JP6295912B2 - 非水電解液二次電池およびその製造方法 - Google Patents
非水電解液二次電池およびその製造方法 Download PDFInfo
- Publication number
- JP6295912B2 JP6295912B2 JP2014203951A JP2014203951A JP6295912B2 JP 6295912 B2 JP6295912 B2 JP 6295912B2 JP 2014203951 A JP2014203951 A JP 2014203951A JP 2014203951 A JP2014203951 A JP 2014203951A JP 6295912 B2 JP6295912 B2 JP 6295912B2
- Authority
- JP
- Japan
- Prior art keywords
- negative electrode
- mixture layer
- electrode mixture
- secondary battery
- flat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
上記の構成では、含浸時に気体が抜け難い(すなわち濡れ難い)負極合材層の中央部から、気体の抜出口となる電極巻回体の両端部に及ぶ連通溝が設けられている。中央部に位置する連通溝の起点部は、底部から蓋に向かう方向(典型的には鉛直上方向)において、第1の終端部および第2の終端部よりも底部側(典型的には最も鉛直下側)に位置している。そのため含浸時には気体が連通溝を通って容易に抜き出され、電解液および被膜形成用の添加剤を負極合材層の中央部にまで行き渡らせることができる。これにより負極合材層の面内方向において、被膜の形成にムラが生じることを抑制することができる。
図1は、本実施形態の非水電解液二次電池の構成の一例を示す概略図である。図1に示されるように、電池100は密閉型電池であり、角形筐体50を備えている。角形筐体50は、底部51と、底部51と連なる側壁52と、側壁52と連なりかつ底部51の反対側に位置する蓋53とを含む。角形筐体50の素材は、たとえばアルミニウム(Al)合金である。側壁52と蓋53とは、たとえばレーザ溶接によって接合されている。蓋53には、正極端子70および負極端子72が設けられている。角形筐体50には、注液孔、安全弁、電流遮断機構(いずれも図示せず)等がさらに設けられていてもよい。
図6は、負極20の構成の一例を示す概略図である。図6に示されるように、負極20は、長尺帯状の負極集電芯材21と、その両主面上に形成された長尺帯状の負極合材層22とを含んでいる。負極集電芯材21は、たとえば銅(Cu)箔である。
負極合材層22は、造粒体から得られた合材層であり、表面に複数の連通溝Trを有する。連通溝Trは、第1の終端部Tr1および第2の終端部Tr2において、負極合材層22の側面側へと開口しており、気体の抜出口として機能している。
図8では、平板部FpにおいてV字状に延びる連通溝Trを示している。このように起点部Tr0を通り、巻回軸方向ADに交差する方向VDに延びる直線に対して線対称な形状を採用することにより、気体の排出効率が向上する。連通溝TrがV字状に延びる場合、起点部Tr0から第1の終端部Tr1または第2の終端部Tr2に向かって延びる傾斜部Tr3と、巻回軸方向ADとのなす角度θは、次式(i)および(ii):
1°<θ×n<90° ・・・(i)
Tan(θ×n)=2H/W・・・(ii)
を同時に満たすことが好ましい。式(i)および(ii)中、「n」は一つの平板部Fpにおける連通溝Trの個数を示し、「W」は平板部Fpの巻回軸方向ADの寸法を示し、「H」は底部51から蓋53に向かう方向VD(巻回軸方向ADと交差する方向)の寸法を示している。一つの平板部Fpに含まれる連通溝Trの個数nは、1個以上50個以下が好ましい。これらの関係を満たすことにより、平板部Fp内に複数の連通溝Trを効率的に配置することができ、気体の排出効率をいっそう高めることができる。
