JP6625559B2 - 電極製造方法、電極、並びに二次電池及びその製造方法 - Google Patents
電極製造方法、電極、並びに二次電池及びその製造方法 Download PDFInfo
- Publication number
- JP6625559B2 JP6625559B2 JP2016566563A JP2016566563A JP6625559B2 JP 6625559 B2 JP6625559 B2 JP 6625559B2 JP 2016566563 A JP2016566563 A JP 2016566563A JP 2016566563 A JP2016566563 A JP 2016566563A JP 6625559 B2 JP6625559 B2 JP 6625559B2
- Authority
- JP
- Japan
- Prior art keywords
- insulating layer
- electrode
- active material
- electrode active
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本願は、2014年12月26日に、日本に出願された特願2014−266525号に基づき優先権を主張し、その内容をここに援用する。
ここで、前記表面粗さRzはJIS B0601 1994に準拠した測定法で測定される十点平均粗さである。
(2)前記電極活物質層の上に前記絶縁層を積層する工程は、前記電極活物質層の上に絶縁材を含む組成物を塗工して前記絶縁層を積層することを含む工程であって、前記組成物を、形成される前記絶縁層の厚さが前記電極活物質層の表面粗さRzの2倍以上となる厚さで塗工する工程である、前記(1)に記載の電極製造方法。
(3)前記表面粗さRzが35μm以下である、前記(1)に記載の電極製造方法。
(4)前記組成物を、形成される前記絶縁層の厚さが2μm〜35μmとなる厚さで塗工する、前記(2)又は(3)に記載の電極製造方法。
(5)ブレードコーティング法によって前記組成物を塗工する、前記(2)〜(4)の何れか一項に記載の電極製造方法。
(6)電極活物質層の上に絶縁層が積層された積層体を有する電極であり、前記絶縁層の厚さtと、前記電極活物質層の表面粗さRzとの比(t/Rz)が、2以上である電極。
ここで、前記表面粗さRzはJIS B0601 1994に準拠した測定法で測定される十点平均粗さである。
(7)前記絶縁層が形成された前記電極活物質層の表面粗さRzが35μm以下である、前記(6)に記載の電極。
(8)前記絶縁層の厚さが2μm〜35μmである、前記(6)又は(7)に記載の電極。
(9)正極と負極とその間に絶縁層が積層された積層体を有する二次電池の製造方法であって、正極又は負極の何れか一方の電極活物質層の上に前記絶縁層を積層する工程を含み、前記絶縁層の厚さが前記電極活物質層の表面粗さRzの2倍以上となる厚さである、二次電池の製造方法。
ここで、前記表面粗さRzはJIS B0601 1994に準拠した測定法で測定される十点平均粗さである。
(10)前記表面粗さRzが35μm以下である、前記(9)に記載の二次電池の製造方法。
(11)前記絶縁層の厚さが2μm〜35μmである、前記(9)又は(10)に記載の二次電池の製造方法。
(12)正極、負極及び前記正極と負極との間に配置された電解質層を備える二次電池であって、前記正極及び負極の少なくとも一方の電極が、他方の電極に対向する面に設けられた電極活物質層の上に絶縁層が積層された積層構造を有し、前記絶縁層を有する電極は、前記絶縁層の厚さtと、前記電極活物質層の表面粗さRzとの比(t/Rz)が、2以上であることを特徴とする、二次電池。
(13)前記電極活物質層の表面粗さRzが35μm以下である、前記(12)に記載の二次電池。
(14)前記絶縁層の厚さが2μm〜35μmである、前記(12)又は(13)に記載の二次電池。
