JP4858857B2 - 白金を主触媒として空気中の有機化合物を分解し除去させる方法および光触媒物品および光触媒層の形成方法並びに光触媒体 - Google Patents
白金を主触媒として空気中の有機化合物を分解し除去させる方法および光触媒物品および光触媒層の形成方法並びに光触媒体 Download PDFInfo
- Publication number
- JP4858857B2 JP4858857B2 JP2007521186A JP2007521186A JP4858857B2 JP 4858857 B2 JP4858857 B2 JP 4858857B2 JP 2007521186 A JP2007521186 A JP 2007521186A JP 2007521186 A JP2007521186 A JP 2007521186A JP 4858857 B2 JP4858857 B2 JP 4858857B2
- Authority
- JP
- Japan
- Prior art keywords
- platinum
- photocatalyst
- superphotocatalyst
- supported
- air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
即ち、白金を主触媒とし光触媒物質を補助的触媒とすることで昼夜を問わずに空気中の有害な有機化合物などを除去することを可能とする新規な手法を提案しようとするものである。
また、光触媒物品に係り、特に、窓ガラスなどの基体表面に光触媒物品を簡易び塗布することができる光触媒物品に関する。
また、基体の上に付着した汚れや有害な有機物を紫外線等の光によって光触媒組成物を励起して分解除去する光触媒層の形成方法に関するものである。
さらに、プラスチック板やガラス板などの基体上に設けられ、この基体に付着した汚れや有害な有機物などを紫外線等の光により光触媒組成物を励起して分解除去する光触媒体に関するものである。
すなわち、従来、光触媒の室内の窓ガラスへの塗布は、浸漬、噴霧、スピンコーティング、ロール塗布、ドクタープレードなどの慣用の方法が行われ、光触媒膜を、光触媒塗料の塗布と加熱乾燥により、又は、(焼成せずに)バインダーを用いた塗布法により簡便に成膜する方法が開示されている(例えば、特許文献1参照)。
また、従来、基体の表面に付着した汚れや有害な有機物などを除去する方法として、光触媒組成物を利用して分解除去する方法が知られている。
この場合、汚れ等の有機物などの分解を行うためにはこの有機物などと光触媒組成物とが接した状態で、紫外線等の光を照射する必要があるため、光触媒組成物を最表面に露出させなければ効果を発揮しない。したがって、従来は光触媒組成物とバインダ剤とを含んだ表面塗布剤を、また、場合によっては、有機溶剤等を含有した液状の光触媒体を、基体上に直接塗布した後、バインダ剤等を拭き取ることによって光触媒組成物を最表面に露出させて光触媒層を形成させていた(特許文献2参照)。
自然光である太陽光には天気のよい日は窓ガラス内側間近で350〜1500μW/cm2の光源がある。しかし夜間は働かないため、光触媒反応を手段とするのでは浄化機能ができない欠点があった。
ただし、人工光で補助すればエネルギーが掛かり資源の無駄遣いである。
また、建物の外壁や道路のNOxその他汚れを落とす機能は、従来技術の二酸化チタンを利用する光触媒では光源に無理がある。
また、従来技術では、バインダー内に光触媒が含有されてバインダー表面に十分に光触媒が頭出し状態で塗布されていないので、バインダー量が多いときには有機物除去率の低下が見られるように、光触媒の効果が十分に発揮できないという問題点があった。
本発明は、上記問題点を除去するようにした光触媒物品を提供するものである。
さらに、従来技術では、光触媒層が形成される基体の表面に光触媒組成物の粒径に比べて大きな凹凸があったり、網戸のように孔が開いているような基体に表面塗布剤を塗布する場合、バインダ剤等を拭き取る際に基体の凹部や孔に光触媒組成物及びバインダ剤が溜まってしまい、最表面に光触媒組成物が十分に露出しないため、汚れ等の有機物などの分解除去を十分に行うことができないという問題があった。
本発明は、前記した問題を解決するためになされたものであり、基体の表面に光触媒組成物の粒径に比べて大きな凹凸があったり、基体に孔が開いているような場合であっても、光触媒組成物を最表面に十分に露出させて固着することができる光触媒層の形成方法を提供することを目的としている。
さらにまた、光触媒組成物は直径が6〜10ナノメートル程度の非常に小さな粒状の物質であり、バインダ剤や有機溶剤等と混合して基体上に塗布できるように液状にすると、多数の光触媒組成物の粒子同士が凝集して大きな粒子(以下、「二次粒子」という。)となってしまい、これらの二次粒子は基体上に局在化してしまうため、基体上の部位によっては光触媒組成物が塗布されず、汚れ等の有機物などを十分に分解して除去することができなかった。
本発明は、前記した問題を解決するためになされたものであり、二次粒子の形成を抑え、光触媒組成物の粒子を基体上に万遍なく分散させることができる光触媒体を提供することを目的としている。
つまり、光触媒の欠点を補い且つ白金の持っている吸着、分解の機能を十二分に発揮する方法で課題を解決できる。
具体的には以下の如くである。
(1) 白金を主触媒とし、光触媒物質である二酸化チタンを補助触媒とする技術的思想に基づいて、バインダーと白金と二酸化チタンを混合して基体に塗布し、二酸化チタンの含有量に対して0.05〜50%とする白金は光のないときでも常温で有機化合物を吸着し、吸着の際に白金は空気中の有機化合物を吸着、分解し、このまま放置すると数時間で分解された物質で白金が覆われてしまい触媒毒となり吸着、分解をしなくなるので、太陽光などのあたる昼間、光触媒により白金の表面に覆われた物質を酸化させて触媒毒を取り払い、触媒毒がなくなった白金は吸着分解能を回復し、昼間は光触媒反応を行う二酸化チタンと併用させて効果を発揮し夜間は白金で吸着分解をすることを特徴とする白金を主触媒として空気中の有機化合物を分解し除去させる方法。
(2) 白金は光がない夜間に空気中の有機化合物を分解、吸着し昼間は二酸化チタンが太陽光の390nm以下の波長の光を利用して光触媒反応を起こして白金の周りについた触媒毒を酸化させて除去することで、24時間有機化合物を分解除去できることを特徴とする(1)項に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
(3) 白金が主体とした光触媒なので以後、白金担持超光触媒と呼ぶところの、白金担持超光触媒はその機能を発揮させるためには、白金および二酸化チタンが空気と接触していなければならないし、加えて白金の粒子と二酸化チタンの粒子が程よく攪拌されて混ざって担持されなくてはならないので、塗布する際によく伸ばせるようバインダーとして珪藻土を微粉末20nmから100nmにしてバインダー補助材である植物油を加え、必要に応じて寒冷地にも使用できるように不凍液としてエチレングリコールを加え、さらに拡散材としてタウリン、カテキンを加えることを特徴とする(1)項に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
(4) 出来上がった白金担持超光触媒を樹脂製のへらを使用して、ガラスを清掃するよう5〜100nm程度に塗り伸ばし、次に不織布でできたタオル状の布で拭き取る作業によって白金担持二酸化チタンが空気と触れることができるようにしたことを特徴とする(1)項に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
(5) 室内の有機化合物を分解除去するに十分の紫外線量が室内で一番多く確保できる窓ガラスの室内側に塗布し、建築物に必要な塗布面積は床面積に対して換算するなら1/7以上を塗布面積にし、容積に対して換算するなら1立方メートルに対して0.08平方メートル以上を必要とすることを特徴とする(1)項に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
