JP4895279B2 - 導電性ローラの製造方法及び画像形成装置 - Google Patents
導電性ローラの製造方法及び画像形成装置 Download PDFInfo
- Publication number
- JP4895279B2 JP4895279B2 JP2006271609A JP2006271609A JP4895279B2 JP 4895279 B2 JP4895279 B2 JP 4895279B2 JP 2006271609 A JP2006271609 A JP 2006271609A JP 2006271609 A JP2006271609 A JP 2006271609A JP 4895279 B2 JP4895279 B2 JP 4895279B2
- Authority
- JP
- Japan
- Prior art keywords
- roller
- conductive roller
- elastic layer
- developer
- conductive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
請求項1は、軸体とその軸体の外周にシリコーンゴム組成物の硬化により形成された弾性層とを備え、前記弾性層中の重合度170〜2700の範囲内にあるシロキサンオリゴマー含有量が0.5質量%以下で、かつ前記弾性層中の重合度170未満のシロキサンオリゴマー含有量が1.5〜8質量%である導電性ローラを製造する導電性ローラの製造方法であって、前記軸体の外周に前記シリコーンゴム組成物を成形し、前記シリコーンゴム組成物を160℃以上200℃未満で二次加熱することを特徴とする導電性ローラの製造方法であり、
請求項2は、前記二次加熱は160℃以上180℃以下で実施される前記請求項1に記載の導電性ローラの製造方法であり、
請求項3は、前記二次加熱は1〜24時間にわたって実施される前記請求項1又は2に記載の導電性ローラの製造方法であり、
請求項4は、前記導電性ローラはアスカーF硬度が40〜80の前記弾性層を備えたトナー供給ローラである前記請求項1〜3のいずれか一項に記載の導電性ローラの製造方法であり、
請求項5は、前記導電性ローラはJIS A硬度が20〜70の前記弾性層を備えた現像ローラである前記請求項1〜3のいずれか一項に記載の導電性ローラの製造方法であり、
請求項6は、前記請求項1〜5のいずれか一項に記載の導電性ローラの製造方法で製造された導電性ローラを備えて成る画像形成装置である。
R1 bHcSiO(4-b-c)/2 (1)
但し、式(1)において、R1は炭素数1〜10の置換又は非置換の一価炭化水素基である。また、bは0.7〜2.1、cは0.001〜1.0で、かつb+cは0.8〜3.0を満足する正数である。
導電性の棒状体である硫黄快削鋼に無電解ニッケルメッキを施した直径6mm、長さ250mmのシャフトを設け、その外周面にシリコーン系プライマーNo.101A/B(商品名、信越化学工業株式会社製)を塗布した。
次いで、ギヤオーブン中で150℃、10分間焼き付けて導電性ローラ用の芯金すなわち軸体を得た。
シリコ−ンゴムコンパウンド「KE551U」(商品名、信越化学工業株式会社)40質量部、シリコ−ンゴムコンパウンド「KE3502U」(商品名、信越化学工業株式会社)50質量部、シリコーン生ゴム「KE76VBS」10質量部、カーボンブラック(商品名「アサヒサーマル」、旭カーボン株式会社製)10質量部、有機発泡剤KEP−13(商品名、信越化学工業株式会社)5質量部、有機過酸化物架橋剤C−3(商品名、信越化学工業株式会社)3質量部、塩化白金酸触媒C−25A(商品名、信越化学工業株式会社)2質量部、架橋剤としてC−25B(商品名、信越化学工業株式会社)2質量部を配合し、二本ロールを使用して混合することによりシリコーンゴム配合物を調製した。得られたシリコーンゴム配合物を押出し機で前記軸体と一体で押出し、所定の外径のゴムローラを得た。
二次加熱の条件を180℃のオーブンにて7時間に変更した以外は、実施例1と同様にし、導電性ローラIIを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、アスカーF硬度、電気抵抗値を測定した。結果を表1に示す。
二次加熱の条件を180℃のオーブンにて13時間に変更した以外は、実施例1と同様にし、導電性ローラIIIを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、アスカーF硬度、電気抵抗値を測定した。結果を表1に示す。
二次加熱の条件を180℃のオーブンにて24時間に変更した以外は、実施例1と同様にし、導電性ローラIVを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、アスカーF硬度、電気抵抗値を測定した。結果を表1に示す。
二次加熱の条件を160℃のオーブンにて24時間に変更した以外は、実施例1と同様にし、導電性ローラVを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、アスカーF硬度、電気抵抗値を測定した。結果を表1に示す。
有機発泡剤KEP−13(商品名、信越化学工業株式会社製)12質量部に変更した以外は、実施例2と同様にし、導電性ローラVIを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、アスカーF硬度、電気抵抗値を測定した。結果を表1に示す。
有機発泡剤KEP−13(商品名、信越化学工業株式会社製)2.5質量部に変更した以外は、実施例2と同様にし、導電性ローラVIIを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、アスカーF硬度、電気抵抗値を測定した。結果を表1に示す。
