JP6304236B2 - 電気化学素子電極用複合粒子の製造方法 - Google Patents
電気化学素子電極用複合粒子の製造方法 Download PDFInfo
- Publication number
- JP6304236B2 JP6304236B2 JP2015505451A JP2015505451A JP6304236B2 JP 6304236 B2 JP6304236 B2 JP 6304236B2 JP 2015505451 A JP2015505451 A JP 2015505451A JP 2015505451 A JP2015505451 A JP 2015505451A JP 6304236 B2 JP6304236 B2 JP 6304236B2
- Authority
- JP
- Japan
- Prior art keywords
- particles
- composite particles
- electrode
- positive electrode
- slurry composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
電気化学素子用電極は、電極活物質、結着剤、導電材等を含むスラリー組成物を集電体上に塗布し、溶剤を熱などにより除去する方法で製造されていたが、結着剤などのマイグレーションにより、均一な電気化学素子の製造が困難であった。また、この方法はコスト高で作業環境が悪くなり、製造装置が大きくなる課題があった。
本発明の目的は、造粒粒子から金属異物を除去することができる電気化学素子電極用複合粒子の製造方法を提供することである。
(1) 電極活物質及び粒子状結着剤を含む水系スラリー組成物を得るスラリー製造工程と、前記水系スラリー組成物を噴霧機に移送する移送工程と、前記噴霧機を用いて噴霧、乾燥することにより造粒粒子を得る造粒工程と、前記造粒粒子から粗大粒子を分離する分離工程とを含む電気化学素子電極用複合粒子の製造方法であって、前記造粒工程により得られた前記造粒粒子から磁気により金属異物を除去する第1除去工程および/または前記分離工程より前記粗大粒子が除去された前記造粒粒子から磁気により金属異物を除去する第2除去工程を含むことを特徴とする電気化学素子電極用複合粒子の製造方法、
(2) 前記分離工程は、メッシュにより前記造粒粒子から前記粗大粒子を分離することを特徴とする(1)記載の電気化学素子電極用複合粒子の製造方法、
(3) 前記電気化学素子電極用複合粒子の体積平均粒子径は10〜150μmであって、前記メッシュの開口径は前記電気化学素子電極用複合粒子の体積平均粒子径の1.1〜6.0倍であることを特徴とする(2)記載の電気化学素子電極用複合粒子の製造方法、
(4) 前記メッシュは、金属製メッシュであることを特徴とする(2)または(3)記載の電気化学素子電極用複合粒子の製造方法、
(5) 前記金属製メッシュは、磁気による金属除去機能を有することを特徴とする(4)記載の電気化学素子電極用複合粒子の製造方法、
(6) 前記移送工程は、磁性を有する材料または磁化され得る材料の少なくとも一方を含む配管を用いて前記水系スラリー組成物を移送することを特徴とする(1)〜(5)の何れかに記載の電気化学素子電極用複合粒子の製造方法、
(7) 前記スラリー製造工程および/または前記移送工程は、さらに前記水系スラリー組成物から磁気により金属異物を除去する工程を含むことを特徴とする(1)〜(6)の何れかに記載の電気化学素子電極用複合粒子の製造方法、
が提供される。
本発明のスラリー製造工程(S1)においては、電極活物質及び粒子状結着剤を含む水系スラリー組成物が製造される。また、スラリー製造工程(S1)において得られる水系スラリー組成物は、後述する増粘剤を含有するのが好ましく、必要に応じて導電材および添加剤等のその他の成分を含んでもよい。
