JP6699548B2 - 凹凸転写フィルム - Google Patents
凹凸転写フィルム Download PDFInfo
- Publication number
- JP6699548B2 JP6699548B2 JP2016514196A JP2016514196A JP6699548B2 JP 6699548 B2 JP6699548 B2 JP 6699548B2 JP 2016514196 A JP2016514196 A JP 2016514196A JP 2016514196 A JP2016514196 A JP 2016514196A JP 6699548 B2 JP6699548 B2 JP 6699548B2
- Authority
- JP
- Japan
- Prior art keywords
- uneven
- layer
- transfer film
- film
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、かかる従来の問題を解決しようとするものであって、加圧によっても表面凹凸が潰れにくく安定している凹凸転写フィルムを提供しようとするものである。
1. フィルムの片面が表面凹凸を有し、片面に表面凹凸を有するフィルムが、基材フィルムの片面に凹凸層を有するものであり、前記凹凸層が、樹脂(A)及び粒子(B)を含み、前記樹脂(A)が、アクリル系樹脂、ポリエステル樹脂、ウレタン系樹脂、メラミン系樹脂、エポキシ系樹脂から選ばれる1種または2種類以上の樹脂が混合されており、前記凹凸層が、以下の式(1)を満足し、前記表面凹凸を有する面の60°グロスが20%以下であり、40MPaの圧力で30秒間の加圧プレスを施した後の60°グロスの上昇率が、前記加圧プレスを施す前の60°グロスに対して25%以下であり、前記凹凸層上に離型層を有することを特徴とする凹凸転写フィルム。
(1/4)×D≦d≦(3/4)×D ・・・(1)
ここで、dは凹凸層の膜厚[μm]、Dは粒子(B)の平均粒子径[μm]を示す。
2. フィルムの表面凹凸を有する面の表面粗さRaが0.2μm以上2.5μm以下であり、40MPaの圧力で30秒間の加圧プレスを施した後の表面粗さRaの低減率が、前記加圧プレスを施す前の表面粗さRaに対して20%以下であることを特徴とする上記第1に記載の凹凸転写フィルム。
3. 粒子(B)の平均粒子径が、1μm以上10μm以下であることを特徴とする上記第1または第2に記載の凹凸転写フィルム。
4. 粒子(B)の含有量が、樹脂成分100質量部に対して20質量部以上70質量部以下であることを特徴とする上記第1〜第3のいずれかに記載の凹凸転写フィルム。
5. 離型層の凹凸層と接していない反対面の60°グロスが、20%以下であることを特徴とする上記第1〜第4のいずれかに記載の凹凸転写フィルム。
6. 上記第1〜第5のいずれかに記載の凹凸転写フィルムを使用して作成された保護層を有することを特徴とする電磁波シールドフィルム。
本発明の凹凸転写フィルムは、片面に表面凹凸を有するフィルムであって、ヘアーライン加工、サンドブラスト加工、梨地加工、賦形加工が施されてなるものであっても良いが、例えば、図1に示されるように、基材フィルム11、凹凸層12を含んでなることが好ましい。また、凹凸層12上にさらに離型層13を設けることも可能である。凹凸層12には、少なくともバインダー樹脂および粒子14を含むことが好ましい。凹凸層12に粒子14を含むことで適度な表面凹凸性をもった凹凸転写フィルムを提供することができる。