負極合材層22は、複数の造粒体を含む。負極合材層22が塗料ではなく、造粒体から構成されていることにより、後述するように、圧縮成形によって負極合材層22を得る際に、局所的に合材密度を高めることなく、連通溝Trを形成することができる。負極合材層22は、面内方向に略均一な合材密度を有することが望ましい。電極反応のムラが小さくなり、電池寿命を延ばすことができるからである。たとえば、連通溝Trの底での合材密度を、連通溝Trを除く部分の合材密度の0.90倍以上1.10倍以下(より好ましくは1.00倍以上1.10倍以下)とすればよい。造粒体から負極合材層22を形成すれば、こうした略均一な合材密度を容易に実現することができる。他方、塗料から負極合材層を形成する場合には、連通溝を設けつつ合材密度を均一に保つことは極めて困難である。塗料を乾燥した後でなければ連通溝を形成できず、乾燥後では負極合材が流動性を示さないからである。負極合材層22において連通溝Trを除く部分の合材密度は、たとえば0.8g/cm3以上1.6g/cm3以下程度であり、同部分の厚さは、たとえば50μm以上100μm以下程度である。
図7は、正極10の構成の一例を示す概略図である。図7に示されるように、正極10は、長尺帯状の正極集電芯材11と、その両主面上に形成された長尺帯状の正極合材層12とを含んでいる。正極集電芯材11は、たとえばAl箔である。正極合材層12の厚さは、たとえば50μm以上100μm以下程度であり、合材密度は、たとえば1.5g/cm3以上3.0g/cm3以下程度である。
セパレータ40はLiイオンを透過させつつ、正極10と負極20との電気的な接触を防止する。セパレータ40は、機械的な強度と化学的な安定性の観点からポリオレフィン系材料からなる微多孔膜が好ましい。たとえばポリエチレン(PE)、ポリプロピレン(PP)等の微多孔膜が好適である。
電解液は、非プロトン性溶媒にLi塩(支持塩)を溶解させた電解質溶液である。非プロトン性溶媒には、たとえばエチレンカーボネート(EC)、プロピレンカーボネート(PC)、ブチレンカーボネート(BC)、およびγ−ブチロラクトン(γBL)等の環状カーボネート類、ならびにジメチルカーボネート(DMC)、エチルメチルカーボネート(EMC)およびジエチルカーボネート(DEC)等の鎖状カーボネート類等を使用することができる。これらの非プロトン性溶媒は電気伝導率および電気化学的な安定性の観点から2種以上を併用することが望ましい。特に環状カーボネートと鎖状カーボネートとを混合して使用することが望ましく、その際、環状カーボネートと鎖状カーボネートの体積比は1:9〜5:5程度が好ましい。
以上に説明した本実施形態の非水電解液二次電池は次のような方法によって製造することができる。
正極作製工程(S100)では、図7に示される正極10が作製される。たとえば正極活物質、導電材および結着材を、N−メチル−ピロリドン(NMP)中で混練して正極塗料を得、ダイコータ等を用いて正極塗料を、正極集電芯材11上の所定の位置に塗工、乾燥して正極合材層12を形成すればよい。さらにロール圧延機等を用いて正極合材層12の厚さおよび合材密度を調整してもよい。
負極作製工程(S200)では、図6に示される負極20が作製される。
造粒工程(S201)では、湿潤粉粒体である造粒体が作製される。造粒体は、負極活物質、増粘材、結着材および溶媒を混合して混合体を得た後、該混合体を造粒することにより作製される。たとえば混合装置内で、負極活物質、増粘材および結着材を水とともに混合することにより、混合体を作製することができる。混合装置には、たとえば株式会社アーステクニカ製の「ハイスピードミキサ」等を使用することができる。このとき混合体が粘土状となるように、混合体の固形分比率を調整することが好ましい。また結着材の分散性を考慮すると、溶媒は分割投入し、段階的に目標とする固形分比率に近づける態様が好ましい。
成形工程(S202)では、図6に示されるように、表面に複数の連通溝Trを有する負極合材層22が形成される。
配置工程(S203)では、負極集電芯材21上の所定の位置に負極合材層22が配置される。図18に示されるように、成形工程(S202)においてシート状に成形された負極合材層22は、Bロール92上を矢印の方向に搬送される。負極集電芯材21は、Cロール93上を矢印の方向に搬送される。Bロール92とCロール93との隙間では、負極合材層22および負極集電芯材21に、Bロール92およびCロール93から圧力が加わり、負極合材層22がBロール92上から負極集電芯材21上へと転写されるとともに、負極集電芯材21に圧着される。
乾燥工程(S204)では、負極集電芯材21上に配置された負極合材層22を乾燥する。乾燥には、一般的な乾燥炉を使用することができる。乾燥時間、乾燥温度は、造粒体の固形分比率および負極合材層22の厚さ等に合わせて適宜調整すればよい。以上のようにして負極20を作製することができる。
