JP2021504739A - 偏光板、これを含む画像表示装置および偏光板保護層用の光硬化性組成物 - Google Patents
偏光板、これを含む画像表示装置および偏光板保護層用の光硬化性組成物 Download PDFInfo
- Publication number
- JP2021504739A JP2021504739A JP2020528092A JP2020528092A JP2021504739A JP 2021504739 A JP2021504739 A JP 2021504739A JP 2020528092 A JP2020528092 A JP 2020528092A JP 2020528092 A JP2020528092 A JP 2020528092A JP 2021504739 A JP2021504739 A JP 2021504739A
- Authority
- JP
- Japan
- Prior art keywords
- polarizing plate
- protective layer
- parts
- weight
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本明細書は、偏光板、これを含む画像表示装置および偏光板保護層用の光硬化性組成物に関する。
本明細書は、第1のエポキシ系化合物、第2のエポキシ系化合物およびオキセタン化合物からなる光重合性化合物と、光カチオン重合開始剤とを含み、
前記光重合性化合物の全体100重量部に対して、前記第1のエポキシ系化合物は、50〜80重量部で含まれ、
前記光カチオン重合開始剤は、短波長開始剤および長波長開始剤を含み、
前記偏光板保護層用の光硬化性組成物の全体100重量部に対して、前記短波長開始剤は、2〜2.5重量部で含まれ、前記長波長開始剤は、0.8〜1.5重量部で含まれる偏光板保護層用の光硬化性組成物を提供する。
本明細書において、ある部分がある構成要素を「含む」としたとき、これは、特に反対の意味の記載がない限り、他の構成要素を除くのではなく、他の構成要素をさらに含み得ることを意味する。
本明細書において、ある部材が他の部材「上に」位置しているとしたとき、これは、ある部材が他の部材に接している場合だけでなく、両部材の間にさらに他の部材が存在する場合も含む。
また、図3は本明細書のさらに他の一実施態様に係る偏光板を図示した図である。前記図3には、偏光子10の両面に保護層20が備えられた偏光板の構造が例示されている。前記図3のように、偏光子の両面に保護層が備えられる場合、位相差がほとんどなく、且つ薄膜化が可能であるという利点がある。
前記紫外線の波長は、100nm〜400nmが好ましく、320nm〜400nmがより好ましい。また、前記照射光の光量は、100mJ/cm2〜1000mJ/cm2が好ましく、500mJ/cm2〜1000mJ/cm2がより好ましい。
具体的には、前記脂環式エポキシ系化合物は、エポキシ基が脂肪族炭化水素環を構成する隣り合う2個の炭素原子の間に形成されているエポキシ系化合物を意味する。例えば、2‐(3,4‐エポキシ)シクロヘキシル‐5,5‐スピロ‐(3,4‐エポキシ)シクロヘキサン‐m‐ジオキサン、3,4‐エポキシシクロヘキシルメチル‐3,4‐エポキシシクロヘキサンカルボキシレート、3,4‐エポキシ‐6‐メチルシクロヘキシルメチル‐3,4‐エポキシ‐6‐メチルシクロヘキサンカルボキシレート、ビニルシクロヘキサンジオキシド、ビス(3,4‐エポキシシクロヘキシルメチル)アジペート、ビス(3,4‐エポキシ‐6‐メチルシクロヘキシルメチル)アジペート、エキソ‐エキソビス(2,3‐エポキシシクロペンチル)エーテル、エンド‐エキソビス(2,3‐エポキシシクロペンチル)エーテル、2,2‐ビス[4‐(2,3‐エポキシプロポキシ)シクロヘキシル]プロパン、2,6‐ビス(2,3‐エポキシプロポキシシクロヘキシル‐p‐ジオキサン)、2,6‐