JP2019214723A - インク組成物及び捺染方法 - Google Patents
インク組成物及び捺染方法 Download PDFInfo
- Publication number
- JP2019214723A JP2019214723A JP2019122693A JP2019122693A JP2019214723A JP 2019214723 A JP2019214723 A JP 2019214723A JP 2019122693 A JP2019122693 A JP 2019122693A JP 2019122693 A JP2019122693 A JP 2019122693A JP 2019214723 A JP2019214723 A JP 2019214723A
- Authority
- JP
- Japan
- Prior art keywords
- monomer
- pigment
- ink composition
- ink
- dispersion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
一方、顔料を着色剤として用いた記録画像は、光、オゾン、水等に対する各種堅牢性には優れることが知られている。
しかし、顔料のように水に不溶な着色剤を含有するインクは、何らかの要因により含有する水分を失って乾燥状態になると顔料の分散状態が壊れ、顔料の凝集が生じるという欠点があった。このように一度凝集したインク中の顔料は、水等の液媒体を加えても再び分散状態に戻すことができない(再分散性が悪い)ため、その改善が強く求められている。
顔料、水、下記式(1)で表されるモノマーA、モノマーB、及びモノマーCよりなる群から選択される少なくとも2種類のモノマーからなるポリマーD、スチレン−ブタジエン樹脂、水溶性有機溶剤、及びノニオン界面活性剤を含有する、インクジェット捺染に用いるインク組成物(但し、染料を含有した樹脂からなる着色微粒子、染料を被覆した樹脂からなる着色微粒子、及び染料を含有した樹脂の表面を更に樹脂で被覆した着色微粒子から選ばれる少なくとも1種の着色微粒子を含有するインク組成物を除く。)。
モノマーA:下記式(1)中、Rが水素原子であるモノマー。
モノマーB:下記式(1)中、RがC1−C4アルキル基であるモノマー。
モノマーC:下記式(1)中、Rがアリール基又はアリールC1−C4アルキル基であるモノマー。
インク組成物の総質量に対する各成分の含有量が、
上記顔料:1〜15質量%、
上記ポリマーD:0.1〜15質量%、
上記スチレン−ブタジエン樹脂:1〜20質量%、
上記水溶性有機溶剤:10〜45質量%、
上記ノニオン界面活性剤:0.01〜5質量%であり、
残部が水である、上記[1]に記載のインク組成物。
[3]
上記スチレン−ブタジエン樹脂がカルボキシ変性スチレン−ブタジエン樹脂である、上記[1]又は[2]に記載のインク組成物。
[4]
上記水溶性有機溶剤がポリグリセリルエーテル及びC2−C6ジオールを含む、上記[1]〜[3]のいずれか一項に記載のインク組成物。
[5]
25℃において、表面張力が20〜40mN/m、粘度が2〜10mPa・sである、上記[1]〜[4]のいずれか一項に記載のインク組成物。
[6]
上記[1]〜[5]のいずれか一項に記載のインク組成物の液滴を、記録信号に応じて吐出させ、被記録材に付着させることにより捺染を行うインクジェット捺染方法。
[7]
上記被記録材が、ポリエステル、セルロース、ポリアミド、及び天然繊維よりなる群から選択される繊維、これらの繊維を含有する混紡繊維、又はこれらの繊維を含有する布帛である、上記[6]に記載のインクジェット捺染方法。
[8]
上記[6]又は[7]に記載のインクジェット捺染方法を用いて被記録材に付着させたインク組成物が含有する顔料を、スチーミング又はベーキング処理により上記被記録材に染着させ、染色を行うインクジェット染色方法。
[9]
上記スチーミング又はベーキング処理の処理温度が80〜250℃であり、処理時間が10秒から30分の範囲である、上記[8]に記載のインクジェット染色方法。
上記の顔料としては、特に限定されるものではなく、公知の顔料が使用できる。顔料としては、無機顔料、有機顔料、体質顔料等が知られている。
カーボンブラックには種類があり、例えば、熱分解法により得られるサーマルブラック、アセチレンブラック;不完全燃焼法により得られるオイルファーネスブラック、ガスファーネスブラック、ランプブラック、ガスブラック、及びチャンネルブラック;等が挙げられる。
