JP4561989B2 - 熱圧着用複層ゴムシート - Google Patents
熱圧着用複層ゴムシート Download PDFInfo
- Publication number
- JP4561989B2 JP4561989B2 JP2005125011A JP2005125011A JP4561989B2 JP 4561989 B2 JP4561989 B2 JP 4561989B2 JP 2005125011 A JP2005125011 A JP 2005125011A JP 2005125011 A JP2005125011 A JP 2005125011A JP 4561989 B2 JP4561989 B2 JP 4561989B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- parts
- component
- thermocompression bonding
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
〔1〕 シリコーンゴム層の少なくとも一方の面に、フッ素系ゴム層が設けられた複層のゴム層からなる熱圧着用複層ゴムシートであって、シリコーンゴム層が、(A)平均重合度が200以上のオルガノポリシロキサン:100質量部、(B)カーボンブラック及び/又は微粉末シリカ系充填材:0〜150質量部、(C)金属、前記(B)成分中の微粉末シリカ以外の金属酸化物、金属窒化物及び金属炭化物から選択される少なくとも一種:0〜1,600質量部(但し、(B)成分と(C)成分の合計が10〜1,600質量部)、及び(D)硬化剤を含有してなるシリコーンゴム組成物を成形・硬化した層であり、フッ素系ゴム層が、(E)1分子中に少なくとも2個のアルケニル基を有し、かつ主鎖中にパーフルオロポリエーテル構造を有する直鎖状フルオロポリエーテル化合物、(F)1分子中にケイ素原子に結合した水素原子を少なくとも2個有する有機ケイ素化合物、及び(G)ヒドロシリル化反応触媒を含有してなるパーフルオロポリエーテル系ゴム組成物を成形・硬化した層であることを特徴とする熱圧着用複層ゴムシート。
〔2〕 (B)成分の配合量が、(A)成分100質量部に対して10〜120質量部である〔1〕の熱圧着用複層ゴムシート。
〔3〕 (C)成分の配合量が、(A)成分100質量部に対して10〜1,000質量部である〔1〕又は〔2〕の熱圧着用複層ゴムシート。
〔4〕 (E)成分が、下記一般式(2)で表される分岐を有するポリフルオロジアルケニル化合物である〔1〕〜〔3〕のいずれかの熱圧着用複層ゴムシート。
CH 2 =CH−(X) b −Rf−(X’) b −CH=CH 2 (2)
[式中、Xは−CH 2 −、−CH 2 O−、−CH 2 OCH 2 −又は−Y−NR 2 −CO−(Yは−CH 2 −又は下記構造式(Z)
で示されるo,m又はp−ジメチルシリルフェニレン基であり、R 2 は水素原子、メチル基、フェニル基又はアリル基である。)で表される基、X’は−CH 2 −、−OCH 2 −、−CH 2 OCH 2 −又は−CO−NR 2 −Y’−(Y’は−CH 2 −又は下記構造式(Z’)
で示されるo,m又はp−ジメチルシリルフェニレン基、R 2 は上記と同じである。)で表される基であり、Rfは二価のパーフルオロポリエーテル基であり、bは独立に0又は1である。]
〔5〕 (F)成分が、1分子中に1個以上のフッ素含有基を有するものである〔1〕〜〔4〕のいずれかの熱圧着用複層ゴムシート。
〔6〕 パーフルオロポリエーテル系ゴム組成物に、更にフィラーを(E)成分100質量部に対して5〜200質量部含有してなる〔1〕〜〔5〕のいずれかの熱圧着用複層ゴムシート。
