JPH0192923A - 磁気記録媒体 - Google Patents
磁気記録媒体Info
- Publication number
- JPH0192923A JPH0192923A JP24917787A JP24917787A JPH0192923A JP H0192923 A JPH0192923 A JP H0192923A JP 24917787 A JP24917787 A JP 24917787A JP 24917787 A JP24917787 A JP 24917787A JP H0192923 A JPH0192923 A JP H0192923A
- Authority
- JP
- Japan
- Prior art keywords
- cobalt
- iron oxide
- magnetic powder
- contg
- containing iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は磁性粉末としてコバルト含有酸化鉄磁性粉末
を使用した磁気記録媒体に関し、さらに詳しくは、摩擦
係数が小さくて走行性および耐久性に優れた前記の磁気
記録媒体に関する。
を使用した磁気記録媒体に関し、さらに詳しくは、摩擦
係数が小さくて走行性および耐久性に優れた前記の磁気
記録媒体に関する。
〔従来の技術]
コバルト含有酸化鉄磁性粉末は、従来の磁気記録媒体の
記録素子として汎用されている酸化鉄磁性粉末に比べ、
高保磁力を有するため、高性能磁気記録媒体の記録素子
として、広く使用されている。
記録素子として汎用されている酸化鉄磁性粉末に比べ、
高保磁力を有するため、高性能磁気記録媒体の記録素子
として、広く使用されている。
ところが、この種のコバルト含有酸化鉄磁性粉末は、酸
化鉄磁性粉末を核晶とし、強アルカリ中で反応させるこ
とによって、粒子表面にコバ用1−フェライトINを形
成させてつくられているため、充分に水洗してもpHが
高く、一般にpHを8.5以下にするのが困難で、この
ようなp Ifの高いこの種の磁性粉末を使用して磁気
記録媒体を形成すると、磁性粉末の脂肪酸吸着量が多い
ため、摩擦係数が高くなり、走行性が不安定となる。ま
たこのような欠点を改善し、摩擦係数を小さくするため
、多量の脂肪酸を磁性層中に添加したのでは、磁性層が
弱くなり、かえって耐久性が劣化する。
化鉄磁性粉末を核晶とし、強アルカリ中で反応させるこ
とによって、粒子表面にコバ用1−フェライトINを形
成させてつくられているため、充分に水洗してもpHが
高く、一般にpHを8.5以下にするのが困難で、この
ようなp Ifの高いこの種の磁性粉末を使用して磁気
記録媒体を形成すると、磁性粉末の脂肪酸吸着量が多い
ため、摩擦係数が高くなり、走行性が不安定となる。ま
たこのような欠点を改善し、摩擦係数を小さくするため
、多量の脂肪酸を磁性層中に添加したのでは、磁性層が
弱くなり、かえって耐久性が劣化する。
て問題点を解決するための手段〕
この発明は、かかる現状に鑑み鋭意研究を重ねた結果な
されたもので、BET法による比表面積が35m/i以
上で、粒子表面にコバルトを含む酸化鉄層が形成された
pHが7.0以下のコバルト含有酸化鉄磁性粉末を記録
素子として使用することによって、走行性および耐久性
を充分に向上させたものである。
されたもので、BET法による比表面積が35m/i以
上で、粒子表面にコバルトを含む酸化鉄層が形成された
pHが7.0以下のコバルト含有酸化鉄磁性粉末を記録
素子として使用することによって、走行性および耐久性
を充分に向上させたものである。
この発明において使用するコバルト含有酸化鉄磁性粉末
は、BET法による比表面積が35d/g以上で、粒子
表面にコバルトを含む酸化鉄層が形成されたpHが7.
