モデル材用樹脂組成物、サポート材用樹脂組成物、光造形品、および、光造形品の製造方法 Download PDFInfo
- Publication number
- JP6679234B2 JP6679234B2 JP2015149753A JP2015149753A JP6679234B2 JP 6679234 B2 JP6679234 B2 JP 6679234B2 JP 2015149753 A JP2015149753 A JP 2015149753A JP 2015149753 A JP2015149753 A JP 2015149753A JP 6679234 B2 JP6679234 B2 JP 6679234B2
- Authority
- JP
- Japan
- Prior art keywords
- glycol
- ether
- resin composition
- weight
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本実施形態に係るモデル材用樹脂組成物は、樹脂組成物全体100重量部に対して、19〜49重量部の非水溶性単官能エチレン性不飽和単量体(A)と、15〜50重量部の二官能以上の多官能エチレン性不飽和単量体(B)と、10〜45重量部のオリゴマー(C)と、3〜15重量部の光重合開始剤(D)と、0.005〜3.0重量部の表面調整剤(E)と、を含有する。
非水溶性単官能エチレン性不飽和単量体(A)は、光照射により重合して、モデル材用樹脂組成物を硬化させる成分である。上記(A)成分の含有量は、樹脂組成物全体100重量部に対して、19〜49重量部とする。上記(A)成分の含有量が19重量部未満であると、モデル材用樹脂組成物を光硬化させて得られるモデル材は、硬化収縮が大きくなる。その結果、モデル材の寸法精度が悪化する。一方、上記(A)成分の含有量が49重量部を超えると、モデル材用樹脂組成物を光硬化させて得られるモデル材には、硬化性不足が生じる。その結果、モデル材の寸法精度が悪化する。上記(A)成分の含有量は、25重量部以上であることが好ましく、47重量部以下であることが好ましい。
二官能以上の多官能エチレン性不飽和単量体(B)は、光照射により重合して、モデル材用樹脂組成物を硬化させる成分である。上記(B)成分の含有量は、樹脂組成物全体100重量部に対して、15〜50重量部とする。上記(B)成分の含有量が15重量部未満であると、モデル材用樹脂組成物を光硬化させて得られるモデル材には、硬化性不足が生じる。その結果、モデル材の寸法精度が悪化する。一方、上記(B)成分の含有量が50重量部を超えると、モデル材用樹脂組成物を光硬化させて得られるモデル材は、硬化収縮が大きくなる。その結果、モデル材の寸法精度が悪化する。上記(B)成分の含有量は、20重量部以上であることが好ましく、45重量部以下であることが好ましい。
オリゴマー(C)は、光照射により重合してモデル材用樹脂組成物を硬化させ、かつ、該硬化により得られるモデル材の破断強度を高める成分である。上記(C)成分の含有量は、樹脂組成物全体100重量部に対して、10〜45重量部とする。上記(C)成分の含有量が10重量部未満であると、モデル材用樹脂組成物を光硬化させて得られるモデル材には、硬化収縮がやや大きくなる。その結果、モデル材の寸法精度が悪化する可能性がある。また、モデル材用樹脂組成物を光硬化させて得られるモデル材の破断強度が劣る。一方、上記(C)成分の含有量が45重量部を超えると、モデル材用樹脂組成物の粘度が高くなる。そのため、モデル材用樹脂組成物をインクジェットヘッドから吐出させる際、ジェッティング特性が悪化して、飛行曲がりを起こす可能性がある。その結果、モデル材用樹脂組成物を光硬化させて得られるモデル材の寸法精度が悪化する可能性がある。上記(C)成分の含有量は、15重量部以上であることが好ましく、30重量部以下であることが好ましい。
