JP7375499B2 - 積層ポリエステルフィルム及びその製造方法 - Google Patents
積層ポリエステルフィルム及びその製造方法 Download PDFInfo
- Publication number
- JP7375499B2 JP7375499B2 JP2019213481A JP2019213481A JP7375499B2 JP 7375499 B2 JP7375499 B2 JP 7375499B2 JP 2019213481 A JP2019213481 A JP 2019213481A JP 2019213481 A JP2019213481 A JP 2019213481A JP 7375499 B2 JP7375499 B2 JP 7375499B2
- Authority
- JP
- Japan
- Prior art keywords
- polyester film
- resin layer
- film
- laminated polyester
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
そのため、樹脂層によるエステル環状三量体などのオリゴマーの低減策を講じる場合には、ポリエステルフィルムが、従来よりも一段と高度な耐熱性を有し、かつ樹脂層自体のエステル環状三量体封止性能が良好であることが必要とされる。
[1]ポリエステルフィルムと、前記ポリエステルフィルムの少なくとも片面に設けられた樹脂層とを備える積層ポリエステルフィルムであって、
前記樹脂層がフェノール樹脂を含む積層ポリエステルフィルム。
[2]前記樹脂層が処理剤から形成されてなり、該処理剤がさらに架橋剤を含有する上記[1]に記載の積層ポリエステルフィルム。
[3]前記樹脂層の厚さが0.001~0.15μmである上記[1]又は[2]に記載の積層ポリエステルフィルム。
[4]前記フェノール樹脂がレゾール型フェノール樹脂である上記[1]~[3]のいずれか1項に記載の積層ポリエステルフィルム。
[5]ポリエステルフィルムと、前記ポリエステルフィルムの少なくとも片面に設けられた樹脂層とを備える積層ポリエステルフィルムの製造方法であって、前記ポリエステルフィルムの少なくとも片面にフェノール樹脂を含む処理剤によって前記樹脂層を形成する、ポリエステルフィルムの製造方法。
本発明の積層ポリエステルフィルムは、ポリエステルフィルムと、ポリエステルフィルムの少なくとも片面に設けられた樹脂層とを備える。
本発明で使用するポリエステルフィルムは、単層構造であっても多層構造であってもよい。多層構造の場合、2層構造、3層構造などでもよいし、本発明の要旨を逸脱しない限り、4層またはそれ以上の多層であってもよく、層数は特に限定されない。また、ポリエステルフィルムは、二軸延伸ポリエステルフィルムが好ましい。
共重合ポリエステルは、例えば、ジカルボン酸成分とグリコール成分の重縮合ポリマーであるとよく、共重合ポリエステルにおいて使用するジカルボン酸成分としては、イソフタル酸、フタル酸、テレフタル酸、2,6-ナフタレンジカルボン酸、アジピン酸、セバシン酸、オキシカルボン酸(例えば、p-オキシ安息香酸など)等の一種または二種以上が挙げられる。また、グリコール成分として、エチレングリコール、ジエチレングリコール、プロピレングリコール、ブタンジオール、4-シクロヘキサンジメタノール、ネオペンチルグリコール等の一種または二種以上が挙げられる。
また、共重合体ポリエステルは、ジカルボン酸成分、グリコール成分以外の二官能性化合物由来の構成単位を含んでもよく、ジカルボン酸成分、グリコール成分以外の二官能性化合物由来の構成単位は、ポリエステルを構成する全構成単位の総モルに対して、20モル%以下であることが好ましく、10モル%以下であることがより好ましい。二官能性化合物としては、各種のヒドロキシカルボン酸、芳香族ジオールなどが挙げられる。
ポリエステルの極限粘度は、特に限定されないが、製膜性、生産性などの観点から、0.45~1.0dl/gが好ましく、0.5~0.9dl/gがより好ましい。