(6) 塗布されたガラスは透明になり、塗布したガラスは樹脂製のへらを使用して、ガラスを清掃するように5〜100nmレベルに塗りのばし、次に不織布でできたタオル状の布でふき取ることにより、塗布されたガラスを基体として塗布された白金担持超光触媒は10〜30nmで塗布することができるためガラスは透明になることを特徴とする(1)項に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
(7) 透明性が要求されない基体としての建物内外に使用するタイル又はコンクリートブロック材、外壁材等に塗布するときは吹きつける二種類の液として最初にバインダーを塗布して半渇きの間に白金担持超光触媒を付けることを特徴とする(1)項に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
(8) 建物内外に使用するタイル又はコンクリートブロック材、外壁材等を焼き付けて製品を製造する場合は、温度は400℃以下であれば白金担持超光触媒を焼付けしても性能は変化しないことを特徴とする(1)項に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
(9) 窒素化合物の分解を促進させるために、二酸化チタンの酸化熱や白金の酸化熱を利用して窒素化合物を酸化還元することができる酸化セリウムを白金担持超光触媒に加えてNOxの分解を促進させることを特徴とする(1)項に記載の白金を主触媒として空気中の有機化合物に加えて窒素化合物を分解させる方法。
(10) 白金担持超光触媒のため、空気中の有機化合物の吸着分解を白金側で行い、酸素の酸化還元を二酸化チタン側で行うため空気中のシックハウスの原因物質や花粉症の原因の花粉を分解、アトピー性皮膚炎、アトピー性喘息およびアトピー性鼻炎の原因であるダニの糞の分解速度が速くなることを特徴とする(1)項に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
(11) 白金担持超光触媒は撥水性であるため無機質の汚れがつきにくいことを特徴とする(1)項に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
また、前記した目的を達成するための本発明の請求項12の光触媒物品は、清掃用部材と、光触媒表面塗布剤を含浸した光触媒表面塗布部材と、拭取り用部材とを備えた光触媒物品であって、前記清掃用部材は、窓ガラスなどの基体表面を清掃するものであり、前記光触媒表面塗布部材は、前記基体表面を前記清掃用部材で清掃した後、前記基体表面に前記光触媒表面塗布剤を塗布するものであり、前記拭取り用部材は、前記基体表面に前記光触媒表面塗布剤を塗布した後、前記基体表面を拭き仕上げるものである。
また、請求項13記載の光触媒物品は、請求項12の光触媒物品において、清掃用部材、光触媒表面塗布部材、拭取り用部材は、それぞれ独立に密閉包装袋に内包され、前記光触媒表面塗布部材を内包する密閉包装袋は、光不透過性の部材で形成されているものである。
また、請求項14記載の光触媒物品は、請求項12又は請求項13記載の光触媒物品において、基体はガラスであり、清掃用部材、光触媒表面塗布部材及び拭取り用部材は、何れも、超極細化学繊維の多孔質不織布を用いるものである。
また、請求項15に係る手段は、基体に、少なくともバインダ剤と有機溶剤とを含有する光触媒下地剤を塗布して前記基体の上に光触媒下地層を形成し、この光触媒下地層に、少なくとも光触媒組成物と分散剤とを含有する表面塗布剤を塗布して前記光触媒下地層の上に光触媒層を形成する光触媒層の形成方法である。
請求項16に係る手段は、請求項15に記載の発明において、バインダ剤は、変性エポキシ樹脂または酸化珪素(SiO2)のいずれか一つを含有している光触媒層の形成方法である。
さらにまた、請求項17に係る手段は、少なくとも光触媒組成物と、バインダ剤と、油成分を含有するバインダ補助剤と、を含有してなる光触媒体において、分散剤を含有する構成の光触媒体である。
請求項18に係る手段は、0.1〜20質量%の光触媒組成物と、0.1〜20質量%のバインダ剤と、20〜70質量%の油成分を含有するバインダ補助剤と、0.01〜1質量%の分散剤と、を含有する構成の光触媒体である。
請求項19に係る手段は、0.1〜20質量%の光触媒組成物と、0.1〜20質量%のバインダ剤と、20〜70質量%の油成分を含有するバインダ補助剤と、0.1〜1質量%の研磨剤と、0.01〜1質量%の分散剤と、を含有する構成の光触媒体である。
請求項20に係る手段は、請求項17〜19に記載の光触媒体であって、分散剤は、アミノ酸を含有している構成の光触媒体である。
請求項21に係る手段は、請求項17〜20に記載の光触媒体であって、分散剤は、ショ糖脂肪酸エステルを含有している構成の光触媒体である。
請求項22に係る手段は、請求項17〜21に記載の光職媒体であって、分散剤は、ポリフェノール類を含有している構成の光職媒体である。
また、二酸化チタンが光触媒効果を発揮するには390nm以下の波長の光があれば足りるので、屋外から部屋に差し込む通常の太陽光を利用して24時間常に本発明効果が継続することが可能となる。
光触媒である二酸化チタンに従来のレベルを遥かに超える白金を担持させることによる白金主体の白金担持超光触媒とすることで、光がない状態でも長時間空気清浄効果が持続することが可能となる。
基体である透明窓ガラスなどの表面にヘラを使って5〜100nmの薄さに塗り延ばし、更に不織布などの布地で拭き取ることで十分な量の白金を担持させた二酸化チタンが有効に空気と接触して効率的な空気清浄機能が実現される。
塗布面積は床面積に対して換算するなら1/7以上を塗布面積にし、容積に対して換算するなら1立方メートルに対して0.08平方メートル以上とすることで、本発明による空気清浄効果が十分に発揮できることを確認した。
塗布された白金担持超光触媒を10〜30nmの薄さとすることで、基体である透明ガラスの透明性が確保されることを見出した。
透明性が要求されない基体としての建物内外に使用するタイル又はコンクリートブロック材、外壁材等に塗布するときは、吹きつける二種類の液として最初にバインダーを塗布して半渇きの間に白金担持超光触媒を付けることで、基体の特性に応じて最も効果的な塗布状態を実現できるようになった。
建物内外に使用するタイル又はコンクリートブロック材、外壁材等を焼き付けて製品を製造する場合は、温度は400℃以下であれば白金担持超触媒焼付けしても性能は変化しないことを見出し、このような基体に対する簡易な施工を実現した。
窒素化合物の分解を促進させるために、二酸化チタンの酸化熱や白金の酸化熱を利用して窒素化合物を酸化還元することができる酸化セリウムを白金担持超触媒に加えてNOxの分解を促進させることを見出し、多様な物質に対しての空気清浄化の可能性を示した。
白金担持超光触媒のため、空気中の有機化合物の吸着分解を白金側で行い、酸素の酸化還元を二酸化チタン側で行うため空気中のシックハウスの原因物質や花粉症の原因の花粉を分解、アトピー性皮膚炎、アトピー性喘息およびアトピー性鼻炎の原因であるダニの糞の分解速度が速くなるので、多くの症状に対して有効な発明である。
白金担持超光触媒は撥水性であるため無機質の汚れがつきにくいことを見出し、表面の汚れによる効果低下は起こり難いものとすることが可能となる。
請求項12記載の光触媒物品によれば、清掃用部材と、光触媒表面塗布剤を含浸した光触媒表面塗布部材と、拭取り用部材とを備えた光触媒物品であって、前記清掃用部材は、窓ガラスなどの基体表面を清掃するものであり、前記光触媒表面塗布部材は、前記基体表面を前記清掃用部材で清掃した後、前記基体表面に前記光触媒表面塗布剤を塗布するものであり、前記拭取り用部材は、前記基体表面に光触媒表面塗布剤を塗布した後、前記基体表面を拭き仕上げるものであるから、清掃用部材→光触媒表面塗布部材→拭取り用部材の簡易な使用手順で室内の窓ガラスなどの基体表面に頭出しされて光触媒組成物を固着させ、拭取り用部材で仕上げて、浮遊する有機物を分解する光触媒効果で室内の空気を清浄化することができる。
また、請求項13記載の光触媒物品によれば、前述した請求項12の発明の効果に加え、清掃用部材、光触媒表面塗布部材、拭取り用部材は、それぞれ独立に密閉包装袋に内包されているので、室内の窓ガラスなどの基体表面にスプレーなどの塗布器を使わずに、清掃用部材→光触媒表面塗布部材→拭取り用部材の使用手順で光触媒組成物を簡便に固着させることができ、しかも、光触媒表面塗布部材を内包する密閉容器は光不透過性の部材で形成されているため、光触媒表面塗布部材に含浸された光触媒表面塗布剤の劣化を防ぐことができる。