本発明で用いる電極活物質は、製造される電気化学素子用電極の種類によって適宜選択される。たとえば、製造される電気化学用素子用電極が、リチウムイオン二次電池用の正極である場合、正極活物質としては、リチウムイオンを可逆的にドープ・脱ドープ可能な金属酸化物が挙げられる。かかる金属酸化物としては、例えば、コバルト酸リチウム、ニッケル酸リチウム、マンガン酸リチウム、燐酸鉄リチウム、燐酸マンガンリチウム、燐酸バナジウムリチウム、バナジン酸鉄リチウム、ニッケル−マンガン−コバルト酸リチウム、ニッケル−コバルト酸リチウム、ニッケル− マンガン酸リチウム、鉄−マンガン酸リチウム、鉄−マンガン−コバルト酸リチウム、珪酸鉄リチウム、珪酸鉄− マンガンリチウム、酸化バナジウム、バナジン酸銅、酸化ニオブ、硫化チタン、酸化モリブデン、硫化モリブデン、等を挙げることができる。なお、上記にて例示した正極活物質は適宜用途に応じて単独で使用してもよく、複数種混合して使用してもよい。さらに、ポリアセチレン、ポリ−p−フェニレン、ポリキノンなどのポリマーが挙げられる。これらのうち、リチウム含有金属酸化物を用いることが好ましい。
本発明で用いる粒子状結着剤としては、上述した電極活物質を相互に結着させることができる化合物であれば特に制限はないが、本発明においては、溶媒に分散する性質を有する分散型の粒子状結着剤が好ましい。分散型の粒子状結着剤としては、たとえば、シリコン系重合体、フッ素含有重合体、共役ジエン系重合体、アクリレート系重合体、ポリイミド、ポリアミド、ポリウレタン等の高分子化合物が挙げられ、これらのなかでもフッ素系含有重合体、共役ジエン系重合体及びアクリレート系重合体が好ましく、共役ジエン系重合体及びアクリレート系重合体がより好ましい。
水系スラリー組成物には、電極活物質及び粒子状結着剤に加えて、増粘剤を含有するのが好ましい。増粘剤は、電極用複合粒子を構成する各成分を、溶媒に分散又は溶解させて水系スラリー組成物とする際に、各成分を溶媒中に均一に分散させる作用を有する成分である。増粘剤の具体例としては、カルボキシメチルセルロース、メチルセルロース、エチルセルロース及びヒドロキシプロピルセルロースなどのセルロース系ポリマー、ならびにこれらのアンモニウム塩又はアルカリ金属塩、アルギン酸プロピレングリコールエステルなどのアルギン酸エステル、ならびにアルギン酸ナトリウムなどのアルギン酸塩、ポリアクリル酸、及びポリアクリル酸(又はメタクリル酸)ナトリウムなどのポリアクリル酸(又はメタクリル酸)塩、ポリビニルアルコール、変性ポリビニルアルコール、ポリエチレンオキシド、ポリビニルピロリドン、ポリカルボン酸、酸化スターチ、リン酸スターチ、カゼイン、各種変性デンプン、キチン、キトサン誘導体などが挙げられる。これらの分散剤は、それぞれ単独で又は2種以上を組み合わせて使用できる。中でも、セルロース系ポリマーが好ましく、カルボキシメチルセルロース又はそのアンモニウム塩もしくはアルカリ金属塩が特に好ましい。本発明において、「(変性)ポリ」は「未変性ポリ」又は「変性ポリ」を意味し、「(メタ)アクリル」は、「アクリル」又は「メタアクリル」を意味する。
また、水系スラリー組成物には、電極活物質、粒子状結着剤及び増粘剤に加えて、必要に応じて、導電材、界面活性剤等を含有させてもよい。
導電材としては、導電性を有する粒子状の材料であればよく、導電材の具体例としては、ファーネスブラック、アセチレンブラック、及びケッチェンブラック(アクゾノーベル ケミカルズ ベスローテン フェンノートシャップ社の登録商標)などの導電性カーボンブラックが挙げられる。これらの中でも、アセチレンブラックおよびケッチェンブラックが好ましい。導電材の平均粒子径は、特に限定されないが、より少ない使用量で十分な導電性を発現させる観点から、電極活物質の平均粒子径よりも小さいものが好ましく、好ましくは0.001〜10μm、より好ましくは0.05〜5μm、さらに好ましくは0.01〜1μmである。
界面活性剤としては、アニオン性、カチオン性、ノニオン性、ノニオニックアニオン等の両性の界面活性剤が挙げられるが、アニオン性又はノニオン性界面活性剤で熱分解しやすいものが好ましい。界面活性剤の配合量は、電極活物質100重量部に対して、好ましくは50重量部以下であり、より好ましくは0.1〜10重量部、さらに好ましくは0.5〜5重量部である。
本発明に用いる水系スラリー組成物は、水を溶媒として用いたスラリーであり、上述の電極活物質、粒子状結着剤、増粘剤及び導電材等の必要に応じて用いられるその他の成分を水中で混合することにより得ることができる。なお、粒子状結着剤が溶媒としての水に分散された水分散体として得られる場合には、粒子状結着剤を水に分散させた状態で添加することができる。