光重合開始剤(D)は、紫外線、近紫外線または可視光領域の波長の光を照射するとラジカル反応を促進する化合物であれば、特に限定されない。上記(D)成分としては、例えば、炭素数14〜18のベンゾイン化合物〔例えば、ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインプロピルエーテル、ベンゾインイソブチルエーテル等〕、炭素数8〜18のアセトフェノン化合物〔例えば、アセトフェノン、2,2−ジエトキシ−2−フェニルアセトフェノン、2,2−ジエトキシ−2−フェニルアセトフェノン、1,1−ジクロロアセトフェノン、2−ヒドロキシ−2−メチル−フェニルプロパン−1−オン、ジエトキシアセトフェノン、1−ヒドロキシシクロヘキシルフェニルケトン、2−メチル−1−[4−(メチルチオ)フェニル]−2−モルホリノプロパン−1−オン等〕、炭素数14〜19のアントラキノン化合物〔例えば、2−エチルアントラキノン、2−t−ブチルアントラキノン、2−クロロアントラキノン、2−アミルアントラキノン等〕、炭素数13〜17のチオキサントン化合物〔例えば、2,4−ジエチルチオキサントン、2−イソプロピルチオキサントン、2−クロロチオキサントン等〕、炭素数16〜17のケタール化合物〔例えば、アセトフェノンジメチルケタール、ベンジルジメチルケタール等〕、炭素数13〜21のベンゾフェノン化合物〔例えば、ベンゾフェノン、4−ベンゾイル−4’−メチルジフェニルサルファイド、4,4’−ビスメチルアミノベンゾフェノン等〕、炭素数22〜28のアシルフォスフィンオキサイド化合物〔例えば、2,4,6−トリメチルベンゾイル−ジフェニル−フォスフィンオキサイド、ビス−(2、6−ジメトキシベンゾイル)−2,4,4−トリメチルペンチルフォスフィンオキサイド、ビス(2,4,6−トリメチルベンゾイル)−フェニルフォスフィンオキサイド〕、これらの化合物の混合物等が挙げられる。これらは単独で用いてもよいし、2種以上を併用してもよい。これらの中でも、モデル材用樹脂組成物を光硬化させて得られるモデル材が黄変しにくいという耐光性の観点から、2,4,6−トリメチルベンゾイル−ジフェニル−フォスフィンオキサイドであることが好ましい。また、入手可能なアシルフォスフィンオキサイド化合物としては、例えば、BASF社製のDAROCURE TPO等が挙げられる。
表面調整剤(E)は、樹脂組成物の表面張力を適切な範囲に調整するために含有させる。樹脂組成物の表面張力を適切な範囲に調整することにより、モデル材用樹脂組成物とサポート材用樹脂組成物とが界面で混ざり合うことを抑制することができる。その結果、これらの樹脂組成物を用いて、寸法精度が良好な光造形品を得ることができる。この効果を得るため、上記(E)成分の含有量は、樹脂組成物全体100重量部に対して、0.005〜3.0重量部とする。
本実施形態に係るモデル材用樹脂組成物は、さらに、保存安定化剤(F)を含有することが好ましい。保存安定化剤(F)は、樹脂組成物の保存安定性を高めることができる。また、熱エネルギーにより重合性化合物が重合することで生じるヘッド詰まりを防止することができる。これらの効果を得るため、上記(F)成分の含有量は、樹脂組成物全体100重量部に対して、0.05〜3.0重量部であることが好ましい。
本実施形態に係るモデル材用樹脂組成物は、水溶性単官能エチレン性不飽和単量体(G)を含有しないことが好ましい。モデル材用樹脂組成物が上記(G)成分を含むと、光硬化時および硬化後の水または吸湿により、モデル材の膨潤変形が起こる場合がある。その結果、モデル材の寸法精度が悪化する可能性がある。上記(G)成分の詳細については後述する。
本実施形態に係るサポート材用樹脂組成物は、樹脂組成物全体100重量部に対して、20〜50重量部の水溶性単官能エチレン性不飽和単量体(G)と、20〜49重量部のオキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコール(H)と、35重量部以下の水溶性有機溶剤(I)と、5〜20重量部の光重合開始剤(D)と、0.005〜3.0重量部の表面調整剤(E)と、を含有する。
水溶性単官能エチレン性不飽和単量体(G)は、光照射により重合して、サポート材用樹脂組成物を硬化させる成分である。また、サポート材用樹脂組成物を光硬化させて得られるサポート材をすばやく水に溶解させる成分である。上記(G)成分の含有量は、樹脂組成物全体100重量部に対して、20〜50重量部とする。上記(G)成分の含有量が20重量部未満であると、サポート材用樹脂組成物を光硬化させて得られるサポート材における自立性が充分ではない。そのため、該サポート材をモデル材の下層に配置した際、モデル材を充分に支えることができない。その結果、モデル材の寸法精度が悪化する。一方、上記(G)成分の含有量が50重量部を超えると、サポート材用樹脂組成物を光硬化させて得られるサポート材は、水への溶解性が劣る。サポート材を完全に除去するまでの水への浸漬時間が長くなると、モデル材がわずかに膨張する。その結果、モデル材の微細構造部分において、寸法精度が悪化する場合がある。上記(G)成分の含有量は、25重量部以上であることが好ましく、45重量部以下であることが好ましい。
オキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコール(H)は、サポート材用樹脂組成物を光硬化させて得られるサポート材の水への溶解性を高める。上記(H)成分の含有量は、樹脂組成物全体100重量部に対して、20〜49重量部とする。上記(H)成分の含有量が20重量部未満であると、サポート材用樹脂組成物を光硬化させて得られるサポート材は、水への溶解性が劣る。サポート材を完全に除去するまでの水への浸漬時間が長くなると、サポート材がわずかに膨張する。その結果、該サポート材の上層に成形されたモデル材の微細構造部分において、寸法精度が悪化する場合がある。一方、上記(H)成分の含有量が49重量部を超えると、サポート材用樹脂組成物を光硬化させる際、上記(H)成分の浸み出しが生じる場合がある。上記(H)成分の浸み出しが生じると、サポート材とモデル材との界面における密着性が悪くなる。その結果、モデル材は、硬化収縮する際にサポート材から剥がれやすくなり、寸法精度が悪化する場合がある。また、上記(H)成分の含有量が49重量部を超えると、サポート材用樹脂組成物の粘度が高くなる。そのため、サポート材用樹脂組成物をインクジェットヘッドから吐出させる際、ジェッティング特性が悪化して、飛行曲がりを起こす可能性がある。その結果、サポート材用樹脂組成物を光硬化させて得られるサポート材の寸法精度が悪化するため、該サポート材の上層に成形されたモデル材の寸法精度も悪化する。上記(H)成分の含有量は、25重量部以上であることが好ましく、45重量部以下であることが好ましい。
水溶性有機溶剤(I)は、サポート材用樹脂組成物を光硬化させて得られるサポート材の水への溶解性を向上させる成分である。また、サポート材用樹脂組成物を低粘度に調整する成分である。上記(I)成分の含有量は、樹脂組成物全体100重量部に対して、35重量部以下とする。上記(I)成分の含有量が35重量部を超えると、サポート材用樹脂組成物を光硬化させる際、上記(I)成分の浸み出しが生じる。そのため、該サポート材の上層に成形されたモデル材は、寸法精度が悪化する。上記(I)成分の含有量は、サポート材の水への溶解性を向上させ、かつ、サポート材用樹脂組成物を低粘度に調整する観点から、5重量部以上であることが好ましく、10重量部以上であることがより好ましい。また、上記(I)成分の含有量は、30重量部以下であることが好ましい。
光重合開始剤(D)としては、本実施形態に係るモデル材用樹脂組成物と同様の成分を用いることができる。上記(D)成分の含有量は、樹脂組成物全体100重量部に対して、5〜20重量部である。上記(D)成分の含有量が上記範囲であると、サポート材用樹脂組成物の自立性が良好となる。そのため、該サポート材の上層に成形されたモデル材は、寸法精度が向上する。上記(D)成分の含有量は、7重量部以上であることが好ましく、18重量部以下であることが好ましい。なお、上記(D)成分が2種以上含まれる場合、上記含有量は、各(D)成分の含有量の合計として定める。
表面調整剤(E)は、本実施形態に係るモデル材用樹脂組成物と同様の成分を同様の含有量で用いることができる。
本実施形態に係るサポート材用樹脂組成物は、さらに、保存安定化剤(F)を含有することが好ましい。保存安定化剤(F)は、本実施形態に係るモデル材用樹脂組成物と同様の成分を同様の含有量で用いることができる。
本実施形態に係る光造形品は、インクジェット光造形法により、本実施形態に係るモデル材用樹脂組成物を光硬化させてモデル材を得るとともに、本実施形態に係るサポート材用樹脂組成物を光硬化させてサポート材を得る工程(I)と、上記サポート材を除去する工程(II)とを経て製造される。上記工程(I)および上記工程(II)は、特に限定されないが、例えば、以下の方法により行われる。
