JP6182328B2 - 表面平滑性に優れた樹脂組成物 - Google Patents
表面平滑性に優れた樹脂組成物 Download PDFInfo
- Publication number
- JP6182328B2 JP6182328B2 JP2013037155A JP2013037155A JP6182328B2 JP 6182328 B2 JP6182328 B2 JP 6182328B2 JP 2013037155 A JP2013037155 A JP 2013037155A JP 2013037155 A JP2013037155 A JP 2013037155A JP 6182328 B2 JP6182328 B2 JP 6182328B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- resin composition
- mfrr
- cables
- cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
表1に、実施例1〜8及び比較例1〜5で使用したポリオレフィン系樹脂を示した。フィルムグレードのエチレン‐α‐オレフィン共重合体としては、エチレン‐1・ブテン共重合体を用い、PP系樹脂としては、h‐PP、r‐PP、及び、b‐PPをそれぞれ用いた。
表2に示した各配合比で、PE系樹脂と各種PP系樹脂のペレット混合物を作製した。まず、PP系樹脂に、着色剤、酸化防止剤、及び、滑剤等の添加剤を加え、バンバリミキサーで溶融混合してPP系樹脂ペレットを作製する。次いで、作製した各種PP系樹脂ペレットをPE系樹脂とドライブレンドして、電線被覆用樹脂組成物のペレット混合物とした。
上記電線被覆用樹脂組成物のペレットを電線製造用押出成形機に送入し、シリンダー温度をフィーダー側から160℃、170℃、210℃、クロスヘッド温度220℃の条件で、導体径0.8mmの軟銅線上に厚み0.8mmで押出成形被覆し、被覆電線を製造した。押出成形速度は8m/分であった。
各樹脂のMFRは、JIS K 7210に従い、190℃の温度で、10、2、及び、0.5Kgの荷重で測定し、その結果からMFRR=I10/I0.5を求めると共に、従来技術との比較のため、MFRR=I10/I2も算出した。
表2に測定した結果をまとめた。図1及び2には、表2の結果に基づき、縦軸に算術平均粗さ(Ra、μm)、横軸にMFRR=(I10/I0.5)及びMFRR=I10/I2をプロットした。
Claims (5)
- 190℃、10Kg荷重で測定したメルトフローレート(I10)と190℃、0.5Kg荷重で測定したメルトフローレート(I0.5)の比(=I10/I0.5)をMFRRと定義し、MFRR≧43であって、エチレン‐α‐オレフィン共重合体の少なくとも1種とポリプロピレン系樹脂の少なくとも1種とから構成されていることを特徴とする押出成形に適用する絶縁電線又はケーブルの被覆用ポリオレフィン樹脂組成物。
- 前記ポリプロピレン系樹脂の190℃、2.16kg荷重で測定したメルトフローレートが、1〜100g/10分であることを特徴とする請求項1に記載の押出成形に適用する絶縁電線又はケーブルの被覆用ポリオレフィン樹脂組成物。
- 請求項1又は2に記載のポリオレフィン樹脂組成物が押出成形で被覆されていることを特徴とする絶縁電線又はケーブル。
- 請求項1又は2に記載の2種以上のポリオレフィン系樹脂を押出機直上で混合し、前記押出機に送入して成形することを特徴とする絶縁電線又はケーブルの製造方法。
- 請求項1又は2に記載のポリプロピレン系樹脂が、酸化防止剤、カーボン、着色剤、滑剤の少なくとも1種を含んだ樹脂組成物のペレットで供給され、前記エチレン‐α‐オレフィン共重合体の少なくとも1種と押出機直上で混合し、前記押出機に送入して成形することを特徴とする絶縁電線又はケーブルの製造方法。