JP7012577B2 - マイクロカプセル剤積層シート - Google Patents
マイクロカプセル剤積層シート Download PDFInfo
- Publication number
- JP7012577B2 JP7012577B2 JP2018060862A JP2018060862A JP7012577B2 JP 7012577 B2 JP7012577 B2 JP 7012577B2 JP 2018060862 A JP2018060862 A JP 2018060862A JP 2018060862 A JP2018060862 A JP 2018060862A JP 7012577 B2 JP7012577 B2 JP 7012577B2
- Authority
- JP
- Japan
- Prior art keywords
- microcapsule
- group
- salt
- base material
- microcapsules
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の一実施形態に係るマイクロカプセル剤積層シート(本明細書においては、「積層シート」と略記することがある)は、シート状の基材(本明細書においては、「基材」と略記することがある)と、前記基材上に積層され、かつマイクロカプセル剤を含有するマイクロカプセル剤含有層と、を備えており、前記マイクロカプセル剤の体積基準中位径(本明細書においては、「体積基準中位径D」又は「D」と称することがある)が25μm以下であり、前記マイクロカプセル剤の膜形成成分がポリウレアであり、前記基材の、前記マイクロカプセル剤含有層が積層されている側の面(本明細書においては、「第1面」と称することがある)の、JIS B0601:2001に準拠して測定された表面粗さ(本明細書においては、「表面粗さ」又は「Ra」と略記することがある)が、2μm以下のものである。
このような薬剤放出抑制効果を奏する本実施形態の積層シートは、マイクロカプセル内の薬剤の効果を、安定して長期間持続させることができる。
本実施形態の積層シートにおいて想定される、目的外の加圧時の温度は、例えば、好ましくは5~35℃である。
本実施形態の積層シートにおいて想定される、目的外の加圧時間は、例えば、好ましくは12時間以上である。
以下、図面を参照しながら、本実施形態について詳細に説明する。
基材11の形状は、シート状であれば、特に限定されない。
基材11の構成材料として、より具体的には、例えば、紙、樹脂等が挙げられる。
前記樹脂としては、例えば、ポリエチレン、ポリプロピレン、ポリ塩化ビニル、ポリスチレン、ポリ酢酸ビニル、アクリル系樹脂、AS樹脂、ABS樹脂、ポリアミド、ポリアセタール、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリトリメチレンテレフタレート、ポリエチレンナフタレート、ポリブチレンナフタレート、ポリフェニレンスルファイド、ポリスルホン、ポリカーボネート、エポキシ樹脂、メラミン樹脂、フェノール樹脂、尿素樹脂、ポリウレタン、ポリイミド、エチレン酢酸ビニル共重合樹脂等の合成樹脂;ポリブタジエンゴム、スチレン・ブタジエンゴム、アクリロニトリル・ブタジエンゴム、ブチルゴム、クロロプレンゴム、ポリイソブチレンゴム、エチレンゴム、プロピレンゴム、シリコンゴム等の合成ゴム等が挙げられる。
なお、本明細書において、「(メタ)アクリル酸」とは、「アクリル酸」及び「メタクリル酸」の両方を包含する概念とする。
なお、本明細書においては、基材の場合に限らず、「複数層が互いに同一でも異なっていてもよい」とは、「すべての層が同一であってもよいし、すべての層が異なっていてもよく、一部の層のみが同一であってもよい」ことを意味し、さらに「複数層が互いに異なる」とは、「各層の材質及び厚さの少なくとも一方が互いに異なる」ことを意味する。
ここで、「基材11の厚さ」とは、基材11全体の厚さを意味し、例えば、複数層からなる基材11の厚さとは、基材11を構成するすべての層の合計の厚さを意味する。
本明細書において、表面粗さ(Ra)とは、特に断りのない限り、JIS B0601:2001(ISO4287:1997)に準拠して測定されたものであり、算術平均粗さを意味する。
基材11の前記表面粗さは、例えば、0.1μm以上であることが好ましく、0.5μm以上であることがより好ましい。
基材11としては、市販品を用いてもよい。
例えば、前記表面粗さ(Ra)は、基材11に対するカレンダー処理等の加圧処理によって、低減できる。また、前記表面粗さ(Ra)は、基材11に対する硬質微粒子の衝突処理等の粗化処理によって、増大させることができる。
