JPS58152353A - X線管回転陽極 - Google Patents
X線管回転陽極Info
- Publication number
- JPS58152353A JPS58152353A JP58025464A JP2546483A JPS58152353A JP S58152353 A JPS58152353 A JP S58152353A JP 58025464 A JP58025464 A JP 58025464A JP 2546483 A JP2546483 A JP 2546483A JP S58152353 A JPS58152353 A JP S58152353A
- Authority
- JP
- Japan
- Prior art keywords
- rotating anode
- ray tube
- coating
- tungsten
- molybdenum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明は、炭素含有モリブデン合金例えばTZMから成
る基体と、タングステン又はタングステン合金から成る
焦点軌道とから成り、回転陽一種以上の酸化物から成る
被膜又は一種以上の金属と一種以上の酸化物との混合物
から成る被膜を有するX線管回転陽極に関する。
る基体と、タングステン又はタングステン合金から成る
焦点軌道とから成り、回転陽一種以上の酸化物から成る
被膜又は一種以上の金属と一種以上の酸化物との混合物
から成る被膜を有するX線管回転陽極に関する。
X線を得る際に回転陽極に供給される電気エネルギーは
約1係がX線エネルギーに変換されるにすぎない。残り
の99チは不所望の熱に変わり、これは回転陽極に著し
い温度負荷をもたらす。従って過去において表面の熱放
散率を大きくすることによって、回転陽極に生じた熱エ
ネルギーを出来るだけ迅速にまだ充分に除去する試みは
欠かせなかった。公知の手段では、黒鉛を有する回転陽
極は粉末状の高融点金属例えばチタン又はタンタルから
成るか、炭化物例えば炭化チタン又は炭化タンタルから
成るか又は酸化物混合物又は酸化物金属混合物から成る
被膜で覆われていた。
約1係がX線エネルギーに変換されるにすぎない。残り
の99チは不所望の熱に変わり、これは回転陽極に著し
い温度負荷をもたらす。従って過去において表面の熱放
散率を大きくすることによって、回転陽極に生じた熱エ
ネルギーを出来るだけ迅速にまだ充分に除去する試みは
欠かせなかった。公知の手段では、黒鉛を有する回転陽
極は粉末状の高融点金属例えばチタン又はタンタルから
成るか、炭化物例えば炭化チタン又は炭化タンタルから
成るか又は酸化物混合物又は酸化物金属混合物から成る
被膜で覆われていた。
西ドイツ特許出願公開第2443354号明細書には、
例えばTZMから成る基体が放熱可能性を高めるだめに
酸化アルミニウム及び酸化チタン記載し/C形式の回転
陽極が記載されている。
例えばTZMから成る基体が放熱可能性を高めるだめに
酸化アルミニウム及び酸化チタン記載し/C形式の回転
陽極が記載されている。
オーストリア特許第3361.43号明細書には同様に
、高融点の金属例えばモリブデン合金から成る基体から
成り、更に焦点軌道の外側に酸化セラミック材例えばT
lO2及び/又はA403及び/又はZrO2を有する
モリブデン及び、/又はタングステン及び/又はニオブ
及び/又はタンタルから成る複合材から成る被覆層を備
えノL回転陽極が記載されている。
、高融点の金属例えばモリブデン合金から成る基体から
成り、更に焦点軌道の外側に酸化セラミック材例えばT
lO2及び/又はA403及び/又はZrO2を有する
モリブデン及び、/又はタングステン及び/又はニオブ
及び/又はタンタルから成る複合材から成る被覆層を備
えノL回転陽極が記載されている。
」−記載つの明細書には炭素含有モリブデン合金を基材
として使用することが示唆もしくは開示されている。従
ってこれらの明細書に基づく場合、炭素含有モリブデン
合金、特にTZMにおいて他の場合に適した被覆層を用
