JPS6339131A - 磁気記録媒体 - Google Patents
磁気記録媒体Info
- Publication number
- JPS6339131A JPS6339131A JP61179889A JP17988986A JPS6339131A JP S6339131 A JPS6339131 A JP S6339131A JP 61179889 A JP61179889 A JP 61179889A JP 17988986 A JP17988986 A JP 17988986A JP S6339131 A JPS6339131 A JP S6339131A
- Authority
- JP
- Japan
- Prior art keywords
- value
- coat layer
- recording medium
- layer
- back coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は磁気記録媒体に係わり、さらに詳しくは基体の
裏面に設けられた潤滑剤層であるバックコート層による
腐食を防止し、耐食性ならびに走行性に優れ信頼性の高
い強磁性金属薄膜型の磁気記録媒体に関する。
裏面に設けられた潤滑剤層であるバックコート層による
腐食を防止し、耐食性ならびに走行性に優れ信頼性の高
い強磁性金属薄膜型の磁気記録媒体に関する。
基体上に、直接もしくは下地層を介して、磁性層である
Co(コバルト)を主成分とする強磁性金属薄膜を形成
させた磁気記録媒体は、高密度記録特性に優れている反
面、磁気記録媒体の表面にCo金属が露出されているた
めに耐食性が劣化するという問題があった。この問題を
解決するために従来技術においては、磁性層表面を加熱
処理してGo、O,などのコバルト酸化撫からなる保護
層を形成させたり(特公昭42−20025号公報)、
オゾン雰囲気に曝すことによってCo、○、とCo、0
3などのコバルト複合酸化物層を形成させたり(特開昭
59−63031号公報)、あるいはグロー放電処理な
どによって磁性層の表面にCo 01Co、○。などの
コバルト酸化物を含む保護層を形成(特開昭58−41
439号公報)などして、磁性層の表面のG。
Co(コバルト)を主成分とする強磁性金属薄膜を形成
させた磁気記録媒体は、高密度記録特性に優れている反
面、磁気記録媒体の表面にCo金属が露出されているた
めに耐食性が劣化するという問題があった。この問題を
解決するために従来技術においては、磁性層表面を加熱
処理してGo、O,などのコバルト酸化撫からなる保護
層を形成させたり(特公昭42−20025号公報)、
オゾン雰囲気に曝すことによってCo、○、とCo、0
3などのコバルト複合酸化物層を形成させたり(特開昭
59−63031号公報)、あるいはグロー放電処理な
どによって磁性層の表面にCo 01Co、○。などの
コバルト酸化物を含む保護層を形成(特開昭58−41
439号公報)などして、磁性層の表面のG。
を酸化し不動態化する処理が行われている。ところが、
これらのCo合金系の強磁性金属薄膜を有する磁気記録
媒体において、その走行特性を向上させるために、媒体
を構成する基体の裏面に潤滑剤層であるバックコート層
を形成させて磁気記録媒体の走行性を改善している。し
かし、このバックコート層は1例えばテープ状に磁気記
録媒体が巻かれた状態、すなわち磁気テープ巻回体の形
にあるときは、磁気記録媒体の表面に形成されている磁
性層であるCO合金系強磁性金属薄膜層と、基体の裏面
に形成されているバックコート層とが密着するために磁
性層はこのバックコート層の影響を受は易く、バックコ
ート層が大気中の水分などによって酸性の状態となると
、磁性層表面に形成されている保護膜であるGo不動態
膜は容易に破壊あるいは溶解されてしまい、その結果磁
性層が腐食されて、磁気記録媒体の特性ならびに走行性
が低下するという欠点があった。
これらのCo合金系の強磁性金属薄膜を有する磁気記録
媒体において、その走行特性を向上させるために、媒体
を構成する基体の裏面に潤滑剤層であるバックコート層
を形成させて磁気記録媒体の走行性を改善している。し