図1は、本実施形態に係る光造形品の製造方法における工程(I)を模式的に示す図である。図1に示すように、三次元造形装置1は、インクジェットヘッドモジュール2および造形テーブル3を含む。インクジェットヘッドモジュール2は、モデル材用樹脂組成物を充填したモデル材用インクジェットヘッド21と、サポート材用樹脂組成物を充填したサポート材用インクジェットヘッド22と、ローラー23と、光源24とを有する。
図2は、本実施形態に係る光造形品の製造方法における工程(II)を模式的に示す図である。図2に示すように、工程(I)で作製したモデル材4およびサポート材5からなる硬化物6は、容器7に入れた溶媒8中に浸漬させる。これにより、サポート材5を溶媒8に溶解させて、除去することができる。
(モデル材用樹脂組成物の製造)
表1に示す配合で、(A)〜(G)成分を、混合攪拌装置を用いて均一に混合し、実施例M1〜M15および比較例m1〜m8のモデル材用樹脂組成物を製造した。そして、これらのモデル材用樹脂組成物を用いて、以下の評価を行った。なお、比較例m1のモデル材用樹脂組成物については、(A)成分の含有量が49重量部を超えることから、光を照射しても、充分に硬化しなかった。また、比較例m7のモデル材用樹脂組成物については、(D)成分の含有量が3重量部未満であることから、光を照射しても、充分に硬化しなかった。したがって、比較例m1およびm7のモデル材用樹脂組成物については、硬化収縮以降の評価を行わなかった。さらに、比較例m8のモデル材用樹脂組成物については、(D)成分の含有量が15重量部を超えることから、(D)成分が充分に溶解せず、溶け残りが生じた。これにより、比較例m8のモデル材用樹脂組成物に光を照射しても、満足に硬化しなかった。したがって、比較例m8のモデル材用樹脂組成物については、以下の評価をすべて行わなかった。
THFA:テトラヒドロフルフリルアクリレート[ビスコート#150(エチレン性二重結合/1分子:1個)、大阪有機化学工業社製]
PEA:フェノキシエチルアクリレート[SR3339(エチレン性二重結合/1分子:1個)、アルケマ社製]
HDDA:1,6−ヘキサンジオールジアクリレート[SR238(エチレン性二重結合/1分子:2個)、アルケマ社製]
TPGDA:トリプロピレングリコールジアクリレート[SR306(エチレン性二重結合/1分子:2個)、アルケマ社製]
PE−3A:ペンタエリスリトールトリアクリレート[ライトアクリレートPE−3A(エチレン性二重結合/1分子:3個)、共栄社化学社製]
CN991:ウレタンアクリレートオリゴマー[CN991(エチレン性二重結合/1分子:2個)、アルケマ社製]
EBECRYL3708:エポキシアクリレートオリゴマー[EBECRYL3708(エチレン性二重結合/1分子:2個)、ダイセル・オルネクス社製]
CN2203:ポリエステルアクリレートオリゴマー[CN2203(エチレン性二重結合/1分子:2個)、アルケマ社製]
DAROCURE TPO:2,4,6−トリメチルベンゾイル−ジフェニル−フォスフィンオキサイド[DAROCURE TPO、BASF社製]
TEGO−Rad2100:ポリジメチルシロキサン構造を有するシリコンアクリレート[TEGO−Rad2100、エボニック デグサ ジャパン社製]
H-TEMPO:4−ヒドロキシ−2,2,6,6−テトラメチルピペリジン−N−オキシル[HYDROXY−TEMPO、エボニック デグサ ジャパン社製]
ACMO:アクリロイルモルフォリン[ACMO(エチレン性二重結合/1分子:1個)、KJケミカルズ社製]
各モデル材用樹脂組成物の粘度は、R100型粘度計(東機産業社製)を用いて、25℃、コーン回転数5rpmの条件下で測定し、下記の基準において評価した。結果を表2に示す。
○:粘度 ≦ 70mPa・s
×:粘度 > 70mPa・s
まず、ポリエチレンテレフタレートからなるフィルム(A4300、東洋紡社製、100mm×150mm×厚さ188μm)上に、各モデル材用樹脂組成物を、それぞれバーコーター(#4)により印刷して、厚さ3μmの印字膜を形成した。この印字膜に、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させた。このようにして硬化させた印字膜を指で触り、指へのインクの付着の有無を目視で調べ、下記の基準において硬化性を評価した。なお、評価は、画像部分から非印刷部分に向かって指で画像を擦って行った。結果を表2に示す。
