JP6279973B2 - 成形用包装材及び成形ケース - Google Patents
成形用包装材及び成形ケース Download PDFInfo
- Publication number
- JP6279973B2 JP6279973B2 JP2014102149A JP2014102149A JP6279973B2 JP 6279973 B2 JP6279973 B2 JP 6279973B2 JP 2014102149 A JP2014102149 A JP 2014102149A JP 2014102149 A JP2014102149 A JP 2014102149A JP 6279973 B2 JP6279973 B2 JP 6279973B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- packaging material
- molding
- mass
- colored ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記着色インキ層は、
主剤としてのポリエステル樹脂と硬化剤としての多官能イソシアネート化合物とによる二液硬化型ポリエステルウレタン樹脂バインダーと、
無機顔料を含む着色顔料と、を含む着色インキ組成物からなり、
前記主剤としてのポリエステル樹脂は、数平均分子量(Mn)が8000〜25000であり、質量平均分子量(Mw)が15000〜50000であり、これらの比率(Mw/Mn)が1.3〜2.5であり、
前記硬化剤としての多官能イソシアネート化合物の50モル%以上が芳香族系多官能イソシアネート化合物であることを特徴とする成形用包装材。
前記耐熱性樹脂層(外側層)2としては、特に限定されるものではないが、例えば、ポリアミドフィルム、ポリエステルフィルム等が挙げられ、これらの延伸フィルムが好ましく用いられる。中でも、前記耐熱性樹脂層2としては、成形性および強度の点で、二軸延伸ポリアミドフィルム、二軸延伸ポリブチレンテレフタレート(PBT)フィルム、二軸延伸ポリエチレンテレフタレート(PET)フィルムまたは二軸延伸ポリエチレンナフタレート(PEN)フィルムを用いるのが特に好ましい。前記ポリアミドフィルムとしては、特に限定されるものではないが、例えば、6ナイロンフィルム、6,6ナイロンフィルム、MXDナイロンフィルム等が挙げられる。なお、前記耐熱性樹脂層2は、単層で形成されていても良いし、或いは、例えばPETフィルム/ポリアミドフィルムからなる複層で形成されていても良い。
前記熱可塑性樹脂層(内側層)3は、リチウムイオン二次電池等で用いられる腐食性の強い電解液などに対しても優れた耐薬品性を具備させるとともに、包材にヒートシール性を付与する役割を担うものである。
前記金属箔層4は、成形用包装材1に酸素や水分の侵入を阻止するガスバリア性を付与する役割を担うものである。前記金属箔層4としては、特に限定されるものではないが、例えば、アルミニウム箔、銅箔、ステンレス箔等が挙げられ、アルミニウム箔が一般的に用いられる。前記金属箔層4の厚さは、20μm〜100μmであるのが好ましい。20μm以上であることで金属箔を製造する際の圧延時のピンホール発生を防止できるとともに、100μm以下であることで張り出し成形時や絞り成形時の応力を小さくできて成形性を向上させることができる。
1)リン酸と、クロム酸と、フッ化物の金属塩及びフッ化物の非金属塩からなる群より選ばれる少なくとも1種の化合物と、を含む混合物の水溶液
2)リン酸と、アクリル系樹脂、キトサン誘導体樹脂及びフェノール系樹脂からなる群より選ばれる少なくとも1種の樹脂と、クロム酸及びクロム(III)塩からなる群より選ばれる少なくとも1種の化合物と、を含む混合物の水溶液
3)リン酸と、アクリル系樹脂、キトサン誘導体樹脂及びフェノール系樹脂からなる群より選ばれる少なくとも1種の樹脂と、クロム酸及びクロム(III)塩からなる群より選ばれる少なくとも1種の化合物と、フッ化物の金属塩及びフッ化物の非金属塩からなる群より選ばれる少なくとも1種の化合物と、を含む混合物の水溶液
のいずれかを塗工した後、乾燥することにより化成処理を施す。
前記着色インキ層10は、前記金属箔層4と前記耐熱性樹脂層2との間に配置される層であり、上記実施形態では、前記第1接着剤層5と前記耐熱性樹脂層2との接合を担うと共に、成形用包装材1の外面側に色(無彩色を含む)を付与する層である。