マイクロカプセル剤含有層12は、マイクロカプセル剤を含有する。
マイクロカプセル剤含有層12は、前記マイクロカプセル剤を含有していることにより、マイクロカプセル剤中の芯物質に由来する作用を有する。すなわち、積層シート1は、マイクロカプセル剤含有層12を備えていることで、マイクロカプセル剤含有層12に特有の効果を発現する。
さらに、マイクロカプセル剤含有層12の厚さは、18~100μmであることが好ましく、18~50μmであることがより好ましく、18~30μmであることが特に好ましい。マイクロカプセル剤含有層12の厚さがこのような範囲であることで、マイクロカプセル剤含有層での薬剤放出抑制効果がより高くなる。
次に、本実施形態におけるマイクロカプセル剤について、詳しく説明する。
前記マイクロカプセル剤は、重縮合物であるポリウレアを膜形成成分とし、芯物質を内包する。
本明細書においては、膜形成成分が微小なカプセル状となって、その内部に芯物質を内包しているものを「マイクロカプセル剤」と称する。本明細書において、単なる「マイクロカプセル」との記載は、マイクロカプセル剤のうち、芯物質を除いたものを意味する。
前記芯物質は、マイクロカプセル剤の使用目的に応じて、適宜選択すればよく、特に限定されない。
芯物質としては、例えば、医薬、殺菌剤、農薬、香料、その他の化学反応剤(特定の化学物質と反応することにより、この化学物質の作用を阻害する、医薬、殺菌剤、農薬及び香料以外の薬剤)等が挙げられる。前記その他の化学反応剤で好ましいものとしては、例えば、ホルムアルデヒド反応剤が挙げられる。
ホルムアルデヒド反応剤は、前記芯物質の中でも、特に好ましいものの一例として挙げられる。
芯物質としてアミノ基及びアミノ基塩形成基を有しないものを用いることで、芯物質を内包するマイクロカプセル(すなわちマイクロカプセル剤)を、より安定して形成できる。
ここで、前記カチオン部としては、例えば、アミノ基(-NH2)の窒素原子に水素イオン(H+)が配位結合したものが挙げられる。この場合の前記アニオンの価数は特に限定されず、1(1価)であってもよいし2(2価)以上であってもよい。前記アニオンが1価である場合、前記塩を形成している前記アニオンの個数と、前記カチオン部の個数は、共に1である。また、前記アニオンがn価(nは2以上の整数である)である場合、前記塩を形成している前記アニオンの個数は通常1であり、前記カチオン部の個数はn以下であり、通常はnである。この場合、複数個の前記カチオン部は、すべて同一であってもよいし、すべて異なっていてもよく、一部のみ同一であってもよい。
芯物質は、「-NH-」基又は「-NH-」塩形成基を有する場合、これら基中の窒素原子は、既に共有結合している1個の水素原子以外に、さらに水素原子と共有結合することはない。
ここで、前記カチオン部としては、例えば、「-NH-」基の窒素原子に水素イオン(H+)が配位結合したものが挙げられる。この場合の前記アニオンの価数は特に限定されず、1(1価)であってもよいし、2(2価)以上であってもよい。前記アニオンが1価である場合、前記塩を形成している前記アニオンの個数と、前記カチオン部の個数は、共に1である。また、前記アニオンがm価(mは2以上の整数である)である場合、前記塩を形成している前記アニオンの個数は通常1であり、前記カチオン部の個数はm以下であり、mであることが好ましい。この場合、複数個の前記カチオン部は、すべて同一であってもよいし、すべて異なっていてもよく、一部のみ同一であってもよい。
好ましい前記無機アニオンとしては、例えば、硝酸イオン、硫酸イオン、硫酸水素イオン、炭酸イオン、炭酸水素イオン、ハロゲン化物イオン等が挙げられ、前記ハロゲン化物イオンとしては、フッ化物イオン、塩化物イオン、臭化物イオン、ヨウ化物イオン等が挙げられる。
好ましい前記有機アニオンとしては、例えば、カルボン酸のアニオン、スルホン酸のアニオン等が挙げられる。
前記カルボン酸のアニオンは、モノカルボン酸(1価カルボン酸)のアニオンであってもよいし、ジカルボン酸、トリカルボン酸等の多価カルボン酸のアニオンであってもよい。
すなわち、1分子の芯物質が2個以上の前記アニオンを有する場合、これら2個以上のアニオンは、すべて同一であってもよいし、すべて異なっていてもよく、一部のみ同一であってもよい。
ただし、芯物質は、分子全体として電気的に中性であること、すなわち、芯物質1分子中の前記カチオン部の価数の合計値とアニオンの価数の合計値とは、同じであることが好ましい。
芯物質が環状構造を有する場合、「-NH-」基及び「-NH-」塩形成基は、前記環状構造の環骨格を形成していてもよいし、環骨格を形成せずに、環骨格を形成している基に結合していてもよい。
