JP4701798B2 - 塩化物環境における耐候性に優れた表面処理鋼材 - Google Patents
塩化物環境における耐候性に優れた表面処理鋼材 Download PDFInfo
- Publication number
- JP4701798B2 JP4701798B2 JP2005107633A JP2005107633A JP4701798B2 JP 4701798 B2 JP4701798 B2 JP 4701798B2 JP 2005107633 A JP2005107633 A JP 2005107633A JP 2005107633 A JP2005107633 A JP 2005107633A JP 4701798 B2 JP4701798 B2 JP 4701798B2
- Authority
- JP
- Japan
- Prior art keywords
- ions
- feooh
- steel material
- anion
- rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
ここで、「生成定数」とは、生成という観点から見た平衡定数のことであり、特に錯体化学の分野でよく用いられる用語である。錯体形成反応の場合、金属イオンをM、配位子をLとした時、下記(2)式で示される錯体形成反応の平衡定数が生成定数となる。
この生成定数が大きいほど、(2)式の平衡反応は右方向(錯体形成方向)に進行する。従って、生成定数は、形成された錯体の安定度を表すことから、安定度定数と呼ばれることもある。
M+L=ML (a)
ML+L=ML2 (b)
・・・・・・・・・
MLn−1+L=MLn (n)
これら(a)〜(n)式の各反応の平衡定数(即ち、生成定数)は、
K1=[ML]/[M][L] (a)
K2=[ML2]/[ML][L] (b)
・・・・・・・・・
Kn=[MLn]/[MLn−1][L] (n)
となる。[ ]はそれぞれの成分のモル濃度(mol dm−3)である。
K1=[FeL]/[Fe][L] (4)
本発明では、上記(1)式に示したように、(4)式で求められるFe3+との生成定数K1の対数(logK1)が2.5より大きいアニオンLの化合物を使用する。
・前記Al 3+ イオンの含有量が0.5〜5質量%であり、
・前記有機樹脂は、表面処理剤の全固形分に基づいて10〜50質量%の量で含有される。
本発明によれば、鋼材の表面に上記表面処理剤から形成された乾燥膜厚5〜50μmの被膜を有する表面処理鋼材も提供される。この表面処理鋼材は、前記被膜が、その上層に形成された乾燥膜厚20〜1000μmの有機樹脂塗膜で被覆されていてもよい。
(1)β−FeOOHの生成反応時に、ある特定のアニオンが共存すると、対イオンであるカチオン種によらず、β−FeOOHが微細化するばかりか、β−FeOOHの生成量が低下する。この共存アニオンの量が増えると、β−FeOOHの生成が実質的に防止され、α−FeOOHが優先的に生成するようになる。
(3)アルミニウムイオン(Al3+)が共存すると、鋼材のさびは、Fe3−δO4(マグネタイト)からα−FeOOH主体のさびとなる。
4:10%<β−FeOOH量+Fe3−δO4量≦20%、
3:20%<β−FeOOH量+Fe3−δO4量≦30%、
2:30%<β−FeOOH量+Fe3−δO4量≦40%、
1:40%<β−FeOOH量+Fe3−δO4量≦50%
0:50%<β−FeOOH量
Claims (6)
- 全固形分に基づいて、硫酸アルミニウム、硝酸アルミニウムおよび/またはシュウ酸アルミニウムを供給源とするAl3+イオンを0.1〜5質量%、クエン酸イオン、酒石酸イオンおよび酢酸イオンからなる群から選ばれ、Fe3+イオンとの生成定数K1が下記(1)式を満たす1種または2種以上のアニオンを1〜40質量%、有機樹脂ならびに溶剤を含み、フッ素イオンおよびリン酸イオンを含まない、鋼材の表面処理剤。
2.5<logK1 (1) - 前記Al 3+ イオンの含有量が0.5〜5質量%である、請求項1に記載の表面処理剤。
- 前記有機樹脂が全固形分に基づいて10〜50質量%の量である、請求項1または2に記載の表面処理剤。
- さらに1種または2種以上の顔料を含有する、請求項1〜3のいずれかに記載の表面処理剤。
- 鋼材の表面に請求項1〜4のいずれかに記載の表面処理剤から形成された乾燥膜厚5〜50μmの被膜を有する表面処理鋼材。
- 前記被膜が乾燥膜厚20〜1000μmの有機樹脂塗膜で被覆されている、請求項5記載の表面処理鋼材。