(15)前記電極活物質層の表面粗さRzが17.5μm以下であり、前記絶縁層の厚さが2μm〜35μmである、前記(12)に記載の二次電池。
(16)前記正極と前記負極との間に樹脂製多孔質セパレータを備える、前記(12)〜(15)の何れか1項に記載の二次電池。
本発明の電極を例えばリチウムイオン二次電池等の二次電池の電極として使用した場合、リチウムデンドライトが正極と負極間に発生したとしても、電極表面の絶縁層の構造的強度は平面方向において均一であり、デンドライトが絶縁層を貫通し易い箇所(例えば、応力集中が起こる箇所)が局在しないため、二次電池の耐久性及び安全性を向上させることができる。
本発明の第一態様の電極の製造方法は、電極活物質層の上に絶縁層が積層された積層体を有する電極の製造方法である。前記絶縁層は、二次電池、キャパシタ等の電気化学デバイスにおける正極と負極を絶縁するセパレータとして機能し得る。
前記電極活物質層の上に前記絶縁層を積層する工程は、例えば、前記電極活物質層の上に絶縁材を含む組成物を塗工して前記絶縁層を積層することによって行うことができる。この際、前記組成物を、形成される前記絶縁層の厚さが前記電極活物質層の表面粗さRzの2倍以上となる厚さで塗工する。
上記の厚さで組成物を塗工することは、すなわち、電極活物質層の表面粗さRz(単位:μm)と、塗工後であって乾燥工程前の組成物の厚さt(単位:μm)との比(t/Rz)が、2よりも大きいことを意味する。
塗工面の表面粗さRzが35μm以下であると、形成する絶縁層を薄くした場合、すなわち塗工する前記組成物の厚さを薄くした場合、における塗工面の表面粗さRzの影響を少なくして、絶縁層の厚さ及び密度を平面方向に亘って充分均一にすることができる。さらに、形成される絶縁層の表面粗さを小さくすることもできる。
形成された前記絶縁層の厚さが、電極活物質層の表面粗さRzの2.0倍以上の厚さになるように前記組成物を塗工することにより、絶縁層の平面方向において厚さの均一性を向上することが可能となる。電極活物質層の表面粗さRzの30倍以下の厚さになるように前記組成物を塗工することにより、絶縁層に由来する電気抵抗が大きくなり過ぎることを防止できる。
一方、1回のみの塗工で、上記のような多孔状態の違いを絶縁層内に積極的に生じさせてもよい。その他、固形分濃度、粘度、組成の異なる組成物を複数回に分けて多段的に積層することによって、厚さ方向に見て、多孔状態が多段的に変化する絶縁層を形成することもできる。
前記電極活物質層の上に塗工する前記組成物は、少なくとも絶縁材を含む。前記組成物は、前記絶縁材としての絶縁性微粒子及び樹脂材料(バインダー)を含むことが好ましい。
前記組成物は、必要に応じて、絶縁材を溶解又は分散させるための溶媒を含んでいてもよい。溶媒を適当な量で含むことにより、組成物の密度ρ、動粘性係数ν、表面張力σ等が所望となるように調整することができる。
前記組成物を均一に薄く塗工する観点から、前記組成物は適度な粘性を有するスラリー状(ペースト状)であることが好ましい。
前記絶縁性微粒子を構成する材料に、無機化合物を含む場合は、本発明の電極が電池に組み込まれた場合に、リチウムイオンが挿入されにくいような無機化合物を用いることが好ましい。換言すれば、リチウムイオンが絶縁層を透過することを妨げないような無機化合物を使用することが好ましい。
前記絶縁性微粒子を構成する材料に、有機化合物を含む場合は、有機化合物の融点あるいは軟化温度は、150℃以上であることが好ましい。より好ましくは180℃以上、さらに好ましくは200℃以上である。有機化合物が上記のような融点あるいは軟化温度を有することにより、本発明の電極が、電池に組み込まれ、電池に過度な発熱が生じた際に、電極間の短絡を抑止する事が可能となる。
本発明の電極が、電池に組み込まれる場合は、一方の電極上に設けられた当該絶縁層と、絶縁層が形成されていない他の電極との間に、樹脂製多孔質セパレータを設けることが好ましい。