1個のカルボニル基にこのように結合している「-NH-」基及び「-NH-」塩形成基の総数は、1個のみであってもよいし、2個であってもよい。
1個の窒素原子にこのように結合している「-NH-」基及び「-NH-」塩形成基の総数は、1個のみであってもよいし、2個であってもよいが、1個であることが好ましい。
なお、「-NH-C(=O)-NH-」塩形成基及び「-HN-N(-)-NH-」塩形成基において、「-NH-」塩形成基の数は1個であってもよいし、2個以上であってもよい。
ヒダントイン、2-イミダゾリジノン、5-ピラゾロン、3-ピラゾロン、1,2,4-トリアゾール-3-オン、ピラゾール、1,2,3-トリアゾール及び1,2,4-トリアゾールはいずれも、環員数が5の化合物である。フタルイミド及び1,2,3-ベンゾトリアゾールはいずれも、環員数が9の化合物である。グリコールウリルは環員数が8の化合物である。
なお、ここに示す化合物は、芯物質のごく一例に過ぎない。
また、2-イミダゾリジノンの塩としては、例えば、2-イミダゾリジノン中の2個の「-NH-」基のいずれか一方又は両方が、「-NH-」塩形成基となったものが挙げられる。
また、5-ピラゾロンの塩としては、例えば、5-ピラゾロン中の「-NH-」基が「-NH-」塩形成基となったもの、水素原子と結合していない方の窒素原子が塩を形成したもの、及び、「-NH-」基が「-NH-」塩形成基となり、かつ水素原子と結合していない方の窒素原子が塩を形成したもの、が挙げられる。
また、3-ピラゾロンの塩としては、例えば、3-ピラゾロン中の2個の「-NH-」基のいずれか一方又は両方が、「-NH-」塩形成基となったものが挙げられる。
また、1,2,4-トリアゾール-3-オンの塩としては、例えば、1,2,4-トリアゾール-3-オン中の2個の「-NH-」基のいずれか一方又は両方が、「-NH-」塩形成基となったものが挙げられる。
また、フタルイミドの塩としては、例えば、フタルイミド中の1個の「-NH-」基が、「-NH-」塩形成基となったものが挙げられる。
また、グリコールウリルの塩としては、例えば、グリコールウリル中の4個の「-NH-」基の少なくとも1個が、「-NH-」塩形成基となったものが挙げられる。
また、1,2,3-トリアゾールの塩としては、例えば、1,2,3-トリアゾール中の「-NH-」基が「-NH-」塩形成基となったもの、水素原子と結合していない方の2個の窒素原子のいずれか一方又は両方が塩を形成したもの、及び、「-NH-」基が「-NH-」塩形成基となり、かつ水素原子と結合していない方の2個の窒素原子のいずれか一方又は両方が塩を形成したもの、が挙げられる。
また、1,2,4-トリアゾールの塩としては、例えば、1,2,4-トリアゾール中の「-NH-」基が「-NH-」塩形成基となったもの、水素原子と結合していない方の2個の窒素原子のいずれか一方又は両方が塩を形成したもの、及び、「-NH-」基が「-NH-」塩形成基となり、かつ水素原子と結合していない方の2個の窒素原子のいずれか一方又は両方が塩を形成したもの、が挙げられる。
また、1,2,3-ベンゾトリアゾールの塩としては、例えば、1,2,3-ベンゾトリアゾール中の「-NH-」基が「-NH-」塩形成基となったもの、水素原子と結合していない方の2個の窒素原子のいずれか一方又は両方が塩を形成したもの、及び、「-NH-」基が「-NH-」塩形成基となり、かつ水素原子と結合していない方の2個の窒素原子のいずれか一方又は両方が塩を形成したもの、が挙げられる。
本明細書において「誘導体」とは、元の化合物の1個又は2個以上の水素原子が水素原子以外の基で置換されているものを意味する。
すなわち、本明細書においては、置換基を有する2-イミダゾリジノンを「2-イミダゾリジノン誘導体」と称し、2-イミダゾリジノン及び2-イミダゾリジノン誘導体を包括して「2-イミダゾリジノン系化合物」と称することがある。そして、置換基を有する2-イミダゾリジノンの塩、すなわち、2-イミダゾリジノン誘導体の塩とは、2-イミダゾリジノン誘導体が、2-イミダゾリジノンの場合と同様に、塩を形成したものである。「置換基を有していてもよい2-イミダゾリジノン及びその塩」とは、換言すると、2-イミダゾリジノン系化合物及びその塩のことである。
