JP5025126B2 - 導電性フェノール樹脂複合材料、導電性フェノール樹脂複合材料の製造方法、導電性複合炭化材料、導電性樹脂組成物、二次電池用電極、電極用炭素材料、電気二重層キャパシタ分極性電極 - Google Patents
導電性フェノール樹脂複合材料、導電性フェノール樹脂複合材料の製造方法、導電性複合炭化材料、導電性樹脂組成物、二次電池用電極、電極用炭素材料、電気二重層キャパシタ分極性電極 Download PDFInfo
- Publication number
- JP5025126B2 JP5025126B2 JP2005353994A JP2005353994A JP5025126B2 JP 5025126 B2 JP5025126 B2 JP 5025126B2 JP 2005353994 A JP2005353994 A JP 2005353994A JP 2005353994 A JP2005353994 A JP 2005353994A JP 5025126 B2 JP5025126 B2 JP 5025126B2
- Authority
- JP
- Japan
- Prior art keywords
- conductive
- phenol resin
- composite material
- electrode
- resin composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
攪拌装置を備えた反応容器にフェノールを450質量部、37質量%のホルマリンを460質量部、ヘキサメチレンテトラミンを50質量部、分散剤としてアラビアゴムを4.5質量部、水を1300質量部仕込み、これを攪拌しながら60分を要して80℃にし、この温度で2時間、付加縮合反応を行なった。この後、平均直径150nm、平均長さ15μm、アスペクト比が100の気相法炭素繊維からなるカーボンナノファイバー(昭和電工株式会社製「VGCF−H」)を6質量部仕込み、そのまま30分間反応を継続させた。次に、内温が30℃になるまで冷却した後、反応容器の内容物をヌッチェで濾別した。
カーボンナノファイバーの代りに、カーボンブラック(ライオン(株)製「カーボンECP」、平均粒子径39nm)を18質量部用いるようにした他は、上記(製造例1)と同様にして未硬化の導電性フェノール樹脂複合材料を得た。
カーボンナノファイバーの代りに、黒鉛((株)エスイーシー製「SPG−3」、平均粒子径3μm)を31質量部用いるようにした他は、上記(製造例1)と同様にして未硬化の導電性フェノール樹脂複合材料を得た。
上記(製造例1)において、攪拌しながら60分を要して沸騰還流状態にし、この温度で2時間、付加縮合反応を行なうようにした他は、(製造例1)と同様にして球状粒子の導電性フェノール樹脂複合材料(フェノール樹脂は不溶不融状態に硬化)を得た。
カーボンナノファイバーの代りに、カーボンブラック(ライオン(株)製「カーボンECP」、平均粒子径39nm)を18質量部用いるようにした他は、上記(製造例4)と同様にして硬化した導電性フェノール樹脂複合材料を得た。
カーボンナノファイバーの代りに、黒鉛((株)エスイーシー製「SPG−3」、平均粒子径3μm)を31質量部用いるようにした他は、上記(製造例4)と同様にして硬化した導電性フェノール樹脂複合材料を得た。
粒径74μm以下に粉砕したレゾール型フェノール樹脂を990質量部とり、これにメタノールを加えてスラリー状にし、これにカーボンナノファイバー(昭和電工株式会社製「VGCF−H」)を10質量部加え、ニーダーで混合攪拌した。これを払い出して風乾し、メタノールを蒸発させた後、さらに45℃の乾燥器中で乾燥を行なった。そしてこれを直径212μm以下に粉砕することによって、粒状の導電性フェノール樹脂複合材料(フェノール樹脂は未硬化)を得た。