カーボンブラックの具体例としては、例えば、Raven760ULTRA、Raven780ULTRA、Raven790ULTRA、Raven1060ULTRA、Raven1080ULTRA、Raven1170、Raven1190ULTRA II、Raven1200、Raven1250、Raven1255、Raven1500、Raven2000、Raven2500ULTRA、Raven3500、Raven5000ULTRA II、Raven5250、Raven5750、Raven7000(以上、コロンビア・カーボン社製);Monarch700、Monarch800、Monarch880、Monarch900、Monarch1000、Monarch1100、Monarch1300、Monarch1400、Regal1330R、Regal1400R、Regal1660R、Mogul L(以上、キャボット社製);Color Black FW1、Color Black FW2、Color Black FW2V、Color Black FW200、Color Black S150、Color Black S160、Color Black S170、Printex 35、Printex U、Printex V、 Printex 140U、 Printex 140V、 SpecIal Black 4、SpecIal Black 4A、SpecIal Black 5、Special Black 6(以上、デグサ社製);MA7、MA8、MA100、MA600、MCF−88、No.25、No.33、No.40、No.47、No.52、No.900、No.2300(以上、三菱化学社製);等が挙げられる。
酸化チタンの具体例としては、例えば、DUAWHITE TCR−52、TITONE R−32、TITONE R−7E、TITONE R−21、TITONE R−62N、TITONE R−42(以上、堺化学工業株式会社製);TIPAQUE CR−50、TIPAQUE CR−50−2、TIPAQUE CR−58、TIPAQUE CR−60、TIPAQUE CR−80、TIPAQUE CR−90(以上、石原産業株式会社製);TITANIX JA−600A、TITANIX JR−605(以上、テイカ株式会社製);ST−455、ST−455WB、ST−457SA、ST−457EC(以上、チタン工業株式会社製);等が挙げられる。
有機顔料の具体例としては、例えば、C.I.Pigment Yellow 1、2、3、12、13、14、16、17、24、55、73、74、75、83、93、94、95、97、98、108、114、128、129、138、139、150、151、154、155、180、185、193、199、202等のイエロー色の顔料;C.I.Pigment Red 5、7、12、48、48:1、57、88、112、122、123、146、149、166、168、177、178、179、184、185、202、206、207、254、255、257、260、264、272等のレッド色の顔料;C.I.Pigment Blue 1、2、3、15、15:1、15:2、15:3、15:4、15:6、16、22、25、60、66、80等のブルー色の顔料;C.I.Pigment Violet 19、23、29、37、38、50等のバイオレット色の顔料;C.I.Pigment Orange13、16、36、34、43、68、69、71、73等のオレンジ〜ブラウン色の顔料;C.I.Pigment Green7、36、54等のグリーン色の顔料;C.I.Pigment Black 1等のブラック色の顔料;等が挙げられる。
さらに、染色物の色相調整のため、無機顔料及び有機顔料から選択される2種以上の顔料を併用することもできる。ここでいう色相調整は、濃淡をつけた染色物を得ること;染色の色域を広げること;等を目的として行われる。このような目的のためには、数種類の有機顔料を併用し、望みの色相に調整することができる。
水性媒体(水と、後記するアルキルエーテル溶剤以外の水溶性有機溶剤及びアルキルエーテル溶剤の混合溶媒を意味する)中で顔料分散物を安定化させる方法としては、一般に樹脂等の分散剤を用いてエントロピー的、イオン反発力、立体反発力等によって顔料分散物を安定化する方法が用いられる。ここで、分散剤は親水性部分と疎水性部分とを有し、疎水性部分が顔料表面に吸着し、親水性部分で水性媒体に分散する性質を有すると考えられる。さらに、顔料表面への吸着状態によっては、顔料を水性媒体に溶解させることも可能である。上記のポリマーDは、このような性質を有する分散剤として使用できる。
