JP6919650B2 - 液状分散体及びその用途 - Google Patents
液状分散体及びその用途 Download PDFInfo
- Publication number
- JP6919650B2 JP6919650B2 JP2018519121A JP2018519121A JP6919650B2 JP 6919650 B2 JP6919650 B2 JP 6919650B2 JP 2018519121 A JP2018519121 A JP 2018519121A JP 2018519121 A JP2018519121 A JP 2018519121A JP 6919650 B2 JP6919650 B2 JP 6919650B2
- Authority
- JP
- Japan
- Prior art keywords
- liquid dispersion
- mass
- inorganic powder
- water
- dispersion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は更に、上記液状分散体を含む化粧料でもある。
本発明の液状分散体は、多価アルコール(A)、非イオン性界面活性剤(B)及び疎水化処理無機粉体(C)を含む。これら必須成分の合計含有量は、液状分散体の総量100質量%に対し、80質量%以上であることが好ましい。より好ましくは85質量%以上、更に好ましくは90質量%以上、特に好ましくは95質量%以上、最も好ましくは97質量%以上である。なお、必要に応じて、その他の成分を含んでもよく、各含有成分はそれぞれ1種又は2種以上を使用することができる。
以下、各含有成分について説明する。
多価アルコール(A)は、2価以上のアルコールであれば特に限定されないが、例えば、炭素数1〜20の多価アルコールであることが好ましい。より好ましくは、エチレングリコール、プロピレングリコール、ジプロピレングリコール、1,3−ブチレングリコール、ペンチレングリコール、グリセリン、ジグリセリン、トリグリセリン及びポリグリセリンからなる群より選択される少なくとも1種である。これにより、非イオン性界面活性剤(B)が疎水化処理無機粉体(C)の表面により均一に配向でき、液状分散体がより一層安定する。中でも特に1,3−ブチレングリコールを用いることが好ましい。1,3−ブチレングリコールの場合、化粧料へ配合した場合、人体への安全性が高い点で特に好ましい。
非イオン性界面活性剤(B)は、非イオン性(ノニオン性)の界面活性剤として通常使用される化合物であれば特に限定されず、例えば、ポリエーテル又はその誘導体、ポリエーテルアルキルエーテル、ポリオキシアルキレンアルケニルフェニルエーテル、ポリエーテル脂肪酸エステル、ソルビタン脂肪酸エステル、ポリエーテルソルビタン脂肪酸エステル、グリセリン脂肪酸エステル、ポリグリセリン脂肪酸エステル、ショ糖脂肪酸エステル、ポリエーテルヒマシ油、ポリエーテル硬化ヒマシ油、ポリエーテル変性シリコーン、ポリグリセリン変性シリコーン等が挙げられる。中でも、ポリエーテル脂肪酸エステル、ポリエーテルソルビタン脂肪酸エステル及び/又はポリエーテル変性シリコーンを用いることが好ましい。より好ましくは、ポリエーテル変性シリコーンを少なくとも用いることであり、これにより、液状分散体の安定性や化粧料に使用した際の使用感等が更に良好になる。ポリエーテル変性シリコーンはまた、安全性や熱安定性が高い点でも好適である。
なお、2種以上の非イオン性界面活性剤を組み合わせて使用する場合は、液状分散体中に配合する混合比で混合した非イオン性界面活性剤について上述した試験を行った場合に、透明溶解又は微濁することが好適である。
なお、2種以上の非イオン性界面活性剤を組み合わせて使用する場合は、液状分散体中に配合する混合比で混合した非イオン性界面活性剤について上述した試験を行った場合に、不溶又は白濁することが好適である。
なお、非イオン性界面活性剤(B)を2種以上用いる場合は、その混合物のHLBが上記範囲内にあることが好ましい。
NHLB=(E+P)/5
(NHLBは、HLB値を表す。Eは、非イオン性界面活性剤(B)の分子全体に対する、非イオン性界面活性剤(B)が有するポリエーテル部の割合(質量%)を表す。Pは、非イオン性界面活性剤(B)の分子全体に対する、非イオン性界面活性剤(B)が有する多価アルコール部の割合(質量%)を表す。)