このような直鎖状又は分岐鎖状のアルキル基としては、例えば、メチル基、エチル基、n-プロピル基、イソプロピル基、n-ブチル基、イソブチル基、sec-ブチル基、tert-ブチル基、n-ペンチル基、イソペンチル基、ネオペンチル基、tert-ペンチル基、1-メチルブチル基、n-ヘキシル基、2-メチルペンチル基、3-メチルペンチル基、2,2-ジメチルブチル基、2,3-ジメチルブチル基、n-ヘプチル基、2-メチルヘキシル基、3-メチルヘキシル基、2,2-ジメチルペンチル基、2,3-ジメチルペンチル基、2,4-ジメチルペンチル基、3,3-ジメチルペンチル基、3-エチルペンチル基、2,2,3-トリメチルブチル基、n-オクチル基、イソオクチル基、2-エチルヘキシル基、ノニル基、デシル基等が挙げられる。
このような環状のアルキル基としては、例えば、シクロプロピル基、シクロブチル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基、シクロオクチル基、シクロノニル基、シクロデシル基、ノルボルニル基、イソボルニル基、1-アダマンチル基、2-アダマンチル基、トリシクロデシル基等が挙げられる。また、このような環状のアルキル基としては、例えば、先に挙げた環状のアルキル基の1個又は2個以上の水素原子が、直鎖状、分岐鎖状又は環状のアルキル基で置換されたものも挙げられる。ここで、水素原子を置換する直鎖状、分岐鎖状及び環状のアルキル基としては、上述の芯物質が有する置換基として挙げたアルキル基と同じものが挙げられる。これら置換基を有する環状のアルキル基の炭素数は、置換基の分も含めて10以下であることが好ましい。
このような直鎖状又は分岐鎖状のアルケニル基としては、例えば、エテニル基(ビニル基)、2-プロペニル基(アリル基)等、直鎖状及び分岐鎖状の前記アルキル基において、炭素原子間の1個の単結合(C-C)が二重結合(C=C)で置換された構造を有する基が挙げられる。
このような環状のアルケニル基としては、例えば、シクロヘキセニル基等、環状の前記アルキル基において、炭素原子間の1個の単結合(C-C)が二重結合(C=C)で置換された構造を有する基が挙げられる。
このようなアリール基としては、例えば、フェニル基、1-ナフチル基、2-ナフチル基、o-トリル基、m-トリル基、p-トリル基、キシリル基(ジメチルフェニル基)等が挙げられる。また、このようなアリール基としては、例えば、先に挙げたアリール基の1個又は2個以上の水素原子が、アリール基又はアルキル基で置換されたものも挙げられる。ここで、水素原子を置換するアリール基及びアルキル基としては、上述の芯物質が有する置換基として挙げたアリール基及びアルキル基と同じものが挙げられる。これら置換基を有するアリール基の炭素数は、置換基の分も含めて15以下であることが好ましい。
前記アリール基の炭素数は6~10であることがより好ましい。
前記アラルキル基の炭素数は、7~20であることが好ましく、7~11であることがより好ましい。
前記アルコキシ基の炭素数は、1~10であることが好ましく、1~8であることがより好ましく、1~6であることがさらに好ましく、1~5であることが特に好ましい。
前記アルケニルオキシ基の炭素数は、2~10であることが好ましく、2~8であることがより好ましく、2~6であることが特に好ましい。
前記アリールオキシ基の炭素数は、6~15であることが好ましく、6~10であることがより好ましい。
前記アラルキルオキシ基の炭素数は、7~20であることが好ましく、7~11であることがより好ましい。
通常、1分子の芯物質が有する前記置換基は、1~4個であることが好ましく、1~3個であることがより好ましい。
芯物質が2個以上の前記置換基を有する場合、これら置換基の結合位置は、すべて同じであってもよいし、すべて異なっていてもよく、一部のみ同じであってもよい。
5,5-ジメチルヒダントイン、3-メチル-5-ピラゾロン、3,5-ジメチルピラゾール、3-n-ブチル-1,2,4-トリアゾール、3,5-ジメチル-1,2,4-トリアゾール、3,5-ジ-n-ブチル-1,2,4-トリアゾール及び3,5-ジフェニル-1,2,4-トリアゾールはいずれも、環員数が5の化合物である。4-メチル-1H-ベンゾトリアゾール及び5-メチル-1H-ベンゾトリアゾールはいずれも、環員数が9の化合物である。
なお、ここに示す化合物は、前記置換基を有する芯物質のごく一例に過ぎない。
マイクロカプセルが内包する芯物質の量(含有量)は、例えば、後述するマイクロカプセルの製造条件によって調節できる。
前記膜形成成分は、芯物質を包み込む外殻の膜を形成する成分であり、本実施形態においてはポリウレアである。膜形成成分は、例えば、界面重縮合法により作製できる。
前記他の化合物は、1種のみであってもよいし、2種以上であってもよく、2種以上である場合、それらの組み合わせ及び比率は、任意に選択できる。