ポリマーDは、上記式(1)で表されるモノマーA、モノマーB、及びモノマーCよりなる群から選択される少なくとも2種類のモノマーを重合してなるポリマーである。好ましくは、モノマーA、モノマーB、及びモノマーCから少なくとも1種類ずつが選択される。
また、ポリマーDは、これらのモノマーのランダム共重合体、交互共重合体、ブロック共重合体、グラフト共重合体のいずれであってもよい。
また、アルカリ土類金属の水酸化物として、例えば、水酸化ベリリウム、水酸化マグネシウム、水酸化カルシウム、水酸化ストロンチウム等が挙げられる。
無機塩基の中ではアルカリ金属の水酸化物及びアンモニアが好ましく、中でも水酸化リチウム、水酸化ナトリウム、及びアンモニアが好ましい。
モノマーAは、上記式(1)中、Rが水素原子であるモノマー、すなわちメタクリル酸である。
モノマーBは、上記式(1)中、RがC1−C4アルキル基であるモノマーである。
モノマーBとしては、メチルメタクリレート、エチルメタクリレート、n−プロピルメタクリレート、イソプロピルメタクリレート、n−ブチルメタクリレート、イソブチルメタクリレート等が挙げられる。
モノマーCは、上記式(1)中、Rがアリール基又はアリールC1−C4アルキル基であるモノマーである。
上記アリールとしては、C6−C10アリール基が好ましく、中でもフェニル基又はナフチル基が好ましい。
上記アリールC1−C4アルキル基としては、フェニルメチル、フェニルエチル、フェニルプロピル、フェニルブチル等のアルキル部分が直鎖又は分岐鎖、好ましくは直鎖のフェニルC1−C4アルキル基;ナフチルメチル、ナフチルエチル、ナフチルプロピル、ナフチルブチル等のアルキル部分が直鎖又は分岐鎖、好ましくは直鎖のナフチルC1−C4アルキル基;等が挙げられる。これらの中ではフェニルC1−C4アルキル基が好ましい。
モノマーCの具体例としては、例えば、フェニルメタクリレート、ベンジルメタクリレート、フェネチルメタクリレートが挙げられる。
上記スチレン−ブタジエン樹脂は、ラテックス(エマルション)の形で販売されていることも多く、容易に購入することができる。その具体例としては、例えば、Nipol LX415M、NipolLX432M,Nipol LX433C、Nipol LX421、Nipol 2507H、Nipol LX303A(以上、日本ゼオン(株)製)、グレードとして0695、0696、0561、0589、0602、2108、0533、0545、0548、0568、0569、0573、0597C、0850Zのラテックス(以上、JSR(株)製)等が挙げられ、その多くは固形分が30〜60%で樹脂を乳化した液体である。
スチレン−ブタジエン樹脂としては、上記したいずれのラテックスも使用することができるが、中でもカルボキシ変性スチレン−ブタジエン樹脂を使用するのが好ましい。そのような樹脂の例としては、例えば、Nipol LX415M、NipolLX432M,Nipol LX433C、Nipol LX421、0695、0696、0533、0545、0548、0568、0569、0573、0597C、0850Zが挙げられ、0695、0533、0568、0597C、0850Zが好ましい。
スチレン−ブタジエン樹脂は単一のものを使用してもよいし、2〜3種類を併用してもよい。
上記水溶性有機溶剤としては、例えば、メタノール、エタノール、n−プロパノール、イソプロパノール、n−ブタノール、イソブタノール、第二ブタノール、第三ブタノール等のC1−C4モノオール;エチレングリコール、1,2−又は1,3−プロピレングリコール、1,2−又は1,4−ブチレングリコール、1,3−ペンタンジオール、1,5−ペンタンジオール、1,2−ヘキサンジオール、1,6−ヘキサンジオール等のC2−C6ジオール;グリセリン、ヘキサン−1,2,6−トリオール、トリメチロールプロパン等のC3−C6トリオール;N,N−ジメチルホルムアミド、N,N−ジメチルアセトアミド等のカルボン酸アミド;2−ピロリドン、N−メチル−2−ピロリドン、1,3−ジメチルイミダゾリジン−2−オン、1,3−ジメチルヘキサヒドロピリミド−2−オン等の複素環式尿素類;アセトン、メチルエチルケトン、2−メチル−2−ヒドロキシペンタン−4−オン等のケトン又はケトアルコール;1,2−ジメトキシエタン、テトラヒドロフラン