本発明における基材として用いるフィルムを構成する樹脂は、ポリエチレン、ポリプロピレンなどのポリオレフィン樹脂、ナイロン6、ナイロン66などのポリアミド樹脂、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレン-2,6-ナフタレート、ポリトリメチレンテレフタレート、および共重合成分として、例えば、ジエチレングリコール、ネオペンチルグリコール、ポリアルキレングリコールなどのジオール成分や、アジピン酸、セバチン酸、フタル酸、イソフタル酸、2,6-ナフタレンジカルボン酸などのジカルボン酸成分などを共重合したポリエステル樹脂などを用いることができる。なかでも、機械的強度、耐薬品性、耐熱性の点からポリエステル樹脂が好ましい。
本発明の凹凸転写フィルムの凹凸層は、少なくとも樹脂(A)および粒子(B)が含有されていることが好ましい。以下、凹凸層を形成するための各成分等について説明する。
本発明の凹凸層に使用する樹脂(A)は、特に限定されるわけではないが、主としてアクリル系樹脂、ポリエステル樹脂、ウレタン系樹脂、メラミン系樹脂、エポキシ系樹脂などで構成することができる。1種を用いてもよいし2種類以上の樹脂を混合してもよい。特に、硬度と加圧に対する耐久性などの点で、熱および活性線硬化性樹脂が好ましい。さらに、硬化性、可撓性および生産性の点で、特に活性線硬化型のアクリル系樹脂からなるものが好ましい。
本発明における凹凸層を形成するために用いる塗布組成物中には、粒子(B)を含有する。該粒子(B)は、凹凸層において表面凹凸を形成し、被転写物にマット性を付与する働きをする。
樹脂成分とは、凹凸層の総固形分から粒子(B)を引いたものである。
(1/4)×D≦d≦(3/4)×D ・・・(1)
ここで、dは凹凸層の膜厚[μm]、Dは粒子(B)の平均粒子径[μm]を示す。
dがDの3/4より大きいと塗膜内に粒子が埋没し十分な表面凹凸効果が得られにくくなり、あまり好ましくない。dがDの1/4より小さいと加圧耐久性が低下してしまうおそれがあり、あまり好ましくない。本発明において凹凸層の膜厚とは、基材フィルムに垂直方向に粒子が存在せず凹凸層の樹脂成分のみが存在している部分の膜厚を表す。
表面凹凸を有する片面の表面粗さRaは、0.2μm以上2.5μm以下であることが好ましい。Raが0.2μm未満であると、60°グロスが高くなってしまい、保護層の被転写面のマット性が不十分になり易く、あまり好ましくない。一方、Raが2.5μmを超えることは、結果として凹凸層の膜厚が厚いことを伴うことであり、生産性が乏しくなり易く、あまり好ましくない。
本発明の凹凸転写フィルムの凹凸層には、他の機能性を付与するために、凹凸層の凹凸を損なわない程度の範囲で、各種の添加剤を含有させても構わない。前記添加剤としては、例えば、蛍光染料、蛍光増白剤、可塑剤、紫外線吸収剤、顔料分散剤、抑泡剤、消泡剤、レベリング剤、防腐剤、帯電防止剤等が挙げられる。
本発明の凹凸転写フィルムの凹凸層には視認性向上のため、染料および/または顔料を添加することも好ましい。さらに基材フィルムと凹凸層の間にアンカー層を設けて、アンカー層に染料および/または顔料を添加することも好ましい形態の一つである。また、基材フィルムの凹凸層を設けた面とは反対側の面に塗布層を設け、該塗布層に着色する形態についても好ましい。
本発明の転写フィルムの製造方法については特に限定されないが、凹凸転写フィルムは、凹凸層を形成する粒子を含有するコーティング組成物を基材フィルムに対して塗布し、硬化させて凹凸層12を形成することにより製造することが好ましい。
本発明で用いられる凹凸層形成組成物には、塗工時の作業性の向上、塗工膜厚のコントロール、基材フィルムとの混在層形成を目的として、有機溶剤を配合しても良い。有機溶剤としては、例えば、イソプロピルアルコール、メタノール、エタノール等のアルコール類。メチルエチルケトン(MEK)、メチルイソブチルケトン(MIBK)、シクロヘキサノン等のケトン類。酢酸メチル、酢酸エチル、酢酸ブチル等のエステル類。トルエン、キシレン等の芳香族炭化水素。またはこれらの混合物を使用しても良い。
