JP2022186762A - 高いホウ素アルミノシリケートの組成の割には改善された低い熱膨張係数を有する、改善された低い誘電率の繊維を作製するための、MgO、ZnO、および希土類酸化物の使用 - Google Patents
高いホウ素アルミノシリケートの組成の割には改善された低い熱膨張係数を有する、改善された低い誘電率の繊維を作製するための、MgO、ZnO、および希土類酸化物の使用 Download PDFInfo
- Publication number
- JP2022186762A JP2022186762A JP2022163164A JP2022163164A JP2022186762A JP 2022186762 A JP2022186762 A JP 2022186762A JP 2022163164 A JP2022163164 A JP 2022163164A JP 2022163164 A JP2022163164 A JP 2022163164A JP 2022186762 A JP2022186762 A JP 2022186762A
- Authority
- JP
- Japan
- Prior art keywords
- weight percent
- glass
- present
- content
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本願は、米国仮特許出願第62/160,709号(2015年5月13日出願)に対する優先権を主張する。この米国仮特許出願は、その全体が本明細書中に参考として援用される。
本発明は、ガラス組成物およびその用途に関する。実施形態は、繊維を形成するためのガラス組成物、繊維および繊維を含む製造物品(例えば、プリント回路板)を含み、プリント回路板は、改善された電気性能および熱安定性を有する。
ガラス繊維は、長年、様々な高分子樹脂を強化するために使用されてきた。強化用途において使用するための、一般に使用されているいくつかのガラス組成物としては、「Eガラス」および「Dガラス」ファミリーの組成物が挙げられる。別の一般に使用されているガラス組成物は、AGY(Aiken、South Carolina)から、「Lガラス」の商品名で市販されている。
本発明の様々な実施形態は、ガラス組成物、繊維化可能なガラス組成物、そのような組成物から形成されるガラス繊維、ならびにガラス組成物および/またはガラス繊維を含む製造物品を提供する。
実施形態のさらなる利益は、当業者には、本明細書において提供される記載から明らかとなるであろう。
特に明記しない限り、以下の明細書において示される数値パラメーターは、本発明によって得ることが求められる所望の特性に応じて変化し得る近似値である。ともあれ、特許請求の範囲に対する均等論の適用を制限することを試みるものではないが、各数値パラメーターは、少なくとも、報告される有効桁数の観点から、通常の丸め技術を適用することによるものとして解釈されるべきである。
8重量パーセントの他の構成成分を含む。
超から約5重量パーセントであってもよい。一部の実施形態では、ZnOの含有量は、約2から約7.5重量パーセントであってもよい。一部の実施形態では、ZnOの含有量は、約2から約5.5重量パーセントであってもよい。一部の実施形態では、組成物は、ZnOを実質的に含まなくてもよい。
形態では、Li2Oの含有量は、約0.8重量パーセントまたはそれ未満であってもよい。一部の実施形態では、Li2Oの含有量は、約0.5重量パーセントまたはそれ未満であってもよい。一部の実施形態では、Li2Oは、0超から約1.5重量パーセントであってもよい。一部の実施形態では、Li2Oは、0超から約0.8重量パーセントであってもよい。一部の実施形態では、Li2Oの含有量は、約0.4から約0.7重量パーセントであってもよい。一部の実施形態では、組成物は、Li2Oを実質的に含まなくてもよい。
セス中の混入に由来するCl2、P2O5、Cr2O3、またはNiOなどの少量の不純物が存在する場合もあるが、これらの特定の化学形態に限定されるものではない。また、As2O3、MnO2、Sb2O3、またはSnO2などの他の精製剤および/または加工助剤が存在する場合もあるが、これらの特定の化学形態に限定されるものではない。これらの不純物および精製剤は、存在する場合、ガラス組成物の重量に基づいて、各々典型的には約0.5重量パーセント未満の量で存在する。
布地に関する。本発明の繊維ガラス布地の一部の実施形態は、強化用途、特に高い弾性率、高い強度、および/または高い伸び率が重要である強化用途における使用にとって特に好適である。さらに、本発明の一部の実施形態は、繊維ガラスストランド、繊維ガラス糸、および繊維ガラス布地を組み込む複合材、例えば繊維強化ポリマー複合材に関する。なおもさらに、本発明の一部の実施形態は、限定されるものではないが、風力エネルギー、自動車、安全/セキュリティー、航空宇宙、航空、および高圧タンクを含む用途のための繊維強化複合材に関する。本発明の一部の実施形態は、チップ実装用基板などの、より低