(A)平均重合度が200以上のオルガノポリシロキサン、
(B)カーボンブラック及び/又は微粉末シリカ系充填材、
(C)金属、前記(B)成分中の微粉末シリカ以外の金属酸化物、金属窒化物及び金属炭化物から選択される少なくとも一種、
(D)硬化剤。
R1 aSiO(4-a)/2 (1)
(式中、R1は非置換もしくは置換一価炭化水素基であり、aは1.95〜2.05の正数である。)
ここで、上記シリコーンゴム組成物を硬化する際の硬化条件は適宜選定されるものであるが、加熱硬化条件としては、60〜200℃、特に80〜150℃で30秒〜60分間、特に1分〜30分間とすることが好ましい。
CH2=CH−(X)b−Rf−(X’)b−CH=CH2 (2)
[式中、Xは−CH2−、−CH2O−、−CH2OCH2−又は−Y−NR2−CO−(Yは−CH2−又は下記構造式(Z)
CgF2g+1−
(式中、gは1〜20、好ましくは2〜10の整数である。)
−CgF2g−
(式中、gは1〜20、好ましくは2〜10の整数である。)
ここで、上記フッ素系ゴム組成物を硬化する際の硬化条件は適宜選定されるものであるが、加熱硬化条件としては、通常100〜180℃、特に120〜150℃の温度で10秒〜30分程度、特に1〜5分程度とすることが好ましい。
ジメチルシロキサン単位99.85モル%及びメチルビニルシロキサン単位0.15モル%からなる、平均重合度が8,000のメチルビニルポリシロキサン100質量部、良熱伝導性充填剤として酸化アルミニウム粉末アルミナAL−45(昭和電工(株)製)400質量部、BET比表面積が200m2/gであるシリカ微粉末アエロジル200(日本アエロジル(株)製)30質量部、並びに下記式(4)で示されるα,ω−ジヒドロキシメチルポリシロキサン5質量部をニーダーを用いて均一に混練りし、150℃で2時間熱処理した。
ジメチルシロキサン単位99.85モル%及びメチルビニルシロキサン単位0.15モル%からなる、平均重合度が8,000のメチルビニルポリシロキサン100質量部、良熱伝導性充填剤として酸化アルミニウム粉末アルミナAL−45(昭和電工(株)製)400質量部、BET比表面積が200m2/gであるシリカ微粉末アエロジル200(日本アエロジル(株)製)30質量部、並びに上記式(4)で示されるα,ω−ジヒドロキシメチルポリシロキサン5質量部をニーダーを用いて均一に混練りし、150℃で2時間熱処理した。
ジメチルシロキサン単位99.85モル%及びメチルビニルシロキサン単位0.15モル%からなる、平均重合度が8,000のメチルビニルポリシロキサン100質量部に、平均粒径23nm、揮発分0.10質量%でBET比表面積が130m2/gのアセチレンブラック50質量部及びBET比表面積が120m2/gである疎水性シリカ(アエロジルR−972:商品名、Degussa社製)5質量部及びBET比表面積が140m2/gの酸化セリウム粉末0.5質量部を二本ロールで配合し、混練りして均一化した。
実施例3と同様にしてシリコーンゴム層を作製し、実施例2と同様にしてフッ素系ゴム層を作製し、本発明の熱圧着用複層ゴムシートを作製した。
実施例1と同様にして、厚さ0.2mmの第一のシリコーンゴム層を作製した。
更に、分子鎖両末端がビニルジメチルシリル基で封鎖された、平均重合度が180のジメチルポリシロキサン85質量部、分子鎖両末端がビニルジメチルシリル基で封鎖された、平均重合度が510のジメチルポリシロキサン10質量部及びジメチルシロキサン単位90.25モル%及びメチルビニルシロキサン単位9.75モル%からなる、平均重合度が8,000のメチルビニルポリシロキサン5質量部に、BET比表面積が約300m2/gである親水性シリカ(アエロジル300:日本アエロジル(株)製商品名)5質量部を加え、更にヘキサメチルジシラザン1質量部と水0.5質量部を加えたものをプラネタリーミキサー中で1時間、室温で混合した後、160℃、4時間加熱処理し、常温まで温度を下げた。
熱圧着用シートは、熱圧着時に異方導電性接着剤に直接接触する部分がある。そこで、この異方導電性接着剤に対しての接着性を見るため、実施例1〜4及び比較例1で作製した本発明の熱圧着用複層ゴムシート及び熱圧着用シリコーンゴムシートの下に、異方導電性接着剤から成る異方性導電膜を直接配し、その下に100μm厚のポリイミドフィルムを挟むように圧着機に設置し、320℃に加熱した加圧ツールを用い、4MPaの押し圧力で20秒間圧着した。被評価物である熱圧着用ゴムシートは、加圧ツール側には、実施例1〜4の場合シリコーンゴム層が、比較例1の場合第一のシリコーンゴム層が、異方性導電膜側には実施例1〜4の場合フッ素系ゴム層が、比較例1の場合第二のシリコーンゴム層が配置するようにセットした。1回の圧着終了後、異方性導電膜を新しい物に替え、熱圧着用ゴムシートはそのまま同じ物を使用してこの圧着を繰り返し、異方導電性接着剤が熱圧着用ゴムシートに接着するまでの回数を測定した。
Claims (6)
- シリコーンゴム層の少なくとも一方の面に、フッ素系ゴム層が設けられた複層のゴム層からなる熱圧着用複層ゴムシートであって、シリコーンゴム層が、(A)平均重合度が200以上のオルガノポリシロキサン:100質量部、(B)カーボンブラック及び/又は微粉末シリカ系充填材:0〜150質量部、(C)金属、前記(B)成分中の微粉末シリカ以外の金属酸化物、金属窒化物及び金属炭化物から選択される少なくとも一種:0〜1,600質量部(但し、(B)成分と(C)成分の合計が10〜1,600質量部)、及び(D)硬化剤を含有してなるシリコーンゴム組成物を成形・硬化した層であり、フッ素系ゴム層が、(E)1分子中に少なくとも2個のアルケニル基を有し、かつ主鎖中にパーフルオロポリエーテル構造を有する直鎖状フルオロポリエーテル化合物、(F)1分子中にケイ素原子に結合した水素原子を少なくとも2個有する有機ケイ素化合物、及び(G)ヒドロシリル化反応触媒を含有してなるパーフルオロポリエーテル系ゴム組成物を成形・硬化した層であることを特徴とする熱圧着用複層ゴムシート。
- (B)成分の配合量が、(A)成分100質量部に対して10〜120質量部である請求項1記載の熱圧着用複層ゴムシート。
- (C)成分の配合量が、(A)成分100質量部に対して10〜1,000質量部である請求項1又は2記載の熱圧着用複層ゴムシート。
- (E)成分が、下記一般式(2)で表される分岐を有するポリフルオロジアルケニル化合物である請求項1〜3のいずれか1項記載の熱圧着用複層ゴムシート。
CH 2 =CH−(X) b −Rf−(X’) b −CH=CH 2 (2)
[式中、Xは−CH 2 −、−CH 2 O−、−CH 2 OCH 2 −又は−Y−NR 2 −CO−(Yは−CH 2 −又は下記構造式(Z)
で示されるo,m又はp−ジメチルシリルフェニレン基であり、R 2 は水素原子、メチル基、フェニル基又はアリル基である。)で表される基、X’は−CH 2 −、−OCH 2 −、−CH 2 OCH 2 −又は−CO−NR 2 −Y’−(Y’は−CH 2 −又は下記構造式(Z’)
で示されるo,m又はp−ジメチルシリルフェニレン基、R 2 は上記と同じである。)で表される基であり、Rfは二価のパーフルオロポリエーテル基であり、bは独立に0又は1である。] - (F)成分が、1分子中に1個以上のフッ素含有基を有するものである請求項1〜4のいずれか1項記載の熱圧着用複層ゴムシート。
- パーフルオロポリエーテル系ゴム組成物に、更にフィラーを(E)成分100質量部に対して5〜200質量部含有してなる請求項1〜5のいずれか1項記載の熱圧着用複層ゴムシート。