図1のように、本発明の凹凸転写フィルムの凹凸層12上には、転写時保護層の離型性を向上させるために離型層13を設けてもよい。離型層13に使用する離型剤は、特に制限はなく、従来公知の離型剤を使用することが可能であり、例えば、長鎖アルキル化合物、フッ素化合物、ワックス、シリコーン化合物、ポリオレフィン等が挙げられる。また、メラミン樹脂などの親水性が高い樹脂を離型剤として使用することもできる。これらの離型剤は単独で用いてもよいし、複数種使用してもよい。
得られた凹凸転写フィルムのフィルムに対して垂直な方向にミクロトーム(大和光機製、LR-85)を用いて断面を切削した。光学顕微鏡にて切断面を観察し、樹脂(A)の膜厚[μm]を測定した。前記樹脂の膜厚とは、基材フィルムに垂直方向に粒子が存在せず凹凸層の樹脂成分のみが存在している部分の膜厚を表す。10箇所測定し、その平均値を凹凸層の膜厚とする。
得られた凹凸転写フィルムおよび離型層を積層した凹凸転写フィルムを黒色インキで裏面反射防止処理を施した後に、表面の角度60°グロス値を光沢計(日本電色工業製、VG−2000)を用いて測定して求めた。
得られた凹凸転写フィルムおよび離型加工後の凹凸転写フィルムの凹凸層表面の算術平均表面粗さ(Ra;単位μm)を、JIS B0601−1994に準拠して、接触型粗さ計(ミツトヨ社製,SJ-410)を用いて測定される粗さ曲線より求めた。
得られた凹凸転写フィルムをステンレス板に挟み、プレス機(理研精機製、10Tonフ゜レス)を用いて40MPaの圧力で30秒間加圧プレスを行った。加圧プレス後のサンプルは凹凸層の60°グロスと表面粗さを測定し、加圧前に対する変化量を算出し凹凸安定性の指標とした。また、目視にて加圧プレス部の圧痕の有無を確認(○:圧痕なし、×:圧痕あり)した。
(加圧後の60°グロスの上昇率)(%)
=100×{(加圧後の60°グロス)−(加圧前の60°グロス)}/(加圧前の60°グロス)
(加圧後の表面粗さRaの低減率)(%)
=−100×{(加圧後の表面粗さRa)−(加圧前の表面粗さRa)}/(加圧前の表面粗さRa)
得られた凹凸転写フィルムに離型層(日立化成製、テスファイン(登録商標)305)を最終的な塗膜が0.03〜1.0g/m2になるように塗布・硬化することで離型加工を行った。離型加工した凹凸転写フィルム上に下記保護層組成物を6μm塗工し、易接着層付きポリエステルフィルム(東洋紡社製,コスモシャイン(登録商標)A4100,厚さ:125μm)の易接着面と貼り合せた後紫外線200mJ/cm2照射し硬化させた。凹凸転写フィルムを剥がして硬化保護層表面に凹凸被転写面を得た。得られた保護層の被転写面を黒色インキで裏面反射防止処理を施した後に、凹凸層表面の角度60°グロス値を光沢計(日本電色工業製、VG−2000)を用いて測定して求めた。
(保護層組成物)
・ウレタンアクリレート(ビームセット577/荒川化学工業社製):97.0質量%
・光重合開始剤(イルガキュア(登録商標)184/BASF社製): 3.0質量%
基材フィルムとしての易接着層付きポリエステルフィルム(東洋紡社製,コスモシャイン(登録商標)A4100,厚さ:50μm)の易接着層側の面に、凹凸層組成物をワイヤーバー#10で塗布し、70℃で30秒間乾燥させた。次いで、紫外線照射装置により紫外線照射400mJ/cm2して凹凸層を形成し、凹凸転写フィルムを得た。
凹凸層組成物は、下記塗布液1を使用した。
塗布液1
・メチルエチルケトン: 40.0質量%
・トルエン: 40.0質量%
・多官能アクリレート(8UX-015A/大成ファインケミカル社製(固形分100質量%)) : 15.0質量%
・PMMA粒子(エポスター(登録商標)MA1006,平均粒子径6μm/日本触媒社製): 4.5質量%
・光重合開始剤(イルガキュア(登録商標)184/BASF社製): 0.5質量%
得られた凹凸転写フィルムについて、60°グロス、表面粗さ、加圧に対する凹凸安定性の評価を行った結果、全ての評価において好適な結果であった。
・トルエン :60.0質量%
・メチルエチルケトン : 38.0質量%