電極活物質、粒子状結着剤、増粘剤及び導電材等の必要に応じて用いられるその他の成分を溶媒中に混合する方法、順序は、特に限定されない。
本発明の移送工程(S2)では、混合装置等において得られた上記水系スラリー組成物を後述するスプレーやアトマイザー等の噴霧機に移送する。
本発明の造粒工程(S3)では、スプレー、アトマイザー等の噴霧機を用いて上記水系
スラリー組成物を噴霧、乾燥することにより造粒粒子を得る。
本発明の第1除去工程(S4)においては、上述のように得られた造粒粒子から磁気により金属異物を除去する。なお、第1除去工程(S4)は、造粒粒子から粗大粒子を分離する分離工程(S5)を行う前に行われる。
本発明の分離工程(S5)においては、造粒粒子から粗大粒子を分離する。造粒粒子から粗大粒子を分離する方法としては、特に限定されないが、メッシュにより粗大粒子を分離する方法が好ましい。
金属製メッシュとしては、通常ステンレス製メッシュが用いられ、タンタル製メッシュ、モリブデン製メッシュを用いてもよい。また、ステンレス製メッシュの中でも、造粒粒子との接触による摩耗により削られたり、破損したりすることにより、複合粒子中に混入した場合でも後述する磁気フィルタにより除去が可能である観点から、磁気フィルタによって磁化され得る材料が好ましく、経済的であり、磁気フィルタによる磁化のされやすさの観点から、SUS304が最も好ましい。
磁性材料製メッシュとしては、磁性を帯びているメッシュであれば特に制限はないが、磁性材料製メッシュに用いられる磁性材料としては、SUS430、SUS440C、SUS420J2、SUS410S、磁性ステンレス鋼ダーマロイ、マグネステン等が挙げられる。
本発明の第2除去工程(S6)においては、上述のように分離工程(S5)により粗大粒子が分離された造粒粒子から磁気により金属異物を除去する。造粒粒子から磁気により金属異物を除去する方法としては、特に制限はないが、上記第1除去工程(S4)に用いることができる方法と同様の方法を用いることができる。
本発明の上記スラリー製造工程(S1)および/または上記移送工程(S2)において、水系スラリー組成物から磁気により金属異物を除去してもよい。水系スラリー組成物から金属異物を除去する方法としては、特に制限はないが、たとえば磁気フィルタを用いて金属異物を除去することができる。即ち、磁性異物が含有されている水系スラリー組成物が磁気フィルタを通過する際に、磁気フィルタの作用により磁性異物が除去される。
磁気フィルタとしては、上記第1除去工程(S4)に用いることができる磁気フィルタと同様の磁気フィルタを用いることができる。
磁性を有する材料あるいは磁気フィルタによって磁化され得る材料で構成するのが好ましい前記部分を含む装置等としては、例えば、スラリー製造工程(S1)における水系スラリーの混合装置として例示した前記各混合装置、造粒工程(S3)における水系スラリーの噴霧に用いる噴霧機として例示した前記各噴霧機、分離工程(S5)におけるメッシュ等を組み込んだ分離装置及び除去工程(S4、S6)における、磁気フィルタを組み込んだ除去装置などが挙げられる。これらの装置等の中でも特に、水系スラリーや造粒粒子等が接触する内壁部分が磁性を有する材料あるいは磁気フィルタによって磁化され得る材料で構成されているのが好ましい。
本発明に係る複合粒子は、少なくとも上記造粒工程(S3)、上記分離工程(S5)及び上記第1除去工程(S4)および/または上記第2除去工程(S5)を行うことにより得られる。
本発明の複合粒子を用いた電気化学素子電極(以下、単に「電極」ということがある。)は、複合粒子を含む電極活物質層を集電体上に積層してなる。電極に使用される集電体用材料としては、例えば、金属、炭素、導電性高分子などが挙げられ、好適な材料としては金属が挙げられる。集電体用金属としては、通常、アルミニウム、白金、ニッケル、タンタル、チタン、ステンレス鋼、その他の合金等が挙げられる。これらの中で導電性、耐電圧性の面からアルミニウムまたはアルミニウム合金が好ましい。また、高い耐電圧性が要求される場合には特開2001−176757号公報等で開示されるような高純度のアルミニウムを好適に用いることができる。集電体は、フィルムまたはシート状であり、その厚みは、使用目的に応じて適宜選択されるが、好ましくは1〜200μm、より好ましくは5〜100μm、さらに好ましくは10〜50μmである。