巻回工程(S300)では、扁平形電極巻回体80が作製される。扁平形電極巻回体80は、先ずセパレータ40を挟んで正極10と負極20とを巻回することにより、楕円状の電極巻回体を得、該電極巻回体を扁平状に成形することにより作製することができる。
挿入工程(S400)では、扁平形電極巻回体80が角形筐体50に挿入される。先ず扁平形電極巻回体80の巻回軸方向ADの両端部に位置する露出部Epに、正極集電板74および負極集電板76が接続される。次いで角形筐体50の蓋53に設けられた正極端子70と正極集電板74とが接続され、負極端子72と負極集電板76とが接続される。その後扁平形電極巻回体80が、底部51および側壁52を含むケースに挿入される。側壁52と蓋53とは、たとえばレーザ溶接によって接合される。
注液工程(S500)では、角形筐体50内に電解液が注入され、扁平形電極巻回体80に電解液が含浸される。電解液は、角形筐体50に設けられた注液孔(図示せず)から注入される。その後、扁平形電極巻回体80に電解液が含浸される。このとき連通溝Trが気体の抜出口として機能するため、気体と電解液との置換が促進され、扁平形電極巻回体80の中央部まで電解液が行き渡るとともに、扁平形電極巻回体80の全域に亘って電解液の分布を均等なものとすることができる。また含浸速度が速まるため、含浸時間を短縮することもできる。
初期充放電は、たとえば3.0V〜4.1V程度の範囲において、低めの電流値(たとえば0.1C〜1.0C程度)で実施される。これにより、負極活物質の表面にSEIの成長を阻害する被膜が形成される。本実施形態では、扁平形電極巻回体80の全域に亘って電解液が略均一に分布しているため、被膜の形成ムラも小さくなる。以上のようにして、長寿命を示す電池100を製造することができる。なおここで、電流値の単位「C」は電池の定格容量を1時間で放電しきる電流値を示している。
以下のようにして試料No.1〜No.8に係る非水電解液二次電池を作製した。ここでは試料No.1〜No.3が実施例に相当し、試料No.4〜No.8が比較例に相当する。
1.正極の作製(S100)
正極活物質(LiNi1/3Co1/3Mn1/3O2)と、導電材(アセチレンブラック)と、結着材(PVDF)とをNMP中で混練することにより、正極塗料を得、正極塗料を正極集電芯材11(厚さ20μmのAl箔)の両主面上に塗工、乾燥することにより、正極合材層12を形成した。正極塗料における固形分の質量比は、正極活物質:導電材:結着材=90:8:2とした。その後、正極合材層12を圧縮して厚さを調整した。
以下の材料を準備した
負極活物質:黒鉛粉末(D50が20μmであるもの)
増粘材 :CMC(製品名「MAC500LC」、日本製紙株式会社製)
結着材溶液:SBRの水分散体(品番「C41」、JSR株式会社製)
溶媒 :水
ここで「D50」は、レーザ回折/散乱法によって得られた粒度分布における積算値50%での粒径を示している。
負極活物質(100質量部)、増粘材(1質量部)、結着材(1質量部)および水をハイスピードミキサ(株式会社アーステクニカ製)に投入した。次いで、同装置においてアジテータ羽根の回転数を300rpm、チョッパー羽根の回転数を1200rpmに設定して5分間に亘って混合を行った。その後さらに水を追加して、固形分比率を71質量%に調整し、粘土状の混合体を得た。この粘土状の混合体を、直径1mmの円形ダイス孔を有するインライン式円筒造粒機(株式会社アーステクニカ製)に投入し、回転数を2000rpmに設定して押出し造粒を行った。これにより複数の造粒体(直径di:1mm、高さh:1.5mm)を得た。
図18に示す成形転写装置90を用いて、連通溝Trを有する負極合材層22を作製し、負極集電芯材21(厚さ14μmのCu箔)の両主面上に負極合材層22を圧着した。試料No.1では、図19に示す凸状の刻印92aを有するBロールを使用し、平板部Fpにおける連通溝Trの形状を図8に示す形状とした。ただし試料No.1では、一つの平板部Fpに含まれる連通溝Trの個数nは1個とした。また連通溝Trの傾斜部Tr3と巻回軸方向ADとのなす角度θは55°とした。
