JP5908859B2 - 分子溶融物ならびに分子溶融物の作製方法および使用方法 - Google Patents
分子溶融物ならびに分子溶融物の作製方法および使用方法 Download PDFInfo
- Publication number
- JP5908859B2 JP5908859B2 JP2013076798A JP2013076798A JP5908859B2 JP 5908859 B2 JP5908859 B2 JP 5908859B2 JP 2013076798 A JP2013076798 A JP 2013076798A JP 2013076798 A JP2013076798 A JP 2013076798A JP 5908859 B2 JP5908859 B2 JP 5908859B2
- Authority
- JP
- Japan
- Prior art keywords
- molecular melt
- bsa
- dpo
- group
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
ポリオレフィンおよび他のポリマーは、そのレオロジー的性質および他の物理的性質を改善するために修飾されることが多い。様々な化学剤が、そのような修飾を行うために使用されている。
(a)「カップリング剤」は、ポリマー鎖のCH基、CH2基またはCH3基の炭素−水素結合(脂肪族および/または芳香族の両方)に挿入し得るカルベン基またはニトレン基をそれぞれが生成し得る少なくとも2つの反応基を含有する化学化合物を意味するものとする。この反応基はともに、ポリマー鎖をカップリングまたは架橋することができる。ポリマー鎖をカップリングし、および/または架橋するためにカップリング剤が効果的であるためには、カップリング剤を、熱、音波エネルギー、放射線または他の化学的な活性化エネルギーで活性化することが必要になる場合がある。
4,4’−オキシジベンゼンスルホニルアジド。
驚くべきことに、抗酸化剤およびカップリング剤(または修飾剤)を一緒に混合して、分子溶融物が形成され得ること、そしてこの分子溶融物の形成がカップリング剤および/または修飾剤を減感し得ることが見出された。
本発明は多くの異なる形態での実施形態が可能であるが、本発明の特定の実施形態が図に示され、そして本明細書中に詳しく記載される。しかし、本開示は、本発明の原理の例示であると見なされるべきであり、そして例示されている特定の実施形態および実施例に本発明を限定することを意図していないことを理解しなければならない。
分子溶融物は少なくとも部分的に非晶質であり、この非晶質性により、カップリング剤を減感する分子溶融物の能力が改善されると考えられる。この非晶質性により、標的ポリマーを修飾する際の分子溶融物の効率が改善されることもまた考えられる。多くの場合において、標的ポリマーにおける分子溶融物の溶解性は、標的ポリマーにおけるカップリング剤の溶解性よりも大きいことが好ましい。
内部滑剤(internal lubricants)、例えば、ポリエチレングリコール(PEG)およびポリプロピレングリコール(PPG)、ステアリン酸カルシウム、グリセロールモノステアラート(GMS)など;
前記に議論されているように、本発明の修飾剤およびカップリング剤は、カルベン基またはニトレン基を生成し得る少なくとも1つの反応基を含有する化学化合物である。修飾剤は1つのそのような反応基を有する。カップリング剤は2つ以上のそのような反応基を有する。
本発明の抗酸化剤には、ポリマーに対する抗酸化剤およびそのような抗酸化剤の化学的誘導体として有用な化学薬品が挙げられ、これにはヒドロカルビルが含まれる。好ましくは、抗酸化剤は、ホスファイトを含有する化合物、または+3の酸化状態のリンを含有する化合物ではない。これらの化合物は、本発明において利用される典型的なカップリング剤との反応性が大きいからである。ホスファイト系抗酸化剤の例には、チバ・スペシャリティ・ケミカルズからIrgafos168の商品名で得られるトリス(2,4−ジ−tert−ブチルフェニル)ホスファイトが挙げられる。
分子溶融物における抗酸化剤は、カップリング剤自身および他の化学化合物(カップリング剤と有害に反応し得る、+3の酸化状態のリンを含有する化合物など)との反応からカップリング剤を少なくとも部分的に保護する。カップリング剤を保護することによって、抗酸化剤は、標的ポリマーとの反応のために利用され得るカップリング剤の割合が増大する。これはカップリング剤のカップリング効率を増大させる(すなわち、副反応により無駄になるカップリング剤が少なくなる)。
分子溶融物は、任意の標的ポリマーを修飾するために使用することができる。好ましくは、標的ポリマーは、スチレン性ポリマーまたはポリオレフィン(エチレンを含む)に基づくポリマーである。ポリオレフィンは、この分野の技術に含まれる手段によって形成される。α−オレフィンモノマーおよび必要な場合には他の付加重合性モノマーが、例えば、ガリ(Galli)ら、Angew.Macromol.Chem.、第120巻、73頁(1984)によって、またはイー・ピー・モア(E.P.More)ら、Polypropylen Handbook(Hanser Publishers、ニューヨーク(New York)、1996、特に、11頁〜98頁)によって開示されるように、この分野の技術に含まれる様々な条件のもとで重合させられる。