上記電気化学素子用電極を用いて電気化学素子を得ることができる。電気化学素子としては、鉛蓄電池、アルカリ電池、リチウムイオン二次電池、電気二重層キャパシタやリチウムイオンキャパシタ等の蓄電デバイスが挙げられ、エネルギー密度と出力密度に優れるリチウムイオン二次電池、電気二重層キャパシタやリチウムイオンキャパシタが好ましい。
電気化学素子用電極以外の他の構成要素としては、セパレータおよび電解液が挙げられる。
セパレータは、電気化学素子用電極の間を絶縁でき、陽イオンおよび陰イオンを通過させることができるものであれば特に限定されない。具体的には、ポリエチレンやポリプロピレンなどのポリオレフィンや芳香族ポリアミド、レーヨンもしくはガラス繊維製の微孔膜または不織布;一般に電解コンデンサ紙と呼ばれるパルプを主原料とする多孔質膜;無機セラミック粉末を含む多孔質の樹脂コートなどを用いることができる。セパレータは、上記一対の電極活物質層が対向するように、電気化学素子用電極の間に配置され、素子が得られる。セパレータの厚みは、使用目的に応じて適宜選択されるが、好ましくは1〜100μm、より好ましくは10〜80μm、さらに好ましくは20〜60μmである。
電解液には、電解液溶媒に電解質が溶解されている。リチウムイオン二次電池、およびリチウムイオンキャパシタの場合には、電解液溶媒には、例えば、非プロトン性極性溶媒を使用することができる。かかる非プロトン性極性溶媒は、非プロトン性有機電解質溶液を形成する。非プロトン性極性溶媒としては、例えば、エチレンカーボネート、プロピレンカーボネート、ジメチルカーボネート、ジエチルカーボネート、エチルメチルカーボネート、γ -ブチロラクトン、アセトニトリル、ジメトキシエタン、テトラヒドロフラン、ジオキソラン、塩化メチレン、ジメチルサルフェート、スルホラン等が挙げられる。さらに、これら非プロトン性極性溶媒の二種以上を混合した混合液を用いても構わない。負極の活物質に黒鉛を用いる場合にはエチレンカーボネートを含むことが好ましい。
実施例および比較例で調製した正極用複合粒子及び負極用複合粒子について酸で煮沸することで溶解し、ICP(Inductively Coupled Plasma)高周波プラズマ発光分析により金属異物含有量として、鉄含有量を測定し、下記の基準により評価した。結果を表1に示した。
A:鉄含有量が30ppm未満
B:鉄含有量が30ppm以上35ppm未満
C:鉄含有量が35ppm以上45ppm未満
D:鉄含有量が45ppm以上55ppm未満
E:鉄含有量が55ppm以上
ラミネート型のリチウムイオン二次電池について25℃で0.1Cの定電流法によって、満充電し、24時間25℃で放置し、電圧低下の割合を測定し、結果を表1に示した。値が小さいほど自己放電特性に優れることを示す。
(カルボキシメチルセルロース水溶液の作製)
カルボキシメチルセルロース(以下、「CMC」ということがある。)として、溶液粘度が8000mPa・sであるCMC(第一工業製薬株式会社製「セロゲンBSH−12」)を用い、CMCの1%水溶液を調整した。
負極活物質として天然黒鉛100部を入れ、これに上記CMC1%水溶液を固形分相当で1.0部加え、イオン交換水で固形分濃度35%に調整した後、25℃で60分ディスパー混合した。次に、粒子状結着剤(BM−400B)を固形分で2部入れ、さらに10分混合して負極用水系スラリー組成物を得た。作製した負極用水系スラリー組成物をエイシン社製高磁力マグ・フィルター(1.7T)に通した。
次に、マグ・フィルターを通した負極用水系スラリー組成物を、スプレー乾燥機(大川原化工機社製)に供給し、回転円盤方式のアトマイザ(直径65mm)を用いて、回転数25,000rpm、熱風温度150℃、粒子回収出口の温度90℃の条件にて、噴霧乾燥造粒を行い、負極用造粒粒子を得た。得られた負極用造粒粒子をエイシン社製格子マグ・フィルターに通した後、磁性メッシュ(開口径125μm)により粗大粒子を除去した。さらにエイシン社製格子マグ・フィルターに通し体積平均粒子径が75μmの負極用複合粒子を得た。ICPにより、得られた負極用複合粒子の鉄の含有量を測定したところ、A判定であった。