このようなアゾール又はその誘導体としては、例えば、上述の置換基を有していてもよい1,2,4-トリアゾール-3-オン及びその塩、置換基を有していてもよい1,2,3-トリアゾール及びその塩、置換基を有していてもよい1,2,4-トリアゾール及びその塩、並びに置換基を有していてもよい1,2,3-ベンゾトリアゾール及びその塩等が挙げられる。
前記マイクロカプセル剤は、芯物質を溶解させるために、溶媒を内包していてもよい。この場合、界面重縮合は、水と疎水性溶媒(可塑剤)との混合溶媒中で反応液を乳化させて行うことが好ましい。このように、内包させる芯物質と、疎水性溶媒と、の共存下で、原料化合物を重縮合させることにより、芯物質及び疎水性溶媒を内包するマイクロカプセル剤が一気に得られる。
また、反応液を乳化させる場合には、後述する乳化剤を併用してもよい。
すなわち、SP値が12(cal/cm3)1/2以下である溶媒を内包するマイクロカプセル剤は、本発明におけるマイクロカプセル剤の中でも、特に好ましいものである。
1-プロパノール(11.9)、2-プロパノール(11.5)、1-ブタノール(11.4)、シクロヘキサノール(11.4)、2-メトキシエタノール(10.8)、1-ヘキサノール(10.7)、2-メチル-2-プロパノール(10.6)、1-ブトキシ-2-プロパノール(10.4)、2-エチルヘキサノール(9.5)等のアルコール;
ジメチルホルムアミド(12.0)等のアミド;
アセトニトリル(11.8)等のニトリル;
アセトン(10.0)、メチルエチルケトン(9.3)、メチルプロピルケトン(8.7)、メチルイソプロピルケトン(8.5)等のケトン;
フタル酸ジn-ブチル(9.4)、酢酸エチル(9.1)、セバシン酸ビス(2-エチルヘキシル)(8.7)、酢酸n-ブチル(8.5)、酢酸イソプロピル(8.4)、酢酸イソブチル(8.3)等のエステル(カルボン酸エステル);
ジオキサン(9.9)、テトラヒドロフラン(9.1)、ジエチルエーテル(7.4)、イソプロピルエーテル(6.9)等の鎖状及び環状のエーテル;
ベンゼン(9.2)、トルエン(8.9)、キシレン(8.8)、エチルベンゼン(8.8)、シクロヘキサン(8.2)、n-オクタン(7.6)、n-ヘキサン(7.3)、n-ペンタン(7.0)等の芳香族及び脂肪族炭化水素;
塩化メチレン(9.7)、クロロホルム(9.3)、トリクロロエチレン(9.2)、四塩化炭素(8.6)等のハロゲン化炭化水素(ハロゲン化脂肪族炭化水素);
二硫化炭素(10.0)等の硫化炭素;
フェノール(11.5)等のフェノール類;
酢酸(10.1)等のカルボン酸
等が挙げられる。溶媒名と並記したカッコ内の数値はSP値((cal/cm3)1/2)を意味する。
前記乳化剤は、公知のものでよく、特に限定されない。
好ましい乳化剤としては、例えば、ポリビニルアルコール、カルボキシメチルセルロース、エチルセルロース、メチルセルロース、カゼイン、アラビアゴム、ゼラチン、ロート油、ベンゼンスルホン酸ナトリウム、ドデシルベンゼンスルホン酸ナトリウム等のアルキルベンゼンスルホン酸塩、ポリオキシエチレン硫酸塩、エチレン-無水マレイン酸共重合体、スチレン-無水マレイン酸共重合体、イソブチレン-無水マレイン酸共重合体、ポリ(メタ)アクリル酸等が挙げられる。
前記乳化剤の使用量は、特に限定されず、その種類に応じて適宜調節すればよい。
また、界面重縮合の時間は、0.5~5時間であることが好ましく、1~4時間であることがより好ましく、1.5~3時間であることが特に好ましい。
得られたマイクロカプセル剤は、そのまま目的とする用途で用いてもよいし、必要に応じて公知の後処理、精製等を行ってから、目的とする用途で用いてもよく、分散媒を除去してから目的とする用途で用いてもよい。
前記他のオリゴマー及びポリマーは、いずれも1種のみであってもよいし、2種以上であってもよく、2種以上である場合、それらの組み合わせ及び比率は、任意に選択できる。
すなわち、前記マイクロカプセル剤において、膜形成成分の総含有量に対する、ポリウレアの含有量の割合は、95質量%以上であることが好ましく、97質量%以上であることがより好ましく、99質量%以上であることが特に好ましい。
なお、本明細書において「体積基準中位径」とは、特に断りのない限り、コールターカウンターを用いる方法で測定された粒子径の、体積累積分布の中央値D50と同義である。
マイクロカプセル剤の体積基準中位径は、0.5μm以上であることが好ましく、例えば、1μm以上、3μm以上、6μm以上、及び9μm以上のいずれかであってもよい。体積基準中位径が前記下限値以上であるマイクロカプセル剤は、作製又は入手が容易である。
マイクロカプセル剤含有層12は、例えば、マイクロカプセル剤を含有する、液状のマイクロカプセル剤含有組成物を、マイクロカプセル剤含有層12の形成対象面に塗工し、乾燥させることで形成できる。
