JPS62127287A - 光記録材料 - Google Patents

光記録材料

Info

Publication number
JPS62127287A
JPS62127287A JP60267719A JP26771985A JPS62127287A JP S62127287 A JPS62127287 A JP S62127287A JP 60267719 A JP60267719 A JP 60267719A JP 26771985 A JP26771985 A JP 26771985A JP S62127287 A JPS62127287 A JP S62127287A
Authority
JP
Japan
Prior art keywords
recording
recording layer
optical recording
cobalt oxide
weather resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP60267719A
Other languages
English (en)
Other versions
JPH042437B2 (ja
Inventor
Masaki Ito
雅樹 伊藤
Akio Morimoto
昭男 森本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NEC Corp
Original Assignee
NEC Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NEC Corp filed Critical NEC Corp
Priority to JP60267719A priority Critical patent/JPS62127287A/ja
Publication of JPS62127287A publication Critical patent/JPS62127287A/ja
Publication of JPH042437B2 publication Critical patent/JPH042437B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 （産業上の利用分野） 本発明はレーザ光によって情報を記録再生することので
きる光記録媒体に関し、さらに詳しくは集光したレーザ
光の熱作用により薄膜にピットを形成して記録する光記
録媒体に関するものである。
（従来の技術） レーザ光によって情報を媒体に記録し、かつ再生する追
記型光デイスクメモリは、記録密度が高いことから大容
量記録装置として優れた特徴を有している。このような
追記型光デイスクメモリの記録媒体としては、低融点金
属であるビスマス、テルルが使用されている（特公昭４
６−４０４７９．特公昭５７−４５６７６、特公昭５９
−４１８７５．特公昭５４−１５４８３．特公昭５９−
３５３５６）。
（発明が解決しようとする問題点） しかし、ビスマス、テルルは耐候性が悪いため実用に供
することはできなかった。
本発明の目的は、耐候性がよく、かつ高感度で信号品質
の良好な光記録媒体に用いる光記録材料を提供すること
にある。
（問題を解決するための手段） 本発明の光記録材料は光記録媒体の記録層に用いる光記
録材料であって、主成分のテルルに加えて、コバルト酸
化物を体積％で１０％から５０％含有してなることを特
徴とする。
（作用） 本発明による記録膜は主成分のテルルに加えて体積％で
１０％から５０％のコバルト酸化物を不可欠な構成要素
として含んでいる。テルルは低融点の半金属のため高い
記録感度を有している。しかし、酸化しやすいために長
期保存性に欠は問題であり実用に供することはできなか
った。さらに、材料の結晶性に起因して表面性がやや悪
いので未記録ノイズが充分小さな値にならないという問
題もあった。本発明者らはテルルに体積％で１０％から
５０％のコバルト酸化物を含有させることにより、高感
度を維持したまま耐候性が著しく向上し加えて表面性が
良好になることを見出し、本発明に到ったものである。
記録層の膜厚は１００〜６００人程度が記録感度及び信
号品質の点で望ましく、とくに２００〜５００人が望ま
しい。記録層はテルルとコバルト酸化物のみの混合物で
も充分に優れた光記録媒体特性と耐候性を有するが、更
に耐候性を向上させたり、反射率を所定の値に調整する
ためには第３物質等を含有させてもよい。第３物質とし
ては、炭素、アルミニウム、シリコン、チタン、クロム
、鉄、コバルト、ニッケル、銅、亜鉛、ガリウム、ゲル