カーボンナノファイバの代りに、カーボンブラック(ライオン(株)製「カーボンECP」、平均粒子径39nm)を30質量部用いるようにした他は、上記(比較製造例1)と同様にして未硬化の導電性フェノール樹脂複合材料を得た。
カーボンナノファイバーの代りに、黒鉛((株)エスイーシー製「SPG−3」、平均粒子径3μm)を50質量部用いるようにした他は、上記(比較製造例1)と同様にして未硬化の導電性フェノール樹脂複合材料を得た。
比較製造例1で得た未硬化の導電性フェノール樹脂複合材料を80℃の乾燥機に48時間入れ、フェノール樹脂を不溶不融状態に硬化させ、硬化した粒状の導電性フェノール樹脂複合材料を得た。
比較製造例3で得た未硬化の導電性フェノール樹脂複合材料を80℃の乾燥機に48時間入れ、フェノール樹脂を不溶不融状態に硬化させ、硬化した粒状の導電性フェノール樹脂複合材料を得た。
比較製造例2で得た未硬化の導電性フェノール樹脂複合材料を80℃の乾燥機に48時間入れ、フェノール樹脂を不溶不融状態に硬化させ、硬化した粒状の導電性フェノール樹脂複合材料を得た。
*1:粒子の表面に隙間なく導電材料が存在している。
*2:粒子の表面に部分的に導電材料が存在している。
*3:粒子の表面に殆ど導電材料が存在していない。
疎充填かさ密度(g/cm3)
=(試料の重量:g)/(試料容器の容量:100cm3)
また、製造例1〜3及び比較製造例1〜3で得た球状あるいは粒状の導電性フェノール樹脂複合材料について、成形の際の流れの測定をした。流れの測定は、試料量を10g、荷重を39.2kN、加圧時間を2分に設定して、JIS K 6911「成形材料(円板式流れ)」に準拠して行なった。上記の各結果を表1に示す。
上記の製造例1〜3及び比較製造例1〜3で得た未硬化の導電性フェノール樹脂複合材料を用い、これらの導電性フェノール樹脂複合材料を予め160℃に加熱した金型に充填し、約15MPaの面圧で加圧しながら3分間加熱して成形することによって、樹脂成形体を得た。そしてこの樹脂成形体を試験片として、曲げ強さ、抵抗率を測定した。
上記の製造例4〜6及び比較製造例4〜6で得た硬化した導電性フェノール樹脂複合材料を40質量部、ポリフェニレンエーテル樹脂(三菱エンジニアリングプラスチック(株)製「ユピエースAH8」)を60質量部とり、これをドライブレンドした後、ラボテストミルを用いて320℃で均一に溶融混練した。そしてこれを冷却して固化させた後、粉砕することによって、樹脂組成物を得た。
上記(製造例1)で得た未硬化の導電性フェノール樹脂複合材料を、ステンレスバットに敷いたポリエチレンシートの上に広げ、これを100℃の乾燥機に入れて5時間加熱することによって、不溶不融性に硬化させた。そしてこの硬化した導電性フェノール樹脂複合材料を窒素雰囲気下、100℃/hの昇温速度で1000℃まで昇温し、1000℃で3時間熱処理することによって焼成し、導電性複合炭化材料の球状粒子を得た。
上記(製造例2)で得た未硬化の導電性フェノール樹脂複合材料を用いるようにした他は、(製造例7)と同様にして導電性複合炭化材料を得た。
上記(製造例3)で得た未硬化の導電性フェノール樹脂複合材料を用いるようにした他は、(製造例7)と同様にして導電性複合炭化材料を得た。
上記(比較製造例1)で得た未硬化の導電性フェノール樹脂複合材料を用いるようにした他は、(製造例7)と同様にして導電性複合炭化材料を得た。
上記(比較製造例2)で得た未硬化の導電性フェノール樹脂複合材料を用いるようにした他は、(製造例7)と同様にして導電性複合炭化材料を得た。
上記(比較製造例3)で得た未硬化の導電性フェノール樹脂複合材料を用いるようにした他は、(製造例7)と同様にして導電性複合炭化材料を得た。