また、重縮合時に未使用の成分としては、例えば、樹脂、酸化防止剤等も挙げられる。前記樹脂としては、例えば、基材11における樹脂と同様のものが挙げられる。
アミノ基又はアミノ基塩形成基を有する芯物質を用いた場合には、マイクロカプセルの製造時において、重縮合物である膜形成成分を形成する際に、重縮合させる必須の原料化合物(例えば、前記イソシアネート化合物等)と、アミノ基又はアミノ基塩形成基を有する芯物質とが反応してしまい、マイクロカプセルの形成が阻害されると推測される。これに対して、アミノ基及びアミノ基塩形成基を有しない芯物質を用いることにより、このようなマイクロカプセルの形成阻害が抑制されるのではないかと推測される。
また、マイクロカプセル剤含有組成物は、例えば、前記マイクロカプセル剤を調製して得られた液状物(分散物)であってもよく、この液状物に、必要に応じて前記他の成分及び溶媒のいずれか一方又は両方を配合することでも得られる。
例えば、上述の界面重縮合を行う方法によって得られたマイクロカプセル剤水分散体は、それ自体が前記マイクロカプセル剤含有組成物として使用できる。また、前記マイクロカプセル剤水分散体に、何らかの成分を新たに添加して得られた組成物も、前記マイクロカプセル剤含有組成物として使用できる。また、前記マイクロカプセル剤水分散体に対して、公知の後処理、精製等の操作を行って得られた組成物も、前記マイクロカプセル剤含有組成物として使用でき、さらに、この組成物に、何らかの成分を新たに添加して得られた組成物も、前記マイクロカプセル剤含有組成物として使用できる。
マイクロカプセル剤含有組成物を調製するときの温度は、各配合成分が劣化しない限り特に限定されず、例えば、5~90℃とすることができるが、これは一例である。
マイクロカプセル剤含有組成物を調製するときの時間も、各配合成分が劣化しない限り特に限定されず、例えば、10分~24時間とすることができるが、これは一例である。
例えば、積層シート1は、マイクロカプセル剤含有層12の基材11側とは反対側に、前記他の層を備えていてもよい。この場合の前記他の層としては、例えば、接着剤層、印刷層、密着層、マイクロカプセル剤含有層12とは別途に設けられたマイクロカプセル剤含有層等が挙げられる。この別途に設けられたマイクロカプセル剤含有層は、マイクロカプセル剤含有層12と同様の形態とすることができ、マイクロカプセル剤含有層12と同一であってもよいし、異なっていてもよい。
例えば、前記第2面11b上に、マイクロカプセル剤含有層を備える場合には、このマイクロカプセル剤含有層は、第1面11a上のマイクロカプセル剤含有層12と同様の形態とすることができ、第1面11a上のマイクロカプセル剤含有層12と同一であってもよいし、異なっていてもよい。
例えば、ホルムアルデヒドの除去作用を有する前記積層シートは、建物の内装材(例えば、壁紙等)や家具、又はこれら内装材や家具の構成材料等、ホルムアルデヒドの除去対象物に対して設けるのに好適である。
本実施形態の積層シートは、例えば、その使用対象物に対して、接着剤を用いたり、取り付け用の治具を用いるなど、公知の方法で設けることができる。
これら基材について、その使用前の、マイクロカプセル剤含有層側となる面の表面粗さ(Ra)を、レーザ顕微鏡(KEYENCE社製「LASER MICROSCOPE VK-100シリーズ」)を用いて、JIS B0601:2001に準拠して測定した。その結果も以下にあわせて示す。
これら基材としては、いずれも、大きさが15cm×15cmであるものを用いた。
<基材>
基材(B1):コート紙(王子製紙社製「OKトップコート135kg」、厚さ129μm、坪量157g/m2)、表面粗さ(Ra)1.5μm
基材(B2):コート紙(三菱製紙社製「DFカラーGN110kg」、厚さ104μm、坪量128g/m2)、表面粗さ(Ra)1.7μm
基材(B3):コート紙(日本製紙社製「npi90kg」、厚さ127μm、坪量105g/m2)、表面粗さ(Ra)2.3μm
基材(B4):コート紙(三菱製紙社製「DFカラーM110kg」、厚さ130μm、坪量128g/m2)、表面粗さ(Ra)2.8μm
基材(B5):上質紙(日本製紙社製「上質紙」、厚さ87μm)、表面粗さ(Ra、坪量68g/m2)3.9μm
<マイクロカプセル剤積層シートの製造>
(マイクロカプセル剤の製造)
セバシン酸ビス(2-エチルヘキシル)(豊国製油社製、20.0g)と、濃度が75質量%であるイソホロンジイソシアネートのトリメチロールプロパン付加体(IPDI-TMP付加体)の酢酸エチル溶液(三井化学社製「タケネートD-140N」、25.0g、固形分18.8g)と、の混合物に、5-メチル-1H-ベンゾトリアゾール(和光純薬工業社製、10.0g)を添加し、溶解させた。