・テスファイン(登録商標)305(日立化成社製(固形分50質量%)) :2.0質量%
・ドライヤー900(日立化成社製) :0.05質量%
得られた離型処理した凹凸転写フィルムを用いて転写工程を行い、保護層の被転写面の60°グロスの評価を行った結果、好適な結果であった。
凹凸層組成物は、樹脂に対する粒子濃度と固形分が実施例1に比べ増加させた、下記塗布液2を使用した。
塗布液2
・メチルエチルケトン: 34.7質量%
・トルエン: 34.7質量%
・多官能アクリレート(8UX-015A/大成ファインケミカル社製(固形分100質量%)) : 20.0質量%
・PMMA粒子(エポスター(登録商標)MA1006,平均粒子径6μm/日本触媒社製): 10.0質量%
・光重合開始剤(イルガキュア(登録商標)184/BASF社製): 0.6質量%
塗布液2を用いた点を除いては、実施例1と同様にして、凹凸転写フィルムを得た。得られた凹凸転写フィルムについて、60°グロス、表面粗さ、加圧に対する凹凸安定性の評価を行った結果、全ての評価において好適な結果であった。
凹凸層組成物は、実施例2と同様に塗布液2を使用した。
塗工時にはワイヤーバー#8を使用した。ワイヤーバーを#8を用いた点を除いては、実施例1と同様にして、凹凸転写フィルムを得た。得られた凹凸転写フィルムについて、60°グロス、表面粗さ、加圧に対する凹凸安定性の評価を行った結果、全ての評価において好適な結果であった。
・トルエン :60.0質量%
・メチルエチルケトン : 29.75質量%
・テスファイン(登録商標)305(日立化成社製(固形分50質量%)) :10.0質量%
・ドライヤー900(日立化成社製) :0.25質量%
得られた離型処理した凹凸転写フィルムを用いて転写工程を行い、保護層の被転写面の60°グロスの評価を行った結果、好適な結果であった。
凹凸転写フィルムは実施例3と同様に作成した。
また、得られた凹凸転写フィルムに下記の離型層組成物をワイヤーバー#5で塗布し、160℃で30秒間乾燥・硬化させ離型加工した。下記離型層組成物は実施例1と比べ、固形分濃度を増加させた。
・トルエン :60.0質量%
・メチルエチルケトン : 19.5質量%
・テスファイン(登録商標)305(日立化成社製(固形分50質量%)) :20.0質量%
・ドライヤー900(日立化成社製) :0.50質量%
得られた離型処理した凹凸転写フィルムを用いて転写工程を行い、保護層の被転写面の60°グロスの評価を行った結果、好適な結果であった。
凹凸層組成物は、不定形粒子を使用した下記塗布液3を使用した。
塗布液3
・メチルエチルケトン: 34.7質量%
・トルエン: 34.7質量%
・多官能アクリレート(8UX-015A/大成ファインケミカル社製(固形分100質量%)) : 20.0質量%
・不定形PAN粒子(タフチック(登録商標)ASF-7,平均粒子径7μm/東洋紡社製):10.0質量%
・光重合開始剤(イルガキュア(登録商標)184/BASF社製): 0.6質量%
塗布液3を用いた点を除いては、実施例1と同様にして、凹凸転写フィルムを得た。得られた凹凸転写フィルムについて、60°グロス、表面粗さ、加圧に対する凹凸安定性の評価を行った結果、全ての評価において好適な結果であった。
凹凸層組成物は、不定形粒子を使用した下記塗布液4を使用した。
塗布液4
・メチルエチルケトン: 34.7質量%
・トルエン: 34.7質量%
・多官能アクリレート(8UX-015A/大成ファインケミカル社製(固形分100質量%)) : 20.0質量%
・不定形PAN粒子(タフチック(登録商標)AM,平均粒子径10μm/東洋紡社製): 10.0質量%
・光重合開始剤(イルガキュア(登録商標)184/BASF社製): 0.6質量%
塗布液4を用いた点を除いては、実施例1と同様にして、凹凸転写フィルムを得た。得られた凹凸転写フィルムについて、60°グロス、表面粗さ、加圧に対する凹凸安定性の評価を行った結果、全ての評価において好適な結果であった。