樹脂製多孔質セパレータは、電池に過度な発熱が生じた際に、前記樹脂製多孔質セパレータの孔が溶融して閉孔し、電池反応を停止させる機能を持つ。そのため、前記絶縁性微粒子を構成する材料に、無機化合物を含む場合は、樹脂製多孔質セパレータを備えることが好ましい。
前記絶縁性微粒子を構成する材料に、有機化合物が含まれる場合は、有機化合物の融点あるいは軟化温度は、前記樹脂製多孔質セパレータの融点より高いことが好ましい。これにより、電池に過度な発熱が生じた際に、電極間の短絡を抑止しつつ、前記樹脂製多孔質セパレータの孔が溶融して閉孔し、電池反応を停止させる機能を発現することが可能となる。有機化合物の融点あるいは軟化温度は、前記樹脂製多孔質セパレータの融点より20℃以上がより好ましく、さらに好ましくは40℃以上である。
積層時等の加圧時に、絶縁層が薄くなることを防止するために、絶縁層の厚みを100%としたときに、80%〜100%の範囲の平均粒子径を持つ絶縁性微粒子を、全絶縁性微粒子に対し5体積%以上含有することが好ましい。より好ましくは10体積%以上、さらに好ましくは20体積%以上である。
前記合成樹脂は1種単独で使用されてもよいし、2種以上が併用されてもよい。
前記の絶縁膜を別途形成する方法としては、例えば、離型シート等の基台上に、前記の組成物を用いて、前記と同様の方法で絶縁層(絶縁膜)を形成する方法が挙げられる。このようにして形成された絶縁膜を離型シート等の基台から剥離し、前記電極活物質層の上に前記絶縁層を積層することができる。あるいは基台と絶縁膜とを、絶縁膜が電極活物質層側になるように積層し、その後、基台を剥離することができる。積層の際には、表面が平滑な平板ないしロールで加圧してもよい。
前記組成物を塗工する前記電極活物質層の形成方法及び材料は特に限定されず、従来の二次電池の正極又は負極を構成する電極活物質層の形成方法及び材料が適用可能である。例えば、集電材としてのアルミニウム箔又は銅箔の上に、後述する正極活物質又は負極活物質を含むスラリーを塗布して乾燥することによって形成することができる。
本発明の第二態様の電極は、第一態様の方法によって製造された電極であることが好ましい。本発明に係る電極の第一実施形態は、電極活物質層の上に絶縁層が積層された積層体を有する電極である。
前記絶縁層は、二次電池、キャパシタ等の電気化学デバイスにおける正極と負極を絶縁するセパレータとして機能し得る。前記電極活物質層は、集電体の上に形成されていることが好ましい。前記電極活物質は、正極活物質であってもよいし、負極活物質であってもよい。
上記範囲の表面粗さRzであると、構造的強度の信頼性がより一層高くなる。
前記透気度は、JIS P 8117に基づくガーレー試験機法によって求められる。
本発明の第二態様の電極は、種々の電気化学デバイスの電極として使用することができる。例えば、一次電池、充放電することが可能な二次電池、電気二重層キャパシタが好適な電気化学デバイスとして挙げられる。
以下では、本発明の第二態様の電極を、正極及び負極のうち少なくとも一方の電極として備えた電気化学デバイスの一例として、リチウムイオン二次電池の構成を例示する。
本発明の第二態様の電極をリチウムイオン二次電池の負極として使用する場合、以下の材料を使用して、前述した本発明の第一態様の電極製造方法によって、当該負極を製造することができる。
前記導電助剤としては、例えばグラファイト、グラフェン、ハードカーボン、ケッチェンブラック、アセチレンブラック、カーボンナノチューブ等の炭素材料が挙げられる。
前記バインダー樹脂として、例えば、ポリアクリル酸、ポリアクリル酸リチウム、ポリフッ化ビニリデン、ポリフッ化ビニリデン−ヘキサフルオロプロピレン共重合体、スチレンブタジエンゴム、ポリビニルアルコール、ポリビニルアセタール、ポリエチレンオキサイド、ポリエチレングリコール、カルボキシメチルセルロース、ポリアクリルニトリル、ポリイミド等が挙げられる。
前記集電体を構成する材料としては、例えば、銅、アルミニウム、チタン、ニッケル、ステンレス鋼等の導電性を有する金属が挙げられる。