疎水化処理無機粉体(C)は、平均粒子径が150〜700nmであることが好ましい。通常、このような顔料級とされる粒径を持つ無機粉体は沈降しやすいため、従来の技術常識によると、液状分散体としたときの分散安定性は良好ではないと考えられている。だがこの技術常識に反し、本発明の液状分散体では、このような粒径を持つ疎水化処理無機粉体(C)を含む場合であっても極めて良好な分散安定性を有するため、着色顔料用途に特に有用である。より綺麗な発色を奏させる観点から、より好ましくは180nm以上、更に好ましくは200nm以上である。
形状は、走査型電子顕微鏡等によって観察することができる。
本発明の液状分散体は、水を実質的に含まない。「水を実質的に含まない」とは、液状分散体100質量%中の水分量が1質量%以下であることを意味する。本発明では、このように水を実質的に含まない状態でも長時間安定して分散状態を維持することができるという、これまでの技術常識からは想定できない異質な効果を有するうえ、O/W型化粧料及びW/O型化粧料のいずれにも好適に適用することができる。液状分散体100質量%中の水分量は、好ましくは1質量%未満、より好ましくは0.8質量%以下、更に好ましくは0.5質量%以下、特に好ましくは0.3質量%以下、最も好ましくは0.2質量%以下である。
本発明の液状分散体は、更に、レシチン及び/又は水添レシチン(D)を含むことが好ましい。レシチン及び/又は水添レシチン(D)を含有することで、疎水化処理無機粉体(C)の肌への付着性が向上し、化粧持ちが向上する。
なお、レシチン及び/又は水添レシチンを「(水添)レシチン」と総称することもある。
本発明の液状分散体は、必要に応じて、上述した多価アルコール(A)、非イオン性界面活性剤(B)、疎水化処理無機粉体(C)、並びに、レシチン及び/又は水添レシチン(D)以外のその他の成分を含んでもよい。その他の成分としては特に限定されないが、例えば、パラオキシ安息香酸アルキルエステル、安息香酸、安息香酸ナトリウム、ソルビン酸、ソルビン酸カリウム、フェノキシエタノール、サリチル酸、石炭酸、ソルビン酸、パラクロルメタクレゾール、ヘキサクロロフェン、塩化ベンザルコニウム、塩化クロルヘキシジン、感光素、フェノキシエタノール等の防菌防腐剤や抗菌剤等が挙げられる。
本発明の液状分散体は、長時間安定して分散状態を維持することができるため、分散体として保管や輸送が容易であるうえ、当該液状分散体を分散媒に分散する際の分散処理を簡略化又は省略することができる。それゆえ、各種原料として有用であり、化粧料原料、塗料原料、インキ原料として特に有用である。中でも、本発明の液状分散体は発色や感触、取扱い性が良好で、汗や水に強い撥水性の高い化粧料を与えることができるため、化粧料原料として極めて有用である。このように本発明の液状分散体からなる化粧料原料は、本発明の一つである。また本発明の液状分散体を含む化粧料、塗料組成物又はインキ組成物も、本発明者による発明に包含される。このうち化粧料について以下に更に説明する。
本発明の化粧料は、上述した本発明の液状分散体を含む。このような化粧料の製造方法は特に限定されず、通常の化粧料の製法に従えばよい。
なお、各種物性等は以下のようにして評価した。
(1)無機粉体中の水分量
滴定セルにメタノールを入れ、水分気化装置(平沼産業社製「EVAPORATER EV−2000」)にセットし、ブランク操作を行ってから試料0.5gを投入した。加熱保持時間10分で水分測定装置(平沼産業社製「AQUA COUNTER AQV−2200」)を用いて水分量を測定した。
(2)油(無機粉体以外の原料)中の水分量
滴定セルにメタノールを入れ、ブランク操作をしてから試料0.5gを投入し、水分測定装置(平沼産業社製「AQUA COUNTER AQV−2200」)で水分量を測定した。
液状分散体を作製後、40℃で1日又は1週間静置した後、25℃まで冷却し、B型粘度計(LVDV1M、英弘精機社製)にて測定した(測定温度:25℃)。
液状分散体を作製後、40℃で静置し、1週間後に目視で確認した。
表では、ケーキング又は上澄みが発生したものを「発生」と記載し、発生しなかったものを「なし」と記載した。
(1)粒度分布
白色の無機粉体を含む液状分散体について、水で希釈後、堀場製作所製「LA−950」にてメディアン径D50を測定した。
(2)グラインドゲージ
有色の無機粉体を含む液状分散体について、JIS K5600(1999年)に従い、50μmグラインドゲージにより測定した。
金属ビーカーに、表1に示す量で1,3−ブチレングリコール(ダイセル社製)、非イオン性界面活性剤(信越化学工業社製「KF−6013」、ポリエーテル変性シリコーン)、酸化チタン(堺化学工業社製「MKR−1S」、酸化チタン98.5%、ハイドロゲンジメチコン1.5%、平均粒子径:200nm)の順で投入した。それぞれ投入時に、金ベラを用いて馴染ませ、撹拌機で混合した。このようにして得た液状分散体について、上述した評価を行った。結果を表1に示す。