前記第1接着剤層5は、前記金属箔層4と前記耐熱性樹脂層2(上記実施形態では着色インキ層10)との接合を担う層である。前記第1接着剤層5としては、特に限定されるものではないが、例えば、2液硬化型接着剤により形成された接着剤層等が挙げられる。前記2液硬化型接着剤としては、例えば、ポリウレタン系ポリオール、ポリエステル系ポリオール、ポリエーテル系ポリオール及びポリエステルウレタン系ポリオールからなる群より選ばれるポリオールの1種または2種以上からなる第1液と、イソシアネートからなる第2液(硬化剤)とで構成される2液硬化型接着剤などが挙げられる。中でも、ポリエステル系ポリオール及びポリエステルウレタン系ポリオールからなる群より選ばれるポリオールの1種または2種以上からなる第1液と、イソシアネートからなる第2液(硬化剤)とで構成される2液硬化型接着剤を用いるのが好ましい。前記第1接着剤層5は、例えば、前記2液硬化型接着剤等の接着剤が、前記金属箔層4の上面に又は/及び前記耐熱性樹脂層2の下面(例えば着色インキ層10の下面)に、グラビアコート法等の手法により塗布されることによって形成される。
前記第2接着剤層6としては、特に限定されるものではないが、例えば、ポリウレタン系接着剤、アクリル系接着剤、エポキシ系接着剤、ポリオレフィン系接着剤、エラストマー系接着剤、フッ素系接着剤、酸変性ポリプロピレン接着剤等により形成された接着剤層が挙げられる。中でも、アクリル系接着剤、ポリオレフィン系接着剤を用いるのが好ましく、この場合には、成形用包装材1の耐電解液性及び水蒸気バリア性を向上させることができる。
前記マットコート層20は、成形用包装材1の表面に良好な滑り性を付与して成形性を向上させるために設けられた表面層である。
厚さ35μmのアルミニウム箔(A8079アルミニウム箔)4の両面に、ポリアクリル酸、三価クロム化合物、水、アルコールからなる化成処理液を塗布し、150℃で乾燥を行うことによって、両面に化成皮膜を形成したアルミニウム箔を準備した。この化成皮膜によるクロム付着量は、片面で5mg/m2であった。
実施例1と同じ出発材料を用いて、ジカルボン酸全量に対するジオール成分全量の配合モル比を実施例1より多く調整することにより、数平均分子量(Mn)が8900、重量平均分子量(Mw)が15000、これらの比率(Mw/Mn)が1.69であるポリエステルポリオールを得た。
実施例1の硬化剤のジイソシアネート成分を、芳香族のトリレンジイソシアネート(TDI)70モル%と脂肪族イソシアネート化合物であるヘキサメチレンジイソシアネート(HDI)30モル%とからなる混合イソシアネートにトリメチロールプロパンを反応させて得たアダクト体である多官能イソシアネート化合物(NCO%:13.0%、固形分75質量%)に変更した以外は、実施例1と同様にして、図1に示す成形用包装材1を得た。
実施例1の平均粒子径1.0μmのカーボンブラック13.3質量部、ポリエステルポリオール樹脂溶液100質量部、酢酸エチル64.4質量部を混合するのに代えて、平均粒子径1.0μmのカーボンブラック4.4質量部、ポリエステルポリオール樹脂溶液100質量部、酢酸エチル43.6質量部を混合することによって、ポリエステル樹脂とカーボンブラックの合計質量に対するカーボンブラックの含有割合を10質量%に設定した以外は、実施例1と同様にして、図1に示す成形用包装材1を得た。
実施例1の主剤インキ組成物100質量部に対して、硬化剤として、トリレンジイソシアネート(TDI)とトリメチロールプロパンとのアダクト体(NCO%:13.0%、固形分75質量%;芳香族系多官能イソシアネート化合物)を7.1質量部配合し、さらに酢酸エチル34.1質量部を配合して着色インキ組成物を得るのに代えて、主剤インキ組成物100質量部に対して、硬化剤として、トリレンジイソシアネート(TDI)とトリメチロールプロパンとのアダクト体(NCO%:13.0%、固形分75質量%;芳香族系多官能イソシアネート化合物)を3.6質量部配合し、さらに酢酸エチル31質量部を配合して着色インキ組成物を得たことにより、硬化剤のイソシアネート官能基(NCO)とポリエステルポリオール水酸基(OH)のモル比(NCO/OH)を5とした以外は、実施例1と同様にして、図1に示す成形用包装材1を得た。
フルオロエチレンビニルエステル(耐熱性樹脂)80質量部、硫酸バリウム(無機微粒子)10質量部、粉状シリカ(無機微粒子)10質量部を混合してマットコート組成物を得た。このマットコート組成物を、実施例1の工程における二軸延伸ナイロンフィルム(耐熱性樹脂層)2の貼り合わせに続いて、二軸延伸ナイロンフィルム(耐熱性樹脂層)2の表面に塗布して、乾燥後の厚さが2μmのマットコート層20を形成せしめた以外は、実施例1と同様にして、図2に示す構成の成形用包装材1を得た。
実施例1と同じ出発材料を用いて、反応条件を変える(ジカルボン酸全量に対するジオール成分全量の配合モル比を実施例1より多く調整する)ことにより、数平均分子量(Mn)が6700、重量平均分子量(Mw)が8400、これらの比率(Mw/Mn)が1.25であるポリエステルポリオールを得た。