有機発泡剤KEP−13(商品名、信越化学工業株式会社製)2.5質量部、二次加熱の条件を160℃のオーブンにて4時間に変更した以外は、実施例1と同様にし、導電性ローラVIIIを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、アスカーF硬度、電気抵抗値を測定した。結果を表1に示す。
有機発泡剤KEP−13(商品名、信越化学工業株式会社製)15質量部に変更した以外は、実施例1と同様にし、導電性ローラIXを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、アスカーF硬度、電気抵抗値を測定した。結果を表1に示す。
(実施例10)
この例では、現像ローラに使用される未発泡タイプの導電性ローラを作成した。
メチルビニルシリコーン生ゴム(商品名「KE−78VBS」、信越化学工業株式会社製)100質量部、ジメチルシリコーン生ゴム(商品名「KE−76VBS」、信越化学工業株式会社製)20質量部、カーボンブラック(商品名「アサヒサーマル」、旭カーボン株式会社製)10質量部、煙霧質シリカ系充填材(商品名「AEROSIL OX−50」、平均一次粒径40nm、嵩密度0.13g/cm3、日本アエロジル株式会社製)15質量部、白金触媒(商品名「C−19A」、信越化学工業株式会社製)0.5質量部、ハイドロジェンポリシロキサン(商品名「C−19B」、信越化学工業株式会社製)2質量部を配合し、加圧ニーダーで混練して、付加硬化型導電性シリコーンゴム組成物を調製した。
二次加熱の条件を200℃のオーブンにて7時間に変更した以外は、実施例1と同様にし、導電性ローラXIを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、アスカーF硬度、電気抵抗値を測定した。結果を表1に示す。
二次加熱の条件を225℃のオーブンにて4時間に変更した以外は、実施例1と同様にし、導電性ローラXIIを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、アスカーF硬度、電気抵抗値を測定した。結果を表1に示す。
二次加熱の条件を225℃のオーブンにて7時間に変更した以外は、実施例1と同様にし、導電性ローラXIIIを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、アスカーF硬度、電気抵抗値を測定した。結果を表1に示す。
二次加熱の条件を225℃のオーブンにて7時間に変更した以外は、実施例10と同様にし、導電性ローラXIVを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、JIS A硬度、電気抵抗値を測定した。結果を表2に示す。
(比較例5)
煙霧質シリカ系充填材(商品名「AEROSIL OX−50」、平均一次粒径40nm、嵩密度0.13g/cm3、日本アエロジル株式会社製)を5質量部に変更した以外は、実施例10と同様にし、導電性ローラXVを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、JIS A硬度、電気抵抗値を測定した。結果を表2に示す。
(比較例6)
煙霧質シリカ系充填材(商品名「AEROSIL OX−50」、平均一次粒径40nm、嵩密度0.13g/cm3、日本アエロジル株式会社製)を25質量部に変更した以外は、実施例10と同様にし、導電性ローラXVIを得た。続いて、前述した測定方法により、シロキサンオリゴマー含有量、JIS A硬度、電気抵抗値を測定した。結果を表2に示す。
前記導電性ローラI〜IX、XI〜XIIIをトナー供給ローラとして、非磁性一成分電子写真方式のプリンター(MicroLine9500PS 株式会社沖データ製)の現像器に配置し、48℃、55RH%の環境下で2週間放置した。その後、室温に戻して、黒ベタ印字、白ベタ印字を実施した。更に、印字率1%の横線パターンでA4用紙5000枚を連続印刷し、白ベタ印字、黒ベタ印字の順で印字を行い、印刷時のカスレ、汚れの発生を目視で確認した。
(印字評価:白スジ)
前記導電性ローラX、XIV〜XVIを現像ローラとして、非磁性一成分電子写真方式のプリンター(MicroLine9500PS 株式会社沖データ製)の現像器に配置し、48℃、55RH%の環境下で2週間放置した。その後、室温に戻して、黒ベタ印字を実施した。
2 軸体
3 弾性層
30 画像形成装置
31 像担持体
32 帯電手段
33 露光手段
34 転写手段
35 定着手段
36 被転写体
37 クリーニング手段
40 現像手段
41 現像剤収納部
42 現像剤
43 トナー供給ローラ
44 現像ローラ
45 現像剤規制部材
50 筐体
52 開口
53 定着ローラ
54 無端ベルト支持ローラ
55 無端ベルト
56 加圧ローラ
Claims (6)
- 軸体とその軸体の外周にシリコーンゴム組成物の硬化により形成された弾性層とを備え、前記弾性層中の重合度170〜2700の範囲内にあるシロキサンオリゴマー含有量が0.5質量%以下で、かつ前記弾性層中の重合度170未満のシロキサンオリゴマー含有量が1.5〜8質量%である導電性ローラを製造する導電性ローラの製造方法であって、
前記軸体の外周に前記シリコーンゴム組成物を成形し、前記シリコーンゴム組成物を160℃以上200℃未満で二次加熱することを特徴とする導電性ローラの製造方法。 - 前記二次加熱は、160℃以上180℃以下で実施される前記請求項1に記載の導電性ローラの製造方法。
- 前記二次加熱は、1〜24時間にわたって実施される前記請求項1又は2に記載の導電性ローラの製造方法。
- 前記導電性ローラは、アスカーF硬度が40〜80の前記弾性層を備えたトナー供給ローラである前記請求項1〜3のいずれか一項に記載の導電性ローラの製造方法。
- 前記導電性ローラは、JIS A硬度が20〜70の前記弾性層を備えた現像ローラである前記請求項1〜3のいずれか一項に記載の導電性ローラの製造方法。
- 前記請求項1〜5のいずれか一項に記載の導電性ローラの製造方法で製造された導電性ローラを備えて成る画像形成装置。