JP7473485B2 - 皮膚貼付材 - Google Patents
皮膚貼付材 Download PDFInfo
- Publication number
- JP7473485B2 JP7473485B2 JP2020569627A JP2020569627A JP7473485B2 JP 7473485 B2 JP7473485 B2 JP 7473485B2 JP 2020569627 A JP2020569627 A JP 2020569627A JP 2020569627 A JP2020569627 A JP 2020569627A JP 7473485 B2 JP7473485 B2 JP 7473485B2
- Authority
- JP
- Japan
- Prior art keywords
- adhesive layer
- substrate
- skin
- skin patch
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
このようなデバイスの貼り付けには、粘着性を有するテープ状の皮膚貼付材が用いられる場合がある。
本発明の皮膚貼付材の一態様において、基材の粘着剤層を備える面の反対側の面に、他の粘着剤層をさらに備えてもよい。
本発明の皮膚貼付材の一態様において、粘着剤層はドット状、格子状、直線状、又は波線状に形成されていてもよい。
本発明の皮膚貼付材の一態様において、粘着剤層はアクリル系共重合体を含んでもよい。
本発明の皮膚貼付材の一態様において、アクリル系共重合体は、(メタ)アクリル酸アルキルエステル単量体とアルコキシ基含有エチレン性不飽和単量体とを含む単量体混合物を共重合して得られるアクリル系共重合体であってもよい。
本発明の皮膚貼付材の一態様において、発泡体シートの気泡率が70~98.5%であってもよい。
本実施形態の一態様にかかる皮膚貼付材の概略側面図を図1に示す。本態様の皮膚貼付材1は、基材(支持体)2と、粘着剤層3とを有する皮膚貼付材である。
また、本態様において、粘着剤層3は、基材2の片面に部分的に形成されている。なお、以下において、基材2の、部分的に形成された粘着剤層3を備える側の面を「第1の面」と記載し、第1の面の反対側の面を「第2の面」と記載する場合がある。
本態様の皮膚貼付材1は、この粘着剤層3を介して皮膚に貼着される。すなわち、本態様の皮膚貼付材1は、皮膚側の面に粘着剤層3が形成されていない部分を備える。
上記の構成を有する本態様の皮膚貼付材1においては、皮膚から発生した汗等の水分が、粘着剤層3が形成されていない部分を通って基材2の第1の面に到達し、連続気泡内を通って基材2の端面や第2の面から外部に脱出できる。すなわち、本態様の皮膚貼付材1は、水分の透過性に優れる。したがって、本態様の皮膚貼付材1は、汗等の水分による剥離や不快感、皮膚刺激の発生が抑制されている。
一方、皮膚貼付材の強度を確保する観点からは、基材(発泡体シート)の気泡率は、98.5%以下が好ましく、97.5%以下がより好ましい。
このように両面が粘着面である本態様の皮膚貼付材11を用いると、以下に説明するように、特にはがれにくく、不快感及び皮膚刺激を抑制して皮膚15にウェアラブルデバイス16を装着することができるため好ましい。
一方、基材が厚すぎると、基材が割れやすくなる恐れやズレやすくなる恐れがある。したがって、基材(発泡体シート)の厚みは、3.000mm以下が好ましく、2.000mm以下がより好ましく、1.000mm以下が更に好ましい。
一方、皮膚貼付材の強度を確保する観点からは、基材の密度は小さすぎないことが好ましい。したがって、基材(発泡体シート)の密度は、0.15g/cm3以上が好ましく、0.2g/cm3以上がより好ましく、0.25g/cm3以上が更に好ましい。
ここで、伸縮性を向上させる観点から、基材(発泡体シート)は、破断強度が20N/20mm以下が好ましく、10N/20mm以下がより好ましく、5N/20mm以下が更に好ましく、また、破断伸びが100%以上が好ましく、200%以上がより好ましく、250%以上が更に好ましい。
基材の製造方法も特に限定されず、例えば適宜公知の方法により製造することができる。
なお、上記はあくまで例示であり、粘着剤層3の構成はこれらに限定されない。
上記より、粘着剤層(第1の粘着剤層)の厚みは50μm以上が好ましく、60μm以上がより好ましく、また、120μm以下が好ましく、100μm以下がより好ましい。
なお、この場合において、第2の粘着剤層は、基材の第2の面に部分的に形成されていてもよく、あるいは基材の第2の面の全体に形成されていてもよい。
また、第2の粘着剤層を形成する粘着剤としては、例えば、第1の粘着剤層を形成する粘着剤として例示したアクリル系粘着剤、ゴム系粘着剤、ウレタン系粘着剤、シリコーン系粘着剤等を使用可能であるが、これに限定されるものではない。
