지 3)
폴리우레탄엘라스토머 필름의 두께 및 건조 후의 점착제층의 두께를 표 3에 기재하는 바와 같이 변경한 것 이외는 실시예 2와 마찬가지로 하여, 실시예 3 내지 5 및 비교예 2 내지 3의 피부 접착재를 얻었다.
(비교예 4)
트리카프릴산글리세릴 및 가교제로서의 3관능성 이소시아네이트 화합물을 배합하지 않고 균일한 점착제 용액을 제작한 것 이외는 실시예 2와 마찬가지로 하여, 비교예 4의 피부 접착재를 얻었다.
(비교예 5)
두께 8㎛의 폴리우레탄엘라스토머 필름을, 두께 6㎛의 폴리에틸렌테레프탈레이트 필름으로 바꾼 것 이외는 실시예 2와 마찬가지로 하여, 비교예 5의 피부 접착재를 얻었다.
실시예 2 내지 5 및 비교예 2 내지 5의 피부 접착재에 대하여, 표 3에 통합하여 나타낸다.
(모듈러스)
실시예 2 내지 5 및 비교예 2 내지 5의 피부 접착재에 대하여, 피부 접착재를 폭 10㎜×길이 100㎜의 직사각 형상으로 재단하고, 박리 라이너를 박리한 후, 인장 시험기의 척간이 40㎜가 되도록 장착하였다. 다음에, 담지 필름을 박리한 후, 속도 300㎜/분으로 인장하여, 신장률이 10%, 30%, 100%일 때의 하중(N/10㎜)을 판독하였다(n=3의 평균값).
(투습도)
실시예 2 내지 5 및 비교예 2 내지 5의 피부 접착재에 대하여, 실시예 1 및 비교예 1의 피부 접착재와 마찬가지로 하여 투습도를 측정하였다.
(끈적거림)
실시예 2 내지 5 및 비교예 2 내지 5의 피부 접착재에 대하여, 피부 접착재를 폭 19㎜×길이 약 70㎜의 직사각 형상으로 재단하고, 박리 라이너를 박리한 후, 피험자의 손가락의 제1 관절부터 제2 관절에 걸쳐 감은 후, 담지 필름을 박리하였다. 손바닥으로 피부 접착재를 30초간 누르고, 그 후 피부 접착재를 감은 상태에서 5분간 경과 후, 피부 접착재를 박리하였을 때의 끈적거림 상태를 5단계로 평가하였다(n=5의 평균값).
5점 : 접착하기 전과 변함없이 끈적거림이 발생하지 않음
4점 : 약간 유상 성분을 느낌
3점 : 약간 끈적거리는, 점착분을 느낌
2점 : 눈으로 보아 약간의 점착제 잔류가 있음
1점 : 눈으로 보아 명백한 점착제 잔류가 있음
(박리 시의 통증)
실시예 2 내지 5 및 비교예 2 내지 5의 피부 접착재에 대하여, 피부 접착재를 폭 19㎜×길이 약 70㎜의 직사각 형상으로 재단하고, 박리 라이너를 박리한 후, 피험자의 손가락의 제1 관절부터 제2 관절에 걸쳐 감은 후, 담지 필름을 박리하였다. 손바닥으로 피부 접착재를 30초간 누르고, 그 후 피부 접착재를 감은 상태에서 5분간 경과 후, 피부 접착재를 박리하였을 때의 통증을, 도 1의 Face Pain Scale에 따라 5단계로 평가하였다(n=5의 평균값).
<평가점>
5점 : 통증을 느끼지 않음
4점 : 약간 통증을 느낌
3점 : 견딜 수 있을 정도의 통증을 느낌
2점 : 뚜렷이 통증을 느낌
1점 : 견디기 어려운 통증을 느낌
결과를 표 4에 나타낸다.
실시예 2 내지 5의 피부 접착재는 낮은 모듈러스를 나타내기 때문에, 접착되어 있는 것을 잊어버리도록 하는 양호한 피트감을 가짐과 함께, 높은 투습도를 나타내기 때문에 접착 시에 있어서의 땀차기가 발생하기 어려운 것이었다. 또한, 실시예 2 내지 5의 피부 접착재는, 접착 후의 끈적거림이나 박리 시의 통증에 대하여 양호한 결과를 나타내고, 접착 시의 소양감이 발생하기 어렵고 박리 시의 물리 자극을 억제하여, 피부에 친화적인 특성을 갖는 것이었다.