0以下の磁性粉末であることが好ましく、pHを7.0
以下にしたこの種のコバルト含有酸化鉄磁性粉末は、磁
性層中において脂肪酸をほとんど吸着しない。従って、
この種のBET法による比表面積が35m/g以上で、
粒子表面にコバルトを含む酸化鉄層が形成されたpHが
7.0以下のコバルト含有酸化鉄磁性粉末を使用して磁
性層を形成をすると、優れた電磁変換特性が得られると
ともに、脂肪酸の使用量が少量であっても摩擦係数がき
わめて低くなり、走行性および耐久性が充分に向上され
る。
は、BET法による比表面積が35d/g以上で、粒子
表面にコバルトを含む酸化鉄層が形成されたpHが7.
0以下の磁性粉末であることが好ましく、pHを7.0
以下にしたこの種のコバルト含有酸化鉄磁性粉末は、磁
性層中において脂肪酸をほとんど吸着しない。従って、
この種のBET法による比表面積が35m/g以上で、
粒子表面にコバルトを含む酸化鉄層が形成されたpHが
7.0以下のコバルト含有酸化鉄磁性粉末を使用して磁
性層を形成をすると、優れた電磁変換特性が得られると
ともに、脂肪酸の使用量が少量であっても摩擦係数がき
わめて低くなり、走行性および耐久性が充分に向上され
る。
このようなコバルト含有酸化鉄磁性粉末は、酸化鉄磁性
粉末を、コバルト塩および第一鉄塩とアルカリとを含む
水溶液中で反応させ、酸化鉄磁性粉末の表面にコバルト
を含む酸化鉄層を形成した後、水洗してアルカリを除去
し、その後、弱酸性の金属塩水溶液を、処理液のpHが
7.0以下となるように加えて攪拌し、脱水、乾燥する
ことによって得られる。
粉末を、コバルト塩および第一鉄塩とアルカリとを含む
水溶液中で反応させ、酸化鉄磁性粉末の表面にコバルト
を含む酸化鉄層を形成した後、水洗してアルカリを除去
し、その後、弱酸性の金属塩水溶液を、処理液のpHが
7.0以下となるように加えて攪拌し、脱水、乾燥する
ことによって得られる。
ここで、処理液のpHを7.0以下にするのに使用する
弱酸性の金属塩水溶液としては、硫酸アルミニウム、塩
化アルミニウム、硝酸アルミニウム等の金属塩を溶解し
た水溶液が使用され、これらの水溶液は、処理液のpH
が3.0〜7.0となる範囲内で加えられる。
弱酸性の金属塩水溶液としては、硫酸アルミニウム、塩
化アルミニウム、硝酸アルミニウム等の金属塩を溶解し
た水溶液が使用され、これらの水溶液は、処理液のpH
が3.0〜7.0となる範囲内で加えられる。
また、コバルトを含む酸化鉄層を形成するのに使用され
るコバルト塩としては、塩化コバルト、硫酸コバルト、
硝酸コバルト等が好適なものとして使用され、第一鉄塩
としては塩化第一鉄、硫酸第一鉄、硝酸第−鉄等が好ま
しく使用される。
るコバルト塩としては、塩化コバルト、硫酸コバルト、
硝酸コバルト等が好適なものとして使用され、第一鉄塩
としては塩化第一鉄、硫酸第一鉄、硝酸第−鉄等が好ま
しく使用される。
さらに、アルカリとしては、通常、苛性ソーダが用いら
れ、その好適な配合量は、コバルト塩と第一鉄塩とめ総
量に対して当量以上とするのが好ましい。
れ、その好適な配合量は、コバルト塩と第一鉄塩とめ総
量に対して当量以上とするのが好ましい。
また、出発原料として用いる酸化鉄磁性粉末は、たとえ
ば、いずれもBET法による比表面積が35rrf/g
以上のr−Fe203粉末、Fe3O4粉末、γ−Fe
2O3を水素気流中で部分還元することによって得られ
るγ−Fe2O3とFe3O4との中間の酸化状態の酸
化鉄磁性粉末等が好適なものとして使用される。
ば、いずれもBET法による比表面積が35rrf/g
以上のr−Fe203粉末、Fe3O4粉末、γ−Fe
2O3を水素気流中で部分還元することによって得られ
