JPWO2019107500A1 - 導電性ペースト、電子部品、及び積層セラミックコンデンサ - Google Patents
導電性ペースト、電子部品、及び積層セラミックコンデンサ Download PDFInfo
- Publication number
- JPWO2019107500A1 JPWO2019107500A1 JP2019557328A JP2019557328A JPWO2019107500A1 JP WO2019107500 A1 JPWO2019107500 A1 JP WO2019107500A1 JP 2019557328 A JP2019557328 A JP 2019557328A JP 2019557328 A JP2019557328 A JP 2019557328A JP WO2019107500 A1 JPWO2019107500 A1 JP WO2019107500A1
- Authority
- JP
- Japan
- Prior art keywords
- conductive paste
- mass
- dispersant
- powder
- conductive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本実施形態の導電性ペーストは、導電性粉末、分散剤、バインダー樹脂及び有機溶剤を含む。以下、各成分について詳細に説明する。
導電性粉末は、特に限定されず、例えば、Ni、Pd、Pt、Au、Ag、Cu、およびこれらの合金から選ばれる1種以上の粉末を用いることができる。これらの中でも、導電性、耐食性及びコストの観点から、Ni、またはその合金の粉末が好ましい。Ni合金としては、例えば、Mn、Cr、Co、Al、Fe、Cu、Zn、Ag、Au、PtおよびPdからなる群より選択される少なくとも1種以上の元素とNiとの合金を用いることができる。Ni合金におけるNiの含有量は、例えば、50質量%以上、好ましくは80質量%以上である。また、Ni粉末は、脱バインダー処理の際、バインダー樹脂の部分的な熱分解による急激なガス発生を抑制するために、数百ppm程度のSを含んでもよい。
平均粒径=6/S.A×ρ・・・(式)
(ρ=8.9(ニッケルの真密度)、S.A=ニッケル粉末のBET比表面積)
導電性ペーストは、セラミック粉末を含んでもよい。セラミック粉末としては、特に限定されず、例えば、積層セラミックコンデンサの内部電極用ペーストである場合、適用する積層セラミックコンデンサの種類により適宜、公知のセラミック粉末が選択される。セラミック粉末としては、例えば、Ba及びTiを含むペロブスカイト型酸化物が挙げられ、好ましくはチタン酸バリウム(BaTiO3)である。なお、セラミック粉末は、1種類を用いてもよく、2種類以上を用いてもよい。
バインダー樹脂は、アセタール系樹脂を含む。アセタール系樹脂としては、ポリビニルブチラールなどのブチラール系樹脂が好ましい。バインダー樹脂がアセタール系樹脂を含む場合、グラビア印刷に適した粘度に調整することができ、かつ、グリーンシートとの接着強度をより向上させることができる。バインダー樹脂は、例えば、バインダー樹脂全体に対して、アセタール系樹脂を20質量%以上含んでもよいし、30質量%以上含んでもよいし、60質量%以上含んでもよいし、アセタール系樹脂のみからなってもよい。
有機溶剤は、グリコールエーテル系溶剤、及び、アセテート系溶剤のうち、少なくとも一つを含み、グリコールエーテル系溶剤を含むことが好ましい。
本実施形態の導電性ペーストは、酸系分散剤としてリンを含む酸系分散剤、中でもリン酸アルキルエステル化合物を含むことが好ましい。本発明者は、導電性ペーストに用いる分散剤について、種々の分散剤を検討した結果、上述したバインダー樹脂及び有機溶剤と併せて、リン酸アルキルエステル化合物を含む分散剤を用いることにより、その理由は不明であるが、内部電極を形成した際に塊状物の発生が非常に抑制され、ペーストの分散性が向上することを見出した。
本実施形態の導電性ペーストは、必要に応じて、上記の成分以外のその他の成分を含んでもよい。その他の成分としては、例えば、消泡剤、可塑剤、界面活性剤、増粘剤などの従来公知の添加物を用いることができる。