かし、このバックコート層は1例えばテープ状に磁気記
録媒体が巻かれた状態、すなわち磁気テープ巻回体の形
にあるときは、磁気記録媒体の表面に形成されている磁
性層であるCO合金系強磁性金属薄膜層と、基体の裏面
に形成されているバックコート層とが密着するために磁
性層はこのバックコート層の影響を受は易く、バックコ
ート層が大気中の水分などによって酸性の状態となると
、磁性層表面に形成されている保護膜であるGo不動態
膜は容易に破壊あるいは溶解されてしまい、その結果磁
性層が腐食されて、磁気記録媒体の特性ならびに走行性
が低下するという欠点があった。
本発明は、上述した従来技術において、磁気記録媒体の
基体の裏面に設けられている潤滑剤層であるバックコー
ト層が、大気中の水分などの影響によって酸性化し、そ
れと接触するGoもしくはCoを主成分とする合金から
なる磁性層を腐食させるという欠点を解消し、もって耐
食性ならびに走行性が良好で優れた耐久性を有する信頼
性の高い磁気記録媒体を提供することを目的とする。
基体の裏面に設けられている潤滑剤層であるバックコー
ト層が、大気中の水分などの影響によって酸性化し、そ
れと接触するGoもしくはCoを主成分とする合金から
なる磁性層を腐食させるという欠点を解消し、もって耐
食性ならびに走行性が良好で優れた耐久性を有する信頼
性の高い磁気記録媒体を提供することを目的とする。
本発明者らは、磁性層であるCOもしくはG。
を主成分とする強磁性金属薄膜層表面に形成されたGo
不動態膜は、pH値が6.3未満の酸性の溶液あるいは
雰囲気に曝されるとCO不動態膜は破壊あるいは溶解さ
れてしまうことを種々の実験の結果見い出した。そして
、リール状に巻き取られた磁気テープ巻同体の磁性層と
接触する潤滑剤層であるバックコート層のpH値を6.
3以上にあらかじめ調整しておくことにより、たとえ大
気中の水分などが凝縮し付着しても、このバックコート
層に隣接する磁性層表面のGo不動態膜が破壊あるいは
溶解されることがなく、したがって磁性層は腐食されず
耐久性ならびに信頼性の高い磁気記録媒体が得られるこ
とを確認するに至った。
不動態膜は、pH値が6.3未満の酸性の溶液あるいは
雰囲気に曝されるとCO不動態膜は破壊あるいは溶解さ
れてしまうことを種々の実験の結果見い出した。そして
、リール状に巻き取られた磁気テープ巻同体の磁性層と
接触する潤滑剤層であるバックコート層のpH値を6.
3以上にあらかじめ調整しておくことにより、たとえ大
気中の水分などが凝縮し付着しても、このバックコート
層に隣接する磁性層表面のGo不動態膜が破壊あるいは
溶解されることがなく、したがって磁性層は腐食されず
耐久性ならびに信頼性の高い磁気記録媒体が得られるこ
とを確認するに至った。
本発明の潤滑剤層であるバックコート層のpH値の調整
は、バックコート層を形成する種々の潤滑剤にアルカリ
性化合物を適量添加し、通常用いられているpHメータ
によってpH値を甜定して、所望するpH値に制御する
ことにより行なわれる。
は、バックコート層を形成する種々の潤滑剤にアルカリ
性化合物を適量添加し、通常用いられているpHメータ
によってpH値を甜定して、所望するpH値に制御する
ことにより行なわれる。
そして、バックコート層のpH値は6.3未満の酸性で
はCO不動態膜は破壊されてしまうので好ましくなく、
アルカリ性であればある程Go不動態膜はより安定とな
るので、その上限はpHの最大値である14まで許容さ
れる。
はCO不動態膜は破壊されてしまうので好ましくなく、
アルカリ性であればある程Go不動態膜はより安定とな
るので、その上限はpHの最大値である14まで許容さ
れる。
本発明の磁気記録媒体において、バックコート層を構成
する潤滑剤としては、通常用いられている潤滑剤を使用
することができ、脂肪族系潤滑剤、フッ素系潤滑剤、シ
リコーン系潤滑剤および炭化水素系潤滑剤などが挙げら
れる。すなわち、脂肪族系潤滑剤としては、脂肪酸、脂
肪酸の金属塩、脂肪酸エステル、脂肪酸アミド、脂肪族
アルコールなどがある。上記脂肪酸としては、例えばラ
ウリン酸、ミリスチン酸、バルミチン酸、オレイン酸、