ビス(2,3‐エポキシプロポキシ)ノルボルネン、リモネンジオキシド、2,2‐ビス(3,4‐エポキシシクロヘキシル)プロパン、ジシクロペンタジエンジオキシド、1,2‐エポキシ‐6‐(2,3‐エポキシプロポキシ)ヘキサヒドロ‐4,7‐メタノインダン、p‐(2,3‐エポキシ)シクロペンチルフェニル‐2,3‐エポキシプロピルエーテル、1‐(2,3‐エポキシプロポキシ)フェニル‐5,6‐エポキシヘキサヒドロ‐4,7‐メタノインダン、o‐(2,3‐エポキシ)シクロペンチルフェニル‐2,3‐エポキシプロピルエーテル)、1,2‐ビス[5‐(1,2‐エポキシ)‐4,7‐ヘキサヒドロメタノインダノキシル]エタンシクロペンテニルフェニルグリシジルエーテル、メチレンビス(3,4‐エポキシシクロヘキサン)エチレングリコールジ(3,4‐エポキシシクロヘキシルメチル)エーテル、エチレンビス(3,4‐エポキシシクロヘキサンカルボキシレート)、3,4‐エポキシシクロヘキサンメタノールのc‐カプロラクトン付加物と多原子価(3〜20)アルコールのエステル化化合物などがあり、特に、3,4‐エポキシシクロヘキシルメチル‐3,4‐エポキシシクロヘキサンカルボキシレートが好ましいが、これに限定されるものではない。
具体的には、前記脂肪族エポキシ系化合物は、分子内に脂肪族鎖または脂肪族環を含むエポキシ系化合物を意味する。例えば、1,4‐シクロヘキサンジメタノールジグリシジルエーテル、1,4‐ブタンジオールジグリシジルエーテル、1,6‐ヘキサンジオールジグリシジルエーテル、ネオペンチルジグリシジルエーテル、レゾシノールジグリシジルエーテル、ジエチレングリコールジグリシジルエーテル、エチレングリコールジグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル、n‐ブチルグリシジルエーテル、2‐エチルヘキシルグリシジルエーテルなどがあり、特に、1,4‐シクロヘキサンジメタノールジグリシジルエーテルとネオペンチルジグリシジルエーテルを使用することが好ましいが、これに限定されるものではない。また、前記第2のエポキシ系化合物は、前記脂肪族エポキシ系化合物から選択される1種または2種以上の化合物であってもよい。
では、前記例示のうち、1種または2種以上を使用することが好ましいが、これに限定されるものではない。
前記保護層の厚さが前記数値範囲よりも小さい場合には、保護層の強度や高温耐久性の低下およびクラックが生じる恐れがあり、前記数値範囲を超える場合には、偏光板の薄型化の面で好適でない。
前記偏光板保護層用の光硬化性組成物の粘度が前記数値範囲を満たす場合、保護層の厚さを薄く形成することができ、作業性に優れるという利点がある。
前記保護層の貯蔵弾性率が前記数値範囲を満たす場合、偏光子に加えられるストレスを効果的に抑制して、高温または高湿環境で、偏光子の収縮または膨張による偏光子のクラックの発生を効果的に抑制する効果がある。また、偏光子に対する接着力も改善することができる。したがって、高温での偏光板の収縮および膨張を効果的に抑制することで、偏光板が液晶パネルなどに適用されたときに、優れた接着力は言うまでもなく、光漏れ現象が発生することを防止することができる。
本明細書において、前記キャリアフィルムは、偏光板の作製工程の際、保護層を保護するための工程用フィルムを意味する。具体的には、ロール工程で作製される偏光板は、「キャリアフィルム/保護層/偏光子(PVA)/接着剤層/保護フィルム」の積層体からキャリアフィルムを除去して保護層上に接着剤層を形成した後、パネルに貼り付けられるが、キャリアフィルムは、この過程で使用される工程用フィルムである。前記キャリアフィルムは、偏光板の製造工程で剥離が容易なものであれば、特に制限されない。例えば、ポリエチレンテレフタレート(PET)、シクロオレフィンポリマー、ポリカーボネートまたはトリアセチルセルロースがある。前記のようにキャリアフィルムを使用する場合、保護層の形成時に、キャリアフィルムが偏光子を効果的に保護して、保護層形成用の組成物によって他の構成が汚染されることを防止することができ、加圧手段によって加えられる圧力をキャリアフィルムが吸収して、偏光子に作用する応力が緩和し、破断や押圧を効果的に抑制する効果がある。