ポリエステルフィルムにおけるリン元素含有量は、好ましくは1~300ppm、より好ましくは3~200ppm、さらに好ましくは5~100ppmの範囲である。リン化合物の含有量を上記上限値以下とすることで、リン化合物がゲル化や異物の原因となることを防止できる。また、上記下限値以上とすることで、チタン化合物の活性を十分に下げることができ、黄色味のあるフィルムとなることを防止できる。
なお、リン元素含有量は、ポリエステルフィルムが多層である場合には、チタン元素を含有する層におけるリン元素含有量が上記範囲内となるとよい。
また、ポリエステルフィルムを3層以上の構成とし、ポリエステルフィルムの最外層を、エステル環状三量体の含有量が少ないポリエステル原料を用いた層とすることで、熱処理後のエステル環状三量体の析出量を抑えてもよい。
また、ポリエスエルは、エステル化もしくはエステル交換反応をした後に、さらに反応温度を高くして減圧下で溶融重縮合して得てもよい。
ポリエステルフィルムが粒子を含有しない場合、あるいは含有量が少ない場合は、ポリエステルフィルムの透明性が高くなり、外観が良好なフィルムとなるが、滑り性が不十分となる場合がある。そのため、後述する樹脂層中に粒子を入れることにより、滑り性を向上させたりするとよい。
これら一連の粒子は、必要に応じて2種類以上を併用してもよい。
ポリエステルフィルムが、多層である場合には、少なくともいずれか1つの層に粒子を含有させるとよいが、最外層に粒子を含有させることが好ましい。例えば、最外層、中間層、及び最外層をこの順に備える多層構造においては、各最外層に粒子を含有させるとよい。
本発明において、樹脂層は、上記したポリエステルフィルムの少なくとも片面に設けられる層であり、フェノール樹脂を含有する。樹脂層は、ポリエステルフィルムの片面のみに設けられてもよいし、両面に設けられてもよい。
本発明において、積層ポリエステルフィルムは、フェノール樹脂を含有する樹脂層を有することで、高温下に長時間曝されても、ポリエステルフィルムからエステル環状三量体がフィルム表面に析出することを抑制できる。その理由は定かではないが、フェノール樹脂が三次元の緻密な網目構造を形成するため、その網目構造が高温下でも長時間にわたって維持され、その網目構造によりフィルム中に含まれるエステル環状三量体の析出が防止できるためと考えられる。また、エステル環状三量体の析出を防止することで、異物が発生したり、フィルムヘーズが大きくなったりすることも防止できる。
本発明におけるフェノール樹脂としては、レゾール型フェノール樹脂及びノボラック型フェノール樹脂が挙げられる。レゾール型フェノール樹脂は、フェノール類と過剰のアルデヒド類とを塩基性触媒の存在下で反応させることで得られる熱硬化性樹脂である。ノボラック型フェノール樹脂は、フェノール類とアルデヒド類とを酸触媒の存在下で反応させることで得られる熱可塑性樹脂である。なお、レゾール型フェノール樹脂を使用する場合、レゾール型フェノール樹脂を硬化することで樹脂層を形成するとよい。レゾール型フェノール樹脂及びノボラック型フェノール樹脂は、それぞれ従来公知のフェノール樹脂の合成条件により製造できる。
アルデヒド類としては特に制限がなく、例えば、ホルムアルデヒド、アセトアルデヒド、パラホルムアルデヒド、フルフラール、ブチルアルデヒド、アセタール類等が挙げられる。これらの中では、樹脂層を緻密な網目構造とする観点からは、ホルムアルデヒド、パラホルムアルデヒドが好ましい。アルデヒド類は、1種単独で使用してもよいし、2種以上を併用してもよい。
酸触媒としては特に制限はないが、例えば、塩酸、硫酸、ぎ酸、酢酸、p-トルエンスルホン酸及びシュウ酸が挙げられる。これらの酸触媒は、1種を単独で又は2種以上を組み合わせて用いることができる。
また、後述する架橋剤を使用する場合、架橋剤を一定量以上配合するために、フェノール樹脂の含有量は、処理剤における不揮発成分に対して、通常99質量%以下、好ましくは95質量%以下、より好ましくは92質量%以下、さらに好ましくは90質量%以下である。