한편, 비교예 2, 3의 피부 접착재는 실시예 2 내지 5의 피부 접착재와 비교하여 높은 모듈러스를 갖고, 접착 시의 피트감이 떨어지는 경향을 나타내고, 또한 투습도가 약간 낮아, 끈적거림이 발생하기 쉬운 경향을 나타냈다. 비교예 5의 피부 접착재는, 명백하게 높은 모듈러스를 갖고, 접착 시의 피트감이 나쁘고, 또한 투습도도 낮아, 끈적거림이 발생하기 쉬운 것이었다.
실시예 2의 피부 접착재와 비교예 4의 피부 접착재는, 액상 혹은 페이스트상인 성분의 유무에 의한 차이이지만, 실시예 2의 피부 접착재에서는 액상 혹은 페이스트상인 성분이 포함되어 있음으로써, 박리 시의 통증을 경감한다는 효과뿐만 아니라, 투습도의 향상이라는 예기치 못한 효과가 나타나, 끈적거림의 평가점이 높은 값을 나타내었다고 생각된다.
이상, 본 발명을 상기 구체예에 기초하여 상세하게 설명하였지만, 본 발명은 상기 구체예에 한정되는 것은 아니고, 본 발명의 범주를 일탈하지 않는 한에 있어서, 모든 변형이나 변경이 가능하다.
Claims (9)
- 폴리우레탄엘라스토머 필름의 한쪽의 면에 점착제층이 형성되고, 상기 점착제층의 점착면을 덮어 박리 가능하게 적층된 박리 라이너를 갖는 피부 접착재이며,
상기 폴리우레탄엘라스토머 필름의 두께는 1 내지 9㎛이고,
상기 점착제층은, 아크릴계 공중합체와, 실온에서 액상 혹은 페이스트상인 성분을 포함하는 것을 특징으로 하는, 피부 접착재. - 제1항에 있어서, 상기 실온에서 액상 혹은 페이스트상인 성분이 카르복실산에스테르인 것을 특징으로 하는, 피부 접착재.
- 제2항에 있어서, 상기 카르복실산에스테르가 포화 지방산의 글리세린에스테르인 것을 특징으로 하는, 피부 접착재.
- 제3항에 있어서, 상기 포화 지방산이 카프릴산, 카프르산 및 2-에틸헥실산으로 이루어지는 군에서 선택된 적어도 1종인 것을 특징으로 하는, 피부 접착재.
- 제2항 내지 제4항 중 어느 한 항에 있어서, 상기 카르복실산에스테르가 트리카프릴산글리세릴, 트리카프르산글리세릴 및 트리-2-에틸헥산산글리세릴로 이루어지는 군에서 선택된 적어도 1종인 것을 특징으로 하는, 피부 접착재.
- 제1항 내지 제5항 중 어느 한 항에 있어서, 상기 아크릴계 공중합체가 (메트)아크릴산알킬에스테르 단량체 및 알콕시기 함유 에틸렌성 불포화 단량체를 포함하는 단량체 혼합물로부터 얻어지는 아크릴계 공중합체를 함유하는 것을 특징으로 하는, 피부 접착재.
- 제1항 내지 제6항 중 어느 한 항에 있어서, 상기 점착제층은, 상기 아크릴계 공중합체 100질량부에 대하여 실온에서 액상 혹은 페이스트상인 성분을 20 내지 100질량부 포함하는 것을 특징으로 하는, 피부 접착재.
- 제1항 내지 제7항 중 어느 한 항에 있어서, 상기 폴리우레탄엘라스토머 필름의 다른 쪽의 면을 덮어 박리 가능하게 적층된 담지 필름을 갖는 것을 특징으로 하는, 피부 접착재.
- 제8항에 기재된 피부 접착재를 권회하여 이루어지는 것을 특징으로 하는, 피부 접착재 권회체.