前記負極活物質、導電助剤、バインダー樹脂及び溶媒は、何れも一種が単独で使用されてもよいし、二種以上が併用されてもよい。
本発明の第二態様の電極をリチウムイオン二次電池の正極として使用する場合、以下の材料を使用して、前述した本発明の第一態様の電極製造方法によって、当該正極を製造することができる。
前記電解質は特に限定されず、例えば、公知のリチウムイオン二次電池で使用される公知の電解質、電解液等が適用可能である。電解液としては、電解質を固体状で用いたり、有機溶媒に電解質塩を溶解したりした混合溶液が例示できる。有機溶媒としては、高電圧に対する耐性を有するものが好ましく、例えば、エチレンカーボネート、プロピレンカーボネート、ジメチルカーボネート、γ−ブチロラクトン、スルホラン、ジメチルスルホキシド、アセトニトリル、ジメチルホルムアミド、ジメチルアセトアミド、1,2−ジメトキシエタン、1,2−ジエトキシエタン、テトロヒドラフラン、2−メチルテトラヒドロフラン、ジオキソラン、メチルアセテートなどの極性溶媒、又はこれら溶媒の2種類以上の混合物が挙げられる。電解質塩としては、例えばリチウムイオン二次電池の場合、LiClO4、LiPF6、LiBF4、LiAsF6、LiCF6、LiCF3CO2、LiPF6SO3、LiN(SO3CF3)2、Li(SO2CF2CF3)2、LiN(COCF3)2及びLiN(COCF2CF3)2、リチウムビスオキサレートボラート(LiB(C2O4)2等のリチウムを含む塩が挙げられる。また、有機酸リチウム塩−三フッ化ホウ素錯体、LiBH4等の錯体水素化物等の錯体が挙げられる。これらの塩又は錯体は、2種以上の混合物であってもよい。
電解質が溶媒を含む場合は、更に高分子化合物を含むゲル状電解質とされてもよい。前記高分子化合物としては、例えば、ポリフッ化ビニリデン等のフッ素系ポリマー、ポリ(メタ)アクリル酸メチル等のポリアクリル系ポリマーが挙げられる。
黒鉛80質量部と、ハードカーボン15質量部と、ポリフッ化ビニリデン5質量部とを混合して、得られた混合物をN−メチルピロリドン中に分散させて、負極材スラリーを調製した。
各試験例における負極活物質層の表面粗さRzは、ロールプレスの加圧条件を適宜調整すること、及び、下記の様に材料を選定することによって、0.8μm〜40.7μmの範囲で調整した。
負極活物質の表面粗さRzが16.2μm〜28.1μmの範囲の試験例においては、表面粗さRzが6μmの銅箔を用い、平均粒子径が1.5μmの黒鉛と、平均粒子径が4μmのハードカーボンを用いた。
負極活物質の表面粗さRzが35.4μm〜40.7μmの範囲の試験例においては、表面粗さRzが10μmの銅箔を用い、平均粒子径が3μmの黒鉛と、平均粒子径が8μmのハードカーボンを用いた。
エチレングリコール1質量部、エタノール20質量部、2−プロパノール20質量部及びトルエン50質量部を含む混合溶剤を調製した。この混合溶剤に、ポリビニルアルコール(平均重合度1700、ケン化度98モル%)をn−ブチルアルデヒドを用いてアセタール化したポリビニルブチラール樹脂(ブチラール化度は38モル%)20質量部と、スチレンブタジエン共重合体(SBR)5質量部とを加え、さらに直径2mmのセラミックボールを100ml加え、ボールミル(セイワ技研工業社製 BM−10)を用い、回転数100rpmで1時間撹拌した。
その後、さらにアルミナ粒子(TM−5D 大明化学工業社製社製、平均粒子径0.2μm)75質量部を加えて、前記ボールミルを用いて、回転数300rpmで2時間撹拌することにより、無機粒子の分散液(以下、無機分散液)を作製した。
<負極の製造>
上記で作製した各負極基材を用いて、下記表に記載の表面粗さRzを有する負極活物質層の上に、上記スラリー組成物を適切な厚さで塗工して、さらに乾燥することにより、厚さtの絶縁層が積層されてなる負極を作製した。
作製した負極をカットして、負極活物質層の積層部分(104×62mm)と、負極活物質層の非積層部分(タブ部分、2×2cm程度)とを有する負極に成形して使用した。