具体的には、本明細書の一実施態様に係る偏光板は、前記保護層が偏光子の一面に形成された場合、保護層が形成された面の反対面に、偏光子を支持および保護するために、接着剤層を介して別の透明保護フィルムを貼り付けることができる。
前記光増感剤は、例えば、カルボニル化合物、有機硫化合物、過硫化物、レドックス系化合物、アゾおよびジアゾ化合物、アントラセン系化合物、ハロゲン化合物、光還元性色素などが挙げられるが、これに限定されるものではない。
本明細書において、前記画像表示装置は、液晶表示装置(LCD)、プラズマ表示装置(PDP)および有機電界発光表示装置(OLED)であってもよい。
本明細書は、第1のエポキシ系化合物、第2のエポキシ系化合物およびオキセタン化合物からなる光重合性化合物と、光カチオン重合開始剤とを含み、前記光重合性化合物の全体100重量部に対して、前記第1のエポキシ系化合物は、50〜80重量部で含まれ、前記光カチオン重合開始剤は、短波長開始剤および長波長開始剤を含み、前記偏光板保護層用の光硬化性組成物の全体100重量部に対して、前記短波長開始剤は、2〜2.5重量部で含まれ、前記長波長開始剤は、0.8〜1.5重量部で含まれる偏光板保護層用の光硬化性組成物を提供する。
<実験例1>‐光硬化性組成物1の製造
3,4‐エポキシシクロヘキシルメチル‐3´,4´‐エポキシシクロヘキサンカルボキシレート(商品名:セロキサイド‐2021P)65重量部、3‐エチル‐3‐[(3‐エチルオキセタン‐3‐イル)メトキシメチル]オキセタン(東亞合成社製、アロンオキセタンOXT‐221)15重量部および1,4‐シクロヘキシルジメタノールジグリシジルエーテル(CHDMDGE)20重量部を使用し、短波長開始剤として、Irgacure 250を2.11重量部および長波長開始剤として、ESACURE ITXを0.84重量部添加し、光硬化性組成物1を製造した。
3,4‐エポキシシクロヘキシルメチル‐3´,4´‐エポキシシクロヘキサンカルボキシレート(商品名:セロキサイド‐2021P)65重量部、3‐エチル‐3‐[(3‐エチルオキセタン‐3‐イル)メトキシメチル]オキセタン(東亞合成社製、アロンオキセタンOXT‐221)15重量部および1,4‐シクロヘキシルジメタノールジグリシジルエーテル(CHDMDGE)20重量部を使用し、短波長開始剤として、Irgacure 250を2重量部および長波長開始剤として、ESACURE ITXを0.79重量部添加し、光硬化性組成物2を製造した。
3,4‐エポキシシクロヘキシルメチル‐3´,4´‐エポキシシクロヘキサンカルボキシレート(商品名:セロキサイド‐2021P)65重量部、3‐エチル‐3‐[(3‐エチルオキセタン‐3‐イル)メトキシメチル]オキセタン(東亞合成社製、アロンオキセタンOXT‐221)15重量部および1,4‐シクロヘキシルジメタノールジグリシジルエーテル(CHDMDGE)20重量部を使用し、短波長開始剤として、Irgacure 250を2.64重量部および長波長開始剤として、ESACURE ITXを1.05重量部添加し、光硬化性組成物3を製造した。
3,4‐エポキシシクロヘキシルメチル‐3´,4´‐エポキシシクロヘキサンカルボキシレート(商品名:セロキサイド‐2021P)65重量部、3‐エチル‐3‐[(3‐エチルオキセタン‐3‐イル)メトキシメチル]オキセタン(東亞合成社製、アロンオキセタンOXT‐221)15重量部および1,4‐シクロヘキシルジメタノールジグリシジルエーテル(CHDMDGE)20重量部を使用し、短波長開始剤として、Irgacure 250を1.85重量部および長波長開始剤として、ESACURE ITXを0.74重量部添加し、光硬化性組成物4を製造した。