上記の製造例7〜9及び比較製造例7〜9で得た導電性複合炭化材料を40質量部、ポリフェニレンエーテル樹脂(三菱エンジニアリングプラスチック(株)製「ユピエースAH8」)を60質量部とり、これをドライブレンドした後、ラボテストミルを用いて320℃で均一に溶融混練した。そしてこれを冷却して固化させた後、粉砕することによって、樹脂組成物を得た。
製造例7〜8及び比較製造例7〜8で得た導電性複合炭化材料3gに、ポリビニリデンフルオライドをN−メチルピロリドンに10質量%溶解させて調製したバインダー3gを加え、これを混合してスラリー状にした。そしてこのスラリーを厚さ20μm、直径12mmの円形の銅箔に塗布し、130℃で10時間真空乾燥した後、減圧下でプレス成形して電極を作製した。
製造例7〜8及び比較製造例7〜8で得た導電性複合炭化材料を、水蒸気流量5ml、窒素流量2l/分の流速で流通されるロータリーキルン炉の混合ガス雰囲気下、850℃で2時間処理して賦活し、活性炭を得た。得られた活性炭のヨウ素吸着性能、充填密度をJIS K 1474に準拠して測定した。結果を表6に示す。
2 導電層
3 フェノール樹脂炭化物
Claims (13)
- フェノール樹脂の球状粒子の表層に、黒鉛、カーボンブラック、炭化珪素、メソフェースカーボン、コークス、木炭、炭素繊維、炭化ホウ素から少なくとも一つ選ばれる導電性材料からなる導電層が形成されて成ることを特徴とする導電性フェノール樹脂複合材料。
- フェノール樹脂の球状粒子に対して0.01質量%以上の質量比率で導電性材料の導電層が形成されていることを特徴とする請求項1に記載の導電性フェノール樹脂複合材料。
- 導電性材料は、フェノール樹脂の球状粒子の1/5以下の平均粒子径であることを特徴とする請求項1又は2に記載の導電性フェノール樹脂複合材料。
- フェノール類とアルデヒド類とを、分散剤と混合しつつ、反応触媒の存在下で付加縮合反応させると共に、黒鉛、カーボンブラック、炭化珪素、メソフェースカーボン、コークス、木炭、炭素繊維、炭化ホウ素から少なくとも一つ選ばれる導電性材料をこの付加縮合反応の途中でフェノール類とアルデヒド類の反応系に投入することによって、フェノール樹脂の球状粒子を調製すると共にフェノール樹脂の球状粒子の表層に導電性材料からなる導電層を形成することを特徴とする導電性フェノール樹脂複合材料の製造方法。
- 導電性材料を複数回に分けて反応系に投入することを特徴とする請求項4に記載の導電性フェノール樹脂複合材料の製造方法。
- 付加縮合反応を、調製されるフェノール樹脂の球状粒子が熱硬化性を有する状態で停止することを特徴とする請求項4又は5に記載の導電性フェノール樹脂複合材料の製造方法。
- 付加縮合反応を、調製されるフェノール樹脂の球状粒子が不溶不融状態になるまで継続した後に停止することを特徴とする請求項4又は5に記載の導電性フェノール樹脂複合材料の製造方法。
- 請求項1乃至3のいずれかに記載の導電性フェノール樹脂複合材料のフェノール樹脂が、非酸化性雰囲気下で熱処理して炭化されたものであることを特徴とする導電性複合炭化材料。
- 請求項8に記載の導電性複合炭化材料を導電性フィラーとして樹脂に配合して成ることを特徴とする導電性樹脂組成物。
- 請求項8に記載の導電性複合炭化材料を電極用炭素材料として用いて形成されたことを特徴とする二次電池用電極。
- 請求項8に記載の導電性複合炭化材料を賦活処理して成ることを特徴とする電極用炭素材料。
- 請求項8に記載の導電性複合炭化材料を電極用炭素材料として用いて形成されたことを特徴とする電気二重層キャパシタ分極性電極。
- 請求項11に記載の電極用炭素材料を用いて形成されたことを特徴とする電気二重層キャパシタ分極性電極。