PPの微多孔膜(PP膜)と、PEの微多孔膜(PE膜)とが、PP膜/PE膜/PP膜の順に積層されたセパレータ基材(厚さ25μm)を準備した。無機フィラーであるアルミナ粒子(96質量部)と、アクリルゴム(4質量部)と、溶媒(イオン交換水)とをクレアミックス(エム・テクニック株式会社製)を用いて混合し、耐熱層となるべき塗料を得た。当該塗料をグラビアコータによってセパレータ基材上に塗工、乾燥し耐熱層を形成した。これによりセパレータ40を得た。図5に示すセパレータ40の幅Wsは、112mmとした。
扁平形電極巻回体80の露出部Epに正極集電板74および負極集電板76を接続した。角形筐体50の蓋53に設けられた正極端子70および負極端子72と、正極集電板74および負極集電板76とをそれぞれ接続した後、図2に示すように、底部51および側壁52からなるケース(Al製)に扁平形電極巻回体80を挿入し、さらに側壁52と蓋53とを接合した。
組成が[LiPF6(1.0mоl/L) EC:DMC:EMC=3:4:3(体積比)]である電解液を準備し、さらにCHB(1質量%)、BP(1質量%)およびLiBOB(1質量%)を溶解させた。角形筐体50の蓋53に設けられた注液孔から電解液(125g)を注入し、扁平形電極巻回体80に含浸させた。注液孔は封止栓(ねじ)によって封止した。
1Cの電流値で4.1Vに達するまで充電を行い、その後1/3C(3分の1C)の電流値で3.0Vに達するまで放電を行った。以上のようにして試料No.1に係る電池(定格容量24Ah)を得た。
成形工程(S202)において、Bロール上の刻印の形状を変更することにより、図8に示すように、負極合材層22の一つの平板部Fpに含まれる連通溝Trの個数nを2個とし、傾斜部Tr3と巻回軸方向ADとのなす角度θを35°とすることを除いては、試料No.1と同様にして試料No.2に係る電池を得た。
成形工程(S202)において、Bロール上の刻印の形状を変更することにより、負極合材層22の一つの平板部Fpに含まれる連通溝Trの個数nを50個とし、傾斜部Tr3と巻回軸方向ADとのなす角度θを2°とすることを除いては、試料No.1と同様にして試料No.3に係る電池を得た。なお試料No.1〜No.3では、いずれもTan(θ×n)=2H/Wとなる関係が満たされている。
負極合材層22に連通溝Trを設けないことを除いては、試料No.1と同様にして試料No.4に係る電池を得た。
成形工程(S202)において、Bロール上の刻印の形状を変更することにより、図20に示される連通溝TrWを形成することを除いては、試料No.1と同様にして試料No.5に係る電池を得た。図20に示されるように連通溝TrWは、巻回軸方向ADに平行に延びるものである。
成形工程(S202)において、Bロール上の刻印の形状を変更することにより、図21に示される連通溝TrXを形成することを除いては、試料No.1と同様にして試料No.6に係る電池を得た。図21に示されるように連通溝TrXは、巻回軸方向ADと交差する方向VDに延びるものである。
成形工程(S202)において、Bロール上の刻印の形状を変更することにより、図22に示される連通溝TrYを形成することを除いては、試料No.1と同様にして試料No.7に係る電池を得た。図22に示されるように連通溝TrYでは、傾斜部同士が交差する構造ではあるが、最も底部51側に位置する起点部が存在しない。
成形工程(S202)において、Bロール上の刻印の形状を変更することにより、図23に示される連通溝TrZを形成することを除いては、試料No.1と同様にして試料No.8に係る電池を得た。図23に示されるように連通溝TrZでは、傾斜部が鉛直下向きに延びており、傾斜部と巻回軸方向ADとのなす角度θが−50°となっている。
各電池を以下のようにして評価した。
初期充放電後の各電池を解体し、各負極を回収した。図24に示すように、巻回軸方向ADに等間隔にサンプル(mp1〜mp7)を採取し、誘導結合プラズマ発光分光分析装置(ICP−AES)によってホウ素濃度[質量%]を測定した。結果を図25および表1に示す。ここでホウ素は添加剤(LiBOB)に由来する被膜成分である。よってホウ素濃度の分布は、被膜量の分布とみなすことができる。
各電池において定電流サイクルを2000サイクル実施した。初回および500サイクル毎に容量確認を行い、サイクル後容量を初回の容量で除することにより容量維持率[%]を算出した。容量維持率の推移を図26に示す。また2000サイクル後の容量維持率を表1に示す。ここで使用した定電流サイクル条件および容量確認条件を以下に示す。