各原料成分の量を表1に示す量に変更したこと以外は、実施例1と同様にして液状分散体を作製し、上述した評価を行った。結果を表1に示す。
酸化チタンの平均粒子径を500nmに変更したこと以外は、実施例1と同様にして液状分散体を作製し、上述した評価を行った。結果を表1に示す。
酸化チタンを酸化鉄(黄色)(三好化成社製「SI−イエロー LL−100P LHC」、ハイドロゲンジメチコン処理、平均粒子径:700nm)に変更したこと、及び、各原料成分の量を表1に示す量に変更したこと以外は、実施例1と同様にして液状分散体を作製し、上述した評価を行った。結果を表1に示す。
酸化チタンを酸化鉄(赤色)(三好化成社製「SI−レッド R−516PS LHC」、ハイドロゲンジメチコン処理、平均粒子径:700nm)に変更したこと、及び、各原料成分の量を表1に示す量に変更したこと以外は、実施例1と同様にして液状分散体を作製し、上述した評価を行った。結果を表1に示す。
酸化チタンを酸化鉄(黒色)(三好化成社製「SI−ブラック BL−100P LHC」、ハイドロゲンジメチコン処理、平均粒子径:300nm)に変更したこと、及び、各原料成分の量を表1に示す量に変更したこと以外は、実施例1と同様にして液状分散体を作製し、上述した評価を行った。結果を表1に示す。
金属ビーカーに、表1に示す量で1,3−ブチレングリコール(ダイセル社製)、非イオン性界面活性剤(信越化学工業社製「KF−6013」、ポリエーテル変性シリコーン)、レシチン(J−オイルミルズ製「レシチンCL」)、酸化チタン(堺化学工業社製「MKR−1S」、酸化チタン98.5%、ハイドロゲンジメチコン1.5%、平均粒子径:200nm)の順で投入した。それぞれ投入時に、金ベラを用いて馴染ませ、撹拌機で混合した。このようにして得た液状分散体について、上述した評価を行った。結果を表1に示す。
酸化チタン(堺化学工業社製MKR−1S」、酸化チタン98.5%、ハイドロゲンジメチコン1.5%、平均粒子径:200nm)60.1g、酸化鉄(黄色)(三好化成社製「SI−イエロー LL−100P LHC」、ハイドロゲンジメチコン処理、平均粒子径:700nm)2.6g、酸化鉄(黒色)(三好化成社製「SI−ブラック BL−100P LHC」、ハイドロゲンジメチコン処理、平均粒子径:300nm)0.7g、酸化鉄(赤色)(三好化成社製「SI−レッド R−516PS LHC」、ハイドロゲンジメチコン処理、平均粒子径:700nm)7.8gを混合し、肌色に調色した疎水化処理無機粉体を得た。
金属ビーカーに、表1に示す量で1,3−ブチレングリコール(ダイセル社製)、非イオン性界面活性剤(信越化学工業社製「KF−6013」、ポリエーテル変性シリコーン)上記肌色に調色した疎水化処理無機粉体の順で投入した。それぞれ投入時に、金ベラを用い馴染ませ、撹拌機で混合した。このようにして得た液状分散体について、上述した評価を行った。結果を表1に示す。
非イオン性界面活性剤を使用しなかったこと及び各原料成分の量を表1に示す量に変更したこと以外は、実施例1と同様にして液状分散体を作製しようとしたが、分散しなかった。それゆえ、液状分散体を得ることができなかった。
金属ビーカーに、表1に示す量で1,3−ブチレングリコール(ダイセル社製)、非イオン性界面活性剤(信越化学工業社製「KF−6013」、ポリエーテル変性シリコーン)、酸化チタン(堺化学工業社製「MKR−1S」、酸化チタン98.5%、ハイドロゲンジメチコン1.5%、平均粒子径:200nm)、水の順で投入した。それぞれ投入時に、金ベラを用いて手で馴染ませた。このようにして得た液状分散体について、上述した評価を行った。結果を表1に示す。
平均粒子径200nmの酸化チタン:0.126質量%
平均粒子径500nmの酸化チタン:0.103質量%
酸化鉄(赤色):0.130質量%
酸化鉄(黄色):0.487質量%
酸化鉄(黒色):0.061質量%
1,3−ブチレングリコール:0.262質量%
非イオン性界面活性剤(KF−6013):0.272質量%
レシチン:0.186質量%
実施例1〜6、8は、多価アルコール(A)、非イオン性界面活性剤(B)及び疎水化処理無機粉体(C)を含む液状分散体であり、実施例7は更にレシチン及び/又は水添レシチン(D)を含む液状分散体であって、かつ液状分散体100質量%中の水分量が1質量%以下である例であるが、この場合、粘度が経時的に安定しており、上澄みやケーキングの発生も抑制された液状分散体が得られた。実施例1〜3、7ではメディアン径D50も小さく、疎水化処理無機粉体(C)の分散が良好であり、実施例4〜6、8ではグラインドゲージによる粗粒確認を行った場合にも粗粒は確認されなかった。