ステアリン酸、ベヘン酸などが好ましく、またこれらの
金属塩として、例えばリチウム塩、ナトリウム塩、カル
シウム塩、マグネシウム塩、アルミニウム塩、鉄塩、コ
バルト塩、亜鉛塩、バリラム塩、鉛塩などが好適である
。また、脂肪酸エステルとしては、例えばステアリン酸
ブチル、ミリスチン酸オクチル、ステアリン酸モノグリ
セリド、パリミチン酸モノグリセリド、オレイン酸モノ
グリセリド、ペンタエリスリトールテトラステアレート
などを挙げることができ、脂肪酸アミドとしては、例え
ばカプロン酸アミド、カプリン酸アミド、ラウリン酸ア
ミド、パルミチン酸アミド。
する潤滑剤としては、通常用いられている潤滑剤を使用
することができ、脂肪族系潤滑剤、フッ素系潤滑剤、シ
リコーン系潤滑剤および炭化水素系潤滑剤などが挙げら
れる。すなわち、脂肪族系潤滑剤としては、脂肪酸、脂
肪酸の金属塩、脂肪酸エステル、脂肪酸アミド、脂肪族
アルコールなどがある。上記脂肪酸としては、例えばラ
ウリン酸、ミリスチン酸、バルミチン酸、オレイン酸、
ステアリン酸、ベヘン酸などが好ましく、またこれらの
金属塩として、例えばリチウム塩、ナトリウム塩、カル
シウム塩、マグネシウム塩、アルミニウム塩、鉄塩、コ
バルト塩、亜鉛塩、バリラム塩、鉛塩などが好適である
。また、脂肪酸エステルとしては、例えばステアリン酸
ブチル、ミリスチン酸オクチル、ステアリン酸モノグリ
セリド、パリミチン酸モノグリセリド、オレイン酸モノ
グリセリド、ペンタエリスリトールテトラステアレート
などを挙げることができ、脂肪酸アミドとしては、例え
ばカプロン酸アミド、カプリン酸アミド、ラウリン酸ア
ミド、パルミチン酸アミド。
ベヘン酸アミド、オレイン酸アミド、リノール酸アミド
、メチレンビスステアリン酸アミドなどが好ましい。さ
らに、脂・肪族アルコールとしては、例えばステアリル
アルコール、ミリスチルアルコールなどが好ましく使用
され、この他にトリメチルステアリルアンモニウムクロ
ライド、塩化ステアロイルなどの塩化物、ステアリルア
ミン、ステアリルアミンアセテート、ステアリルアミン
ハイドロクロライドなどのアミンなども使用される。
、メチレンビスステアリン酸アミドなどが好ましい。さ
らに、脂・肪族アルコールとしては、例えばステアリル
アルコール、ミリスチルアルコールなどが好ましく使用
され、この他にトリメチルステアリルアンモニウムクロ
ライド、塩化ステアロイルなどの塩化物、ステアリルア
ミン、ステアリルアミンアセテート、ステアリルアミン
ハイドロクロライドなどのアミンなども使用される。
そして、上記フッ素系潤滑剤としては、例えばトリクロ
ロフルオロエチレン、パーフルオロポリエーテル、パー
フルオロアルキルポリエーテル、パーフルオロアルキル
カルボン酸などが好ましく、市販品の具体例としては、
ダイキン社製ダイフロン#20、デュポン社製クライト
ツクスM、クライトツクスH、パイダックスAR、モン
テジソン社製フオンブリンZなどが挙げられる。
ロフルオロエチレン、パーフルオロポリエーテル、パー
フルオロアルキルポリエーテル、パーフルオロアルキル
カルボン酸などが好ましく、市販品の具体例としては、
ダイキン社製ダイフロン#20、デュポン社製クライト
ツクスM、クライトツクスH、パイダックスAR、モン
テジソン社製フオンブリンZなどが挙げられる。
さらに、上記シリコーン系潤滑剤としては、シリコーン
オイル、変性シリコーンオイルなどがあり、上記炭化水
素系潤滑剤としては、パラフィン。
オイル、変性シリコーンオイルなどがあり、上記炭化水
素系潤滑剤としては、パラフィン。
スクアラン、ワックスなどが好適なものとして使用され
る。
る。
なお、潤滑剤層であるバックコート層は、上記潤滑剤の
少なくとも1種によって構成される他、防錆剤などの添
加剤を混在させてもよい。
少なくとも1種によって構成される他、防錆剤などの添
加剤を混在させてもよい。
そして、上記潤滑剤を用いてバックコート層のpH値を
調整する場合に、使用する潤滑剤自身のpH値が6.3
以上であれば、そのまま使用することができるし、pH
値が6.3未満の潤滑剤である場合には、例えば水酸化
ナトリウム、水酸化カリウム、炭酸水素ナトリウムなど