当業者は、カップリング剤の反応性、カップリング剤、および所望するレオロジーもしくは所定のレオロジー、または鎖カップリングの量により、カップリング剤の使用量が決定されることを認識する。この量を決定することはこの分野の技術の範囲内である。本発明のこの態様では、実質的に架橋した網目構造の形成は避けるべきである。これは、得られる物質が加工しにくくなるからである。従って、ポリ(スルホニルアジド)は、鎖がカップリングされたか、またはレオロジーが変化した(しかし、実質的には架橋されていない)ポリオレフィンが得られるそのような量に好ましくは制限される。しかし、いくつかの適用(フォーム適用など)では、ある量の架橋は許容される。一般に、使用されるアジドのレベルは、好ましくは、標的ポリマーの1モルあたり1.6モル未満のカップリング剤である。フィルムについては、好ましいカップリング剤のポリ(スルホニルアジド)は、ポリオレフィン(好ましくはポリプロピレンまたはポリプロピレン/エチレンコポリマー混合物)の総重量に基づいて、好ましくは0.5重量パーセント未満であり、より好ましくは0.20重量パーセント未満であり、最も好ましくは0.10重量パーセント未満である。
レオロジー改変の場合のように、当業者は、反応性、使用されるカップリング剤、および所望する架橋度により、カップリング剤の使用量が決定されることを認識する。しかし、レオロジー改変とは異なり、架橋を適用する場合には、架橋された網目構造を形成させるために十分なカップリング剤を添加することが必要である。これは、カルベン基またはニトレン基を生成し得る反応基のより高い濃度がそれぞれのポリマー分子のために使用されることを必要としている。典型的には、反応基対標的ポリマーのモル比は0.9〜6.0でなければならない。いくつかの実施形態においては、カップリング剤分子あたり3つ以上の反応基を有するカップリング剤を使用することが好ましい。これにより、使用しなければならないカップリング剤の量が少なくなる。また、架橋された適用の場合には、典型的には、標的ポリマーに添加される抗酸化剤の量を最小限にすることが望ましい。従って、用いられる分子溶融物は、レオロジー改変のために典型的に用いられる分子溶融物よりも比較的大きいカップリング剤対抗酸化剤のモル比を有することが、これらの適用では好ましい。
実施例1: 4,4’−オキシジベンゼンスルホニルアジド(DPO−BSA)の製造方法
下記の実施例のすべてにおいて使用されるサンプルを作製するために使用されたベースポリプロピレンは、ザ・ダウ・ケミカル・カンパニーからDow H700−12PPおよびDow C105−02PPの名称で得られるアイソタクチックポリプロピレンペレットである。Dow H700−12PPはプロピレンのホモポリマーであり、メルトフローレイト(MFR)=12dg/分(230℃)/2.16kgである。Dow C105−02PPは、16重量パーセント〜22重量パーセントのエチレンを伴うプロピレンのインパクトコポリマーであり、メルトフローレイト(MFR)=1.7dg/分(230℃)/2.16kgである。
ポリマーサンプル(A1、B1およびCA)を下記のように調製する。1500グラムのポリマーを重量測定して容器に入れた。1.5グラムのオイルを加えて、容器を30分間にわたって回転させた。そのとき、所望する量の分子溶融物(1:3.3重量比のDPO−BSA:Irganox1010)および添加剤(表2参照)を加え、容器をさらに30分間にわたって回転させた。回転混合された混合物を、単一の振動式供給装置を使用して20mmの押出し機に直接供給した。供給速度は、80%のトルクが達成されるように調節された。
Claims (8)
- a) フェノール性化合物およびその誘導体、ヒンダードアミンおよびその誘導体、ヒドロキシルアミンおよびその誘導体、チオエステル化合物およびその誘導体、ヒンダードフェノール性化合物およびその誘導体、ラクトンおよびその誘導体、ならびにそれらの混合物からなる群から選択される抗酸化剤、および
b) ニトレンを生成し得る基およびカルベンを生成し得る基およびこれらの混合物からなる群から選択される修飾剤
を含む分子溶融物。 - 修飾剤が、スルホニルアジド、ホスファゼンアジド、シリルアジド、ホルミルアジド、アジド、N−クロロスルホンアミドの塩、N,N−ジクロロスルホンアミド、2−トリアルキル−1−スルホニルヒドラジド、ジアゾアルカン、ケテン、メタロカルベン、およびそれらの混合物からなる群から選択される、請求項1に記載の分子溶融物。
- 修飾剤がスルホニルアジドを含む、請求項1に記載の分子溶融物。
- 抗酸化剤がフェノール性化合物を含む、請求項1に記載の分子溶融物。
- 抗酸化剤がヒンダードフェノール性化合物を含む、請求項1に記載の分子溶融物。
- 抗酸化剤がテトラキス[メチレン(3,5−ジ−t−ブチル−4−ヒドロキシヒドロシンナメート)]またはその誘導体である、請求項1に記載の分子溶融物。
- 修飾剤が、前記ニトレンを生成し得る基、カルベンを生成し得る基およびそれらの混合物からなる群から選択される基に加え、アミド、イミド、エポキシ、エステル、ヒドロキシ基、アミノ基およびこれらの混合物からなる群から選択される官能基を含有する、請求項1に記載の分子溶融物。
- 前記修飾剤が、ニトレンまたはカルベンを生成し得る1またはそれ以上のジェミナル置換されたメチレン基由来である、請求項1に記載の分子溶融物。