本発明の樹脂層の形成に用いる処理剤は、さらに架橋剤を含有してもよい。すなわち、樹脂層は、架橋剤により架橋されていてもよい。本発明の樹脂層は、架橋剤が用いられなくても、エステル環状三量体の析出を抑制できるが、樹脂層の耐久性及び塗布性向上の観点からは架橋剤を使用することが好ましい。
架橋剤としては、種々公知の架橋剤が使用できるが、例えば、メラミン化合物、オキサゾリン化合物、エポキシ化合物、イソシアネート系化合物、カルボジイミド系化合物、シランカップリング化合物等が挙げられる。これらの中でもより緻密な樹脂層を形成し、高温下で長時間曝された場合におけるエステル環状三量体の析出防止効果という観点から、メラミン化合物が好適に用いられる。架橋剤は、1種単独で使用してもよいし、2種以上を併用してもよい。
また、メラミン化合物としては、単量体、あるいは2量体以上の多量体のいずれであってもよく、あるいはこれらの混合物を用いてもよい。さらに、メラミンの一部に尿素等を共縮合したものも使用できる。さらに、メラミン化合物の反応性を上げるために、処理剤には、さらに触媒を配合してもよい。
また、樹脂層を形成するための処理剤には、上記したフェノール樹脂、架橋剤以外のポリマー成分を含有させることも可能である。ポリマー成分を併用することで、例えば、樹脂層の外観の向上を図ることができ、また、樹脂層の表面に種々の表面機能層又は透明電極膜などを形成したときに、その表面機能層などに対する密着性を向上させることなどもできる。処理剤におけるポリマー成分の含有量は、特に限定されないが、高温下で長時間曝された時におけるエステル環状三量体の析出を効果的に抑えることから、多くし過ぎないことが好ましく、具体的には質量基準でフェノール樹脂より少なくすることが好ましく、フェノール樹脂の50質量%以下がより好ましく、フェノール樹脂の20質量%以下がさらに好ましい。
ポリマー成分の具体例としては、ポリエステル樹脂、ポリアクリル樹脂、ウレタン樹脂、ポリビニル(ポリビニルアルコール等)、導電性ポリマー、ポリアルキレングリコール、ポリアルキレンイミン、メチルセルロース、ヒドロキシセルロース、でんぷん類等が挙げられる。また、ポリマー成分は、活性エネルギー照射や加熱により重合してポリマーとなる光重合性成分、熱重合性成分であってもよい。
本発明の処理剤において粒子の含有量は、処理剤中の不揮発成分に対して、通常0.1~20質量%、好ましくは1~15質量%、より好ましくは2~10質量%の範囲である。粒子の含有量を上記範囲内とすることで、ヘーズ値を良好にしつつ、ブロッキング、滑り性を適切に改良できる。
本発明における積層ポリエステルフィルムは、ポリエステルフィルムの少なくとも片面にフェノール樹脂を含む処理剤によって前記樹脂層を形成することで製造できる。樹脂層は、上記した処理剤を塗布液として、ポリエステルフィルムの少なくとも片面に塗布して形成すればよい。樹脂層は、ポリエステルフィルムに処理剤を塗布した後に必要に応じて加熱などして、適宜乾燥、硬化などさせるとよい。
それゆえ、コーティング後に施される熱処理が他の方法では達成されない高温とすることができるために、樹脂層の造膜性が向上し、樹脂層とポリエステルフィルムをより強固に密着させることができ、さらには、強固な樹脂層とすることができる。
一方、インラインコーティングにより樹脂層を設ける場合、通常、70~270℃で3~200秒間を目安として熱処理を行うのがよい。
ハードコート層は、例えば、ポリエステルフィルムの樹脂層が設けられない面に設けられるとよく、例えばポリエステルフィルムの一方の面に樹脂層が設けられ、他方の面にハードコート層が設けられるとよい。また、ハードコート層は、ポリエステルフィルムの樹脂層が設けられる面に設けられてもよく、例えば、ポリエステルフィルムの両面に樹脂層が設けられる場合には、その一方の樹脂層の上に設けられるとよい。
したがって、他の層を有する積層ポリエステルフィルムにおいては、樹脂層が最外層を構成してもよいが、必ずしも最外層となる必要もない。
ハードコート剤は、必要に応じて、架橋剤、重合開始剤、滑剤、可塑剤、有機粒子、無機粒子、防汚剤、酸化防止剤、触媒等の添加剤を含有してもよい。