のアルカリ性化合物を適量添加することによって、所望
のpH値に調整したものを用いることができ、これを、
例えばトルエン、メチルイソブチルケトン、メチルエチ
ルケトン、シクロヘキサノン、酢酸エチル、イソプロピ
ルアルコール、フレオン、テトラヒドロフラン、ジメチ
ルホルムアミド、ジオキサンなどの適当な溶剤を用いて
溶解し、これを塗布、噴霧あるいは浸漬することによっ
てpH値が6.3以上に調整されたバックコート層を形
成させることができる。
調整する場合に、使用する潤滑剤自身のpH値が6.3
以上であれば、そのまま使用することができるし、pH
値が6.3未満の潤滑剤である場合には、例えば水酸化
ナトリウム、水酸化カリウム、炭酸水素ナトリウムなど
のアルカリ性化合物を適量添加することによって、所望
のpH値に調整したものを用いることができ、これを、
例えばトルエン、メチルイソブチルケトン、メチルエチ
ルケトン、シクロヘキサノン、酢酸エチル、イソプロピ
ルアルコール、フレオン、テトラヒドロフラン、ジメチ
ルホルムアミド、ジオキサンなどの適当な溶剤を用いて
溶解し、これを塗布、噴霧あるいは浸漬することによっ
てpH値が6.3以上に調整されたバックコート層を形
成させることができる。
なお、バックコート層のpH値を調整するために加える
アルカリ性化合物は、上記の水酸化ナトリウムなどの他
に、磁性層上に形成されたCO不動態膜を破壊あるいは
溶解しないものであって、pH値を6.3〜14の範囲
に制御可能な無機あるいは有機化合物のいずれであって
も用いることができ特にその種類を限定するものではな
い。
アルカリ性化合物は、上記の水酸化ナトリウムなどの他
に、磁性層上に形成されたCO不動態膜を破壊あるいは
溶解しないものであって、pH値を6.3〜14の範囲
に制御可能な無機あるいは有機化合物のいずれであって
も用いることができ特にその種類を限定するものではな
い。
以下に本発明の一実施例を挙げ図面を参照しながらさら
に詳細に説明する。
に詳細に説明する。
(実施例 1)
第1図に示す構造の磁気テープを、以下の手順にしたが
って作製した。
って作製した。
酸素ガスを導入しながら、6 X 1O−sT orr
の真空中で、厚さ9taのポリエチレンテレフタレート
フィルムの基体1上に、Go−20vt%Ni合金から
なる膜厚が1500人の強磁性金属薄膜層2を連続斜め
蒸着法によって形成し、ロール状に巻き取った。その後
、−慶大気中に取り出して再度密閉容器内に入れ、50
m Torrまで排気した後、酸素ガスを1.3気圧に
なるまで封入し、150時間静置することにより強磁性
金属薄膜層2の表面を不動態化しCo不動態膜3を形成
させた。次に、基体1であるポリエチレンテレフタレー
トフィルムの裏面に、潤滑剤としてフオンブリンZ、D
IOL (モンテジソン社製)を用い、炭酸水素ナトリ
ウムを加えてpH値が6.5となるように調整したバッ
クコート層4を形成し、所定の幅に裁断して磁気テープ
を作製した。
の真空中で、厚さ9taのポリエチレンテレフタレート
フィルムの基体1上に、Go−20vt%Ni合金から
なる膜厚が1500人の強磁性金属薄膜層2を連続斜め
蒸着法によって形成し、ロール状に巻き取った。その後
、−慶大気中に取り出して再度密閉容器内に入れ、50
m Torrまで排気した後、酸素ガスを1.3気圧に
なるまで封入し、150時間静置することにより強磁性
金属薄膜層2の表面を不動態化しCo不動態膜3を形成
させた。次に、基体1であるポリエチレンテレフタレー
トフィルムの裏面に、潤滑剤としてフオンブリンZ、D
IOL (モンテジソン社製)を用い、炭酸水素ナトリ
ウムを加えてpH値が6.5となるように調整したバッ
クコート層4を形成し、所定の幅に裁断して磁気テープ
を作製した。
(実施例 2)
実施例1において用いた潤滑剤であるフオンブリンZ、
DIOLの代りに、パイダックス84(デュポン社製)
を潤滑剤として用い、バックコート層のpH値を7.3
となるように調整した以外は、実施例1と同様にして磁
気テープを作製した。
DIOLの代りに、パイダックス84(デュポン社製)