凹凸層組成物は、実施例1に比べ樹脂を変更し固形分濃度を増加させた、下記塗布液5を使用した。
塗布液5
・メチルエチルケトン: 37.0質量%
・トルエン: 37.0質量%
・ポリエステル(バイロン(登録商標)200/東洋紡社製(固形分100質量%)) : 20.0質量%
・PMMA粒子(エポスター(登録商標)MA1006,平均粒子径6μm/日本触媒社製): 6.0質量%
基材フィルムとしての易接着層付きポリエステルフィルム(東洋紡社製,コスモシャイン(登録商標)A4100,厚さ:50μm)の易接着層側の面に、凹凸層組成物をワイヤーバー#10で塗布し、160℃で30秒間乾燥させ、凹凸転写フィルムを得た。得られた凹凸転写フィルムについて、60°グロス、表面粗さ、加圧に対する凹凸安定性の評価を行った結果、全ての評価において好適な結果であった。
また、得られた凹凸転写フィルムに実施例1と同様に離型加工施し、保護層の被転写面の60°グロスの評価を行った結果、好適な結果であった。
凹凸層組成物は、実施例2に比べ樹脂を変更した、下記塗布液6を使用した。
塗布液6
・メチルエチルケトン: 35.0質量%
・トルエン: 35.0質量%
・ポリエステル(バイロン(登録商標)200/東洋紡社製(固形分100質量%)) : 20.0質量%
・PMMA粒子(エポスター(登録商標)MA1006,平均粒子径6μm/日本触媒社製): 10.0質量%
塗布液6を用いた点を除いては、実施例7と同様にして、凹凸転写フィルムを得た。得られた凹凸転写フィルムについて、60°グロス、表面粗さ、加圧に対する凹凸安定性の評価を行った結果、全ての評価において好適な結果であった。
凹凸層組成物は、実施例1に比べ樹脂を変更し固形分濃度を増加させた、下記塗布液7を使用した。
塗布液7
・メチルエチルケトン: 36.7質量%
・トルエン: 36.7質量%
・多官能アクリレート(DPHA/ダイセル・オルネクス社製(固形分100質量%)) : 20.0質量%
・PMMA粒子(エポスター(登録商標)MA1006,平均粒子径6μm/日本触媒社製): 6.0質量%
・光重合開始剤(イルガキュア(登録商標)184/BASF社製): 0.6質量%
塗布液7を用いた点を除いては、実施例1と同様にして、凹凸転写フィルムを得た。得られた凹凸転写フィルムについて、60°グロス、表面粗さ、加圧に対する凹凸安定性の評価を行った結果、全ての評価において好適な結果であった。
凹凸層組成物は、実施例1に比べ平均粒子径が小さい、下記塗布液8を使用した。
塗布液8
・メチルエチルケトン: 14.7質量%
・トルエン: 14.7質量%
・ウレタン変性アクリル樹脂(8UA-347A/大成ファインケミカル社製(固形分30質量%))
: 54.5質量%
・PMMA粒子(エポスター(登録商標)MA1002,平均粒子径2.5μm/日本触媒製): 10.0質量%
・架橋剤(MF-K60B/旭化成ケミカルズ社製(固形分60質量%)): 6.1質量%
基材フィルムとしての易接着層付きポリエステルフィルム(東洋紡社製,コスモシャイン(登録商標)A4100,厚さ:50μm)の易接着層側の面に、凹凸層組成物をワイヤーバー#5で塗布し、160℃で30秒間乾燥・硬化させ、凹凸転写フィルムを得た。
また、得られた凹凸転写フィルムに下記の離型層組成物をワイヤーバー#5で塗布し、160℃で30秒間乾燥・硬化させ離型加工した。下記離型層組成物は実施例1と比べ、固形分濃度を減少させた。
・トルエン :60.0質量%
・メチルエチルケトン : 38.97質量%
・テスファイン(登録商標)305(日立化成社製(固形分50質量%)) :1.0質量%
・ドライヤー900(日立化成社製) :0.03質量%
得られた離型処理した凹凸転写フィルムを用いて転写工程を行い、保護層の被転写面の60°グロスの評価を行った結果、好適な結果であった。