充電 :電流値6A、カット電圧4.1V
放電 :電流値240A、カット電圧3.0V
環境温度:60℃
(500サイクル毎の容量確認条件)
充電 :電流値8A、カット電圧4.1V
放電 :電流値8A、カット電圧3.0V
環境温度:60℃。
1.被膜の均一性について
図25および表1より、試料No.4〜No.8に比べて、試料No.1〜No.3では負極合材層の中央部に相当するmp3〜mp5と、端部に相当するmp1およびmp7とで、ホウ素濃度の差が小さくなっている。つまり試料No.1〜No.3では、試料No.4〜No.8よりも被膜が均一に形成されているといえる。
図26および表1より、試料No.1〜No.3のサイクル寿命は、試料No.4〜No.8に比して良好である。この結果から、被膜を均一に形成することにより、電池寿命を長期化できることが分かる。
91,92,93 ロール、92a 刻印、94 仕切り部材、95 フィーダ、A1,A2 矢印、AD 巻回軸方向、CR 中央部、E1 第1の端部、E2 第2の端部、Ep 露出部、Fp 平板部、La,Lc 長さ、Tr,TrA,TrB,TrC,TrD,TrW,TrX,TrY,TrZ 連通溝、Tr0 起点部、Tr1 第1の終端部、Tr2 第2の終端部、Tr3 傾斜部、VD 方向、W,Wa1,Wa2,Wc1,Wc2,Wt 幅、di 直径、dp 深さ、H,h 高さ。
Claims (8)
- 正極合材層と負極合材層とを含む扁平形電極巻回体と、
底部と、前記底部と連なる側壁と、前記側壁と連なりかつ前記底部の反対側に位置する蓋とを含む角形筐体と、を備え、
前記角形筐体は、前記扁平形電極巻回体の巻回軸方向が、前記底部から前記蓋に向かう方向と交差するように、前記扁平形電極巻回体を収容し、
前記扁平形電極巻回体は、前記正極合材層および前記負極合材層の平板部が積層されてなる扁平部を含み、
前記扁平部は、前記側壁に面しており、
前記平板部は、前記巻回軸方向の一方の端部に第1の端部と、前記第1の端部の反対側に位置する第2の端部と、前記第1の端部と前記第2の端部に挟まれた中央部とを含み、
前記負極合材層の前記平板部には、前記第1の端部から前記第2の端部まで延びる複数の連通溝が設けられており、
前記連通溝は、前記第1の端部に第1の終端部と、前記第2の端部に第2の終端部と、前記中央部に前記第1の終端部および前記第2の終端部よりも前記底部側に位置する起点部とを含み、前記起点部から前記第1の終端部および前記第2の終端部に向かって延びており、
前記負極合材層は、複数の造粒体を含み、
前記造粒体は、負極活物質と、結着材とを含有する、非水電解液二次電池。 - 前記平板部において、
前記連通溝は、前記起点部を通り、前記巻回軸方向と交差する方向に延びる直線に対して線対称である、請求項1に記載の非水電解液二次電池。 - 前記平板部において、
前記連通溝は、V字状に延びる、請求項1または請求項2に記載の非水電解液二次電池。 - 一つの前記平板部に、前記連通溝が1個以上50個以下設けられている、請求項1〜請求項3のいずれか1項に記載の非水電解液二次電池。
- 一つの前記平板部に含まれる前記連通溝の個数をn、
前記負極合材層の前記平板部の前記巻回軸方向の寸法をW、
前記平板部の前記巻回軸方向と交差する前記方向の寸法をH、
前記連通溝のうち、前記起点部から前記第1の終端部または前記第2の終端部に向かって延びる傾斜部と、前記巻回軸方向とのなす角度をθとするとき、
1°<θ×n<90°かつTan(θ×n)=2H/Wを満たす、請求項4に記載の非水電解液二次電池。 - 請求項1〜請求項5に記載の非水電解液二次電池の製造方法であって、
前記負極活物質、前記結着材および溶媒を混合し、造粒することにより、前記複数の造粒体を得る造粒工程と、
前記複数の造粒体を、表面に前記連通溝に対応する形状の刻印を有する第1のロールと、第2のロールとの間で圧縮成形することにより、前記複数の連通溝を有する前記負極合材層を得る成形工程と、を含む、非水電解液二次電池の製造方法。 - 前記成形工程において、前記複数の造粒体の固形分比率は、65質量%以上80質量%以下である、請求項6に記載の非水電解液二次電池の製造方法。
- 前記成形工程の後に、
前記負極合材層を負極集電芯材上に配置する配置工程と、
前記負極合材層を乾燥する乾燥工程と、をさらに含む、請求項6または請求項7に記載の非水電解液二次電池の製造方法。