○:表面はさらさらしており、指への付着感は無かった。
△:表面はややしっとりとしており、指への付着感はペタペタ感が有った。
×:表面はべたべたしており、指に未硬化インクの一部が付着した。
ガラス板(商品名「GLASS PLATE」、アズワン社製、200mm×200mm×厚さ5mm)の上面四辺に厚さ1mmのスペーサーを配し、10cm×10cmの正方形に仕切った。該正方形内に各モデル材用樹脂組成物を注型した後、別の上記ガラス板を重ねて載せた。そして、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させた。その後、硬化物をガラス板から離型し、カッターで幅5mm、長さ50mmの形状に切り出して、試験片を得た。該試験片について、下記の方法で性能評価を行った。なお、評価結果は、試験片5枚について評価して得られた結果の平均結果を示す。
まず、調整した28%ヨウ化カリウム水溶液中に、各モデル材用樹脂組成物から得られた試験片を浸した。その際、上記試験片は、水溶液中に浮かんでいた。次に、上記試験片が水浴内中層部に浮遊する状態になるまで、上記水溶液に純水を加えた。この際のヨウ化カリウム水溶液の比重を計算し、試験片の比重とした。また、各モデル材用樹脂組成物の比重は、密度比重計DA−130(京都電子工業社製)で測定した。硬化収縮は、下記(i)式により求め、下記の基準において評価した。結果を表2に示す。
○:硬化収縮 ≦ 10%
△:10% < 硬化収縮 < 13%
×:硬化収縮 ≧ 13%
各モデル材用樹脂組成物から得られた試験片のガラス転移点Tgは、熱重量測定装置(TG−DTA2000S Thermo Plus EvoII DSC8230、株式会社リガク製)を用いて測定した。測定は、昇温温度:10℃/min、測定温度範囲:−60℃〜200℃で行った。結果を表2に示す。
オートグラフ(株式会社島津製作所製)を用いて、各モデル材用樹脂組成物から得られた試験片を試験速度50mm/minで引張り、JIS K7113に準じて引張破断強度を測定し、破断強度とした。破断強度は、下記の基準において評価した。結果を表2に示す。
○:破断強度 ≧ 30MPa
×:破断強度 < 30MPa
(サポート材用樹脂組成物の製造)
表3に示す配合で、(D)〜(F)、(G)〜(I)成分を、混合攪拌装置を用いて均一に混合し、実施例S1〜S15および比較例s1〜s8のサポート材用樹脂組成物を製造した。そして、これらのサポート材用樹脂組成物を用いて、以下の評価を行った。なお、比較例s8のサポート材用樹脂組成物については、(D)成分の含有量が20重量部を超えることから、(D)成分が充分に溶解せず、溶け残りが生じた。これにより、比較例s8のサポート材用樹脂組成物に光を照射しても、満足に硬化しなかった。したがって、比較例s8のサポート材用樹脂組成物については、以下の評価をすべて行わなかった。
ACMO:アクリロイルモルフォリン[ACMO(エチレン性二重結合/1分子:1個)、KJケミカルズ社製]
DMAA:N,N’−ジメチルアクリルアミド[DMAA(エチレン性二重結合/1分子:1個)、KJケミカルズ社製]
PPG−400:ポリプロピレングリコール[ユニオールD400(分子量400)、日油社製]
PPG−1000:ポリプロピレングリコール[ユニオールD1000(分子量1000)、日油社製]
PEG−400:ポリエチレングリコール[PEG#400(分子量400)、日油社製]
PEG−1000:ポリエチレングリコール[PEG#1000(分子量1000)、日油社製]
MTG:トリエチレングリコールモノメチルエーテル[MTG、日本乳化剤社製]
DPMA:ジプロピレングリコールモノメチルエーテルアセテート[ダワノールDPMA、ダウケミカル社製]
各サポート材用樹脂組成物の粘度は、R100型粘度計(東機産業社製)を用いて、25℃、コーン回転数5rpmの条件下で測定し、下記の基準において評価した。結果を表4に示す。
○:粘度 ≦ 70mPa・s
×:粘度 > 70mPa・s
直径50mmのアルミカップに、各サポート材用樹脂組成物2.0gを採取した。次に、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させ、サポート材を得た。その後、サポート材をアルミカップから離型した。続いて、ビーカーに入れたイオン交換水500ml中に、上記サポート材を浸漬した。10分毎にサポート材を目視で観察し、浸漬開始から完全溶解または元の形状が無くなるまでに要した時間(以下、水溶解時間という)を計測し、下記の基準において溶解性を評価した。結果を表4に示す。