本実施形態の導電性ペーストの製造方法は、特に限定されず、従来公知の方法を用いることができる。導電性ペーストは、例えば、上記の各成分を、3本ロールミル、ボールミル、ミキサーなどで攪拌・混練することにより製造することができる。その際、導電性粉末表面に予め分散剤を塗布すると、導電性粉末が凝集することなく十分にほぐれて、その表面に分散剤が行きわたるようになり、均一な導電性ペーストを得やすい。また、予め、バインダー樹脂を有機溶剤の一部に溶解させて、有機ビヒクルを作製した後、ペースト調整用の有機溶剤へ、導電性粉末、セラミック粉末、分散剤、及び、有機ビヒクルを添加した後、攪拌・混練し、導電性ペーストを作製してもよい。
以下、本発明の電子部品等の実施形態について、図面を参照しながら説明する。図面においては、適宜、模式的に表現することや、縮尺を変更して表現することがある。また、部材の位置や方向などを、適宜、図1などに示すXYZ直交座標系を参照して説明する。このXYZ直交座標系において、X方向およびY方向は水平方向であり、Z方向は鉛直方向(上下方向)である。
(導電性ペーストの粘度)
導電性ペーストの製造後の粘度を、レオメーターを用いて、ずり速度100sec−1、10000sec−1の条件で測定した。
導電性ペーストの分散性を下記の方法により評価した。
ガラス基板(2inch)上に、サンプル(作製した導電性ペースト)を印刷し(GAP厚=5μm)、乾燥する。乾燥は、ベルト炉内の最大温度120〜150℃、大気雰囲気にて行った。乾燥後に得られた乾燥膜(2cm×2cm、厚さ3μm)を、光学顕微鏡を用いて、ガラス基板の裏面から光(バックライト)を当てながら、×100(接眼、対物;各10倍)で観察して(バックライト=ガラス基板の裏面から光を当てる)、塊状物の有無を確認した。塊状物が観察されない場合、導電性ペーストの分散性を「良好」である、塊状物が1以上観察される場合、導電性ペーストの分散性を「不良」である、と評価した。
(導電性粉末)
導電性粉末としては、Ni粉末(平均粒径0.3μm)を使用した。
セラミック粉末としては、チタン酸バリウム(BaTiO3;平均粒径0.06μm)を使用した。
バインダー樹脂としては、ポリビニルブチラール樹脂(PVB、アセタール系樹脂)、エチルセルロース(EC)を使用した。
(1)酸系分散剤(A)として、リン酸アルキルポリオキシアルキレン化合物を用いた。
(3)上記の酸系分散剤(A)以外の酸系分散剤(比較例用)として、リン酸ポリエステル(リン酸基を有するポリエステル)を主成分として含み、残部がリン酸であるリン酸系分散剤(E)を用いた。
有機溶剤としては、プロピレングリコールモノブチルエーテル(PNB、グリコールエーテル系溶剤)、ミネラルスピリット(MA)、ターピネオール(TPO)を使用した。
導電性粉末であるNi粉末100質量部に対して、セラミック粉末25質量部と、分散剤として酸系分散剤(A)0.28質量部と、バインダー樹脂として、EC4質量部と、PVB2質量部と、有機溶剤としてPNB48質量部およびMA21質量部と、を混合して導電性ペーストを作製した。作製した導電性ペーストの粘度及びペーストの分散性を上記方法で評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
[実施例2]
分散剤として、酸系分散剤(A)を0.5質量部とした以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
[実施例3]
分散剤として、酸系分散剤(A)を1.0質量部とした以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
分散剤として、酸系分散剤(A)0.28質量部およびロジンアミン(B)0.10質量部を混合した以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
分散剤として、酸系分散剤(A)0.28質量部およびポリエチレングリコールラウリルアミン(C)0.10質量部を混合した以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
[実施例6]
分散剤として、酸系分散剤(A)0.28質量部およびオレイルアミン(D)0.10質量部を混合した以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
[実施例7]