次いで、得られた混合物を、濃度が7質量%であるカルボキシメチルセルロース水溶液(300g、固形分21.0g)に添加し、乳化機(プライミクス社製)を用いて、回転数12000rpm、時間5分の条件で乳化させた。
次いで、1,3-ビス(アミノメチル)シクロヘキサン(東京化成工業社製、3.3g)を、上記で得られた乳化液に添加し、80℃で2時間攪拌することで、界面重縮合を行った。
以上により、1,3-ビス(アミノメチル)シクロヘキサンと、IPDI-TMP付加体と、の重縮合物を膜形成成分とし、ホルムアルデヒド反応剤として5-メチル-1H-ベンゾトリアゾールと、溶媒としてセバシン酸ビス(2-エチルヘキシル)及び酢酸エチルと、をそれぞれ内包したマイクロカプセル(マイクロカプセル剤)を、水分散体として得た。
コールターカウンター(ベックマン・コールター社製)を用いて、得られたマイクロカプセル剤の体積基準中位径Dを測定した。結果を表1に示す。
ワイヤーバーを用いて、基材(B1)の表面粗さ(Ra)が1.5μmである面に、上記で得られたマイクロカプセル剤水分散体を塗工し、105℃で2分乾燥させることにより、マイクロカプセル剤含有層を形成した。このマイクロカプセル剤含有層を形成した基材(B1)について、3点紙厚測定器(シチズンファインデバイス社製、紙厚測定器「MEI-11」)を用いて、3点で厚さを測定し、その測定値から、これら3点でのマイクロカプセル剤含有層の厚さを算出して、その平均値としてマイクロカプセル剤含有層の厚さを求めたところ、20μmであった。また、マイクロカプセル剤含有層の前記基材上での形成量は、10g/m2であった。
以上により、図1に示すものと同じ構成のマイクロカプセル剤積層シートを製造した。
(マイクロカプセルの膜厚(T)の測定)
上記で得られたマイクロカプセル剤積層シートの一部を裁断し、走査型電子顕微鏡(SEM)を用いて、このとき生じた断面を観察した。観察視野の中から無作為に、断面が生じている20個のマイクロカプセル剤(又はマイクロカプセル)を選択し、さらに、そのマイクロカプセル剤1個ごとに、潰れ等の変形が認められない領域のうち、マイクロカプセルの膜厚が最大である箇所、最小である箇所、及びそれ以外の箇所の3箇所を選択し、これらの箇所での膜厚を測定して、これらすべての膜厚の測定値(60個の測定値)から平均値を算出し、マイクロカプセルの膜厚Tを求めた。結果を表1に示す。
さらに、上記のD及びTから算出したT/Dの値を表1に示す。
上記で得られたマイクロカプセル剤積層シートを、ロール紙(日本製紙社製「npi55kg」)間に挟み込み、そのままロール状に巻き取った状態で、25℃の条件下で24時間静置保存した。この間、マイクロカプセル剤積層シートのマイクロカプセル剤含有層への加圧圧力が、4.4MPa(45kgf/cm2)となるようにした。
次いで、ロールを繰り出し、マイクロカプセル剤積層シートを取り出して、評価用の加圧保存後のマイクロカプセル剤積層シートを得た。
図2に示すように、加圧保存後において、マイクロカプセル剤含有層中のマイクロカプセル剤には、ほとんど潰れが認められず、球形の形状が維持されていた。なお、図2は、マイクロカプセル剤含有層の一部の領域のデータであるが、他の領域でも同様に、マイクロカプセル剤の潰れが抑制されていることを確認した。
この撮像データを取得後のマイクロカプセル剤積層シートは、速やかに、以降の評価に供した。
別途、上記のマイクロカプセル剤積層シートの場合と同じ方法で、使用前の基材(B1)を加圧保存した。すなわち、基材(B1)の表面粗さ(Ra)が1.5μmである面への加圧圧力は、4.4MPa(45kgf/cm2)となるようにした。
次いで、この加圧保存後の基材(B1)について、加圧保存前に表面粗さ(Ra)が1.5μmであった面の表面粗さ(Ra)を、上記と同じ方法で測定した。
その結果、加圧保存の前後で、基材(B1)の表面粗さ(Ra)にほとんど変化は認められなかった。
IPDI-TMP付加体の酢酸エチル溶液と、5-メチル-1H-ベンゾトリアゾールと、1,3-ビス(アミノメチル)シクロヘキサンと、を用いなかった点以外は、実施例1における、マイクロカプセル剤水分散体の製造時と同じ方法で、比較用の液状組成物を製造した。
そして、マイクロカプセル剤水分散体に代えて、この比較用の液状組成物を用いた点以外は、実施例1におけるマイクロカプセル剤積層シートの製造時と同じ方法で、標準積層シートを製造した。すなわち、この標準積層シートは、マイクロカプセル剤が基材上に積層されていない点を除いて、実施例1で製造したマイクロカプセル剤積層シートと同じものである。