るγ−Fe2O3とFe3O4との中間の酸化状態の酸
化鉄磁性粉末等が好適なものとして使用される。
この発明の磁気記録媒体を製造するには、常法に準じて
行えばよく、たとえば、BET法による比表面積が35
rd/g以上で、粒子表面にコバルトを含む酸化鉄層が
形成されたpHが7.0以下のコバルト含有酸化鉄磁性
粉末を、結合剤成分、有機溶剤およびその他の添加剤と
ともに混合分散して磁性塗料を調製し、この磁性塗料を
ポリエステルフィルムなどの基体上に、吹きつけもしく
はロール塗りなど任意の手段で塗布し、乾燥すればよい
。
行えばよく、たとえば、BET法による比表面積が35
rd/g以上で、粒子表面にコバルトを含む酸化鉄層が
形成されたpHが7.0以下のコバルト含有酸化鉄磁性
粉末を、結合剤成分、有機溶剤およびその他の添加剤と
ともに混合分散して磁性塗料を調製し、この磁性塗料を
ポリエステルフィルムなどの基体上に、吹きつけもしく
はロール塗りなど任意の手段で塗布し、乾燥すればよい
。
ここで、使用される結合剤成分としては、塩化ビニル−
酢酸ビニル系共重合体、繊維素系樹脂、ポリビニルブチ
ラール系樹脂、ポリウレタン系樹脂、ポリエステル系樹
脂、イソシアネート化合物など一般に磁気記録媒体に使
用される結合剤樹脂がいずれも好適に使用される。
酢酸ビニル系共重合体、繊維素系樹脂、ポリビニルブチ
ラール系樹脂、ポリウレタン系樹脂、ポリエステル系樹
脂、イソシアネート化合物など一般に磁気記録媒体に使
用される結合剤樹脂がいずれも好適に使用される。
また、有機溶剤としては、シクロヘキサノン、メチルイ
ソブチルケトン、メチルエチルケトン、酢酸エチル、ベ
ンゼン、トルエン、ジメチルスルホキシド、テトラヒド
ロフラン、ジオキサンなど、使用する結合剤樹脂を溶解
するのに通した溶剤が、特に制限されることなく、単独
または二種以上混合して使用される。
ソブチルケトン、メチルエチルケトン、酢酸エチル、ベ
ンゼン、トルエン、ジメチルスルホキシド、テトラヒド
ロフラン、ジオキサンなど、使用する結合剤樹脂を溶解
するのに通した溶剤が、特に制限されることなく、単独
または二種以上混合して使用される。
なお、磁性塗料中には、通常使用されている各種添加剤
、たとえば、分散剤、研磨剤、帯電防止剤などを適宜に
添加使用してもよい。
、たとえば、分散剤、研磨剤、帯電防止剤などを適宜に
添加使用してもよい。
次に、この発明の実施例について説明する。
実施例1
BET法による比表面積が43.5m/gの針状T−F
e203粉末3000gを、201の水に分散させ、こ
孔に硫酸コバル)(CoSO4・7H20)501gと
硫酸第一鉄(FeSO+7820)1487gとを加え
て溶解させた。これにlORの水に熔解させた苛性ソー
ダ2970gを加えて、45℃の温度で8時間攪拌して
反応させ、酸化鉄磁性粉末の粒子表面にコバルトを含む
酸化鉄屑を形成した。しかる後、上澄み液のpHが7.
5になるまで水洗してアルカリを除去し、懸濁液のpH
が4.0となるまで塩化アルミニウムの水溶液を加えて
1時間攪拌した後、脱水、乾燥してコバルト含有酸化鉄
磁性粉末を得た。このようにして得られたコバルト含有
酸化鉄磁性粉末のp HをJISK−5101の煮沸、
濾過法によって測定したところ6.5であった。
e203粉末3000gを、201の水に分散させ、こ
孔に硫酸コバル)(CoSO4・7H20)501gと
硫酸第一鉄(FeSO+7820)1487gとを加え
て溶解させた。これにlORの水に熔解させた苛性ソー
ダ2970gを加えて、45℃の温度で8時間攪拌して
反応させ、酸化鉄磁性粉末の粒子表面にコバルトを含む
酸化鉄屑を形成した。しかる後、上澄み液のpHが7.