マニウム、セレン、ジルコニウム、ニオブ、モリブデン
、ロジウム、パラジウム、銀、インジウム、スズ、アン
チモン、タンタル、タングステン、白金、金、鉛、ビス
マスのうちの１以上が望ましい。これらは体積％で１０
〜１５％以下で効果を示すものが多いが、物質によって
はこれらより多く含ませることもある。
コバルト酸化物としてはＣＯＯ，ＣＯ２Ｏ３，ＣＯ３Ｏ
４があるが、耐候性の観点からはＣＯ３Ｏ４が最も望ま
しい。
基板としては種々のものを使用できるが、一般には合成
樹脂、ガラス、磁器、アルミニウム合金が望ましい。合
成樹脂としては、ポリメチルメタクリレート等のアクリ
ル樹脂、ポリカーボネート、ポリエーテルイミド、ポリ
サルホン、エポキシ樹脂、塩化ビニル樹脂がある。基板
にはその上に断熱層やスムージング層を設けてよい。基
板の形状は円板状、シート状、テープ状とすることがで
きる。
記録層への情報の記録は、記録層にピットを形成するこ
とによりなされる。円板状の基板を用いるディスク媒体
では、ピットは同心円状又はスパイラル状の多数のトラ
ックに形成するように記録される。多数のトラックを一
定間隔で精度よく記録するには、通常基板上に光の案内
溝が設けられる。ビーム径程度の溝に光が入射すると光
が回折される。ビーム中心が溝からずれるにつれて回折
光強度の空間分布が異なり、これを検出してビームを溝
の中心に入射させるようにサーボ系を構成できる。通常
溝の幅は０．３〜１．２ｐｍ、その深さは使用する記録
再生レーザ波長の１ノ１２〜１／４の範囲に設定される
。
（実施例１） 以下、本発明の実施例について説明する。内径１５ｍｍ
、外径１３０ｍｍ、厚さ１．２ｍｍの案内溝付きポリカ
ーボネート樹脂ディスク基板を真空蒸着装置内に入れ、
２Ｘ１０−５Ｔｏｒｒ以下に排気した。蒸発源としては
抵抗加熱用ボート（モリブデン製）にＴｅを入れ、電子
ビーム加熱用るつぼにＣＯ３Ｏ４を入れた。水晶振動子
式膜厚モニターを用いて、それぞれの蒸着物質の蒸着速
度を制御しながら共蒸着することにより、ディスク基板
上に記録層を形成した。
Ｔｅの蒸着速度は毎分約６０人とし、ＣＯ３Ｏ４蒸着速
度は毎分約１７人として、ＣＯ３Ｏ４の体積率が２２％
の組成の約２７５０厚の膜を記録層とした。この光記録
媒体のフラット部の光学特性を波長８３００人の平行光
で測定したところ、基板入射反射率は２２％、吸収率は
約５７％であった。波長５ａｏｏＡのＡｌＧａＡｓ半導
体レーザを光学系を用いて収光し、基板を通して記録層
に照射し、ピットを記録層に形成した。媒体線速度５゜
６５ｍ／ｓｅｅ、記録レーザパワー１０ｍＷにおいてレ
ーザ照射時間１００ｎｓｅｃで記録が可能であった。記
録されたピットをレーザパワー０．４ｍＷで再生したと
ころ、１０５ｍＶの良好な品質の信号を得た。次に、こ
の光記録媒体を７０°０８０％の高温高湿度の環境に２
００時間保存した後に上記の特性を調べたところ、はと
んど変化はなく、本光言己録材料が高い耐候性を有して
いることがわかった。
（実施例２） 実施例１と同様にして、第１表のような光記録媒体を作
製した。第１表には基板入射反射率、記録再生結果、耐
候性試験結果をあわせて示す。反射率はＣＯ３Ｏ４の含
有率が増大するにしたがって低下する傾向となる。記録
再生の信号品質は、ＣＯ３Ｏ４を添加することにより少
し良好となるが、６０％以上の添加では感度不足となり
悪くなる。高温高湿度条件下での保存性は、ＣＯ３Ｏ４
の含有率が５％以下ではＴｅの性質がでて悪い。したが
って、ＣＯ３Ｏ４の体積含有率は１０％から５０％が実
用可能な組成範囲であることが（実施例３） 抵抗加熱用ボートにＴｅを入れ、もう一つの抵抗加熱用
ボートにＳｅを入れ、電子ビーム加熱用るつぼにＣＯ３
Ｏ４を入れ、体積率でそれぞれ７１％、９％。
２０％となるように共蒸着してディスク基板上に３７５
人厚０記録層を形成した。実施例１と同様にして記録再
生したところ良好な記録ができた。次に、７０°０８０
％の環境に２００時間保存した後、上記の特性を調べた
がほとんど変化がなく、耐候性が良好であることが確認
された。
（発明の効果） 上記実施例から明らかなように、本発明により耐候性が
高くかつ高感度で信号品質の良好な光記録材料が得られ
る。

Claims (1)

    【特許請求の範囲】
  1. 光記録媒体の記録層に用いる光記録材料において、主成
    分のテルルに加えて、コバルト酸化物を体積％で１０％
    から５０％含有してなることを特徴とする光記録材料。
JP60267719A 1985-11-27 1985-11-27 光記録材料 Granted JPS62127287A (ja)