、ジオキサン等の直鎖又は環状エーテル;ジエチレングリコール、トリエチレングリコール、ジプロピレングリコール、チオジグリコール等のジ若しくはトリC2−C3アルキレングリコール又はチオグリコール;テトラエチレングリコール、ポリエチレングリコール(好ましくは分子量400、800、1540等の分子量が2000以下のもの)、ポリプロピレングリコール等の、繰り返し単位が4以上で、分子量が約20000以下程度のポリC2−C3アルキレングリコール(好ましくは液状のもの);ジグリセリン、トリグリセリン、ポリグリセリン等のポリグリセリルエーテル;ポリオキシエチレンポリグリセリルエーテル、ポリオキシプロピレンポリグリセリルエーテル等のポリオキシC2−C3アルキレンポリグリセリルエーテル;エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル(ブチルカルビトール)、トリエチレングリコールモノメチルエーテル、トリエチレングリコールモノエチルエーテル、トリエチレングリコールモノブチルエーテル等の多価アルコールのC1−C4アルキルエーテル;γ−ブチロラクトン、エチレンカーボネート等の環状エステル又はカーボネート;ジメチルスルホキシド;酢酸;等が挙げられる。
これらの中では、C2−C6ジオール(中では1,2−プロピレングリコール);C3−C6トリオール(中ではグリセリン);ポリグリセリルエーテル(中ではジグリセリン);及び、多価アルコールのC1−C4アルキルエーテル(中ではブチルカルビトール);が好ましい。
これらの水溶性有機溶剤は1種類を使用してもよく、また複数を併用してもよい。これらの中では、ポリグリセリルエーテル(好ましくはグリセリン及び/又はジグリセリン)と、C2−C6ジオール(好ましくはエチレングリコール、1,2−又は1,3−プロピレングリコール、より好ましくはエチレングリコール、1,2−プロピレングリコール)とを含有するのが好ましい。
上記ノニオン界面活性剤としては、例えば、ポリオキシエチレンノニルフェニルエーテル、ポリオキシエチレンオクチルフェニルエーテル、ポリオキシエチレンドデシルフェニルエーテル、ポリオキシエチレンオレイルエーテル、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンアルキルエーテル等のエーテル系;ポリオキシエチレンオレイン酸エステル、ポリオキシエチレンジステアリン酸エステル、ソルビタンラウレート、ソルビタンモノステアレート、ソルビタンモノオレエート、ソルビタンセスキオレエート、ポリオキシエチレンモノオレエート、ポリオキシエチレンステアレート等のエステル系;2,4,7,9−テトラメチル−5−デシン−4,7−ジオール、3,6−ジメチル−4−オクチン−3,6−ジオール、3,5−ジメチル−1−ヘキシン−3−オール等のアセチレングリコール(アルコール)系;日信化学社製 商品名サーフィノールRTM104、105PG50、82、420、440、465、485、DF−110D、オルフィンRTMSTG;ポリグリコールエーテル系(例えばSIGMA−ALDRICH社製のTergItolRTM15−S−7等);等が挙げられる。上記ノニオン界面活性剤は、単独又は混合して用いることができ、好ましくはサーフィノール系、より好ましくはサーフィノールRTM420、サーフィノールRTM440、サーフィノールRTM465である。
なお、本明細書において、上付きの「RTM」は登録商標を意味する。
顔料:通常1〜15%、好ましくは1〜10%、より好ましくは1〜7%。
ポリマーD:通常0.1〜15%、好ましくは0.1〜9%、より好ましくは0.2〜6%。
スチレン−ブタジエン樹脂:通常1〜20%、好ましくは3〜15%、より好ましくは3〜12%。
水溶性有機溶剤:通常10〜45%、好ましくは15〜38%、より好ましくは20〜35%。
ノニオン界面活性剤:通常0.01〜5%、好ましくは0.05〜3%、より好ましくは0.1〜2.5%。
なお、残部は水である。
このような条件で分散を行うことにより、顔料の粒子サイズを小さくすることができ、分散性が良好な分散液を得ることができる。
また、該分散液の調製後に、濾過及び/又は遠心分離等により、粒子サイズの大きい成分を除去することも好ましく行われる。
また、該分散液の調製時に激しく泡立ち等が生じるときは、これを抑える目的で、シリコーン系、アセチレングリコール系等の消泡剤を極微量添加してもよい。ただし、消泡剤には、顔料の分散や微粒子化を阻害するものがあるため、そのような悪影響を及ぼさないものを適宜選択して使用するのが好ましい。