また、請求項14記載の光触媒物品によれば、前述した請求項12又は13記載の発明の効果に加え、清掃用部材、光触媒表面塗布部材及び拭取り用部材は、何れも、超極細化学繊維の多孔質不織布を用いるので、基体であるガラスの表面を傷つけることを防ぐことができる。
また、本発明による光触媒層の形成方法は、基体の上に光触媒下地層を形成し、この光触媒下地層の上に光触媒層を形成したため、基体の表面に光触媒組成物の粒径に比べて大きな凹凸があったり、基体に孔が開いているような場合であっても、光触媒組成物を最表面に露出させて固着することができ、光触媒組成物の効果を発揮させることが可能となる。
さらに、本発明においては、少なくとも光触媒体と、バインダ剤と、油成分を含有し、更に必要に応じてバインダ補助剤を含有する液状の光触媒体に分散剤を含有させているため、光触媒組成物の粒子同士が凝集し難く、二次粒子の形成を抑制して基体上での光触媒組成物の局在化を防止し、光触媒組成物の粒子を基体上に万遍なく分散させることが可能となる。
また、分散剤として、アミノ酸、ショ糖脂肪酸エステル、ポリフェノール類を光触媒体に含有させているため、光触媒体に含有している光触媒組成物の粒子の分散性を高めることが可能となる。
まず、有機化合物等を適切に分解除去して空気清浄効果を発揮させる上で、白金を主触媒とし、光触媒物質である二酸化チタンを補助触媒とする技術的思想について説明するが、これは、従来は、二酸化チタンなどの光触媒物質を利用して空気清浄を図る場合に、光触媒作用による酸化・還元反応を利用して空気中の有機化合物等を分解・除去するという発想に基づき多様な研究開発がなされてきていたところ、理論どおりの成果が容易には得られないことの原因究明が本発明のスタートとなっているものである。
すなわち、より効率的な空気清浄効果を光触媒物質により達成するために、光触媒層の形成方法や基体への有効な塗布状態を実現するための物品、分散剤により光触媒物質粒子を万遍なく分散させる手法などに関して鋭意研究開発が進んでいるが、なお理論どおりの成果が得られていない現状があったのである。
発明者は、このような現状の原因究明を行っている過程で、補助的機能を果たす助剤として極少量の白金を含有させた光触媒物質を利用する場合に、夜間のように外部からの光線が遮断された状態にあっても、なお一定の時間は空気清浄効果が繰り返し持続することに着目したのである。つまり、光触媒作用のみによって空気清浄効果が達成されているとすれば、光線が遮断された状態では効果が発揮されなくなる筈であるが、効果が持続するのは光触媒作用以外の原因がある筈であり、その究明を行ったのである。
ここで、発明者は、助剤として極微量含有させた白金にも触媒としての酸化還元作用があることに着目したが、白金は触媒として機能するとその表面が分解物質によって覆われてしまい、この表面の触媒毒(触媒機能を阻害する物質)を継続的に除去しないと有効な効果が持続しないという難点があった。
発明者は、この難点を克服するために検討を重ね、光触媒物質の酸化還元作用を応用した有機化合物等の分解除去機能によって白金表面の触媒毒物質を継続的に除去してやることで光線の有無に関わらず、昼夜を問わず空気清浄機能を長期間継続的に発揮し続けることを可能としたものである。
すなわち、発明者は、空気清浄化機能を果たす主たる触媒としては白金を用い、白金の表面の触媒毒を除去するために二酸化チタンなどの光触媒物質を補助的に利用するという新たな発想に到達し、本発明を完成したものである。
具体的に、白金を主触媒とするというのは、従来技術においては添加するとしても極めて少量しか添加しなかった白金を、その有機化合物等を分解除去して空気清浄化する機能を十分に果たさせるために、相当量を光触媒物質である二酸化チタンなどに万遍なく担持させるということであり、二酸化チタンの含有量に対して0.05〜50%とし、より好ましくは5〜30%とするものである。つまり、含有量として主たる量を占めるというのではなく、空気清浄化という機能を果たす上で主たる役割を果たすということを意味している。
図1は、本発明による白金担持光触媒を新築の部屋に新品の家具類を配置した状態の実験室の窓ガラスや壁部に塗布して、室内のホルムアルデヒド濃度を30分毎に測定しながら24時間以上経過せしめ、本発明による空気浄化機能の働きを実験した場合の結果の1例を示したグラフであり、昼夜を問わずホルムアルデヒド濃度が低く抑えられていることが理解される(なお、グラフは24時間経過時までの結果を示しているが、その後さらに実験を継続しても同様の効果を持続した結果を得られることが確認されている)。
グラフは、ホルムアルデヒドの発生量に関係する温度や湿度の条件と、光触媒物質の働きに関連する部屋内の紫外線量の変化を測定時間の変化によって示している。すなわち、実験室中のホルムアルデヒドは、部屋内の気温が上昇するとその蒸散が多くなるものであるから、外部からの太陽光の量が少なく、しかも、外部からの紫外線量が少ないが故に光触媒が機能し難い、曇りや雨の日の昼間に多く発生するものである。一方、二酸化チタンなどの光触媒物質は多くの太陽光が差し込み、紫外線量が多い晴れの日の昼間により多く働くものである。
以上を前提として図1の実験結果を解釈すると、午前中に実験室内のホルムアルデヒド濃度が幾らか上昇するのは、実験室内の気温上昇に起因するものと理解できる。また、実験室内の紫外線量が豊富な昼間にホルムアルデヒド濃度が一定値以下に抑えられるのは光触媒物質による空気浄化機能のためであると理解できる(気温等の他の条件による影響も当然に受けてはいるが)。さらに、夕方から夜にかけてホルムアルデヒド濃度が上昇するのは太陽光がなくなり紫外線が室内に入らなくなるので、光触媒作用が行われなくなるからであると理解できる。
しかし、上記した前提からのみ解釈すると、実験室中の紫外線量が著しく少なくなる夜間(19時以降から夜明け前にかけて)などには、ホルムアルデヒド濃度が明確に上昇する筈であるが、グラフに示した実験結果から判るように、逆にこのように紫外線量が絶対的に少ない環境であっても実験室内のホルムアルデヒド濃度は低く抑えられたままとなっている(ここでも、室温等の他の条件の影響があることは確かであるが)。
このような結果は、実験室中の空気を浄化するに足る量の白金を、二酸化チタン等の光触媒物質に適切に担持させているためであると考えられる。すなわち、白金を触媒とする空気浄化機能は室内の紫外線量による制限を受けるものではないから、夜間でも有効に機能していると考えられるのである。
さらに、本来なら空気中の有機化合物等の分解物質によってその表面を覆われてしまい触媒毒により空気浄化機能を喪失してしまう筈の白金が、理論的な予測を超えて継続的に何日間も機能し続けるのは、光触媒物質に適切な状態で担持されている白金は、その表面を覆った分解物質(触媒毒物質)を、光触媒作用を利用して排除することができているためと解釈される。
つまり、二酸化チタン等の光触媒物質は、紫外線を利用した光触媒作用によって適切に担持状態とされた白金表面の触媒毒物質を除去する役割を果たしているのである。例えば、夜間中などにその表面が吸着作用により触媒毒物質で覆われ、それにより空気浄化機能を果たしている白金も、翌日の日中に光触媒作用により表面の清浄化が行われ、その結果、次の夜間中などに再び空気浄化機能を果たせる状態に復帰することが可能となるのである。
すなわち、図1に示された結果から、本発明の白金担持光触媒を有効活用すると、太陽光などによる紫外線が豊富に存在する場合は勿論、夜間などのように光触媒作用が働かない時間帯においても、主触媒として二酸化チタンなどの光触媒物質に担持させた白金の触媒作用によって空気清浄化機能が継続し、しかも、日中の光触媒反応によって白金表面を覆ってしまった触媒毒物質の除去が適宜になされることから、長期間休み無く継続的に空気清浄化機能が働き続けるようになることが説明されるのである。
また、スギ花粉など所謂花粉症アレルギーの原因物質となる各種花粉については、従来の光触媒物質では十分な分解除去効果が期待できない実情があったが、本発明のように空気浄化機能を果たす主触媒として機能するに足る量の白金を担持させた場合(例えば、10%程度)、僅か数時間で各種の花粉類が完全に分解されて除去されることを確認することができている。