○:水溶解時間 ≦ 1時間
△:1時間 < 水溶解時間 <1.5時間
×:水溶解時間 ≧ 1.5時間
100mm×100mmのアルミ箔に、各サポート材用樹脂組成物1.0gを採取した。次に、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させ、サポート材を得た。なお、この時点でサポート材は固体状態である。このサポート材を2時間放置し、サポート材表面における油状浸み出しの有無を目視で観察し、下記の基準において評価した。結果を表4に示す。
○:油状浸み出しが全く観察されなかった
△:わずかに油状浸み出しが観察された
×:油状浸み出しが多く観察された
ガラス板(商品名「GLASS PLATE」、アズワン社製、200mm×200mm×厚さ5mm)の上面四辺に厚さ1mmのスペーサーを配し、10cm×10cmの正方形に仕切った。該正方形内に各サポート材用樹脂組成物を注型した後、別の上記ガラス板を重ねて載せた。そして、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させ、サポート材を得た。その後、サポート材をガラス板から離型し、カッターで縦10mm、横10mmの形状に切り出して、試験片を得た。次に、該試験片を10枚重ねて、高さ10mmの試験片群を得た。該試験片群は、上から100gの重しを乗せ、そのまま30℃に設定したオーブンの中に入れ、1時間放置した。その後、試験片の形状を観察し、下記の基準において自立性を評価した。結果を表4に示す。
○:形状に変化がなかった
△:形状がわずかに変化し、重しが傾いた状態になった
×:形状が大きく変化した
(密着性の評価)
ガラス板(商品名「GLASS PLATE」、アズワン社製、200mm×200mm×厚さ5mm)の上面四辺に厚さ1mmのスペーサーを配し、10cm×10cmの正方形に仕切った。該正方形内に各サポート材用樹脂組成物を注型した後、照射手段として紫外線LED(NCCU001E、日亜化学工業株式会社製)を用い、全照射光量が500mJ/cm2となるように紫外線を照射して硬化させ、サポート材を得た。
○:モデル材とサポート材とは密着していた。
△:モデル材とサポート材とは密着していたが、モデル材とサポート材との界面を爪でひっかくと剥がれが生じた。
×:モデル材とサポート材との界面で剥がれが生じ、モデル材の硬化収縮でモデル材が反るように剥がれた。
5 サポート材
Claims (15)
- インクジェット光造形法によりモデル材を造形するために使用されるモデル材用樹脂組成物であって、
樹脂組成物全体100重量部に対して、
19〜49重量部の非水溶性単官能エチレン性不飽和単量体(A)と、
15〜50重量部の二官能以上の多官能エチレン性不飽和単量体(B)と、
10〜45重量部のオリゴマー(C)と、
3〜15重量部の光重合開始剤(D)と、
0.005〜3.0重量部の表面調整剤(E)と、
を含有し、ここで、オリゴマー(C)成分は、ウレタン(メタ)アクリレートオリゴマー、エポキシ(メタ)アクリレートオリゴマー、および、ポリエステル(メタ)アクリレートオリゴマーから選択される1種以上である、モデル材用樹脂組成物。 - 前記(A)成分の含有量は、樹脂組成物全体100重量部に対して、25〜47重量部である、請求項1に記載のモデル材用樹脂組成物。
- 前記(B)成分の含有量は、樹脂組成物全体100重量部に対して、20〜45重量部である、請求項1または2に記載のモデル材用樹脂組成物。
- 前記(C)成分の含有量は、樹脂組成物全体100重量部に対して、15〜30重量部である、請求項1〜3のいずれか一つに記載のモデル材用樹脂組成物。
- 前記(D)成分の含有量は、樹脂組成物全体100重量部に対して、5〜13重量部である、請求項1〜4のいずれか一つに記載のモデル材用樹脂組成物。
- さらに、保存安定化剤(F)を、樹脂組成物全体100重量部に対して、0.05〜3.0重量部含有する、請求項1〜5のいずれか一つに記載のモデル材用樹脂組成物。
- インクジェット光造形法によりサポート材を造形するために使用されるサポート材用樹脂組成物であって、