ポリマーDにより顔料をマイクロカプセル化するときは、いずれの手法を用いてもよく、特に限定されないが、これらの中では表面析出法が好ましく、中でも転相乳化法が好ましい。
上記のようにして調製される顔料分散液中における顔料の平均粒径は、通常200nm以下、好ましくは50〜150nm、より好ましくは60〜120nmである。平均粒径をこの範囲とすることによって、分散安定性及び吐出安定性が優れるとともに、染色濃度が高くなる。なお、平均粒径は、レーザ光散乱法を用いて測定できる。
また、インク組成物の25℃における表面張力としては、10〜50mN/mが好ましく、20〜40mN/mがより好ましい。
さらに、インク組成物の25℃における粘度としては、30mPa・s以下が好ましく、20mPa・s以下がより好ましく、2〜10mPa・sが特に好ましい。
本発明のインク組成物のpH、表面張力は、後記するようなpH調整剤、界面活性剤で適宜調整することが可能である。
分原比=ポリマーDの部数/顔料の部数
有機ハロゲン系化合物の具体例としては、例えばペンタクロロフェノールナトリウムが挙げられる。ピリジンオキシド系化合物の具体例としては、例えば2−ピリジンチオール−1−オキサイドナトリウムが挙げられる。イソチアゾリン系化合物の具体例としては、例えば、1,2−ベンズイソチアゾリン−3−オン、2−n−オクチル−4−イソチアゾリン−3−オン、5−クロロ−2−メチル−4−イソチアゾリン−3−オン、5−クロロ−2−メチル−4−イソチアゾリン−3−オンマグネシウムクロライド、5−クロロ−2−メチル−4−イソチアゾリン−3−オンカルシウムクロライド、2−メチル−4−イソチアゾリン−3−オンカルシウムクロライド等が挙げられる。その他の防腐防黴剤の具体例としては、無水酢酸ナトリウム、ソルビン酸ナトリウム、安息香酸ナトリウム、アーチケミカル社製、商品名プロクセルRTMGXL(S)やプロクセルRTMXL−2(S)等が挙げられる。
他の具体例としては、例えば、炭酸リチウム、炭酸ナトリウム、炭酸水素ナトリウム、炭酸カリウム等のアルカリ金属の炭酸塩;ケイ酸ナトリウム、酢酸カリウム等の有機酸のアルカリ金属塩;リン酸二ナトリウム等のリン酸塩;等が挙げられる。
ポリエステル繊維としては、ポリエチレンテレフタレートを主成分とする繊維が挙げられる。
セルロース繊維としては、綿、木綿、レーヨン、トリアセテート繊維、ジアセテート繊維等が挙げられる。
ポリアミド繊維としては、ナイロン繊維等が挙げられる。
天然繊維としては、絹、羊毛等が挙げられる。
上記の繊維は単一素材の繊維であっても、これらの混紡繊維であってもよい。また、これらの繊維にインク受容層(滲み防止層)を設けたものでもよい。この繊維へのインク受容層の形成方法は公知公用の技術であり、インク受容層を有する繊維は市場から入手できる。また、公知公用の技術から適宜構成成分、形成方法等を選定し、該繊維にインク受容層を設けることもできる。該インク受容層はその機能を有するものであれば、特に限定されるものではない。
スチーミング処理としては、例えば、高温スチーマーでは通常80〜250℃、好ましくは170〜180℃、通常10秒〜30分、好ましくは10分程度の処理で染着させることができる(湿熱固着)。
また、ベーキング(サーモゾル)処理としては、通常80〜250℃、好ましくは190〜210℃、通常10秒〜30分、好ましくは60〜180秒程度の処理で染着させることができる(乾熱固着)。
このようにして、上記インクジェット染色方法により染色された染色物が得られる。なお、染色物とは、上記インクジェット染色方法により染色された被記録材を意味する。
上記インクジェット捺染方法は、上記インク組成物中に含有する顔料の種類を選択してインクセットとして使用し、フルカラー捺染を行うことができる。例えば、上記イエロー、レッド、ブルー、及びブラックの4色のインクセットとして使用してもよいし、必要に応じて、グリーン、バイオレット、オレンジ〜ブラウン等の各色の顔料から適宜選択し、4色以上のインクセットとして使用することもできる。
また、貯蔵時の保存安定性が良好であり、仮にインク組成物中の水分等を失って、インク組成物を乾燥させてしまったときであっても、再分散性が極めて良好である。
また、繊維の染色において、滲みがなく高発色であり、フルカラー捺染において隣接した色が混ざらず高品質である。
また、染着後の各種の堅牢性、例えば耐光性、耐水性等にも優れる。