3,4‐エポキシシクロヘキシルメチル‐3´,4´‐エポキシシクロヘキサンカルボキシレート(商品名:セロキサイド‐2021P)65重量部、3‐エチル‐3‐[(3‐エチルオキセタン‐3‐イル)メトキシメチル]オキセタン(東亞合成社製、アロンオキセタンOXT‐221)15重量部および1,4‐シクロヘキシルジメタノールジグリシジルエーテル(CHDMDGE)20重量部を使用し、短波長開始剤として、Irgacure 250を1.72重量部および長波長開始剤として、ESACURE ITXを0.68重量部添加し、光硬化性組成物5を製造した。
3,4‐エポキシシクロヘキシルメチル‐3´,4´‐エポキシシクロヘキサンカルボキシレート(商品名:セロキサイド‐2021P)65重量部、3‐エチル‐3‐[(3‐エチルオキセタン‐3‐イル)メトキシメチル]オキセタン(東亞合成社製、アロンオキセタンOXT‐221)15重量部および1,4‐シクロヘキシルジメタノールジグリシジルエーテル(CHDMDGE)重量部を使用し、短波長開始剤として、Irgacure 250を1.58重量部および長波長開始剤として、ESACURE ITXを0.63重量部添加し、光硬化性組成物6を製造した。
3,4‐エポキシシクロヘキシルメチル‐3´,4´‐エポキシシクロヘキサンカルボキシレート(商品名:セロキサイド‐2021P)30重量部、3‐エチル‐3‐[(3‐エチルオキセタン‐3‐イル)メトキシメチル]オキセタン(東亞合成社製、アロンオキセタンOXT‐221)15重量部、1,4‐シクロヘキシルジメタノールジグリシジルエーテル(CHDMDGE)(商品名:LD‐204)45重量部およびノナンジオールジアクリレート(商品名:A‐NOD‐N)10重量部を使用し、短波長開始剤として、Irgacure 250を3重量部および長波長開始剤として、ESACURE ITXを1重量部添加し、接着剤組成物Aを製造した。
3,4‐エポキシシクロヘキシルメチル‐3´,4´‐エポキシシクロヘキサンカルボキシレート(商品名:セロキサイド‐2021P)30重量部、3‐エチル‐3‐[(3‐エチルオキセタン‐3‐イル)メトキシメチル]オキセタン(東亞合成社製、アロンオキセタンOXT‐221)15重量部、1,4‐シクロヘキシルジメタノールジグリシジルエーテル(CHDMDGE)(商品名:LD‐204)45重量部およびノナンジオールジアクリレート(商品名:A‐NOD‐N)10重量部を使用し、光開始剤として、ジフェニル‐(4‐フェニルチオ)フェニルスルホニウムヘキサフルオロホスフェート(CPI100P、Sanapro社製)を5重量部添加し、接着剤組成物Bを製造した。
<実施例1‐1>
(1)積層体(保護フィルム/接着剤層/PVA)の製造
ポリビニルアルコール(PVA)系樹脂フィルムに二色性染料を染着した後、所定の方向に延伸し架橋させる方法で偏光子を製造した。前記製造した偏光子の一面に、接着剤組成物Aを、ロールコータを使用してコーティングして接着剤層を形成し、保護フィルムとして、PETフィルム(TA‐044、Toyobo社製)を積層した後、紫外線照射装置を用いて、1,000mJ/cm2の紫外線を照射して硬化し、前記偏光子と保護フィルムを互いに接着した。前記接着剤層の厚さは、2μmであった。
前記偏光子の保護フィルムが積層された面の他面に光硬化性組成物1をバーコータまたはロールコータを使用してコーティングし、紫外線照射装置を用いて、1,000mJ/cm2の紫外線を照射して6μmの厚さを有する保護層を形成し、偏光板を製造した。前記偏光板は、偏光子の一面に接着剤層を介して保護フィルムが積層され、前記偏光子の保護フィルムが積層された面の他面に保護層が直接形成された構造である。
前記実施例1‐1で光硬化性組成物1の代わりに、光硬化性組成物2〜6をそれぞれ使用した以外は、実施例1‐1と同じ方法で偏光板を製造した。
<評価例1‐1>‐高温促進評価(クラック発生率評価)