また、実施例1〜8で得た液状分散体はいずれも、O/W型化粧料(水中油型化粧料)のみならず、W/O型化粧料(油中水型化粧料)にも安定に配合することができた。
実施例9(O/Wファンデーション)
下記表2に示す成分を用い、以下の製造方法にてO/Wファンデーションを得た。
(製造方法)
(1)成分15〜18を成分19の一部に均一に混合する。
(2)成分1〜7を均一に混合し、加熱する。
(3)成分8〜14及び成分19の残部を均一に混合し、加熱する。
(4)上記(3)に上記(2)を添加して乳化し、冷却して上記(1)を添加し、O/Wファンデーションを得た。
下記表3に示す成分を用い、以下の製造方法にてO/Wファンデーションを得た。
(製造方法)
(1)成分16〜19を成分20の一部に均一に混合する。
(2)成分1〜8を均一に混合し、加熱する。
(3)成分9〜15及び成分20の残部を均一に混合し、加熱する。
(4)上記(3)に上記(2)を添加して乳化し、冷却して上記(1)を添加し、O/Wファンデーションを得た。
下記表4に示す成分を用い、以下の製造方法にてO/Wファンデーションを得た。
(製造方法)
(1)成分11〜14を成分17の一部に均一に混合する。
(2)成分1〜6を均一に混合し、加熱する。
(3)成分7〜10及び成分17の残部を均一に混合し、加熱する。
(4)上記(3)に上記(2)を添加して乳化し、冷却して成分15、16及び上記(1)を添加し、O/Wファンデーションを得た。
下記表5に示す成分を用い、以下の製造方法にてW/Oファンデーションを得た。
(製造方法)
(1)成分8〜11を成分15の一部に均一に混合する。
(2)成分1〜7を均一に混合する。
(3)成分12〜14及び成分15の残部を均一に混合し、上記(1)を添加する。
(4)上記(2)に上記(3)を添加して乳化し、W/Oファンデーションを得た。
下記表6に示す成分を用い、以下の製造方法にてW/Oファンデーションを得た。
(製造方法)
(1)成分6〜9を成分15の一部に均一に混合する。
(2)成分1〜5を均一に混合する。
(3)成分10〜14及び成分15の残部を均一に混合し、上記(1)を添加する。
(4)上記(2)に上記(3)を添加して乳化し、W/Oファンデーションを得た。
下記表7に示す成分を用い、以下の製造方法にてO/Wマスカラを得た。
(製造方法)
(1)成分10を成分11の一部に均一に混合する。
(2)成分2〜4及び成分11の残部を混合する。
(3)上記(2)に成分5を加え、更に成分6を添加する。
(4)上記(3)に成分7,8を加え、均一して加熱する。
(5)上記(4)に加熱した成分1を加えて乳化する。
(6)上記(5)に成分9及び上記(1)を加え、均一にしてO/Wマスカラを得た。
Claims (9)
- 多価アルコール(A)、非イオン性界面活性剤(B)及び疎水化処理無機粉体(C)を含む液状分散体であって、
該多価アルコール(A)と非イオン性界面活性剤(B)との質量比(A/B)は、70〜95/30〜5であり、
該疎水化処理無機粉体(C)の含有量は、液状分散体の総量100質量%に対し、60質量%以上であり、
該液状分散体100質量%中の水分量は1質量%以下である
ことを特徴とする液状分散体。 - 更に、レシチン及び/又は水添レシチン(D)を含む
ことを特徴とする請求項1記載の液状分散体。 - 前記疎水化処理無機粉体(C)の平均粒子径は、150〜700nmである
ことを特徴とする請求項1に記載の液状分散体。 - 前記疎水化処理無機粉体(C)は、シリコーン、アルキルシラン、脂肪酸(塩)、アミノ酸(塩)及びアルキルリン酸(塩)からなる群より選択される少なくとも1種で表面処理された無機粉体である
ことを特徴とする請求項1〜3のいずれかに記載の液状分散体。 - 前記多価アルコール(A)は、エチレングリコール、プロピレングリコール、ジプロピレングリコール、1,3−ブチレングリコール、ペンチレングリコール、グリセリン、ジグリセリン、トリグリセリン及びポリグリセリンからなる群より選択される少なくとも1種である
ことを特徴とする請求項1〜4のいずれかに記載の液状分散体。 - 前記非イオン性界面活性剤(B)は、ポリエーテル変性シリコーンである
ことを特徴とする請求項1〜5のいずれかに記載の液状分散体。 - 25℃での粘度が2000〜50万mPa・sである
ことを特徴とする請求項1〜6のいずれかに記載の液状分散体。 - 請求項1〜7のいずれかに記載の液状分散体からなる
ことを特徴とする化粧料原料。 - 請求項1〜7のいずれかに記載の液状分散体を含む
ことを特徴とする化粧料。