ハードコート層の厚さは、特に限定されないが、例えば0.5~15μm、好ましくは1~10μmの範囲である。
本発明における積層ポリエステルフィルムは、フィルムヘーズが、好ましくは5.0%以下、より好ましくは3.0%以下、さらに好ましくは2.0%以下である。積層ポリエステルフィルムは、フィルムヘーズを5.0%以下とすることで、視認性及び外観が良好となる。積層ポリエステルフィルムは、例えば、タッチパネル用等に使用される場合など、高度な透明性が要求される場合があるが、そのような場合でもフィルムヘーズを5.0%以下とすることで好適に使用できる。なお、フィルムヘーズとは、初期のフィルムヘーズであり、後述する熱処理をする前のヘーズ値である。
積層ポリエステルフィルムは、透明導電性積層体の基材に使用する場合、積層ポリエステルフィルムの表面にITO膜などの透明導電膜が設けられるとよい。透明導電膜は、積層ポリエステルフィルムの樹脂層が設けられた面に設けられてもよいし、樹脂層が設けられない面に設けられてもよい。また、上記のとおりハードコート層が設けられる場合には、例えば、積層ポリエステルフィルムのハードコート層が設けられた面とは反対側の面に透明導電膜が設けられるとよく、この場合には透明電極膜は、積層ポリエステルフィルムの樹脂層が設けられた面に設けられることが好ましい。
一般的に「シート」とは、JISにおける定義上、薄く、その厚さが長さと幅のわりには小さく平らな製品をいい、一般的に「フィルム」とは、長さ及び幅に比べて厚さが極めて小さく、最大厚さが任意に限定されている薄い平らな製品で、通常、ロールの形で供給されるものをいう(日本工業規格;JIS K6900)。しかし、シートとフィルムの境界は定かでなく、本発明において文言上両者を区別する必要がないので、本発明においては、「フィルム」と称する場合でも「シート」を含むものとし、「シート」と称する場合でも「フィルム」を含むものとする。
また、「X以上」(Xは任意の数字)と記載した場合、特に断らない限り「好ましくはXより大きい」の意を包含し、「Y以下」(Yは任意の数字)と記載した場合、特にことわらない限り「好ましくはYより小さい」の意も包含するものである。
(1)ポリエステルの極限粘度の測定方法
ポリエステル1gを精秤し、フェノール/テトラクロロエタン=50/50(質量比)の混合溶媒100mlを加えて溶解させ、30℃で測定した。
遠心沈降式粒度分布測定装置(株式会社島津製作所社製SA-CP3型)を使用して測定した等価球形分布における積算(重量基準)50%の値を平均粒径とした。
樹脂層の表面をRuO4で染色し、エポキシ樹脂中に包埋した。その後、超薄切片法により作成した切片をRuO4で染色し、樹脂層断面をTEM(株式会社日立ハイテクノロジーズ製 H-7650、加速電圧100kV)を用いて測定した。
各実施例、比較例において積層ポリエステルフィルムの樹脂層がむき出しとなる状態でケント紙と重ねて固定し、窒素雰囲気下で、150℃で90分間放置して熱処理を行った。ただし、比較例1では、樹脂層が設けられないので、ポリエステルフィルムの一方の表面がむき出しとなる状態でケント紙を重ねた。
試料フィルムをJIS-K-7136に準じ、株式会社村上色彩技術研究所製ヘーズメーター「HM-150」により、フィルムヘーズを測定した。
各実施例、比較例において積層ポリエステルフィルムの樹脂層が設けられた面とは反対側の面に、ジペンタエリスリトールヘキサアクリレート80質量部、2-ヒドロキシ-3-フェノキシプロピルアクリレート20質量部、光重合開始剤(商品名:イルガキュア184、チバスペシャルティケミカルズ株式会社製)5質量部、及びメチルエチルケトン200質量部からなる混合塗液を乾燥後の厚さが3μmになるように塗布して乾燥させ、かつ紫外線を照射して硬化させハードコート層を形成した。なお、比較例1では、ポリエステルフィルムに樹脂層が設けられず、ポリエステルフィルムの一方の面にハードコート層を形成した。ハードコート層を有する積層ポリエステルフィルムのヘーズを(5)の方法で測定した。次いで(4)項の方法で加熱した後、(5)の方法でヘーズを測定した。熱処理後のヘーズと熱処理前のヘーズの差を計算し、フィルムヘーズ変化量とした。フィルムヘーズ変化量が低いほど、高温処理によるエステル環状三量体の析出が少ないことを示し、良好である。