ニッケル・コバルト・マンガン酸リチウム(Ni:Co:Mn=1:1:1)93質量部と、ポリフッ化ビニリデン3質量部と、導電助剤であるカーボンブラック4質量部とを混合して、得られた混合物をN−メチルピロリドン中に分散させて、正極材スラリーを調製した。
シュウ酸リチウム−三フッ化ホウ素錯体(LOX−BF3)を、エチレンカーボネート(EC)及びジエチルカーボネート(DEC)及びガンマブチロラクトン(GBL)の混合物(EC:DEC:GBL=30:60:10、質量比)に溶解させ、リチウムイオンの濃度が1.0モル/kgである電解液を得た。
各試験例で個別に作製した負極と、各試験例で共通の正極とを、負極の絶縁層が間に挟まれるように重ね合せて配置し、各電極の端子用タブを負極及び正極の外方に突出させ、それぞれのタブを超音波溶接により接合して、各試験例に対応する電極積層体を得た。
<負極の作製>
一酸化ケイ素(SiO、平均粒子径5.0μm、70質量部)、VGCF(登録商標)(5質量部)、SBR(5質量部)、及びポリアクリル酸(10質量部)を試薬瓶に入れ、さらに蒸留水を添加して濃度調整した後、自公転ミキサーを用いて2000rpmで2分間混合した。この混合物にアセチレンブラック(5質量部)、ケッチェンブラック(5質量部)を加え、自公転ミキサーを用いて2000rpmで2分間混合した。この混合物を超音波ホモジナイザーで10分間分散処理した後、再度、自公転ミキサーを用いてこの分散物を2000rpmで3分間混合することにより、負極材スラリーを得た。
上記のVGCF(登録商標)(正式名称:vapor grown carbon fiber)は、昭和電工社製の気相法炭素繊維である。その平均のアスペクト比(B)は400であり、その平均の直径(外径)は12.5nmであり、その平均の長さは5μmである。
続いて、上記負極活物質層上に後述する電解液50μL/cm2を滴下し、その滴下面上に厚さ200μmのリチウム箔を重ねて、この状態で48時間静置することにより、負極前駆体にリチウムをプレドープし、負極を得た。プレドープ後にリチウム箔を負極から取り除いた。
ニッケル・コバルト・マンガン酸リチウム(Ni:Co:Mn=1:1:1)93質量部と、ポリフッ化ビニリデン3質量部と、導電助剤であるカーボンブラック4質量部とを混合して、得られた混合物をN−メチルピロリドン中に分散させて、正極材スラリーを調製した。
ジメチルホルムアミド(DMF)100質量部とポリフッ化ビニリデン樹脂15質量部と直径2mmのセラミックボールを100ml加え、ボールミル(セイワ技研工業社製 BM−10)を用い、回転数100rpmで1時間撹拌した。
その後、さらにアルミナ粒子(TM−5D 大明化学工業社製社製、平均粒子径0.2μm)8質量部を加えて、前記ボールミルを用いて、回転数300rpmで2時間撹拌することにより、無機粒子の分散液(以下、無機分散液)を作製し、前記セラミックボール(直径2mm)を除去し、スラリー組成物を得た。ここまでの操作は、25℃で行った。
上記正極の正極活物質層の上に、上記スラリー組成物を適切な厚さで塗工して、さらに95℃、−0.1MPa、10時間の条件で減圧乾燥させた後、厚さ10μmの絶縁層が積層されてなる正極を作製した。
作製した正極をカットして、正極活物質層の積層部分(104×62mm)と、正極活物質層の非積層部分(タブ部分、2×2cm程度)とを有する正極に成形して使用した。
シュウ酸リチウム−三フッ化ホウ素錯体(LOX−BF3)10重量部と、エチレンカーボネート(EC)10重量部と、ジエチルカーボネート(DEC)10重量部とを混合し溶解させ、組成物を調整した。
エチレンカーボネート(EC)30重量部と、ジエチルカーボネート(DEC)30重量部とポリフッ化ビニリデン樹脂10重量部とを混合し溶解させ、前記組成物に加えて混合し、ゲル状電解質を得た。
各電極の端子用タブを負極及び正極の外方に突出させ、それぞれのタブを超音波溶接により接合した。