ポリエステルフィルムにサンドブラスト処理したサンドマットフィルム(開成工業製 タイフ゜D)を凹凸転写フィルムとした。60°グロス、表面粗さ、加圧に対する凹凸安定性の評価を行った結果、加圧によって表面凹凸が減少し圧痕が目視にて確認でき、60°グロスの上昇および表面粗さRaの減少も著しい結果であった。
凹凸層組成物は、平均粒子径が最適範囲外の粒子を添加した下記塗布液9を使用した。
塗布液9
・メチルエチルケトン: 14.7質量%
・トルエン: 14.7質量%
・ウレタン変性アクリル樹脂(8UA-347A/大成ファインケミカル社製(固形分30質量%))
: 54.5質量%
・PMMA粒子(MX-80H3wT,平均粒子径0.8μm/綜研化学社製): 10.0質量%
・架橋剤(MF-K60B/旭化成ケミカルズ社製(固形分60質量%)): 6.1質量%
塗布液9を用いた点を除いては、実施例10と同様にして、凹凸転写フィルムを得た。得られた凹凸転写フィルムについて、60°グロス、表面粗さ、加圧に対する凹凸安定性の評価を行った結果、60°グロス、表面粗さRaが高くマット性が不十分であった。
凹凸層組成物は、樹脂に対する粒子濃度が最適範囲外である下記塗布液10を使用した。
塗布液10
・メチルエチルケトン: 38.7質量%
・トルエン: 38.7質量%
・多官能アクリレート(8UX-015A/大成ファインケミカル社製) : 20.0質量%
・PMMA粒子(エポスター(登録商標)MA1006,平均粒子径6μm/日本触媒社製): 2.0質量%
・光重合開始剤(イルガキュア(登録商標)184/BASF社製): 0.6質量%
塗布液10を用いた点を除いては、実施例1と同様にして、凹凸転写フィルムを得た。得られた凹凸転写フィルムについて、60°グロス、表面粗さ、加圧に対する凹凸安定性の評価を行った結果、60°グロスが高くマット性が不十分であり、粒子の添加量不足のため加圧による凹凸安定性も悪化した。
2 :被転写層
11:基材フィルム
12:凹凸層
13:離型層
14:粒子
21:被転写体を構成する基材フィルム
22:シールド層
23:保護層
Claims (6)
- フィルムの片面が表面凹凸を有し、片面に表面凹凸を有するフィルムが、基材フィルムの片面に凹凸層を有するものであり、前記凹凸層が、樹脂(A)及び粒子(B)を含み、前記樹脂(A)が、アクリル系樹脂、ポリエステル樹脂、ウレタン系樹脂、メラミン系樹脂、エポキシ系樹脂から選ばれる1種または2種類以上の樹脂からなり、前記凹凸層が、以下の式(1)を満足し、前記表面凹凸を有する面の60°グロスが20%以下であり、40MPaの圧力で30秒間の加圧プレスを施した後の60°グロスの上昇率が、前記加圧プレスを施す前の60°グロスに対して25%以下であり、前記凹凸層上に離型層を有することを特徴とする凹凸転写フィルム。
(1/4)×D≦d≦(3/4)×D ・・・(1)
ここで、dは凹凸層の膜厚[μm]、Dは粒子(B)の平均粒子径[μm]を示す。 - フィルムの表面凹凸を有する面の表面粗さRaが0.2μm以上2.5μm以下であり、40MPaの圧力で30秒間の加圧プレスを施した後の表面粗さRaの低減率が、前記加圧プレスを施す前の表面粗さRaに対して20%以下であることを特徴とする請求項1に記載の凹凸転写フィルム。
- 粒子(B)の平均粒子径が、1μm以上10μm以下であることを特徴とする請求項1または2に記載の凹凸転写フィルム。
- 粒子(B)の含有量が、樹脂成分100質量部に対して20質量部以上70質量部以下であることを特徴とする請求項1〜3のいずれかに記載の凹凸転写フィルム。
- 離型層の凹凸層と接していない反対面の60°グロスが、20%以下であることを特徴とする請求項1〜4のいずれかに記載の凹凸転写フィルム。
- 請求項1〜5のいずれかに記載の凹凸転写フィルムを使用して作成された保護層を有することを特徴とする電磁波シールドフィルム。