上記にて得られた負極用複合粒子を、ロールプレス機(押し切り粗面熱ロール、ヒラノ技研工業社製)のロール(ロール温度100℃、プレス線圧4.0kN/cm)に、集電体としての電解銅箔(厚さ:20μm)とともに供給し、成形速度20m/分で、集電体としての電解銅箔上に、シート状に成形し、厚さ80μmの負極活物質層を有する負極を得た。
ディスパー付プラネタリーミキサーに、LCO(「LiCoO2」の略称)系正極活物質を100部、アセチレンブラック(電気化学工業社製「HS−100」)を4.0部、CMCの1%水溶液(第一工業製薬社製「BSH−12」)を固形分相当で1.0部加え、イオン交換水で全固形分濃度が85%(水分率15%)となるように調製して混合物を得た。得られた混合物を、プラネタリーミキサーを用いて、25℃で60分間混練した。そこに、アクリル系粒子状結着樹脂の40%水分散液を固形分相当で2.0部加え、イオン交換水で全固形分濃度が75%(水分率25%)となるように調製して混合し、正極用スラリー組成物を得た。得られた正極用スラリー組成物の粘度を測定したところ、830mPa・sであった。
上記で得た正極用スラリー組成物を、スプレー乾燥機(大川原化工機社製「OC−16」)に供給し、回転円盤方式のアトマイザー(直径65mm)を用いて回転数25000rpm、熱風温度150℃、粒子回収出口温度90℃の条件にて、噴霧乾燥造粒を行い、正極用造粒粒子を得た。得られた正極用造粒粒子をエイシン社製格子マグ・フィルターに通した後、磁性メッシュ(開口径125μm)により粗大粒子を除去し、さらにエイシン社製格子マグ・フィルターに通し体積平均粒子径は67μmであった。ICPにより、得られた正極用複合粒子の鉄の含有量を測定したところA判定であった。
上記で得られた正極用複合粒子を、定量フィーダ(ニッカ社製「ニッカスプレーK−V」)を用いてロールプレス機(ヒラノ技研工業社製「押し切り粗面熱ロール」)のプレス用ロール(ロール温度100℃、プレス線圧500kN/m)に供給した。プレス用ロール間に、厚さ20μmのアルミニウム箔を挿入し、定量フィーダから供給された上記正極用複合粒子をアルミニウム箔(集電体)上に付着させ、成形速度1.5m/分で加圧成形し、正極活物質層を有する正極を得た。
電池の外装として、アルミ包材外装を用意した。上記で得られた正極を、4.6×4.6cm2の正方形に切り出し、正方形の正極を得た。この正方形の正極を、その集電体側の表面がアルミ包材外装に接するように配置した。正方形の正極の正極活物質層側の面上に、正方形のポリプロピレン製多孔膜からなるセパレータを配置した。
上記で得られたプレス後の負極を、5×5cm2の正方形に切り出し、正方形の負極を得た。この正方形の負極を、上記の正方形のセパレータ上に、負極活物質層側の表面がセパレータに向かい合うよう配置した。電解液(溶媒:EC/DEC/VC=68.5/30/1.5体積比(25℃)、電解質:濃度1MのLiPF6)を空気が残らないように注入し、さらに、150℃のヒートシールをしてアルミ外装を閉口し、アルミ包材の開口を密封した。これにより、リチウムイオン二次電池を製造した。得られたリチウムイオン二次電池について、得られたリチウムイオン二次電池の自己放電特性を測定したところ0.10%であった。
負極用複合粒子の製造において、噴霧乾燥造粒により得られた負極用造粒粒子をエイシン社製格子マグ・フィルターに通した後、磁性メッシュにより粗大粒子を除去した。その後エイシン社製格子マグ・フィルターに通さずに体積平均粒子径73μmの負極用複合粒子を得た以外は、実施例1と同様に負極用複合粒子の製造及び負極の製造を行った。
上述のようにして得られた負極および正極を用いて実施例1と同様にリチウムイオン二次電池の製造を行った。
負極用複合粒子の製造において、噴霧乾燥造粒により得られた負極用造粒粒子をエイシン社製格子マグ・フィルターに通さずに、磁性メッシュにより粗大粒子を除去した。その後エイシン社製格子マグ・フィルターに通して体積平均粒子径77μmの負極用複合粒子を得た以外は、実施例1と同様に負極用複合粒子の製造及び負極の製造を行った。
上述のようにして得られた負極および正極を用いて実施例1と同様にリチウムイオン二次電池の製造を行った。
負極用複合粒子の製造において、噴霧乾燥造粒により得られた負極用造粒粒子をエイシン社製格子マグ・フィルターに通した後、磁性を有しないメッシュ(開口径125μm)により粗大粒子を除去した。その後エイシン社製格子マグ・フィルターに通して体積平均粒子径75μmの負極用複合粒子を得た以外は、実施例1と同様に負極用複合粒子の製造及び負極の製造を行った。