以下、本発明の光触媒物品の実施の形態を図面に基づいて説明する。
光触媒物品Aが塗布される基体(図示せず)は、ガラス(例えば、窓ガラス)、合成樹脂等である。基体の表面に光触媒組成物を固着させ、基体の裏面から紫外線が照射される場合(例えば、太陽光線が窓ガラスを介して進入する場合)は、紫外線透過の合成樹脂を使用し、基体の表面から紫外線を照射する場合は、紫外線透過の材料を用いる必要はない。
光触媒物品Aは、基体の表面を清掃するために汚れ除去剤を浸透させた多孔質不織布の清掃用部材4と、光触媒表面塗布剤(研磨剤、触媒組成物、バインダー剤、バインダー補助剤の混合物)を含浸(浸透)させた光触媒表面塗布部材5(光触媒表面塗布部材5は、例えば、多孔質不織布)と、前記基体表面に前記光触媒表面塗布剤を塗布した後、前記基体表面を拭き仕上げる拭取り用部材6(拭取り用部材6は、例えば、バインダー補助剤を拭取る。)とを備え、第1図に示すように、それぞれ独立に密着性開閉部1、1’、1”を有する密閉包装袋2、2’、2”に内包されている。なお、光触媒物品Aは、図示しない包装箱内に収納されている。
清掃用部材4を内在する密閉包装袋2は両端が圧着加工された圧着部9によって密閉され、光触媒組成物部材5を内在する密閉包装袋2’は両端が圧着加工された圧着部9’によって密閉され、拭取り用部材6を内在する密閉包装袋2”は両端が圧着加工された圧着部9”によって密閉されている。
そして、後述するが、清掃用部材4→光触媒表面塗布部材5→拭取り用部材6の使用手順で室内の窓ガラスなどの基体(図示せず)表面に光触媒組成物を頭出しさせて光触媒組成物を固着させて、仕上げ手段でバインダー補助剤の拭き残しがないように拭取り、浮遊する有機物を分解して室内の空気を清浄化する。
清掃用部材4は、基体(図示せず)表面を清掃するために汚れた除去剤(例えば、その成分が、エチルアルコールや界面活性剤、トコフェロール、イオン交換水、Lアスコルピン酸、クエン酸等を含有する液状の洗浄剤)を多孔質不織布に含浸(浸透)させてある。
汚れ除去剤が含浸(浸透)した基体表面の清掃用多孔質不織布の清掃用部材4で光触媒表面塗布剤を塗布する前に、例えば、室内の窓ガラス等の基体表面(塗布面)の汚れを、特に、ガラス表面の油分を除去する。
光触媒表面塗布部材5は、研磨剤、光触媒組成物、バインダー剤、バインダー補助剤の混合物を多孔質不織布に含浸(浸透)させたものである。
なお、上述した清掃用部材4又は光触媒表面塗布部材5は、それぞれの多孔質不織布の汚れ除去剤又は光触媒表面塗布剤内に浸してそれぞれ作成することができる。
バインダー補助剤を拭取るための多孔質不織布の拭取り用部材6は、上述した清掃用部材4及び光触媒組成物部材5は、含浸(浸透)させないでそのまま使用する。
なお、仕上げ手段としては、若干水分を有するウエスやタオル(好ましくは約40℃の湯を湿らせる、あるいは、タオルの長さ方向1/3部分に水を付け、残りの長さ方向2/3部分の渇いた部分にて濡らした部分を挟み付けて、この渇いた部分を両面の表部としたもの)などの仕上げ手段(図示せず)により、基体表面にバインダー補助剤の吹き残しのないように拭き取る。
清掃用部材4、光触媒表面塗布部材5及び拭き取り用部材6は、何れも、超極細化学繊維によるもので、超極細化学繊維であるので基体であるガラスなどの表面を傷つけることを防ぐことができる。
密閉包装袋2は、複数枚の清掃用部材4を密閉状態で内包するもので、その外観を第2図及び第3図に示す。そして、清掃用部材4は、適宜に多孔質不織布に折り目を施して、適宜に境目を形成して折り畳んで密閉包装袋2に内包する。
1は取り出し口21を開閉する密着性開閉部で、密着性開閉部1の裏面又は密着性開閉部1の裏面に対応する取り出し口21の周囲には再剥離性の接着剤が塗布されていて、取り出し口21を繰り返して蓋をすることにより密閉することができる。密閉することによって、密閉包装袋2内の清掃用部材4がカビ・雑菌によって汚染することを防ぐことができる(第2図、第2図、第5図及び第6図参照)。
密閉包装袋2’は、複数枚の光触媒表面塗布部材5を密閉状態で内包するもので、その外観は第1図及び第3図に示す。そして、光触媒表面塗布部材5は、適宜に多孔質不織布に折り目を施して、適宜に境目を形成して折り畳んで密閉包装袋2’に内包する。
1’は取り出し口21’を開閉する密着性開閉部で、密着性開閉部1’に裏面又は密着性開閉部1の裏面に対応する取り出し口21’の周囲には再剥離性の接着剤が塗布されていて、取り出し口21’を繰り返して蓋をすることにより密閉することができる。密閉することによって、密閉包装袋2’内の光触媒組成部材5がカビ・雑菌によって汚染することを防ぐことができる。なお、特に、光触媒組成物部材を内包する密閉包装袋2’は光不透過性の部材(例えば、アルミ蒸着シート)で形成されている。
光触媒表面塗布部材5に含浸(浸透)する光触媒表面塗布剤の光触媒組成は、酸化チタン、二酸化チタン、またはゾルゲル型チタン化合物、あるいは、酸化亜鉛、酸化錫、酸化鉄、酸化銅、酸化銀、酸化タングステン、酸化ジルコニウム、酸化ビスマス、酸化インジウム、酸化カドミウム、酸化ゲルマニウム、酸化ニッケル、酸化コバルト、酸化クロム、酸化マンガン、酸化バナジウム、酸化ニオブ、酸化アンチモン、チタン酸ストロンチウム等の金属酸化物が挙げられるが、二酸化チタンが好ましく、アナターゼ型二酸化チタン結晶、ルチル型二酸化チタン結晶又はそれらの混合物、あるいは、ゾルゲル型チタン化合物が好ましい。なお、光触媒表面塗布部材5による光触媒には、可視光領域で光触媒効果をしめすものも使用しても良い。
光触媒表面塗布部材5に含浸(浸透)する光触媒表面塗布剤の光触媒組成は、上述に限らず、光触媒粒子は光触媒粒子表面に金属または金属化合物の少なくとも1種が物理的または化学的に光触媒粒子表面に固定化しても良い(特開2000−96800号公報参照)。例えば、金、銀、銅、白金、鉄、コバルト、ニッケル、クロム、亜鉛などがあるが、このうち白金が最も好ましい。光触媒の表面に金属が担持されることにより、光触媒の電荷分離が促進されて、光触媒特性がより大きくなる。光触媒の表面に金属が担持又は金属の表面に光触媒が担持されている場合も光触媒組成物とする。なお、金属などの固定化量は光触媒組成物の全体量に対して、1重量%〜50重量%であることが好ましい。
また、0.1重量%〜30重量%の光触媒をエタノールなどの有機溶剤に入れて、充分攪拌してゾルゲル状にして、光触媒特性がより大きくする金属を添加して充分攪拌する。又は光触媒と光触媒特性がより大きくする金属を混ぜてエタノールなどの有機溶剤に入れて、充分攪拌してゾルゲル状にしても良い。
また、二酸化チタンの粒径は特に限定されないが、有機溶剤に溶解しやすい程度の6nm〜10nmの粒径であればよい。光触媒組成物を含有する有機溶剤の溶液中に含まれる光触媒組成物の濃度は、0.1重量%から80重量%とすることが望ましい。光触媒組成物の濃度が0.1重量%未満であると、光触媒による効果、即ち汚染物質の分解が弱くなり、好ましくない。
また、光触媒組成物の超微粒子溶液は、エチルアルコール、イソプロピレンアルコール、プチルアルコールなどの有機溶剤を30〜60%、硫酸・硝酸を1%以下を含む溶液、アナターゼ又はルチン型チタンアルコキシド結晶を1〜30%になるように混合して調整する二酸化チタンを含む酸性懸濁液である。
また、光触媒表面塗布部材5に含浸(浸透)する光触媒表面塗布剤の光触媒組成は、微粉末に形成されていて、その粒径は、6nm〜10nmであり、光触媒表面塗布剤の全体量に対して、0.1重量%から30重量%が含有される。10nm以上であると、後記するバインダー剤の溶液に溶け込みにくいと共に、塗布後の基体表面が白濁化されて透明性が大きく低下するという不都合を生ずるものである。
光触媒表面塗布剤は光触媒組成物、バインダー剤、バインダー補助剤と研磨剤から構成される。
また、光触媒組成物の前記した配合比率にあって、0.1重量%未満であると、有害物質(有機化合物)が還元酸化されず、充分な光触媒作用を発揮することができないものであり、30重量%以上であると、基体の表面の透明性が得られないという不都合を生ずるものである。
なお、光触媒組成物は、そぼPH(酸性かアルカリ性かを表示する単位)を、慣用の界面活性剤の添加により1〜6の値に調整して、酸性か弱酸性に維持させることによって、酸化されにくく、後記するバインダー補助剤に添加した油成分の品質劣化が避けられる。この調整にあって該PH値が、1未満であると、酸が強すぎて後記する油性成分が変質し、6以上であると、油性成分の品質維持が保てない。