を潤滑剤として用い、バックコート層のpH値を7.3
となるように調整した以外は、実施例1と同様にして磁
気テープを作製した。
(実施例 3)
実施例1において用いた潤滑剤であるフオンブリンZ、
DIOLの代りに、ラウリン酸を潤滑剤として用い、バ
ックコート層のpH値を7.5となるように調整した以
外は、実施例1と同様にして磁気テープを作製した。
DIOLの代りに、ラウリン酸を潤滑剤として用い、バ
ックコート層のpH値を7.5となるように調整した以
外は、実施例1と同様にして磁気テープを作製した。
(比較例 1)
実施例1において用いた潤滑剤であるフオンブリンZ、
DIOLの代りに、ミリスチン酸を潤滑剤として用い、
バックコート層のpH値が4.8となるように調整した
以外は、実施例1と同様にして磁気テープを作製した。
DIOLの代りに、ミリスチン酸を潤滑剤として用い、
バックコート層のpH値が4.8となるように調整した
以外は、実施例1と同様にして磁気テープを作製した。
(比較例 2)
実施例1において用いた潤滑剤であるフオンブリンZ、
DIOLの代りに、ステアリン酸を潤滑剤として用い、
バックコート層のpH値が6.1となるように調整した
以外は、実施例1と同様にして磁気テープを作製した。
DIOLの代りに、ステアリン酸を潤滑剤として用い、
バックコート層のpH値が6.1となるように調整した
以外は、実施例1と同様にして磁気テープを作製した。
以上の実施例および比較例において作製した磁気テープ
をリール状に巻き取り、磁気テープ巻回体となし、バッ
クコート層と磁性層表面とが接触する状態で、60°C
の温度で、関係湿度(RH)が90%の高温高湿の雰囲
気中に静置して、磁性層表面の摩擦係数の変化を測定す
ると共に、肉眼で磁性層の表面状態を観察し耐食性なら
びに走行性を評価した。その結果を第1表に示す。なお
ここで、摩擦係数の測定については、ステンレス製のピ
ンに、所定の荷重をかけた磁気テープを往復摺動させ、
磁気テープにかかる引張り応力を測定し、これを動摩擦
係数に換算することにより求めた。
をリール状に巻き取り、磁気テープ巻回体となし、バッ
クコート層と磁性層表面とが接触する状態で、60°C
の温度で、関係湿度(RH)が90%の高温高湿の雰囲
気中に静置して、磁性層表面の摩擦係数の変化を測定す
ると共に、肉眼で磁性層の表面状態を観察し耐食性なら
びに走行性を評価した。その結果を第1表に示す。なお
ここで、摩擦係数の測定については、ステンレス製のピ
ンに、所定の荷重をかけた磁気テープを往復摺動させ、
磁気テープにかかる引張り応力を測定し、これを動摩擦
係数に換算することにより求めた。
第1表から明らかなごとく、バックコート層のpH値を
6.3以上とした本発明の磁気テープ巻同体においては
、高温高湿の大気中に長時間放置しても優れた耐食性を
示し、また摩擦係数の変化もほとんどなく安定した走行
性が得られ、耐久性ならびに信頼性の高い磁気記録媒体
であることを示している。
6.3以上とした本発明の磁気テープ巻同体においては
、高温高湿の大気中に長時間放置しても優れた耐食性を
示し、また摩擦係数の変化もほとんどなく安定した走行
性が得られ、耐久性ならびに信頼性の高い磁気記録媒体
であることを示している。
上記の実施例において、バックコート層のpH値調整用
のアルカリ化合物として炭酸水素ナトリウムを使用した
が、この他に水酸化ナトリウム、水酸化カリウムを用い
た場合、およびGo不動態膜を破壊しないその他のアル
カリ性の無機もしくは有機化合物を用いた場合において
も、上記実施例と同様の効果のあることを確認している
。
のアルカリ化合物として炭酸水素ナトリウムを使用した
が、この他に水酸化ナトリウム、水酸化カリウムを用い
た場合、およびGo不動態膜を破壊しないその他のアル
カリ性の無機もしくは有機化合物を用いた場合において
も、上記実施例と同様の効果のあることを確認している
。
また、上記の実施例において、バックコート層を構成す
る潤滑剤として、モンテジソン社製のフオンブリンZ、
DIOLおよびデュポン社製のパイダックス84の市販
品を用いたが、この他に脂肪族系潤滑剤、フッ素系潤滑
剤、シリコーン系潤滑剤および炭化水素系潤滑剤を用い