各実施例、比較例において、積層ポリエステルフィルムを空気中、180℃で30分間加熱する。その後、熱処理をした当該フィルムを上部が開いている縦横10cm、高さ3cmになるように、測定面(樹脂層)を内面として箱形の形状を作成した。ただし、比較例1では、樹脂層が設けられないので、ポリエステルフィルムの一方の面を測定面とした。
次いで、上記の方法で作成した箱の中にDMF(ジメチルスルホアミド)4mlを入れて3分間放置した後、DMFを回収し、液体クロマトグラフィー(株式会社島津製作所製:LC-7A 移動相A:アセトニトリル、移動相B:2質量%酢酸水溶液、カラム:三菱化学株式会社製「MCI GEL ODS 1HU」、カラム温度:40℃、流速:1ml/分、検出波長:254nm)に供給して、DMF中のエステル環状三量体量を求め、この値を、DMFを接触させたフィルム面積で割って、フィルム表面エステル環状三量体量(mg/m2)とした。DMF中のエステル環状三量体は、標準試料ピーク面積と測定試料ピーク面積のピーク面積比より求めた(絶対検量線法)。なお、標準試料の作成は、予め分取したエステル環状三量体を正確に秤量し、正確に秤量したDMFに溶解し作成した。
<ポリエステル(A)の製造方法>
テレフタル酸ジメチル100質量部、エチレングリコール60質量部、エチルアシッドフォスフェートを生成するポリエステルに対して30ppm、及び触媒として酢酸マグネシウム・四水和物を生成するポリエステルに対して100ppmを混合して、窒素雰囲気下、260℃でエステル化反応をさせた。引き続いて、テトラブチルチタネートを生成するポリエステルに対して50ppm添加し、2時間30分かけて280℃まで昇温すると共に、絶対圧力0.3kPaまで減圧し、さらに80分間溶融重縮合させ、極限粘度0.63dl/gのポリエステル(A)を得た。
テレフタル酸ジメチル100質量部、エチレングリコール60質量部、及び触媒として酢酸マグネシウム・四水和物を生成するポリエステルに対して900ppmを混合して、窒素雰囲気下、225℃でエステル化反応をさせた。引き続いて、正リン酸を生成するポリエステルに対して3500ppm、二酸化ゲルマニウムを生成するポリエステルに対して70ppm添加し、2時間30分かけて280℃まで昇温すると共に、絶対圧力0.4kPaまで減圧し、さらに85分間溶融重縮合させ、極限粘度0.64dl/gのポリエステル(B)を得た。
ポリエステル(A)の製造方法において、溶融重縮合前に平均粒径2μmのシリカ粒子を0.3質量部添加する以外はポリエステル(A)の製造方法と同様の方法を用いてポリエステル(C)を得た。
・フェノール樹脂(I): レゾール型フェノール樹脂の水分散体
・メラミン化合物(II):ヘキサメトキシメチロールメラミン
・粒子(III):平均粒径0.07μmのシリカ粒子
ポリエステル(A)、(B)、(C)をそれぞれ91質量%、3質量%、6質量%の割合で混合した混合原料を最外層(表層)の原料とし、ポリエステル(A)、(B)をそれぞれ97質量%、3質量%の割合で混合した混合原料を中間層の原料として、2台の押出機に各々を供給し、各々285℃で溶融した後、40℃に設定した冷却ロール上に、2種3層(表層/中間層/表層=1:18:1の吐出量)の層構成で共押出し冷却固化させて未延伸シートを得た。
次いで、ロール周速差を利用してフィルム温度85℃で縦方向に3.4倍延伸した後、この縦延伸フィルムの片面に、下記表1に示す配合を有する塗布液1を塗布した。塗布液1が塗布されたフィルムは、テンターに導き、横方向に110℃で4.3倍延伸し、235℃で30秒間熱処理を行い、塗布液1を乾燥かつ硬化させた後、横方向に2%弛緩し、厚さ(乾燥後)が0.10μmの樹脂層を有する厚さ50μmの二軸延伸ポリエステルフィルムを得た。