前記したバインダー剤は、光触媒組成物を担持するためのバインダー作用をなすもので、例えば、シリコン系樹脂やアクリル系樹脂、フッ素系樹脂、エポキシ樹脂など適宜な組成物あるいは天然糊などが使用され、水やエチルアルコールなどの希釈液によって流動性が良好となる所定濃度の溶液状に形成される。その配合比率は、例えば、光触媒表面塗布剤の全体量に対して、0.1重量%〜20重量%に調整されるもので、希釈する場合、該希釈液:バインダー液との配合は、70重量%〜99.9重量%:30重量%〜0.1重量%程度の配合量とすることが好ましい。前記したバインダー補助剤は、光触媒組成物を基体の表面(塗布対象物)に対して、出来る限り薄く塗布させるためのものである。
このバインダー補助剤は、油成分を有するものであって、この油成分は、例えば、天然物由来のワックスやミネラルスピリット系溶剤、植物油などと、慣用の界面活性剤とで構成される。油成分として、このうち、天然物由来のワックスとしては、例えば、カルバナロウ、キャンデリラロウ、コメヌカロウ、オウリキュリロウ、サトウキビロウ、ホホバロウ、油糧種子ロウ、モクロウ、ウルシロウ、蜜蝋などがあり、少なくともこの群からの一種類を選べば良い。これら油成分は、撥水性を発揮し、塗布表面に艶が出て、合成樹脂を相溶する特性がある。
また、良好な塗膜物性を有し、耐アルカリ性、耐候性、速乾性を併せ持ち、かつ、スプレー、刷毛、ローラー等通常補修の際に用いられる塗装方法での塗装作業が良好で、しかも毒性の少ないミネラルスピリット系溶剤をバインダー補助剤の成分として使用する。前記したバインダー補助剤におけるミネラルスピリットは、例えば、ミネラルターペン、ホワイトスピリット、ミネラルシンナー、ペトロリウムスピリットなどがあり、少なくともこの群から一種類を選べばよい。更に、前記したバインダー補助剤における植物油は、不乾性油の性質があり、酸化・変質しにくい植物油は望ましい。すなわち、薄くよく延びる役割を発揮する素材であれば任意のものが選定し得るもので、例えば、椿油、オリーブ油、ゴマ油、大豆油、サフラワー油、菜種油または月見草油などであり、少なくともこの群から一種類を選べば良い。
また、この光触媒表面塗布剤には、必要に応じて、前記した植物油やワックス類の酸化に起因する変色などを防止する目的で、酸化防止剤を添加することがあるもので、例えば、チルヒドロキシトルエン、トコフェロール、フイチン酸等が用いられる。その他に、フェノール性物質、芳香族アミン、フェノチアジン、ジチオホスフェート、ジチオカルバメート、スルフィド、硫化オレフインなども使用できる。更に、植物油の酸化防止に対しては、L−アスコルビン酸脂肪酸エステルが、L−アスコルビン酸パルミチン酸エステル及び/又はL−アスコルビン酸ステアリン酸エステルなどが有効である。
また、食品添加物の酸化防止剤として、L−アスコルビン酸、L−アスコルビン酸ナトリウム(ビタミンC)、エチレンジアミン四酢酸Ca二Na、エチレンジアミン四酢酸二Na、エルソルビン酸、エルソルビン酸ナトリウム、グアヤク脂、クエン酸イソプロピル、ノルジヒドログアヤレチック酸、没食子酸プロピル、ジブチルヒドロキシトルエン(BHT)、dl−α−トコフェロール(ビタミンE)、ブチルヒデロキシアニソール(BHA)、ローズマリー抽出物質、エトキシキンなどと、食品添加物の防腐剤として、安息香酸、安息香酸ナトリウム、ソルビン酸、ソルビン酸カリウム、デビドロ酢酸ナトリウム、パラオキシ安息香酸イソブチル、パラオキシ安息香酸イソプロピル、パラオキシン安息香酸エチル、パラオキシン安息香酸ブチル、パラオキシン安息香酸プロピル、プロピオン酸、プロピオン酸ナトリウム、プロピオン酸カルシウムなどを利用しても良い。これらの酸化防止剤の中から少なくとも一種類のものを添加しても良い。
次に、本発明に関する光触媒表面塗布剤の基体表面への塗布方法および光触媒表面塗布剤を説明する。
光触媒組成物の超微粒子溶液と、バインダー剤と、油成分を含有するバインダー補助剤と研磨剤とを混合して液状の光触媒表面塗布剤を得て、この光触媒表面塗布剤を含浸(浸透)させた光触媒表面塗布部材5により基体の表面へ塗布して薄く引き延ばして光触媒層が基体の表面に形成させ、この光触媒組成物とバインダー剤とバインダー補助剤との層を、バインダー剤とバインダー補助剤との層に含まれる研磨剤と共に拭取り用部材6により除去して、バインダー補助剤の拭き残しがないように仕上げを行って、光触媒組成物を光触媒層の最外層表面に露出させるものである。
そして、前記した研磨剤は、シリカやセラミック等の素材により0.1ミクロン〜0.5ミクロン粒子に形成してあって、光触媒表面塗布剤へ添加して混合させる
該研磨剤の粒子が、0.1ミクロン未満であると、光触媒層の拭き取りに際して光触媒組成物およびバインダー剤が共に拭き取られて除去される不都合を生じ、0.5ミクロン以上であると、光触媒層全体がこの研磨剤により除去されてしまう不都合を生ずる。
この研磨剤の混合にあっては、バインダー剤やバインダー補助剤等へ添加させた後混合させてもよく、その配合比率にあっては、10重量%〜50重量%を配合混合させる。
研磨剤の添加量が、10重量%未満であると、光触媒表面塗布剤が基体面への塗布前に固化が進行してその塗布工程に不都合を来たし、50重量%以上であると、水溶化されすぎて、光触媒表面塗布部材5による塗布がしにくい。
なお、光触媒組成物およびバインダー剤、バインダー補助剤、研磨剤は、例えば、適宜な容器内において一度に添加して、エチルアルコールや水などの希釈液で所定濃度に希釈し、溶液化させることができるもので、それぞれの配合比率は、本実施の形態に示した配合範囲内において任意に選定し得る。
光触媒表面塗布剤の一例は下記のものが挙げられる。
光触媒表面と不在の一配合例(この配合比率に限定されないことは、勿論のことである。)
・光触媒組成物 …… 5重量%
・バインダー剤 …… 5重量%
・バインダー補助剤 …… 65重量%
・研磨剤 …… 25重量%
をそれぞれ添加して、万遍なく攪拌混合して、液状の光触媒表面塗布剤を得た。
図示しない包装箱(又は包装袋)から光触媒物品Aを取り出す(取り出した状態を図1に示す。)、密閉性開閉部1をはがして差し出し口21から清掃用部材4を、密閉性開閉部1’をはがして差し出し口21’から光触媒表面塗布部材5を、密閉性開閉部1”をはがして差し出し口21”から拭き取り用部材6をそれぞれ取り出す。
汚れ除去剤を浸透させた清掃用部材4で、例えば、室内の窓ガラスの基体表面を清掃して、研磨剤と触媒組成物とバインダー剤とバインダー補助剤の混合物を浸透させた光触媒表面塗布部材5で光触媒組成物を室内の窓ガラスの基体表面に頭出しで固着させ、光触媒組成物の頭出し固着に不要なバインダー補助剤を拭き取り用部材6と仕上げ手段で除去して、室内の窓ガラスなどの基体表面に光触媒組成物を固着させる。一連の操作で光触媒組成物は室内の窓ガラスの表面に透明に塗布される。光触媒組成物が塗布された状態は指先で軽く室内の窓ガラスを触っただけで、ざらざら感触で確認できる。
なお、上記の光触媒物品は、必ずしも白金担持光触媒に関するものではないが、白金担持光触媒を実際に使用する際に有用であることは明らかである。
本発明の光触媒層の形成方法についての実施の形態を、第8図に基づき説明する。
図において、1は基体、2は基体1の上に塗布された光触媒下地剤、3は光触媒下地剤2の上に塗布された表面塗布剤を示している。
基体1は、汚れ等の有機物などを分解除去する対象となるものであり、後記する光触媒組成物31を設ける担体となるものである。この基体1としては、例えば不織布、網戸、ロールカーテン、エアコンのフィルタ、樹脂板、建物の外壁材、テント、テント、コンクリートブロックなどが挙げられる。
光触媒下地剤2は、光触媒組成物31を固着するためのバインダ剤21を含むものであり、バインダ剤21と有機溶剤22とが所定の比率で混合され、例えば、バインダ剤21として0.1質量%〜10質量%の酸化珪素(SiO2)をエタノールなどの有機溶剤22に混合して液状にしたもの、あるいはバインダ剤21として0.1質量%〜10質量%の変性エポキシ樹脂を酢酸ブチル、シクロヘキサン、プロピレングリコールモノメチルエーテル、プロピレングリコールメチルエーテルアセテートなどを含有した有機溶剤22に混合して液状にしたものが用いられる。なお、光触媒下地剤2にはバインダ剤21をより分散させるために後記する分散剤32などを混合させてもよい。