前記実験例1〜6で製造された光硬化性組成物を用いて、前記実施例1‐1と同様に積層体を製造した。次に、先が丸い鉛筆で300gの荷重で掻いて偏光子にクラックを生じさせた以外は、前記実施例1‐1および比較例1‐1〜1‐5と同じ方法で偏光板を製造した。
前記偏光板を幅120mm、長さ100mmに切断した後、80℃で100〜300時間以上放置した後、偏光子の収縮によりクラックが生じて光が漏れるかを観察し、全体のクラックのうち光が漏れるクラックの数を計算して、偏光板内のクラック(crack)発生率を導き出し、その結果を下記表2に示した。
*クラック発生率:(光が漏れるクラックの数/全体クラックの数)×100(%)
前記実験例1〜6で製造された光硬化性組成物を用いて、前記実施例1‐1と同様に積層体を製造した。次に、前記積層体の保護層上にキャリアPETフィルム(XD500、東レ社製)を積層した以外は、前記実施例1‐1および比較例1‐1〜1‐3と同じ方法で偏光板を製造した。
前記で作製された偏光板を5日間エージング(Aging)した後、フィルム高速剥離装置(CBT‐4720、忠北テク社製)を用いて、ASTM 3330測定法により測定することができる。偏光板に対して、180゜の角度で、30m/minの速度でキャリアPETフィルムを剥離し、その結果を下記表2に示した。
前記実施例1‐1および比較例1‐1〜1‐5で作製された偏光板を、温度20℃、湿度50%の条件で7日間放置した後、幅50mm、長さ200mmに切断してから、保護層の前記キャリアフィルムに対する剥離力を、フィルム高速剥離装置(CBT‐4720、忠北テク社製)を用いて、ASTM 3330測定法により測定した。具体的には、キャリアフィルムに対して、前記保護層から30m/minの速度で、180゜の角度で剥離力を測定した。
<比較実施例2‐1ならびに実施例2−2および2‐3>‐(保護フィルム/接着剤層/PVA/保護層)
下記の表3のように、保護層の厚さを異ならせた以外は、前記実施例1‐1と同じ方法で偏光板を製造した。
前記比較実施例2‐1ならびに実施例2−2および2‐3で使用されたものと同じ偏光子の一面に、接着剤組成物Aを、厚さ2μmになるようにロールコータを使用して塗布し、コロナ処理された厚さ80μmのポリエチレンテレフタレートフィルム(TA‐044、Toyobo社製)を接合した。前記偏光子の接着剤組成物Aが塗布された面の他面に、接着剤組成物Bを、厚さ1μmになるようにロールコータを使用して塗布し、保護フィルムAとして厚さ25μmのTACフィルム(富士フィルム社製)を接合した後、紫外線を照射して前記光硬化性接着剤組成物AおよびBを硬化し、偏光板を製造した。
前記比較例2‐1で保護フィルムAとしてRinken社製のアクリルフィルムを使用し、保護フィルムAの厚さを40μmに形成した以外は、比較例2‐1と同じ方法で偏光板を製造した。
<比較例2‐3>‐(保護フィルム/接着剤層/PVA/接着剤層/保護フィルムA)
前記比較例2‐1で保護フィルムAとしてLGC社製のアクリルフィルムを使用し、保護フィルムAの厚さを40μmに形成した以外は、比較例2‐1と同じ方法で偏光板を製造した。
<評価例2‐1>‐高温促進評価(クラック発生率)
前記比較実施例2‐1ならびに実施例2−2および2‐3および比較例2‐1〜2‐3で作製した偏光板に対して、高温促進評価を行った。先が丸い鉛筆で300gの荷重で掻いて偏光子にクラックを生じさせた。次に、前記偏光板を幅120mm、長さ100mmに切断した後、80℃で100時間放置した後、偏光子の収縮によりクラックが生じて光が漏れるかを観察し、全体のクラックのうち光が漏れるクラックの数を計算して、偏光板内のクラック(crack)発生率を導き出し、その結果を下記表3に示した。
*クラック発生率:光が漏れるクラックの数/全体クラックの数×100(%)