硬化剤として、実施例1のトリレンジイソシアネート(TDI)とトリメチロールプロパンとのアダクト体(NCO%:13.0%、固形分75質量%;芳香族系多官能イソシアネート化合物)7.1質量部に代えて、トリレンジイソシアネート(TDI)30モル%とヘキサメチレンジイソシアネート(HDI)70モル%とからなる混合イソシアネートにトリメチロールプロパンを反応させて得たアダクト体(NCO%:13.0%、固形分75質量%;多官能イソシアネート化合物)7.1質量部を用いた以外は、実施例1と同様にして、成形用包装材を得た。
硬化剤として、実施例2のトリレンジイソシアネート(TDI)とトリメチロールプロパンとのアダクト体(NCO%:13.0%、固形分75質量%;芳香族系多官能イソシアネート化合物)4.8質量部に代えて、トリレンジイソシアネート(TDI)30モル%とヘキサメチレンジイソシアネート(HDI)70モル%とからなる混合イソシアネートにトリメチロールプロパンを反応させて得たアダクト体(NCO%:13.0%、固形分75質量%;多官能イソシアネート化合物)4.8質量部を用いた以外は、実施例2と同様にして、成形用包装材を得た。
各実施例毎、各比較例毎に、それぞれ30個の成形用包装材を製造し、これらにおいて耐熱性樹脂層2がアルミニウム箔4から剥離していないことを肉眼で確認した後、パンチとダイス等を用いて、内側の熱可塑性樹脂層3をパンチと接触させる態様で、縦50mm×横35mm×深さ5.5mmの直方体形状に深絞り成形を行って、周囲にフランジ部を有する成形ケースを作製した。
(判定基準)
「○」…30個全てにおいて色むらは認められなかった
「△」…色むらが少し認められるものが存在した
「×」…顕著な色むらが認められるものが存在した。
各実施例毎、各比較例毎に、それぞれ30個の成形用包装材を製造し、これらについて耐熱性樹脂層の剥離の有無等を肉眼で、下記a)、b)、c)の3つの状態時において調べ、下記判定基準に基づいて評価した。
(判定基準)
「◎」…耐熱性樹脂層がアルミニウム箔から剥離したものが、30個中0個である
「○」…耐熱性樹脂層がアルミニウム箔から剥離したものが、30個中、1個又は2個である
「△」…耐熱性樹脂層がアルミニウム箔から剥離したものが、30個中、3個〜5個である
「×」…耐熱性樹脂層がアルミニウム箔から剥離したものが、30個中、6個〜30個である。
b)上記a)の成形ケースと同一構成の成形前のフラットな成形用包装材(以下、「蓋材」という)を準備した。一方、上記a)の成形ケースから耐熱性樹脂層の剥離のなかったもののみを選び出し、この剥離の無い成形ケースのフランジ部に上記蓋材(の周縁部)を重ねて、200℃×0.3MPa×6秒の条件でヒートシールした。このヒートシール直後の成形用包装材
c)上記a)の成形ケースから耐熱性樹脂層の剥離のなかったもののみを選び出し、この剥離の無い成形ケースを、60℃×95%RHの高温高湿試験機の中に72時間入れ続けた後、取り出して常温で5日経過後の成形用包装材。
実施例1〜6、比較例1〜3で使用した二液硬化型ポリエステルウレタン樹脂バインダーの硬化膜(即ち各着色インキ組成物から着色剤のカーボンブラックを取り除いた組成の組成物の硬化膜;換言すれば、主剤と硬化剤とが反応した硬化膜)を作成し、この硬化膜の物性を評価した。
2…耐熱性樹脂層(外側層)
3…熱可塑性樹脂層(内側層)
4…金属箔層
10…着色インキ層
Claims (7)
- 外側層としての耐熱性樹脂層と、内側層としての熱可塑性樹脂層と、これら両層間に配設された金属箔層と、該金属箔層と前記耐熱性樹脂層との間に配設された着色インキ層とを含む成形用包装材であって、
前記着色インキ層は、
主剤としてのポリエステル樹脂と硬化剤としての多官能イソシアネート化合物とによる二液硬化型ポリエステルウレタン樹脂バインダーと、
無機顔料を含む着色顔料と、を含む着色インキ組成物からなり、
前記主剤としてのポリエステル樹脂は、数平均分子量(Mn)が8000〜25000であり、質量平均分子量(Mw)が15000〜50000であり、これらの比率(Mw/Mn)が1.3〜2.5であり、
前記硬化剤としての多官能イソシアネート化合物の50モル%以上が芳香族系多官能イソシアネート化合物であることを特徴とする成形用包装材。 - 前記着色インキ層において、前記主剤としてのポリエステル樹脂と前記着色顔料の合計質量に対する着色顔料の含有質量の割合が5質量%〜60質量%である請求項1に記載の成形用包装材。
- 前記着色顔料の50質量%以上が前記無機顔料で構成されている請求項1または2に記載の成形用包装材。
- 前記二液硬化型ポリエステルウレタン樹脂バインダーは、前記主剤と前記硬化剤とが反応した後の硬化膜の引張試験(JIS K7162)によるヤング率が70MPa〜400MPaである請求項1〜3のいずれか1項に記載の成形用包装材。
- 前記金属箔層の少なくとも一方の面に化成皮膜が形成されている請求項1〜4のいずれか1項に記載の成形用包装材。
- 請求項1〜5のいずれか1項に記載の成形用包装材を深絞り成形または張り出し成形してなる成形ケース。
- 電池ケースとして用いられる請求項6に記載の成形ケース。