いた場合に通常の耐用期間中に残存することが予測され
る高い放熱度を得ることができないというようなことは
、当業者に予測できなかつだしまだ知られてもいなかっ
た。
として使用することが示唆もしくは開示されている。従
ってこれらの明細書に基づく場合、炭素含有モリブデン
合金、特にTZMにおいて他の場合に適した被覆層を用
いた場合に通常の耐用期間中に残存することが予測され
る高い放熱度を得ることができないというようなことは
、当業者に予測できなかつだしまだ知られてもいなかっ
た。
本出願人は当業者にとってまったく予想外であら成る基
体から成り、放熱性を高めるため酸化物から成る被覆を
備えた回転陽極は、その僅かな運転時間後に元の良好な
放散特性を著しく劣化することを発見した。この現象は
おそらく基体から外部酸化物層への炭素拡散に起因する
と思われる。
体から成り、放熱性を高めるため酸化物から成る被覆を
備えた回転陽極は、その僅かな運転時間後に元の良好な
放散特性を著しく劣化することを発見した。この現象は
おそらく基体から外部酸化物層への炭素拡散に起因する
と思われる。
この放熱可能性への好捷しくない影響は、公知技術でも
純粋な炭化物層例えば炭化チタンを放熱増進のため回転
陽極基体に設けることが行われていたにも拘わらず理解
されていなかった。
純粋な炭化物層例えば炭化チタンを放熱増進のため回転
陽極基体に設けることが行われていたにも拘わらず理解
されていなかった。
本発明の目的は、運転期間とは無関係に熱放散率を高め
ることのできる、炭素含有モリブデン合金から成る最初
に記載した形式のX線管用回転陽極を得ることにある。
ることのできる、炭素含有モリブデン合金から成る最初
に記載した形式のX線管用回転陽極を得ることにある。
この目的は本発明によれば、基体と被膜との間にモリブ
デン及び/又はタングステンから成る厚さ10〜200
μmの中間層を配置することによって達成される。
デン及び/又はタングステンから成る厚さ10〜200
μmの中間層を配置することによって達成される。
モリブデン及び/又はタングステンから成る中ノ107
ノ1λ灰#I己旧ヤリノ1ン付蛍1符に゛1゛乙Mが(
3) る回転陽極の熱放散特性の劣化を阻止する働きをする。
ノ1λ灰#I己旧ヤリノ1ン付蛍1符に゛1゛乙Mが(
3) る回転陽極の熱放散特性の劣化を阻止する働きをする。
同時にこの中間層は顕著な付着助剤でもあり、従って被
膜層を良好に基体に付着させる働きをする。モリブデン
及び/又はタングステン中間層を炭素用拡散障壁として
使用することを仮定した場合にも、上記の金属を選択す
ることは予測できない。それというのもこれまで使用さ
れ多数研究されまた発表されてきだ一連の問題点に関し
ては、すなわち黒鉛から成る回転陽極基体に高融点の金
属から成る焦点軌道を設けるためには、炭素拡散障壁と
して中間層を必要とするが、この中間層材料としてモリ
ブデン及びタングステンはあまり好ましくなく、この代
りに特にレニウム及び個々ノ白金金属、更にTi 、Z
r 、Hf 、Nb及びTaの炭化物、硝酸塩、酸化物
及び臭化物を使用することが推薦されているからである
。
膜層を良好に基体に付着させる働きをする。モリブデン
及び/又はタングステン中間層を炭素用拡散障壁として
使用することを仮定した場合にも、上記の金属を選択す
ることは予測できない。それというのもこれまで使用さ
れ多数研究されまた発表されてきだ一連の問題点に関し
ては、すなわち黒鉛から成る回転陽極基体に高融点の金
属から成る焦点軌道を設けるためには、炭素拡散障壁と
して中間層を必要とするが、この中間層材料としてモリ
ブデン及びタングステンはあまり好ましくなく、この代
りに特にレニウム及び個々ノ白金金属、更にTi 、Z
r 、Hf 、Nb及びTaの炭化物、硝酸塩、酸化物
及び臭化物を使用することが推薦されているからである
。
回転陽極基体としては特にモリブデン合金TZM及びT
ZCが実積がある。中間層は砂吹きにより間層は、他の
場合には短い運転時間後に観察され(4) レー、フレーム・パウダ・スプレーのような慣用の被覆