表面塗布剤3は、汚れ等の有機物を分解する光触媒組成物31を含むものであり、0.1質量%〜20質量%の光触媒組成物31と0.01質量%〜1質量%の分散剤32をエタノールなどの有機溶剤33に混合して液状にしたものが用いられる。
前述の光触媒組成物3は、粒子として形成されており、酸化チタン、二酸化チタン、またはゾルゲル型チタン化合物、あるいは、酸化亜鉛、酸化錫、酸化鉄、酸化銅、酸化銀、酸化タングステン、酸化ジルコニウム、酸化ビスマス、酸化インジウム、酸化カドミウム、酸化ゲルマニウム、酸化ニッケル、酸化コバルト、酸化クロム、酸化マンガン、酸化バナジウム、酸化ニオブ、酸化アンチモン、チタン酸ストロンチウム等の金属酸化化合物が挙げられるが、二酸化チタンが好ましく、アナターゼ型二酸化チタン結晶、ルチル型二酸化チタン結晶又はそれらの混合物、あるいは、ゾルゲル型チタン化合物が好ましい。この光触媒組成物31の粒径は特に限定されないが、有機溶剤33に溶解しやすい程度の6ナノメートル〜10ナノメートルの粒径であればよい。粒径が6ナノメートル未満であると、加工が困難で、コストアップとなる不都合を生じ、粒径が10ナノメートル以上であると、有機溶剤33に溶け込みにくいと共に、塗布後の基体1の表面が白濁化されて透明性が大きく低下するためである。
前述の分散剤32は、光触媒組成物31等の粒子を分散させるものであり、例えばテアニン、リジン、グルタミン酸、アスパラギン酸、アルギニン、プロリンなどのアミノ酸、ショ糖ステファン酸エステル、ショ糖ステアリン酸エステル、ショ糖パルミチン酸エステルなどのショ糖脂肪酸エステル、カテキンなどのポリフェノール類が用いられるが、天然物を用いてもよく、例えばポリフェノール類のカテキンやアミノ酸のテアニンなどを成分に含む茶葉をお湯で抽出して得られる抽出液などを用いてもよい。
また、図示していないが、表面塗布剤3には、例えば、金、銀、銅、白金、鉄、コバルト、ニッケル、クロム、亜鉛などの金属または金属化合物を混合してもよい。この金属または金属化合物を混合することにより光触媒組成物31による電荷分離が促進されて、光触媒による有機物の分解特性がより高められるためである。
更に、図示していないが、表面塗布剤3には酸化セリウムを混合してもよい。酸化セリウムは、汚れ等の有機物などを熱により分解除去するものであり、光触媒組成物31の分解除去作用によって発生した有機物の分解に伴う反応熱(発熱)を有効に利用して、分解除去の効果を高めるためである。
次に、光触媒層30の形成方法について説明する。まず、第8図(a)に示したように、へら塗り法などの公知の技術を用いて前述の光触媒下地剤2を基体1上に塗布し、光触媒下地層20を形成する。この光触媒下地層20の厚さは光触媒組成物31や金属または金属化合物を固着できる程度であればよく、例えば乾燥後に約10ナノメートルの厚さとなるように形成される。
光触媒下地剤2の塗布後、有機溶剤22が徐々に蒸発し、光触媒下地剤2が生乾き状態で出来る限り乾燥する直前を見計らって、光触媒下地層20上にへら塗り法などの公知の技術を用いて前述の表面塗布剤3を塗布する(第8図(b)参照)。そして、残りの有機溶剤22および塗布した表面塗布剤3中の有機溶剤33を蒸発させて乾燥させることにより、光触媒組成物31を光触媒下地層20上に固着させることができる。
なお、前述の乾燥は常温で放置して乾燥させる自然乾燥又は温風などを当てて乾燥させる強制乾燥のどちらでもよい。
ところで、光触媒下地剤2が生乾きの状態で表面塗布剤3を塗布するのは光触媒組成物31を光触媒下地層20の上部にバインダ剤21により固着させるためであり、光触媒下地剤2中の有機溶剤22や表面塗布剤3中の有機溶剤33が蒸発して乾燥した後、第8図(c)に示したように光触媒組成物31を最表面に露出させることができる。
また、光触媒下地剤2のバインダ剤21として変性エポキシ樹脂を用いるのは基体1の表面の凹凸が比較的小さくても光触媒組成物31等の粒子を強固に固着できるためであり、バインダ剤21として酸化珪素(SiO2)を用いるのは有機溶剤22が乾燥し終わる前に光触媒組成物31等の粒子が光触媒下地層20内へ沈降して埋没するのを抑制するためである。なお、使用する光触媒下地剤2の種類は基体1の表面状態などに応じて適宜選択すればよい。
さらに、表面塗布剤3に分散剤32を混合したのは、光触媒組成物31等の粒子同士が凝集するのを防止するためであり、塗布前にあっては粒子が沈降しないため塗布直前に攪拌をする必要はなく、塗布後にあっては粒子の凝集による局在化を防いで光触媒下地層20上へ満遍なく固着し光触媒層30を形成することができる。
したがって、表面塗布剤3には従来のように光触媒組成物31を固着するためのバインダ剤21を含まないため、有機溶剤33が乾燥し終われば表面塗布剤3の塗布後に拭き取りを行わなくても最表面に光触媒組成物31が露出できると共に、分散剤を混合したことにより光触媒下地層20上に万遍なく固着させることができ、表面の平坦度が悪く凹凸が大きい基体や網戸のように孔が開いている基体であっても、基体の最表面に光触媒組成物31を露出させて光触媒層30を設けることができる。故に、汚れ等の有機物などが表面に付着した場合、光触媒組成物31に接し、この状態で紫外線等の光が照射されれば光触媒組成物31の励起により汚れ等の有機物などが分解して除去される。
なお、ここでの光触媒層の形成方法は必ずしも白金担持光触媒に関するものではないが、白金担持光触媒を実際に使用する場合にも当然に応用可能なものである。
また、本発明の光触媒体についての実施形態を、第9図〜第10図に基づき説明する。
第9図(A)においてA’は光触媒体であり、建物や自動車などの窓ガラス、プラスチック板あるいはソーラー部、室内における壁面などの基体1の上に塗布され、紫外線等の光の照射により、内部に含有されや光触媒組成物11aの光触媒作用によって、基体1aに付着した汚れや有害な有機物などを分解除去するものである。
この光触媒体A’は、光触媒組成物11aと、分散剤12aと、バインダ剤14aと、油成分を含有するバインダ補助剤15aとが所定の割合でエタノールなどの有機溶剤13aに混合され液状に調整されている。
前述の光触媒組成物11aは粒子状の物質であり、酸化チタン、二酸化チタン、またはゾルゲル型チタン化合物、あるいは、酸化亜鉛、酸化錫、酸化銀、酸化タングステン、酸化ジルコニウム、酸化ビスマス、酸化インジウム、酸化カドミウム、酸化ゲルマニウム、酸化ニッケル、酸化コバルト、酸化クロム、酸化マンガン、酸化バナジウム、酸化ニオブ、酸化アンチモン、チタン酸ストロンチウム等の金属酸化物が挙げられるが、二酸化チタンが好ましく、アナターゼ型二酸化チタン結晶、ルチル型二酸化チタン結晶又はそれらの混合物、あるいは、ゾルゲル型チタン化合物が好ましい。この光触媒組成物11aの粒径は特に限定されないが、有機溶剤13aに溶解しやすい程度の6ナノメートル〜10ナノメートルの粒径であればよい。なお、粒径が6ナノメートル未満であると、加工が困難で、コストアップとなるよいう不都合を生じ、粒径が10ナノメートルを超えると、有機溶剤13aに溶け込みにくいと共に、塗布後の基体1aの表面が白濁化されて透明性が大きく低下するためである。なお、光触媒組成物11aの配合比率は、光触媒体A’の全体量に対して、0.1質量%〜20質量%とするのが好ましい。0.1質量%未満であると汚れ等の有機物などが分解されず、十分な光触媒作用を発揮することができないためであり、20質量%を超えると、基体1aの表面の透明性が得られないという不都合を生ずるものである。
前述の分散剤12aは、光触媒組成物11a等の粒子を分散させるものであり、例えばテアニン、リジン、グルタミン酸、アスパラギン酸、アルギニン、プロリンなどのアミノ酸、ショ糖ステファン酸エステル、ショ糖ステアリン酸エステル、ショ糖パルチミン酸エステルなどのショ糖脂肪酸エステル、カテキンなどのポリフェノール類が用いられるが、天然物を用いてもよく、例えばポリフェノール類のカテキンやアミノ酸のテアニンなどを成分に含む茶葉をお湯で抽出して得られる抽出液などを用いてもよい。なお、分散剤12aの配合比率は、光触媒体A’の全体量に対して、0.01質量%〜1質量%とするのが好ましい。0.01質量%未満であると分散の効果が得られず、1質量%を超えると流動性が低下して塗布が難しくなるためである。