容積1.6L、内径24cmのデシケータ内で、底面よりも上部に、デシケータ内の空間を仕切る素焼き板を、前記底面に対してほぼ平行に固定した。
次いで、デシケータ内の底面上で、前記素焼き板よりも下部に、蒸留水(300mL)を入れたガラス製容器を載置した。
次いで、大気下において、濃度が0.2質量%のホルムアルデヒド水溶液(150mL)を入れたポリエチレン製容器と、上記で得られた、加圧保存後のマイクロカプセル剤積層シートとを、前記素焼き板の上面に並べて載置し、直ちにデシケータを密封した。そして、この状態のまま、前記マイクロカプセル剤積層シートをデシケータ内で保管した。
次いで、保管開始から4日後に、デシケータ内のガラス製容器に入っている蒸留水の一部を試料として採取し、JIS A 6921に準拠して、前記試料のホルムアルデヒドの濃度を測定した。
本実施形態の積層シートの場合、前記ホルムアルデヒド除去率(%)は、30%以上であることが好ましい。
[ホルムアルデヒド除去率(%)]=1-[試料のホルムアルデヒドの濃度]/[標準試料のホルムアルデヒドの濃度]×100 (i)
[実施例2]
基材(B1)に代えて、基材(B2)を用いた点以外は、実施例1の場合と同じ方法で、マイクロカプセル剤積層シートを製造及び評価した。結果を表1に示す。
マイクロカプセル剤水分散体は、基材(B2)の表面粗さ(Ra)が1.7μmである面に塗工した。
マイクロカプセル剤含有層の前記基材上での形成量は、10g/m2であった。
加圧保存の前後で、基材(B2)の表面粗さ(Ra)にほとんど変化は認められなかった。
マイクロカプセル剤の製造時において、IPDI-TMP付加体の使用量を、25.0gに代えて20.0gとし、1,3-ビス(アミノメチル)シクロヘキサンの使用量を、3.3gに代えて2.6gとし、乳化機での回転数を、12000rpmに代えて8000rpmとした点以外は、実施例1の場合と同じ方法で、マイクロカプセル剤を製造し、マイクロカプセル剤積層シートを製造及び評価した。結果を表1に示す。
マイクロカプセル剤含有層の前記基材上での形成量は、10g/m2であった。
基材(B1)に代えて、基材(B3)を用いた点以外は、実施例1の場合と同じ方法で、マイクロカプセル剤積層シートを製造及び評価した。結果を表1に示す。
マイクロカプセル剤水分散体は、基材(B3)の表面粗さ(Ra)が2.3μmである面に塗工した。
マイクロカプセル剤含有層の前記基材上での形成量は、10g/m2であった。
加圧保存の前後で、基材(B3)の表面粗さ(Ra)にほとんど変化は認められなかった。
基材(B1)に代えて、基材(B4)を用いた点以外は、実施例1の場合と同じ方法で、マイクロカプセル剤積層シートを製造及び評価した。結果を表1に示す。
マイクロカプセル剤水分散体は、基材(B4)の表面粗さ(Ra)が2.8μmである面に塗工した。
マイクロカプセル剤含有層の前記基材上での形成量は、10g/m2であった。
加圧保存の前後で、基材(B4)の表面粗さ(Ra)にほとんど変化は認められなかった。
基材(B1)に代えて、基材(B5)を用いた点以外は、実施例1の場合と同じ方法で、マイクロカプセル剤積層シートを製造及び評価した。結果を表1に示す。
マイクロカプセル剤水分散体は、基材(B5)の表面粗さ(Ra)が3.9μmである面に塗工した。
マイクロカプセル剤含有層の前記基材上での形成量は、10g/m2であった。
加圧保存の前後で、基材(B5)の表面粗さ(Ra)にほとんど変化は認められなかった。
図3に示すように、加圧保存後において、マイクロカプセル剤含有層中の多くのマイクロカプセル剤に潰れが認められ、球形の形状が維持されているものは少なかった。なお、図3は、マイクロカプセル剤含有層の一部の領域のデータであるが、他の領域でも同様に、多くのマイクロカプセル剤が潰れていることを確認した。
この撮像データを取得後のマイクロカプセル剤積層シートは、速やかに、以降の評価に供した。
Claims (1)
- シート状の基材と、前記基材上に積層され、かつマイクロカプセル剤を含有するマイクロカプセル剤含有層と、を備えており、
前記マイクロカプセル剤の体積基準中位径(D)が25μm以下であり、
前記マイクロカプセル剤の膜形成成分がポリウレアであり、
前記基材の、前記マイクロカプセル剤含有層が積層されている側の面の、JIS B0601:2001に準拠して測定された表面粗さが、2μm以下であり、
前記マイクロカプセル剤において、マイクロカプセルの膜厚(T)を前記マイクロカプセル剤の体積基準中位径(D)で除した値T/Dが、0.01~0.2である、マイクロカプセル剤積層シート。