5になるまで水洗してアルカリを除去し、懸濁液のpH
が4.0となるまで塩化アルミニウムの水溶液を加えて
1時間攪拌した後、脱水、乾燥してコバルト含有酸化鉄
磁性粉末を得た。このようにして得られたコバルト含有
酸化鉄磁性粉末のp HをJISK−5101の煮沸、
濾過法によって測定したところ6.5であった。
次いで、このようにして得られたコバルト含有酸化鉄磁
性粉末を用いて、下記の配合組成により磁性塗料を調整
し、この塗料を14μm厚のポリエステルベースフィル
ム上に乾燥厚が5μmとなるように塗布、乾燥し、表面
処理を行った後、所定の巾に裁断して磁気テープをつく
った。
性粉末を用いて、下記の配合組成により磁性塗料を調整
し、この塗料を14μm厚のポリエステルベースフィル
ム上に乾燥厚が5μmとなるように塗布、乾燥し、表面
処理を行った後、所定の巾に裁断して磁気テープをつく
った。
コバルト含有酸化鉄磁性粉末 100 重量部ニトロ
セルロース 11.25 〃ポリウレタン
樹脂 10.0 〃イソシアネート化合
物 3.75 〃α−A1203
6.0 ”ミリスチン酸
1.0〃シクロへキサノン 1
50〃トルエン 150〃比較例1 実施例1におけるコバルト含有酸化鉄磁性粉末の製造に
おいて、塩化アルミニウム水溶液の添加を省いた以外は
実施例1と同様にしてコバルト含有酸化鉄磁性粉末を得
、このようにして得られたコバルト含有酸化鉄磁性粉末
を用いて、実施例1と同様にして磁気テープをつくった
。ここで、得られたコバルト含有酸化鉄磁性粉末のp
Hを実施例1と同様にして測定したところ、pHは8.
6であった。
セルロース 11.25 〃ポリウレタン
樹脂 10.0 〃イソシアネート化合
物 3.75 〃α−A1203
6.0 ”ミリスチン酸
1.0〃シクロへキサノン 1
50〃トルエン 150〃比較例1 実施例1におけるコバルト含有酸化鉄磁性粉末の製造に
おいて、塩化アルミニウム水溶液の添加を省いた以外は
実施例1と同様にしてコバルト含有酸化鉄磁性粉末を得
、このようにして得られたコバルト含有酸化鉄磁性粉末
を用いて、実施例1と同様にして磁気テープをつくった
。ここで、得られたコバルト含有酸化鉄磁性粉末のp
Hを実施例1と同様にして測定したところ、pHは8.
6であった。
各実施例および比較例で得られた磁気テープについて、
摩擦係数を測定した。
摩擦係数を測定した。
下表はその結果である。
上表から明らかなように、この発明で得られた磁気テー
プ(実施例1)は、従来の磁気テープ(比較例1)に比
し、摩擦係数が小さく、このことから、p Hが7.0
以下のコバルト含有酸化鉄磁性粉末を使用して得られる
この発明の磁気記録媒体は、摩擦係数が小さくて、走行
性および耐久性に優れていることがわかる。
プ(実施例1)は、従来の磁気テープ(比較例1)に比
し、摩擦係数が小さく、このことから、p Hが7.0
以下のコバルト含有酸化鉄磁性粉末を使用して得られる
この発明の磁気記録媒体は、摩擦係数が小さくて、走行
性および耐久性に優れていることがわかる。
特許出願人 日立マクセル株式会社
Claims (1)
- 1、BET法による比表面積が35m^2/g以上で、
粒子表面にコバルトを含む酸化鉄層が形成されたpHが
7.0以下のコバルト含有酸化鉄磁性粉末が含まれてな
る磁性層を有する磁気記録媒体