い熱膨張係数が特に望ましいプリント回路板に関する。
約50から約55重量パーセントのSiO2、
約17から約26重量パーセントのB2O3、
約13から約19重量パーセントのAl2O3、
約0から約8.5重量パーセントのMgO、
約0から約7.5重量パーセントのZnO、
約0から約6重量パーセントのCaO、
約0から約1.5重量パーセントのLi2O、
約0から約1.5重量パーセントのF2、
約0から約1重量パーセントのNa2O、
約0から約1重量パーセントのFe2O3、
約0から約1重量パーセントのTiO2、および
合計で約0から約8重量パーセントの他の構成成分
を含むガラス組成物を含む複数のガラス繊維を含む。
の直接延伸ロービングを含み得る。本発明の繊維ガラスストランドを含むロービングは、所望される用途に応じて、様々な直径および密度を有する直接延伸シングルエンドロービングを含み得る。一部の実施形態では、本発明の繊維ガラスストランドを含むロービングは、最大で約113ヤード/ポンドの密度を示す。
sizing composition)を含み得る。
態では、布地は、平織布地、あや織布地、クローフット布地、繻子織布地、ステッチボンディングされた布地(ノンクリンプ布地としても公知である)、または「三次元」織り布地を含む。
られる。
温度の関数としての溶融粘度および液相線温度を、それぞれ、ASTM試験方法C965「Standard Practice for Measuring Viscosity of Glass Above the Softening Point」およびC829「Standard Practices for Measurement of Liquidus
Temperature of Glass by the Gradient Furnace Method」を使用して決定した。ガラスの軟化は、ASTM C338-93(2008年)「Standard Test Method
for Softening Point of Glass」を使用して決定した。
ガラスの熱線膨張係数を、ASTM試験方法E228-11「Standard Test Method
for Linear Thermal Expansion of Solid Materials With a Push-Rod Dilatometer」を使用して決定した。同じ方法を使用して、ガラスのガラス転移温度Tgを決
定した。
各ガラスの誘電率(Dk)および誘電正接(Df)を、1GHzの周波数で、ASTM試験方法D150「Standard Test Methods for A-C Loss Characteristics and
Permittivity (Dielectric Constant) of Solid Electrical Insulating Materials」を使用して決定した。周波数1GHzにおける、Agilent E4991A RFインピーダンス/マテリアルアナライザーを使用するDkおよびDfの測定のために、40mmの直径および1~1.5mmの厚さを有する各ガラス試料の研磨ディスクを使用した。
また、以下の技法を使用して、表1のある特定のガラス組成物についてヤング率を測定した。表1の適切な実施例に対応する組成を有するおよそ50グラムのガラスカレットを、90Pt/10Rhるつぼ中で、100ポアズで定義される溶融温度で2時間再溶融させた。続いて、るつぼを、垂直管である電気加熱炉に移した。炉温は、1000ポアズ溶融粘度に近いか、またはそれに等しい繊維牽引温度にプリセットした。ガラスは、その温度で、繊維延伸前に1時間平衡化させた。繊維延伸炉の頂部には、センターホールを備えたカバーがあり、その上に、繊維の冷却を調節するための水冷した銅コイルを載せた。次いで、シリカロッドを、冷却コイルを通して溶融物中に手動で浸漬させ、約1~1.5mの長さで繊維を延伸し、収集した。繊維の直径は、一方の端部における100μmから他方の端部における1000μmまでの範囲であった。
wave reflection time)を、20マイクロ秒の期間、200kHzのパルスを使用して得た。試料の長さを測定し、それぞれの伸縮波速度(VE)を計算した。繊維密度(ρ)を、Micromeritics AccuPyc 1330比重計を使用して測定した。各組成物について約20回の測定を行い、平均ヤング率(E)を以下の式で計算した。
E=VE 2×ρ
弾性率試験器は、1mmの直径を有する導波管を使用し、これにより、導波管との接触側の繊維直径が導波管の直径とほぼ同じになるように設定される。換言すれば、1000μmの直径を有する繊維の端部を、導波管の接触側で接続した。様々な直径を有する繊維をヤング率に関して試験した。結果は、100から1000μmの繊維直径は、繊維の弾性率に影響を及ぼさないことを示している。比弾性率の値は、ヤング率の値を対応する密度で除することで計算した。