法によって又はプラズマスプレーによって層厚10〜2
00μm1有利には40〜50μmに塗布することがで
きる。10μmよりも小さな層厚では所望の作用は得ら
れない。200μmよりも大きい層厚は仕上げ処理が不
経済である。それというのもとの層厚は所望の作用にと
って不必要であり、前記回転陽極の機械的及び熱的特性
がマイナスの影響を受けるからである。外側の酸化物層
の被覆は有利にはフレーム・パウダー・スプレー又はプ
ラズマスプレーによって行なう。それぞれ被覆層の形成
後灼熱処理を水素雰囲気下に1600℃ で約30分間
実施することが好ましい。
ZCが実積がある。中間層は砂吹きにより間層は、他の
場合には短い運転時間後に観察され(4) レー、フレーム・パウダ・スプレーのような慣用の被覆
法によって又はプラズマスプレーによって層厚10〜2
00μm1有利には40〜50μmに塗布することがで
きる。10μmよりも小さな層厚では所望の作用は得ら
れない。200μmよりも大きい層厚は仕上げ処理が不
経済である。それというのもとの層厚は所望の作用にと
って不必要であり、前記回転陽極の機械的及び熱的特性
がマイナスの影響を受けるからである。外側の酸化物層
の被覆は有利にはフレーム・パウダー・スプレー又はプ
ラズマスプレーによって行なう。それぞれ被覆層の形成
後灼熱処理を水素雰囲気下に1600℃ で約30分間
実施することが好ましい。
本発明による技術思想を使用した場合の予期せぬ技術的
進歩性を添付のダイアグラムにより詳述する。
進歩性を添付のダイアグラムにより詳述する。
図は、熱放散率と露出値(電子線での回転陽極照射)と
の関係を示すダイアグラムである。同じするT Z M
基体から成る回転陽極及び71”io2被覆層とモリブ
デン中間層とを有するTZM基体から成る回転陽極を互
いに比較する。
の関係を示すダイアグラムである。同じするT Z M
基体から成る回転陽極及び71”io2被覆層とモリブ
デン中間層とを有するTZM基体から成る回転陽極を互
いに比較する。
熱放散係数を求めるため回転陽極をX線管試験台に設置
I7、そわそれ管電圧8 ]、 k V及び管電流30
0mAで照射時間54秒で500回露出17た。
I7、そわそれ管電圧8 ]、 k V及び管電流30
0mAで照射時間54秒で500回露出17た。
個々の照射間1に5分間の冷却期間を保った。それぞれ
100回露出した後、回転陽極の冷却曲線が熱電対を介
1〜で検出され、次いで換算により熱放散係数を求める
ことができだ。
100回露出した後、回転陽極の冷却曲線が熱電対を介
1〜で検出され、次いで換算により熱放散係数を求める
ことができだ。
両陽極は約0.9の初期放散係数を示しだ。モリブデン
中間層を有さない回転陽極では放散係数は僅かな露出回
数の後に著しく降ドし、約500回露出17だ後では約
05の値になった。
中間層を有さない回転陽極では放散係数は僅かな露出回
数の後に著しく降ドし、約500回露出17だ後では約
05の値になった。
これに対してモリブデン中間層を有する回転陽極では放
散係数は露出の回数が増しても極く僅かに降ドするにす
ぎず、約500回の露出後でも083を示した。
散係数は露出の回数が増しても極く僅かに降ドするにす
ぎず、約500回の露出後でも083を示した。
従って本発明による中間層により顕著な技術的進歩性を
認めることができ、その際製造費が僅かに高まる以外欠
点はない。
認めることができ、その際製造費が僅かに高まる以外欠
点はない。
図面は熱放散率と露出値との関係を示すダイアダラムで
ある。
ある。
Claims (1)
- 1)炭素含有モリブデン合金、例えばTZMから成る基
体と、タングステン又はタングステン合金から成る焦点
軌道とから成り、回転陽極の表面が焦点軌道の外側に少
なくとも部分的に一種以上の酸化物から成る被膜又は一
種以上の金属と一種以上の酸化物との混合物から成る被
膜を有するX線管回転陽極において、基体と被膜との間
にモリブデン及び/又はタングステンから成る厚さ10
〜200μmの中間層を配置したことを特徴とするX線
管回転陽極。