前述のバインダ剤14aは、光触媒組成物11aを基体1aの上に固着するものであり、例えば、シリコーン系樹脂やアクリル系樹脂、フッ素系樹脂、エポキシ系樹脂などの適宜な組成物、あるいは天然糊などが使用され、所定の濃度となるように光触媒体に混合される。なお、バインダ剤14aの配合比率は、光触媒体A’の全体量に対して、0.1質量%〜20質量%とするのが好ましい。0.1質量%未満であると光触媒組成物11aの粒子を十分に基体の上に固着することができず、20質量%を超えると溶液の流動性が低下して塗布し難くなるためである。
前述のバインダ補助剤15aは、光触媒組成物11aを基体1aの表面(塗布対象物)に対して、できる限り薄く塗布させるためのものである。このバインダ補助剤15は、油成分を有するものであって、この油成分は、例えば、天然植物由来のワックスやミネラルスピリット系溶剤、植物油などと、慣用の界面活性剤や水あるいはエタノールなどとで液状に項性されている。油成分として、このうち、天然植物由来のワックスとしては、例えば、ツバキ油、カルナバロウ、キャンデリラロウ、コメヌカロウ、オウリキュリロウ、サトウキビロウ、ホホバロウ、油糧種子ロウ、モクロウ、ウルシロウ、蜜蝋などがあり、少なくともこの群から一種類を選べばよい。これら油成分は、撥水性を発揮し、塗布表面に艶が出て、全体量に対して、20質量%〜70質量%とするのが好ましい。20質量%未満であると光触媒組成物11a等の粒子を含んだ米粒大の塊を生じ、70質量%を超えると光触媒体A’全体が固まって、塗布できない不都合を生じるためである。
ところで、図示していないが、光触媒体A’には、例えば、金、銀、銅、白金、鉄、コバルト、ニッケル、クロム、亜鉛などの金属または金属化合物を混合してもよい。この金属または金属化合物を混合することにより光触媒組成物11aによる電荷分離が促進され、光触媒による有機物などの分解特性がより高められるためである。
また、図示していないが、光触媒体A’には、酸化セリウムを混合してもよい。酸化セリウムは、汚れ等の有機物などを熱により分解除去するものであり、光触媒組成物11aの分解除去作用によって発生した有機物なこの分解に伴う反応熱(発熱)を有効に利用して、分解除去の効果を高めるためである。
更に、第10図(a)に示したように、前述した光触媒体A’には研磨剤16aを混合してもよい。この研磨剤16aは基体1a上に光触媒体A’を塗布した後、第10図(b)に示したように、最表面から光触媒組成物11aが露出できるように拭き取り手段2aに拭き取る際に余剰なバインダ剤14a等を掻き取る役目を果たすものである。
この研磨剤16aは、シリカやセラミック等の素材により粒径が30ナノメートル〜500ナノメートルの粒子状に形成してあって、光触媒体A’へ混合して調整される。研磨剤16aの粒子の粒径が、30ナノメートル未満であると、塗布層3aの拭き取りに際して光触媒組成物11aおよびバインダ剤14aが共に拭き取られて除去される不都合を生じ、500ナノメートルを超えると、拭き取り後においても光触媒体A’が厚く残ってしまい、最表面に露出する光触媒組成物11aの割合が少なくなってしまう不都合を生ずるためである。なお、研磨剤16aの配合比率は、光触媒体A’の全体量に対して、0.1質量%〜50質慮%とするのが好ましい。0.1質量%未満であると油成分が残ってしまって十分に拭き取れず、50質量%を超えると拭き取られた後に基体1a上に残存する光触媒組成物11aおよびバインダ剤14aが少なくなってしまう不都合を生じるためである。
次に、光触媒体A’を用いた基体1a上への形成方法について説明する。
あらかじめ、光触媒体A’の塗布の対象となる基体1aに対して、この基体1aの表面(塗布面)の汚れを、特に表面に付着した油分を、汚れ除去剤(例えば、その成分が、エチルアルコールや界面活性剤、トコフェノール、イオン交換水、Lアスコルビン酸、クエン酸等が含有する液状の洗浄剤)を散布して、ウエスなどにより十分に取り除いておく。
調整された光触媒体Aを、第9図(a)、第10図(b)に示すように、基体1aの表面全体へやヘラ塗り等の公知の技術により万遍なく塗布し、基体1aの表面に塗布層3aを形成させる。
次に、この塗布層3aが乾燥していない状態(まだ湿った状態が残存している状態)において、この基体1aの表面に塗布された光触媒体A’の塗布層3aに対して、第9図(b)、第10図(b)に示すように、拭き取り手段2aにより、例えば、バルキー繊維等のクロス布により拭き取りを行うと、この光触媒体A’における塗布層3aの表層部は、積層した光触媒組成物11aの粒子やバインダ剤14a、バインダ補助剤15aが取り除かれ、光触媒層4aが形成されて最表面に光触媒組成物11aが露出する。
ところで、本発明において、光触媒体A’に分散剤12aを混合したのは、塗布層3a中の光触媒組成物11a等の粒子を分散させ、基体1a上に満遍なく光触媒組成物11a等の粒子を塗り拡げるためであり、拭き取り手段2aにより拭き取った後でも光触媒層4a中の光触媒組成物11a等の粒子が凝集せずに基体1a上に満遍なく設けられるため、光触媒層4aを形成した基体1aの表面全体に渡って汚れ等の有機物などの分解除去効果を発揮することができる。
まず、(実施例)に記載の材料、配合比率で調合された光触媒体A’を用いて、表面を予め清浄にしたガラス板(基体1a)上に光触媒体A’を塗布した後、バルキー繊維のクロス布により拭き取りを行って光触媒層4aを形成した。また、比較のため、(実施例)のうち分散剤12aを含んでいない光触媒体を(比較例)として作製し、同様な方法で光触媒層4aを形成した。
(実施例)本発明の光触媒体A’の一配合例
・光触媒組成物11a………酸化チタン(TiO2)、5質量%
・バインダ剤14a……… シリコーン系樹脂、5質量%
・バインダ補助剤15a……ツバキ油溶液、50質量%
・分散剤12a……… テアニン、0.1質量%
・有機溶剤13a……… エタノール、残分
(比較例)
・光触媒組成物11a………酸化チタン(TiO2)、5質量%
・バインダ剤14a……… シリコーン系樹脂、5質量%
・バインダ補助剤15a……ツバキ油溶液、50質量%
・有機溶剤13a……… エタノール、残分
次に、(実施例)および(比較例)において、拭き取り後のガラス板(基体1a)上の光触媒組成物11aの固着状態を調べたところ、(比較例)においては光触媒組成物11aの粒子が数十層〜数千層に積層した二次粒子となってガラス板上に局在していたのに対し、(実施例)においては二次粒子の形成は見られず、個々の光触媒組成物11aの粒子が分散してガラス板の全面に渡って万遍なく固着していた。
なお、本発明の光触媒体A’における作用効果は、この(実施例)の材料、配合比率には限定されるものではなく、上記で詳述した他の材料、配合比率であっても同様の作用効果が得られた。
なお、ここでの光触媒体A’は、白金担持光触媒に関するものとは限らないが、白金担持光触媒の場合においても有意義に機能するものである。
これらの図面において、Aは、光触媒物品であり、4は、清掃用部材であり、5は、光触媒表面塗布部材であり、6は、拭取り用部材であり、1は、基体であり、2は、光触媒下地剤であり、20は、光触媒下地層であり、21は、バインダ剤であり、3は、表面塗布剤であり、30は、光触媒層であり、31は、光触媒組成物であり、32は、分散剤であり、A’は、光触媒体であり、1aは、基体であり、3aは、塗布層であり、4aは、光触媒層であり、11aは、光触媒組成物であり、12aは、分散剤であり、14aは、バインダ剤であり、15aは、バインダ補助剤であり、16aは、研磨剤である。
Claims (22)
- 白金を主触媒とし、光触媒物質である二酸化チタンを補助触媒とする技術的思想に基づいて、バインダーと白金と粒径6nm以上10nm未満の二酸化チタンを混合して基体に塗布し、二酸化チタンの含有量に対して5〜50%とする白金は光のないときでも常温で有機化合物を吸着し、吸着の際に白金は空気中の有機化合物を吸着し、分解し、このまま放置すると数時間で分解された物質で白金が覆われてしまい触媒毒となり吸着、分解をしなくなるので、太陽光などのあたる昼間、光触媒により白金の表面に覆われた物質を酸化させて触媒毒を取り払い、触媒毒がなくなった白金は吸着分解能を回復し、昼間は光触媒反応を行う二酸化チタンと併用させて効果を発揮し夜間は白金で吸着分解をするよう明暗を繰り返すことで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする白金を主触媒として空気中の有機化合物を分解し除去させる方法。