また、本実施形態の皮膚貼付材は、粘着剤層の表面の汚染を防ぐため、使用時まで粘着剤層が保護されていることが好ましい。粘着剤の保護の方法としては、例えば、粘着剤層に剥離ライナーを貼り合せて保護する方法が挙げられる。また、片面のみが粘着面である場合は、基材の粘着剤層が形成されていない面を剥離処理し、当該面に粘着剤層を貼り合せるようにして皮膚貼付材を巻回して粘着剤層を保護してもよい。加えて、両面が粘着面である場合は、両面に剥離処理面を有する剥離ライナーの一方の剥離処理面を一方の粘着面に貼り合わせた上で、該剥離ライナーの他方の剥離処理面が他方の粘着面に接触するように皮膚貼付材を巻回して両粘着剤層を保護してもよい。
本実施形態の皮膚貼付材の製造方法は特に限定されない。例えば、粘着剤層と基材を別々に形成した後これらを貼り合せてもよいし、あるいは基材上に粘着剤の溶液を塗布し、乾燥することにより粘着剤層を形成してもよい。
また、当初から基材上の一部にのみ粘着剤層を形成して部分的な粘着剤層を形成してもよく、当初は基材上の全体に粘着剤層を形成してその後部分的に粘着剤層を除去することにより部分的な粘着剤層を形成してもよい。
(基材1)
スチレン-ブタジエン共重合体混合物(商品名:AH748-M4、株式会社イーテック製)75gに、加硫促進剤(商品名:CLFB-2、株式会社イーテック製)2.88gを添加した後、攪拌機を用いて1800rpmの回転速度で5分間撹拌した。この溶液を剥離処理されたポリエチレンテレフタレートフィルム(商品名:ダイヤホイルMRF38、三菱ケミカル株式会社製)の剥離処理面に乾燥後の厚みが0.325mmになるように塗布した後、130℃で10分間乾燥し、その後塗布面にプラズマ処理を行い、基材1を得た。なお、基材1は連続気泡を有する多孔質シートであった。
基材2として、ポリウレタン発泡体シート(商品名:HYDROPHILIC FORM1012、Freudenberg社製)を用意した。なお、基材2は連続気泡を有する多孔質シートであった。
基材3として、ポリプロピレン発泡体シート(商品名:FOLEC OPN 1.0t、株式会社イノアックコーポレーション製)を用意した。なお、基材3は連続気泡を有する多孔質シートであった。
スチレン-ブタジエン共重合体混合物(商品名:AH748-M4、株式会社イーテック製)100gに、加硫促進剤(商品名:CLFB-2、株式会社イーテック製)3.84gを添加した以外は基材1と同様にして、基材4を得た。なお、基材4は連続気泡を有する多孔質シートであった。
ポリエチレン発泡体シート(商品名:ボラーラXL-H#03001(80)、積水化学工業株式会社製)にコロナ処理を施して基材5を得た。なお、基材5は連続気泡を有さず、独立気泡のみを有する多孔質シートであった。
基材6として、ポリエチレンテレフタレート不織布シート(商品名:ソンタラ#8010、デュポン株式会社製)を用意した。
ポリウレタンフィルム(商品名:エスマーURS-210、日本マタイ株式会社製)にコロナ処理を施して基材7を得た。
上記基材1~7について、以下のようにして厚み、密度、気泡率、破断強度、破断伸びを測定した。
各基材について、ダイヤルゲージを用いて5点の厚みを測定し、測定結果の平均値を各基材の厚みとした。
各基材を5cm×5cmに切断して、重量を測定した。測定された重量と、上記の厚みとを用いて、下記式により密度を算出した。
密度(g/cm3)=重量(g)/(5×5×厚み(cm3))
下記式により各基材の気泡率を算出した。
気泡率(%)=(1×基材材料の比重-密度)×100
各基材を幅20mm、長さ100mmに切断し、引張試験機(商品名:オートグラフAG-IS、株式会社島津製作所製)にチャック間距離40mmで設置して引張り速度300mm/minで引っ張り、破断した際の荷重と伸びを測定した。同様の測定を3回行い、平均値を各基材の破断強度、破断伸びとした。
(実施例1)
アクリル系共重合体(イソノニルアクリレート:2-メトキシエチルアクリレート:アクリル酸=65部:30部:5部からなる共重合体)100部に、トリカプリル酸グリセリル20部、粘着付与剤としてのロジンエステル類(商品名:ハリタックPCJ、ハリマ化成株式会社製)10部、架橋剤としての三官能性イソシアネート化合物(商品名:コロネートHL、東ソー株式会社製)0.07部をトルエン中にて配合して均一な粘着剤溶液を作製した。
次に、この粘着剤溶液を剥離紙(商品名:KP-64シロマルD マルミズ、リンテック株式会社製)の剥離処理面に、乾燥後の厚みが70μmとなるように塗布し、幅0.5mm、振幅50mm、周期140mm、ピッチ5mmの波状の溝を設けた後、130℃で3分間乾燥して粘着剤層を形成した。次いで、形成した粘着剤層を基材1のプラズマ処理面に転写して貼り合わせ、60℃で72時間放置し、実施例1の皮膚貼付材を得た。
基材1にかえて基材2を使用した以外は実施例1と同様にして、実施例2の皮膚貼付材を得た。