分散剤として、酸系分散剤(A)0.28質量部およびオレイルアミン(D)0.22質量部を混合した以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
[実施例8]
分散剤として、酸系分散剤(A)0.56質量部およびオレイルアミン(D)0.44質量部を混合した以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
[実施例9]
バインダー樹脂として、PVB6質量部のみを用いた以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
[実施例10]
有機溶剤としてPNB57質量部およびMS12質量部を用いた以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
分散剤として、リン酸ポリエステルを主成分として含むリン酸系分散剤(E)0.28質量部及び塩基系分散剤(B)0.10質量部を用いた以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
[比較例2]
有機溶剤としてターピネオール(TPO)のみを用いた以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
[比較例3]
バインダー樹脂としてECのみを用いた以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
[比較例4]
バインダー樹脂としてECのみ、有機溶剤としてターピネオールのみを用いた以外は、実施例1と同様に導電性ペーストを作製して、評価した。導電性ペーストの分散剤等の含有量を表1に、導電性ペーストの粘度、及び、分散性の評価結果を表2に示す。
実施例の導電性ペーストは、ずり速度100sec−1の粘度が0.34〜0.69Pa・Sであり、ずり速度10000sec−1の粘度が0.12〜0.19Pa・Sであり、グラビア印刷に適した粘度であった。また、本実施例の導電性ペーストは、印刷後の乾燥膜表面に塊状物が観察されず、ペーストの分散性に優れることが示された。
10 セラミック積層体
11 内部電極層
12 誘電体層
20 外部電極
21 外部電極層
22 メッキ層
Claims (13)
- 導電性粉末、分散剤、バインダー樹脂及び有機溶剤を含む導電性ペーストであって、
前記分散剤は、酸系分散剤であるリン酸アルキルエステル化合物を含み、
前記バインダー樹脂は、アセタール系樹脂を含み、
前記有機溶剤は、グリコールエーテル系溶剤を含む、
導電性ペースト。 - 前記酸系分散剤は、リン酸アルキルポリオキシアルキレン化合物である、請求項1に記載の導電性ペースト。
- 前記分散剤は、さらに塩基系分散剤を含む、請求項1又は請求項2に記載の導電性ペースト。
- 前記分散剤は、前記導電性粉末100質量部に対して、総量で0.2質量部以上1質量部以下含有される、請求項1〜請求項3のいずれか一項に記載の導電性ペースト。
- 前記導電性粉末は、Ni、Pd、Pt、Au、Ag、Cu及びこれらの合金から選ばれる少なくとも1種の金属粉末を含む、請求項1〜請求項4のいずれか一項に記載の導電性ペースト。
- 前記導電性粉末は、平均粒径が0.05μm以上1.0μm以下である、請求項1〜請求項5のいずれか一項に記載の導電性ペースト。
- セラミック粉末を含む、請求項1〜請求項6のいずれか一項に記載の導電性ペースト。
- 前記セラミック粉末は、ペロブスカイト型酸化物を含む、請求項7に記載の導電性ペースト。
- 前記セラミック粉末は、平均粒径が0.01μm以上0.5μm以下である、請求項7又は請求項8に記載の導電性ペースト。
- 積層セラミック部品の内部電極用である、請求項1〜請求項9のいずれか一項に記載の導電性ペースト。
- ずり速度100sec−1での粘度が0.8Pa・S以下であり、ずり速度10000sec−1での粘度が0.19Pa・S以下である、請求項1〜請求項10のいずれか一項に記載の導電性ペースト。
- 請求項1〜請求項11のいずれか一項に記載の導電性ペーストを用いて形成される、電子部品。
- 誘電体層と内部電極とを積層した積層体を少なくとも有する積層セラミックコンデンサであって、
前記内部電極は、請求項1〜請求項11のいずれか一項に記載の導電性ペーストを用いて形成される、積層セラミックコンデンサ。