上述のようにして得られた負極および正極を用いて実施例1と同様にリチウムイオン二次電池の製造を行った。
負極用複合粒子の製造において、噴霧乾燥造粒により得られた負極用造粒粒子をエイシン社製格子マグ・フィルターに通した後、磁性を有しないメッシュ(開口径125μm)により粗大粒子を除去した。その後エイシン社製格子マグ・フィルターに通さずに体積平均粒子径73μmの負極用複合粒子を得た以外は、実施例1と同様に負極用複合粒子の製造及び負極の製造を行った。
上述のようにして得られた負極および正極を用いて実施例1と同様にリチウムイオン二次電池の製造を行った。
負極用複合粒子の製造において、噴霧乾燥造粒により得られた負極用造粒粒子をエイシン社製格子マグ・フィルターに通さずに、磁性を有しないメッシュ(開口径125μm)により粗大粒子を除去した。その後エイシン社製格子マグ・フィルターに通して体積平均粒子径77μmの負極用複合粒子を得た以外は、実施例1と同様に負極用複合粒子の製造及び負極の製造を行った。
上述のようにして得られた負極および正極を用いて実施例1と同様にリチウムイオン二次電池の製造を行った。
負極用水系スラリー組成物の製造において作製した負極用水系スラリー組成物をエイシン社製高磁力マグ・フィルターに通さなかった以外は、実施例1と同様に負極用水系スラリー組成物の製造を行った。
上述のようにして得られた負極および正極を用いて実施例1と同様にリチウムイオン二次電池の製造を行った。
負極用複合粒子の製造において、噴霧乾燥造粒により得られた負極用造粒粒子をエイシン社製格子マグ・フィルターに通した。その後磁性メッシュを用いた粗大粒子の除去を行わずに体積平均粒子径73μmの負極用複合粒子を得た以外は、実施例1と同様に負極用複合粒子の製造を行った。また、実施例1と同様に負極の製造を行ったところ、負極を製造することができなかった。
負極用複合粒子の製造において、噴霧乾燥造粒により得られた負極用造粒粒子をエイシン社製格子マグ・フィルターに通さず、さらに、磁性を有しないメッシュにより粗大粒子を除去して体積平均粒子径73μmの負極用複合粒子を得た以外は、実施例1と同様に負極用複合粒子の製造及び負極の製造を行った。
上述のようにして得られた負極および正極を用いて実施例1と同様にリチウムイオン二次電池の製造を行った。
Claims (7)
- 電極活物質及び粒子状結着剤を含む水系スラリー組成物を得るスラリー製造工程と、
前記水系スラリー組成物を噴霧機に移送する移送工程と、
前記噴霧機を用いて噴霧、乾燥することにより造粒粒子を得る造粒工程と、
前記造粒粒子から粗大粒子を分離する分離工程と
を含む電気化学素子電極用複合粒子の製造方法であって、
前記造粒工程により得られた前記造粒粒子から磁気により金属異物を除去する第1除去工程および/または前記分離工程より前記粗大粒子が除去された前記造粒粒子から磁気により金属異物を除去する第2除去工程を含むことを特徴とする電気化学素子電極用複合粒子の製造方法。 - 前記分離工程は、メッシュにより前記造粒粒子から前記粗大粒子を分離することを特徴とする請求項1記載の電気化学素子電極用複合粒子の製造方法。
- 前記電気化学素子電極用複合粒子の体積平均粒子径は10〜150μmであって、前記メッシュの開口径は前記電気化学素子電極用複合粒子の体積平均粒子径の1.1〜6.0倍であることを特徴とする請求項2記載の電気化学素子電極用複合粒子の製造方法。
- 前記メッシュは、金属製メッシュであることを特徴とする請求項2または3記載の電気化学素子電極用複合粒子の製造方法。
- 前記金属製メッシュは、磁気による金属除去機能を有することを特徴とする請求項4記載の電気化学素子電極用複合粒子の製造方法。
- 前記移送工程は、磁性を有する材料または磁化され得る材料の少なくとも一方を含む配管を用いて前記水系スラリー組成物を移送することを特徴とする請求項1〜5の何れか一項に記載の電気化学素子電極用複合粒子の製造方法。
- 前記スラリー製造工程および/または前記移送工程は、さらに前記水系スラリー組成物から磁気により金属異物を除去する工程を含むことを特徴とする請求項1〜6の何れか一項に記載の電気化学素子電極用複合粒子の製造方法。