樹脂組成物全体100重量部に対して、
20〜50重量部の水溶性単官能エチレン性不飽和単量体(G)と、
20〜49重量部のオキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコール(H)と、
35重量部以下の水溶性有機溶剤(I)と、
5〜20重量部の光重合開始剤(D)と、
0.005〜3.0重量部の表面調整剤(E)と、
0.05〜3.0重量部の保存安定化剤(F)と、
を含有し、ここで、水溶性有機溶剤(I)はオキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコールではない、サポート材用樹脂組成物。 - 前記水溶性単官能エチレン性不飽和単量体(G)は、炭素数5〜15の水酸基含有(メタ)アクリレート、Mn200〜1,000の水酸基含有(メタ)アクリレート、(メタ)アクリルアミド、N−メチル(メタ)アクリルアミド、N−エチル(メタ)アクリルアミド、N−プロピル(メタ)アクリルアミド、N−ブチル(メタ)アクリルアミド、N,N’−ジメチル(メタ)アクリルアミド、N,N’−ジエチル(メタ)アクリルアミド、N−ヒドロキシエチル(メタ)アクリルアミド、N−ヒドロキシプロピル(メタ)アクリルアミド、N−ヒドロキシブチル(メタ)アクリルアミド、及び(メタ)アクリロイルモルフォリンからなる群から選択される1種又は2種以上である、請求項7に記載のサポート材用樹脂組成物。
- 前記オキシエチレン基および/またはオキシプロピレン基を含むポリアルキレングリコールではない水溶性有機溶剤(I)は、エチレングリコールモノアセテート、プロピレングリコールモノアセテート、ジエチレングリコールモノアセテート、ジプロピレングリコールモノアセテート、トリエチレングリコールモノアセテート、トリプロピレングリコールモノアセテート、テトラエチレングリコールモノアセテート、テトラプロピレングリコールモノアセテート、エチレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテル、ジエチレングリコールモノメチルエーテル、ジプロピレングリコールモノメチルエーテル、トリエチレングリコールモノメチルエーテル、トリプロピレングリコールモノメチルエーテル、テトラエチレングリコールモノメチルエーテル、テトラプロピレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、プロピレングリコールモノエチルエーテル、ジエチレングリコールモノエチルエーテル、ジプロピレングリコールモノエチルエーテル、トリエチレングリコールモノエチルエーテル、トリプロピレングリコールモノエチルエーテル、テトラエチレングリコールモノエチルエーテル、テトラプロピレングリコールモノエチルエーテル、エチレングリコールモノプロピルエーテル、プロピレングリコールモノプロピルエーテル、ジエチレングリコールモノプロピルエーテル、ジプロピレングリコールモノプロピルエーテル、トリエチレングリコールモノプロピルエーテル、トリプロピレングリコールモノプロピルエーテル、テトラエチレングリコールモノプロピルエーテル、テトラプロピレングリコールモノプロピルエーテル、エチレングリコールモノブチルエーテル、プロピレングリコールモノブチルエーテル、ジエチレングリコールモノブチルエーテル、ジプロピレングリコールモノブチルエーテル、トリエチレングリコールモノブチルエーテル、トリプロピレングリコールモノブチルエーテル、テトラエチレングリコールモノブチルエーテル、テトラプロピレングリコールモノブチルエーテル、エチレングリコールジアセテート、プロピレングリコールジアセテート、ジエチレングリコールジアセテート、ジプロピレングリコールジアセテート、トリエチレングリコールジアセテート、トリプロピレングリコールジアセテート、テトラエチレングリコールジアセテート、テトラプロピレングリコールジアセテート、エチレングリコールジメチルエーテル、プロピレングリコールジメチルエーテル、ジエチレングリコールジメチルエーテル、ジプロピレングリコールジメチルエーテル、トリエチレングリコールジメチルエーテル、トリプロピレングリコールジメチルエーテル、テトラエチレングリコールジメチルエーテル、テトラプロピレングリコールジメチルエーテル、エチレングリコールジエチルエーテル、プロピレングリコールジエチルエーテル、ジエチレングリコールジエチルエーテル、ジプロピレングリコールジエチルエーテル、トリエチレングリコールジエチルエーテル、トリプロピレングリコールジエチルエーテル、テトラエチレングリコールジエチルエーテル、テトラプロピレングリコールジエチルエーテル、エチレングリコールジプロピルエーテル、プロピレングリコールジプロピルエーテル、ジエチレングリコールジプロピルエーテル、ジプロピレングリコールジプロピルエーテル、トリエチレングリコールジプロピルエーテル、トリプロピレングリコールジプロピルエーテル、テトラエチレングリコールジプロピルエーテル、テトラプロピレングリコールジプロピルエーテル、エチレングリコールジブチルエーテル、プロピレングリコールジブチルエーテル、ジエチレングリコールジブチルエーテル、ジプロピレングリコールジブチルエーテル、トリエチレングリコールジブチルエーテル、トリプロピレングリコールジブチルエーテル、テトラエチレングリコールジブチルエーテル、テトラプロピレングリコールジブチルエーテル、エチレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテルアセテート、ジエチレングリコールモノメチルエーテルアセテート、ジプロピレングリコールモノメチルエーテルアセテート、トリエチレングリコールモノメチルエーテルアセテート、トリプロピレングリコールモノメチルエーテルアセテート、テトラエチレングリコールモノメチルエーテルアセテート、テトラプロピレングリコールモノメチルエーテルアセテート、エチレングリコールモノエチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート、ジプロピレングリコールモノエチルエーテルアセテート、トリエチレングリコールモノエチルエーテルアセテート、トリプロピレングリコールモノエチルエーテルアセテート、テトラエチレングリコールモノエチルエーテルアセテート、テトラプロピレングリコールモノエチルエーテルアセテート、エチレングリコールモノプロピルエーテルアセテート、プロピレングリコールモノプロピルエーテルアセテート、ジエチレングリコールモノプロピルエーテルアセテート、ジプロピレングリコールモノプロピルエーテルアセテート、トリエチレングリコールモノプロピルエーテルアセテート、トリプロピレングリコールモノプロピルエーテルアセテート、テトラエチレングリコールモノプロピルエーテルアセテート、テトラプロピレングリコールモノプロピルエーテルアセテート、エチレングリコールモノブチルエーテルアセテート、プロピレングリコールモノブチルエーテルアセテート、ジエチレングリコールモノブチルエーテルアセテート、ジプロピレングリコールモノブチルエーテルアセテート、トリエチレングリコールモノブチルエーテルアセテート、トリプロピレングリコールモノブチルエーテルアセテート、テトラエチレングリコールモノブチルエーテルアセテート、及びテトラプロピレングリコールモノブチルエーテルアセテートからなる群から選択される1種又は2種以上である、請求項7または8に記載のサポート材用樹脂組成物。
- 前記(G)成分の含有量は、樹脂組成物全体100重量部に対して、25〜45重量部である、請求項7〜9のいずれか一つに記載のサポート材用樹脂組成物。
- 前記(H)成分の含有量は、樹脂組成物全体100重量部に対して、25〜45重量部である、請求項7〜10のいずれか一つに記載のサポート材用樹脂組成物。
- 前記(D)成分の含有量は、樹脂組成物全体100重量部に対して、7〜18重量部である、請求項7〜11のいずれか一つに記載のサポート材用樹脂組成物。
- 前記(I)成分の含有量は、樹脂組成物全体100重量部に対して、5重量部以上である、請求項7〜10のいずれか一つに記載のサポート材用樹脂組成物。
- インクジェット光造形法により、請求項1〜6のいずれか一つに記載のモデル材用樹脂組成物を光硬化させて得られるモデル材を含む、光造形品。
- インクジェット光造形法により請求項14に記載の光造形品を製造する方法であって、
請求項1〜6のいずれか一つに記載のモデル材用樹脂組成物を光硬化させてモデル材を得るとともに、請求項7〜13のいずれか一つに記載のサポート材用樹脂組成物を光硬化させてサポート材を得る工程(I)と、
前記サポート材を除去する工程(II)と、
を有する、光造形品の製造方法。