(項1)
繊維形成に好適なガラス組成物であって、
約50から約55重量パーセントの量のSiO2、
約17から約26重量パーセントの量のB2O3、
約13から約19重量パーセントの量のAl2O3、
約0から約8.5重量パーセントの量のMgO、
約0から約7.5重量パーセントの量のZnO、
約0から約6重量パーセントの量のCaO、
約0から約1.5重量パーセントの量のLi2O、
約0から約1.5重量パーセントの量のF2、
約0から約1重量パーセントの量のNa2O、
約0から約1重量パーセントの量のFe2O3、
約0から約1重量パーセントの量のTiO2、および
合計で0から約8重量パーセントの量の1種または複数の希土類酸化物(RE2O3)を含む、組成物。
(項2)
SiO2の含有量が、約51から約54重量パーセントである、上記項1に記載の組成物。
(項3)
B2O3の含有量が、約17.5から約25重量パーセントである、上記項1から2のいずれかに記載の組成物。
(項4)
B2O3の含有量が、約19から約24重量パーセントである、上記項1から3のいずれかに記載の組成物。
(項5)
Al2O3の含有量が、約14から約18重量パーセントである、上記項1から4のいずれかに記載の組成物。
(項6)
MgOの含有量が、0超から約7.5重量パーセントである、上記項1から5のいずれかに記載の組成物。
(項7)
MgOの含有量が、約2から約8.5重量パーセントである、上記項1から5のいずれかに記載の組成物。
(項8)
Al2O3+MgOの含有量が、約14から約26.5重量パーセントである、上記項1から7のいずれかに記載の組成物。
(項9)
Al2O3+MgOの含有量が、約14から約26重量パーセントである、上記項1から8のいずれかに記載の組成物。
(項10)
ZnOの含有量が、0超から約5重量パーセントである、上記項1から9のいずれかに記載の組成物。
(項11)
Al2O3+ZnOの含有量が、約14から約22重量パーセントである、上記項1から10のいずれかに記載の組成物。
(項12)
CaOの含有量が、0超から約5.5重量パーセントである、上記項1から11のいずれかに記載の組成物。
(項13)
MgO+CaOの含有量が、約9重量パーセントまたはそれ未満である、上記項1から12のいずれかに記載の組成物。
(項14)
MgO+CaOの含有量が、0超から約9重量パーセントである、上記項1から12のいずれかに記載の組成物。
(項15)
Na2Oの含有量が、0超から約0.5重量パーセントである、上記項1から14のいずれかに記載の組成物。
(項16)
Li2Oの含有量が、約0.8重量パーセントまたはそれ未満である、上記項1から15のいずれかに記載の組成物。
(項17)
Li2Oの含有量が、0超から約0.8重量パーセントである、上記項1から15のいずれかに記載の組成物。
(項18)
Na2O+Li2Oの合計含有量が、約1.5重量パーセントまたはそれ未満である、上記項1から17のいずれかに記載の組成物。
(項19)
F2の含有量が、0超から約1.5重量パーセントである、上記項1から18のいずれかに記載の組成物。
(項20)
Fe2O3の含有量が、0超から約0.5重量パーセントである、上記項1から19のいずれかに記載の組成物。
(項21)
TiO2の含有量が、0超から約0.7重量パーセントである、上記項1から20のいずれかに記載の組成物。
(項22)
TiO2の含有量が、0超から約0.6重量パーセントである、上記項1から21のいずれかに記載の組成物。
(項23)
前記ガラス組成物が、約0.01重量パーセント超の量の1種または複数の希土類酸化物を含む、上記項1から22のいずれかに記載の組成物。
(項24)
1種または複数の希土類酸化物の含有量が、0超から約8重量パーセントである、上記項1から22のいずれかに記載の組成物。
(項25)
1種または複数の希土類酸化物の含有量が、0超から約7.5重量パーセントである、上記項1から22のいずれかに記載の組成物。
(項26)
1種または複数の希土類酸化物の含有量が、0超から約7重量パーセントである、上記項1から25のいずれかに記載の組成物。
(項27)
RE2O3+Al2O3の含有量が、約13から約22重量パーセントである、上記項1から26のいずれかに記載の組成物。
(項28)
前記1種または複数の希土類酸化物が、La2O3、CeO2、Y2O3、およびSc2O3のうち少なくとも1種を含む、上記項1から27のいずれかに記載の組成物。
(項29)
前記組成物が、BaOを実質的に含まない、上記項1から28のいずれかに記載の組成物。
(項30)
前記組成物が、SrOを実質的に含まない、上記項1から29のいずれかに記載の組成物。
(項31)
上記項1から30のいずれかに記載の組成物から形成される、繊維。
(項32)
上記項31に記載の繊維を含む、製造物品。
(項33)
前記製造物品がプリント回路板である、上記項32に記載の製造物品。
Claims (1)
- 改善された低い熱膨張係数。