得られた積層ポリエステルフィルムは、加熱処理によるフィルムヘーズ変化量が小さく、エステル環状三量体の析出量も少なく良好であった。このフィルムの特性を下記表2に示す。
実施例1において、得られる樹脂層の厚さを表2に示すとおりに変更した以外は実施例1と同様に実施して、積層ポリエステルフィルムを得た。得られた積層ポリエステルフィルムは表2に示すとおり、加熱処理によるフィルムヘーズの上昇はなく、エステル環状三量体の析出量も少なく良好であった。
塗布液の組成を表1に示す組成に変更する以外は実施例2と同様に実施して、積層ポリエステルフィルムを得た。得られた積層ポリエステルフィルムは表2に示すとおり、加熱処理によるフィルムヘーズの上昇は実質的になく、エステル環状三量体の析出量も少なく良好であった。
樹脂層を設けないこと以外は実施例1と同様にして実施してポリエステルフィルムを得た。得られたポリエステルフィルムを評価したところ、表2に示すとおり、加熱処理によるフィルムヘーズが大きく上昇し、エステル環状三量体の析出も多いものであった。
塗布液の組成を表1に示す組成に変更する以外は実施例2と同様に実施して、積層ポリエステルフィルムを得た。得られた積層ポリエステルフィルムを評価したところフィルムヘーズの変化量と加熱処理によるエステル環状三量体の析出が多いものであり、外観が悪くかつ工程の汚染が懸念されるものであった。
※表1における各質量%は、処理剤における不揮発成分に対する値である。
Claims (7)
- ポリエステルフィルムと、前記ポリエステルフィルムの少なくとも片面に設けられた樹脂層とを備える積層ポリエステルフィルムであって、前記樹脂層がフェノール樹脂を含み、180℃、30分間の熱処理後の前記樹脂層表面における、ジメチルホルムアミドにより抽出されたエステル環状三量体量が3.0mg/m2以下であり、
前記積層ポリエステルフィルムの前記樹脂層が設けられた片面とは反対側の面に、ジペンタエリスリトールヘキサアクリレート80質量部、2-ヒドロキシ-3-フェノキシプロピルアクリレート20質量部、光重合開始剤5質量部、及びメチルエチルケトン200質量部からなる混合塗液を乾燥後の厚さが3μmになるように塗布して乾燥させ、かつ紫外線を照射して硬化させハードコート層を形成したフィルムに対する、窒素雰囲気下、150℃、90分間の熱処理によるフィルムヘーズ変化量が、1.5%以下である、積層ポリエステルフィルム。 - 前記樹脂層が処理剤から形成されてなり、該処理剤が架橋剤を含有する請求項1に記載の積層ポリエステルフィルム。
- 前記樹脂層の厚さが0.001~0.15μmである請求項1又は2に記載の積層ポリエステルフィルム。
- 前記フェノール樹脂がレゾール型フェノール樹脂である請求項1~3のいずれか1項に記載の積層ポリエステルフィルム。
- ポリエステルフィルムと、前記ポリエステルフィルムの少なくとも片面に設けられた樹脂層とを備え、180℃、30分間の熱処理後の前記樹脂層表面における、ジメチルホルムアミドにより抽出されたエステル環状三量体量が3.0mg/m2以下である、積層ポリエステルフィルムの製造方法であって、
前記積層ポリエステルフィルムの前記樹脂層が設けられた片面とは反対側の面に、ジペンタエリスリトールヘキサアクリレート80質量部、2-ヒドロキシ-3-フェノキシプロピルアクリレート20質量部、光重合開始剤5質量部、及びメチルエチルケトン200質量部からなる混合塗液を乾燥後の厚さが3μmになるように塗布して乾燥させ、かつ紫外線を照射して硬化させハードコート層を形成したフィルムに対する、窒素雰囲気下、150℃、90分間の熱処理によるフィルムヘーズ変化量が、1.5%以下であり、
前記ポリエステルフィルムの少なくとも片面にフェノール樹脂を含む処理剤によって前記樹脂層を形成する、積層ポリエステルフィルムの製造方法。 - 透明導電性積層体の基材用である、請求項1~4のいずれか1項に記載の積層ポリエステルフィルム。
- 前記積層ポリエステルフィルムが、透明導電性積層体の基材用である、請求項5に記載の積層ポリエステルフィルムの製造方法。