前記実験例1で製造された光硬化性組成物1および実験例8で製造された接着剤組成物Bを、それぞれ、離型フィルム(ポリエチレンテレフタレートフィルム、RPK38‐401、東レ先端素材社製)に厚さ50μmで塗布し、光量1000mJ/cm2以上の条件で紫外線を照射して硬化した後、離型フィルムを除去し、試験片を幅5.3mm、長さ4.5cmサイズにレーザを用いて切断した。次に、DMA(Dynamic mechanical analyzer)を用いて、貯蔵弾性率を測定した。測定モードは、Multi‐Frequency‐Strainであり、Strain 10%およびfrequency 1Hzで、−30℃から160℃まで1分当たり5℃ずつ昇温しながら測定した結果を下記表3に示した。
20:保護層
30:接着剤層
40:保護フィルム
Claims (16)
- 偏光子と、
前記偏光子の少なくとも一面に接する保護層とを含む偏光板であって、
前記保護層は、第1のエポキシ系化合物、第2のエポキシ系化合物およびオキセタン化合物からなる光重合性化合物と、光カチオン重合開始剤とを含む偏光板保護層用の光硬化性組成物の硬化物であり、
前記光重合性化合物の全体100重量部に対して、前記第1のエポキシ系化合物は、50〜80重量部で含まれ、
前記光カチオン重合開始剤は、短波長開始剤および長波長開始剤を含み、
前記偏光板保護層用の光硬化性組成物の全体100重量部に対して、前記短波長開始剤は、2〜2.5重量部で含まれ、前記長波長開始剤は、0.8〜1.5重量部で含まれる、偏光板。 - 前記保護層は、前記偏光子に直接コーティングされて形成される、請求項1に記載の偏光板。
- 前記短波長開始剤は、310nm以下の波長を吸収するヨウ素系化合物である、請求項1または2に記載の偏光板。
- 前記長波長開始剤は、350nm以上の波長を吸収するチオキサントン系化合物である、請求項1から3のいずれか一項に記載の偏光板。
- 前記第1のエポキシ系化合物は、脂環式エポキシ系化合物である、請求項1から4のいずれか一項に記載の偏光板。
- 前記第2のエポキシ系化合物は、脂肪族エポキシ系化合物である、請求項1から5のいずれか一項に記載の偏光板。
- 前記光重合性化合物の全体100重量部に対して、前記第2のエポキシ系化合物は、1〜30重量部で含まれる、請求項1から6のいずれか一項に記載の偏光板。
- 前記光重合性化合物の全体100重量部に対して、前記オキセタン化合物は、10〜30重量部で含まれる、請求項1から7のいずれか一項に記載の偏光板。
- 前記保護層の厚さは、5μm〜10μmである、請求項1から8のいずれか一項に記載の偏光板。
- 前記偏光板保護層用の光硬化性組成物の25℃での粘度は、50cps以上200cps以下である、請求項1から9のいずれか一項に記載の偏光板。
- 前記保護層の80℃での貯蔵弾性率は、1,500Mpa〜10,000Mpaである、請求項1から10のいずれか一項に記載の偏光板。
- 前記保護層の偏光子と接する面の他面に備えられたキャリア(Carrier)フィルムをさらに含む、請求項1から11のいずれか一項に記載の偏光板。
- 前記偏光子の保護層が接する面の他面に接着剤層を介して保護フィルムが貼り付けられる、請求項1から12のいずれか一項に記載の偏光板。
- 前記接着剤層は、接着剤組成物の硬化物であり、前記接着剤組成物は、エポキシ化合物およびオキセタン化合物を含む、請求項13に記載の偏光板。
- 請求項1から14のいずれか一項に記載の偏光板を含む、画像表示装置。
- 第1のエポキシ系化合物、第2のエポキシ系化合物およびオキセタン化合物からなる光重合性化合物と、光カチオン重合開始剤とを含み、
前記光重合性化合物の全体100重量部に対して、前記第1のエポキシ系化合物は、50〜80重量部で含まれ、
前記光カチオン重合開始剤は、短波長開始剤および長波長開始剤を含み、
前記偏光板保護層用の光硬化性組成物の全体100重量部に対して、前記短波長開始剤は、2〜2.5重量部で含まれ、前記長波長開始剤は、0.8〜1.5重量部で含まれる、偏光板保護層用の光硬化性組成物。