た場合においても、上記の実施例と同様の効果が得られ
ることを確認している。
る潤滑剤として、モンテジソン社製のフオンブリンZ、
DIOLおよびデュポン社製のパイダックス84の市販
品を用いたが、この他に脂肪族系潤滑剤、フッ素系潤滑
剤、シリコーン系潤滑剤および炭化水素系潤滑剤を用い
た場合においても、上記の実施例と同様の効果が得られ
ることを確認している。
本発明の磁気記録媒体において、用いられる強磁性金属
薄膜層の構成材料としては、Co単体の他、Coを主成
分として含むCo−Ni、 Co−Cr、Co−P、C
o−Pd、Co−Fe、Co−N1−P、Co−Fe−
Cr、 Co−Ni−Cr、 Co−Fe−Nj、Go
−Ti、Co−Cuなどの合金を用いることができる。
薄膜層の構成材料としては、Co単体の他、Coを主成
分として含むCo−Ni、 Co−Cr、Co−P、C
o−Pd、Co−Fe、Co−N1−P、Co−Fe−
Cr、 Co−Ni−Cr、 Co−Fe−Nj、Go
−Ti、Co−Cuなどの合金を用いることができる。
また1本発明の磁気記録媒体に用いることのできる基体
材料としては、ポリエチレンテレフタシー1〜フイルム
の他に、ポリアミド、ポリイミド。
材料としては、ポリエチレンテレフタシー1〜フイルム
の他に、ポリアミド、ポリイミド。
ポリエステルなどの合成樹脂フィルムなど、通常用いら
れているプラスチックフィルムあるいは複合プラスチッ
クフィルムなどを使用することができる。
れているプラスチックフィルムあるいは複合プラスチッ
クフィルムなどを使用することができる。
以上詳細に説明したごとく、本発明のpH値が6.3以
上に調整されたバックコート層を有する磁気記録媒体は
、例えば磁気テープ巻回体の形で長時間、高温高湿の大
気中に置かれても、磁性層であるGoあるいはCoを主
成分とする強磁性金属薄膜層の表面に形成された耐食性
のCo不動態膜が破壊されることがなく、優れた耐食性
ならびに走行性が維持されるので、耐久性および信頼性
の高い磁気記録媒体が得られる。
上に調整されたバックコート層を有する磁気記録媒体は
、例えば磁気テープ巻回体の形で長時間、高温高湿の大
気中に置かれても、磁性層であるGoあるいはCoを主
成分とする強磁性金属薄膜層の表面に形成された耐食性
のCo不動態膜が破壊されることがなく、優れた耐食性
ならびに走行性が維持されるので、耐久性および信頼性
の高い磁気記録媒体が得られる。
第1図は本発明の実施例1において作製した磁気テープ
の断面構造を示す模式図である。 1・・・基体(ポリエチレンテレフタレートフィルム)
2・・・強磁性金属薄膜層 3・・・Co不動態膜
の断面構造を示す模式図である。 1・・・基体(ポリエチレンテレフタレートフィルム)
2・・・強磁性金属薄膜層 3・・・Co不動態膜
Claims (1)
- 【特許請求の範囲】 1、基体上に、直接もしくは下地層を介して磁性層を設
け、該磁性層の表面には不動態膜が形成され、かつ上記
基体の裏面には潤滑剤からなるバックコート層を有する
磁気記録媒体において、上記バックコート層のpH値を
6.3以上、14以下とすることを特徴とする磁気記録
媒体。 2、磁性層は、コバルトもしくはコバルトを主成分とす
る合金からなり、不動態膜がコバルト不動態膜であるこ
とを特徴とする特許請求の範囲第1項に記載の磁気記録
媒体。 3、バックコート層は、脂肪族系潤滑剤、フッ素系潤滑
剤、シリコーン系潤滑剤、炭化水素系潤滑剤のうちの少
なくとも1種からなることを特徴とする特許請求の範囲
第1項または第2項に記載の磁気記録媒体。 4、バックコート層は、該バックコート層を構成する潤
滑剤に、アルカリ性無機化合物およびアルカリ性有機化
合物のうちの少なくとも1種を適量添加し、上記潤滑剤
のpH値が6.3〜14の範囲となるように上記アルカ
リ性化合物を含有することを特徴とする特許請求の範囲
第1項ないし第3項のいずれか1項に記載の磁気記録媒
体。 5、アルカリ性化合物は、水酸化ナトリウム、水酸化カ
リウム、炭酸水素ナトリウムのうちの少なくとも1種を
含むことを特徴とする特許請求の範囲第4項に記載の磁
気記録媒体。