基材1にかえて基材3を使用した以外は実施例1と同様にして、実施例3の皮膚貼付材を得た。
基材1にかえて基材4を使用した以外は実施例1と同様にして、比較例1の皮膚貼付材を得た。
基材1にかえて基材5を使用した以外は実施例1と同様にして、比較例2の皮膚貼付材を得た。
粘着剤層に溝を設けなかった以外は実施例1と同様にして、比較例3の皮膚貼付材を得た。
基材1にかえて基材6を使用した以外は実施例1と同様にして、比較例4の皮膚貼付材を得た。
基材1にかえて基材7を使用した以外は実施例1と同様にして、比較例5の皮膚貼付材を得た。
各例の皮膚貼付材について、以下のようにして水分減少率を測定し、また、貼付感を評価した。
各例の皮膚貼付材を30mm×30mmに切断して試験サンプルを製造した。
また、コラーゲン膜を精製水に10分間浸漬し、取り出して表面の水をふき取り、両面テープによりベーク板に貼り合せた。ベーク板に貼り合せた直後のコラーゲンの表面の水分量を測定し、初期水分率とした。
次いで、試験サンプルの粘着剤層をコラーゲン膜に貼り合わせ、23℃で8時間放置し、その後剥離した。剥離後、コラーゲン膜の試験サンプルが貼り合わされていた部分の水分量を測定し、保存後水分量とした。
なお、水分量の測定にはCorneometer CM825(株式会社インテグラル製)を用いた。また、コラーゲン膜とベーク板の貼り合せ、及び、コラーゲン膜と試験サンプルの貼り合せの際にはハンドローラーを用いた。
上記のようにして測定された初期水分量、及び保存後水分量を用いて、下記式(1)により水分減少率を算出した。
水分減少率(%)=[(初期水分量-保存後水分量)/初期水分量]×100 (1)
各例の皮膚貼付材を10mm×50mmに切断して試験サンプルを製造した。
次いで、剥離紙をはがした試験サンプルの粘着剤層を被験者の人差し指の関節部分に貼付した。その後被験者が人差し指を曲げ、以下の基準で貼付感を評価した。
5:まったくツッパリ感を感じない
4:気にならない程度のツッパリ感を感じる
3:少し気になるが生活できる程度のツッパリ感を感じる
2:気になるが、剥がさずに耐えて生活できる程度のツッパリ感を感じる
1:剥がさなくては耐えられない程度のツッパリ感を感じる
たとえ連続気泡を有する発泡体シートを基材として使用したとしても、その一方の面の全体に粘着剤層を形成した比較例3では、水分減少率が特に小さかった。したがって、比較例3の皮膚貼付材は、汗による剥がれや不快感、皮膚刺激が特に生じやすい。
また、連続気泡を有するが気泡率が70%未満である発泡体シートを基材として使用した比較例1では、水分減少率が十分ではなかった。したがって、比較例1の皮膚貼付材は、汗による剥がれや不快感、皮膚刺激が生じるおそれがある。
発泡体シートではなく不織布を基材として使用した比較例4では、貼付感の評価結果が悪かった。したがって、比較例4の皮膚貼付材は、皮膚の伸縮による剥がれや不快感、皮膚刺激が生じやすい。
発泡体シートではなくウレタンフィルムを基材として使用した比較例5では、水分減少率が特に小さかった。したがって、比較例5の皮膚貼付材は、汗による剥がれや不快感、皮膚刺激が特に生じやすい。
一方、実施例1~3では、水分減少率が大きく、貼付感の評価結果も良好であった。したがって、実施例1~3の皮膚貼付材は、汗や皮膚の伸縮による剥がれや不快感、皮膚刺激が生じにくい。
2、12、22 基材
3、13、23 粘着剤層(第1の粘着剤層)
14 他の粘着剤層(第2の粘着剤層)
15、25 皮膚
16、26 ウェアラブルデバイス
Claims (8)
- 基材と、粘着剤層とを有する皮膚貼付材であって、
前記基材は連続気泡を有し、気泡率が70%以上の発泡体シートからなり、
前記粘着剤層は前記基材の片面に部分的に形成されており、
前記粘着剤層はアクリル系共重合体及び粘着付与剤を含み、
前記粘着付与剤の含有量がアクリル系共重合体100質量部に対して5質量部~30質量部である、皮膚貼付材。 - 前記粘着付与剤がロジンエステル類を含む請求項1に記載の皮膚貼付材。
- 前記基材の前記粘着剤層を備える面の反対側の面に、他の粘着剤層をさらに備える請求項1又は2に記載の皮膚貼付材。
- 前記粘着剤層は波線状に形成されている請求項1~3のいずれか1項に記載の皮膚貼付材。
- 前記アクリル系共重合体は、(メタ)アクリル酸アルキルエステル単量体とアルコキシ基含有エチレン性不飽和単量体とを含む単量体混合物を共重合して得られるアクリル系共重合体である請求項1~4のいずれか1項に記載の皮膚貼付材。
- 前記(メタ)アクリル酸アルキルエステル単量体の含有量が40質量%~80質量%である請求項5に記載の皮膚貼付材。
- 前記アルコキシ基含有エチレン性不飽和単量体の含有量が20質量%~60質量%である請求項5又は6に記載の皮膚貼付材。
- 前記発泡体シートの気泡率が70~98.5%である請求項1~7のいずれか1項に記載の皮膚貼付材。