前記負極に、前記ゲル電解質を25μmの厚さで塗工し、前記正極を、前記ゲル電解質と前記正極の絶縁層とが接するように重ね合せて配置し、電極積層体を得た。
実施例1等と同様に評価を実施した。結果を、表3に示す。
各試験例に対応するリチウムイオン二次電池について、25℃において0.2C(印加電流値/電池の定格容量)の定電流定電圧充電を、上限電圧4.2Vとして電流値が0.1Cに収束するまで行った後、0.2Cの定電流放電を2.7Vまで行った。この時の放電容量を初期値(100%)とした。その後、1Cでの充放電サイクルを繰り返し行い、50サイクルでの放電容量を求め、容量維持率([50サイクル目の放電容量(mAh)]/[1サイクル目の放電容量(mAh)])×100(%)を算出した。その結果を表1〜表3に併記する。
なお、t/Rzが8以下である実施例1〜4、実施例7〜10、実施例12〜13、実施例16〜18、実施例21〜31は、比較例である。
Claims (12)
- 電極活物質層の上に絶縁層が積層された積層体を有する電極の製造方法であって、
基台上に形成された前記電極活物質層の上に前記絶縁層を積層する工程を含み、
前記絶縁層が形成された前記電極活物質層の表面粗さRzが35μm以下であり、
前記絶縁層を、その厚さが前記電極活物質層の表面粗さRzの8倍よりも大きくなるように積層する、電極製造方法。
ここで、前記表面粗さRzはJIS B0601 1994に準拠した測定法で測定される十点平均粗さである。 - 前記電極活物質層の上に前記絶縁層を積層する工程は、
前記電極活物質層の上に絶縁材を含む組成物を塗工して前記絶縁層を積層することを含む工程であって、
前記組成物を、形成される前記絶縁層の厚さが前記電極活物質層の表面粗さRzの8倍よりも大きくなる厚さで塗工する工程である、請求項1に記載の電極製造方法。 - 前記絶縁層の厚さが2μm〜35μmとする、請求項1又は2に記載の電極製造方法。
- ブレードコーティング法によって前記組成物を塗工する、請求項2に記載の電極製造方法。
- 電極活物質層の上に絶縁層が積層された積層体を有する電極であり、
前記絶縁層が形成された前記電極活物質層の表面粗さRzが35μm以下であり、
前記絶縁層の厚さtと、前記電極活物質層の表面粗さRzとの比(t/Rz)が、8よりも大きい電極。
ここで、前記表面粗さRzはJIS B0601 1994に準拠した測定法で測定される十点平均粗さである。 - 前記絶縁層の厚さが2μm〜35μmである、請求項5に記載の電極。
- 正極と負極とその間に絶縁層が積層された積層体を有する二次電池の製造方法であって、
正極又は負極の何れか一方の電極活物質層の上に前記絶縁層を積層する工程を含み、
前記絶縁層が形成された前記電極活物質層の表面粗さRzが35μm以下であり、
前記絶縁層の厚さが前記電極活物質層の表面粗さRzの8倍よりも大きくなる厚さである、二次電池の製造方法。
ここで、前記表面粗さRzはJIS B0601 1994に準拠した測定法で測定される十点平均粗さである。 - 前記絶縁層の厚さが2μm〜35μmである、請求項7に記載の二次電池の製造方法。
- 正極、負極及び前記正極と負極との間に配置された電解質層を備える二次電池であって、前記正極及び負極の少なくとも一方の電極が、他方の電極に対向する面に設けられた電極活物質層の上に絶縁層が積層された積層構造を有し、
前記絶縁層が形成された前記電極活物質層の表面粗さRzが35μm以下であり、
前記絶縁層を有する電極は、前記絶縁層の厚さtと、前記電極活物質層の表面粗さRzとの比(t/Rz)が、8よりも大きいことを特徴とする、二次電池。 - 前記絶縁層の厚さが2μm〜35μmである、請求項9に記載の二次電池。
- 前記電極活物質層の表面粗さRzが17.5μm以下であり、前記絶縁層の厚さが2μm〜35μmである、請求項9に記載の二次電池。
- 前記正極と前記負極との間に樹脂製多孔質セパレータを備える、請求項9〜11の何れか1項に記載の二次電池。