- 白金は光がない夜間に空気中の有機化合物を分解、吸着し昼間は二酸化チタンが太陽光の390nm以下の波長の光を利用して光触媒反応を起こして白金の周りについた触媒毒を酸化させて除去することで24時間有機化合物を分解除去できることで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
- 白金が主体とした光触媒なので、以後白金担持光触媒と呼ぶところの、白金担持超光触媒はその機能を発揮させるためには、白金および二酸化チタンが空気と接触していなければならないし、加えて白金の粒子と二酸化チタンの粒子が程よく攪拌されて混ざって担持されなくてはならないので、塗布する際によく伸ばせるようバインダーとして珪藻土を微粉末20nmから100nmにしてバインダー補助材である植物油を加え、必要に応じて寒冷地にも使用できるように不凍液としてエチレングリコールを加え、さらに拡散材としてタウリン、カテキンを加えることで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
- 出来上がった白金担持超光触媒を樹脂製のへらを使用して、ガラスを清掃するように5〜100nm程度に塗り伸ばし、次に不織布でできたタオル状の布で拭き取る作業によって白金担持二酸化チタンが空気と触れることができるようにしたことで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
- 室内の有機化合物を分解除去するに十分の紫外線量が室内で一番多く確保できる窓ガラスの室内側に塗布し、建築物に必要な塗布面積は床面積に対して換算するなら1/7以上を塗布面積にし、容積に対して換算するなら1立方メートルに対して0.08平方メートル以上を必要とすることで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
- 塗布されたガラスは透明になり、塗布したガラスは樹脂製のへらを使用して、ガラスを清掃するように5〜100nmレベルに塗り伸ばし、次に不織布でできたタオル状の布で拭く取ることにより、塗布されたガラスを基体として塗布された白金担持超光触媒は10〜30nmで塗布することができるためガラスは透明になることで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
- 透明性が要求されない基体としいの建物内外に使用するタイル又はコンクリートブロック材、外壁材等に塗布するときは吹きつける二種類の液として最初にバインダーを塗布して半渇きの間に白金担時超光触媒を付けることで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
- 建物内外に使用するタイル又はコンクリートブロック材、外壁材等を焼き付けて製品を製造する場合は、温度は400℃以下であれば白金担持超光触媒を焼付けしても性能は変化しないことで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
- 窒素化合物の分解を促進させるために、二酸化チタンの酸化熱や白金の酸化熱を利用して窒素化合物を酸化還元することができる酸化セリウムを白金担持超光触媒に加えてNOXの分解を促進させることで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物に加えて窒素化合物を分岐し除去させる方法。
- 白金担持超光触媒のため、空気中の有機化合物の吸着分解を白金側で行い、酸素の酸化還元を二酸化チタン側で行うための空気中のシックハウスの原因物質や花粉症の原因の花粉を分解し、アトピー性皮膚炎、アトピー性喘息およびアトピー性鼻炎の原因であるダニの糞の分解速度が速くなることで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物に加えて窒素化合物を分解し除去させる方法。
- 白金担持超光触媒は撥水性であるため無機質の汚れがつきにくいことで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法。
- 清掃用部材と、バインダーと粒径6nm以上10nm未満の二酸化チタンと二酸化チタンの含有量に対して5〜50%の白金とを含有する白金担持超光触媒表面塗布剤を含浸した白金担持超光触媒表面塗布部材と、拭取り用部材とを備えた白金担持超光触媒物品であって、
前記清掃用部材は、窓ガラスなどの基体表面を清掃するものであり、
前記白金担持超光触媒表面塗布部材は、前記基体表面を前記清掃用部材で清掃した後、前記基体表面に前記白金担持超光触媒表面塗布剤を塗布するものであり、
前記拭取り用部材は、前記基体表面に前記白金担持超光触媒表面塗布剤を塗布した後、前記基体表面を拭き仕上げるものであることで昼夜を問わず空気清浄機能を長期間継続的に発揮させることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法に使用するための白金担持超光触媒物品。 - 清掃用部材、白金担持超光触媒表面塗布部材、拭取り用部材は、それぞれ独立に密閉包装袋に内包され、前記白金担持超光触媒表面塗布部材を内包する密閉包装袋は、光不透過性の部材で形成されていることを特徴とする請求項12に記載の白金担持超光触媒物品。
- 基体はガラスであり、
清掃用部材、白金担持超光触媒表面塗布部材及び拭取り用部材は、何れも、超極細化学繊維の多孔質不織布を用いることを特徴とする請求項12又は13に記載の白金担持超光触媒物品。 - 基体に、少なくともバインダ剤と有機溶剤と粒径6nm以上10nm未満の二酸化チタンと二酸化チタンの含有量に対して5〜50%の白金とを含有する白金担持超光触媒下地剤を塗布して前記基体の上に白金担持超光触媒下地層を形成し、
この白金担持超光触媒下地層に、少なくとも白金担持超光触媒組成物と分散剤とを含有する表面塗布剤を塗布して前記白金担持超光触媒下地層の上に白金担持超光触媒層を形成することを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法に使用するための白金担持超光触媒層の形成方法。 - バインダ剤は、変性エポキシ樹脂または酸化珪素(SiO2)のいずれか一つを含有していることを特徴とする請求項15に記載の白金担持超光触媒層の形成方法。
- 少なくとも粒径6nm以上10nm未満の二酸化チタンと二酸化チタンの含有量に対して5〜50%の白金とを含有する白金担持超光触媒組成物と、バインダ剤と、油成分を含有するバインダ補助剤と、を含有してなる白金担持超光触媒体において、
分散剤を含有する構成であることを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法に使用するための白金担持超光触媒体。 - 0.1〜20質量%の、粒径6nm以上10nm未満の二酸化チタンと二酸化チタンの含有量に対して5〜50%の白金とを含有する白金担持超光触媒組成物と、
0.1〜20質量%のバインダ剤と、
20〜70質量%の有機溶剤を含有するバインダ補助剤と、
0.01〜1質量%の分散剤と、
を含有することを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法に使用するための白金担持超光触媒体。 - 0.1〜20質量%の、粒径6nm以上10nm未満の二酸化チタンと二酸化チタンの含有量に対して5〜50%の白金とを含有する白金担持超光触媒組成物と、
0.1〜20質量%のバインダ剤と、
20〜70質量%の油成分を含有するバインダ補助剤と、
0.1〜1質量%の研磨剤と、
0.01〜1質量%の分散剤と、
を含有することを特徴とする請求項1に記載の白金を主触媒として空気中の有機化合物を分解し除去させる方法に使用するための白金担持超光触媒体。 - 分散剤は、アミノ酸を含有していることを特徴とする請求項17〜19に記載の白金担持超光触媒体。
- 分散剤は、ショ糖脂肪酸エステルを含有していることを特徴とする請求項17〜20に記載の白金担持超光触媒体。
- 分散剤は、ポリフェノール類を含有していることを特徴とする請求項17〜21に記載の白金担持超光触媒体。