星光PMC社製ハイロスX VS−1202(9部)を、2−ブタノン(30部)に溶解した。この溶液に、0.9部の水酸化ナトリウムをイオン交換水(76部)に溶解させた液を加え、1時間撹拌することにより乳化液を得た。得られた液にC.I.Pigment Red 122(High Performance Colours Ltd社製、HPC Red 1220、30部)を加え、サンドグラインダーで1500rpmの条件下、15時間分散処理を行った。得られた液にイオン交換水(150部)を滴下した後、分散用ビーズを濾別した。得られた母液中の2−ブタノン及び水の一部を、エバポレータで減圧留去して濃縮することにより、固形分12.2%の分散液を得た。これを「分散液1」とする。なお、水溶液中の固形分は、株式会社エイ・アンド・デイ社製、MS−70を用いて乾燥重量法により求めた。分散液1に含まれる顔料の平均粒子径は181nm、分散液1の25℃における粘度は6.7mPa・sであった。
上記調製例1で使用したC.I.Pigment Red 122の代わりに、C.I.Pigment Black 7を用いる以外は調製例1と同様にして分散液を得た。これを「分散液2」とする。分散液2の固形分は11.9%、分散液2に含まれる顔料の平均粒子径は88nm、分散液2の25℃における粘度は4.6mPa・sであった。
上記調製例1で使用したC.I.Pigment Red 122の代わりに、C.I.Pigment Blue 15:3を用いる以外は調製例1と同様にして、分散液を得た。これを「分散液3」とする。分散液3の固形分は12.1%、分散液3に含まれる顔料の平均粒子径は102nm、分散液3の25℃における粘度は6.2mPa・sであった。
上記調製例1で使用したC.I.Pigment Red 122の代わりに、C.I.Pigment Yellow 155を用いる以外は調製例1と同様にして、分散液を得た。これを「分散液4」とする。分散液4の固形分は12.2%、分散液4に含まれる顔料の平均粒子径は82nm、分散液4の25℃における粘度は2.4mPa・sであった。
上記分散液1〜4と、下記表1に記載の各成分とを混合し、5μmのメンブランフィルタで夾雑物を濾別することにより、評価試験に用いる実施例5〜16のインクを得た。いずれのインクも、顔料の含有量が6%になるように調整した。
各実施例で用いたスチレン−ブタジエン樹脂の代わりに、ポリカーボネート系ウレタン樹脂ラテックスであるパーマリンUA−150[三洋化成工業(株)製]を使用し、下記表2の各成分を混合することにより、評価試験に用いる比較例1〜4のインクをそれぞれ調製した。いずれのインクも、顔料の含有量が6%になるように調整した。
DG:ジグリセリン
1,2−PG:1,2−プロピレングリコール
0533:JSR(株)製のグレード0533のラテックス
0568:JSR(株)製のグレード0568のラテックス
0597C:JSR(株)製のグレード0597Cのラテックス
SF420:サーフィノール420
DF−110D:サーフィノールDF−110D
TEA:トリエタノールアミン
BC:ブチルカルビトール
UA−150:パーマリンUA−150
上記実施例5〜16、及び比較例1〜4のインク組成物をガラスシャーレの上に5mlのせ、シャーレ底に薄くまんべんなく回し広げた後、余剰の液体を捨てた。これを35℃の乾燥機で4時間乾燥させた後、室温で2mlのイオン交換水を滴下し、乾燥したインク組成物の再分散性を目視にて、下記の4段階で評価した。
乾燥後であっても再分散するものは、残渣を生じることなく全て液状に戻るため、目視にて判断することができる。結果を上記表1及び表2に示す。
A:残渣なく、全て再分散する。
B:残渣が少し残るが、ほとんどが再分散している。
C:残渣は多く残るが、多少再分散している。
D:まったく再分散しない。
各実施例及び比較例のインク組成物をそれぞれ蓋付ガラス製サンプル瓶に入れ、60℃の乾燥機で3日間静置した。各サンプル瓶を静かに逆さまにし、保存安定性として沈殿物の有無を目視にて、下記の2段階で評価した。結果を上記表1及び表2に示す。
A:沈殿物は確認されない。
D:明らかに沈殿物が確認される。
国際公開第2013/115071号の合成例4を追試することにより得た高分子分散剤(ブロック共重合体B)を6部、2−ブタノン30部に溶解させ、均一な溶液とした。これに、0.44部の水酸化ナトリウムを41部のイオン交換水に溶解させた液を加え、1時間撹拌することで高分子分散剤が溶解した乳化溶液を調製した。このとき、結晶の析出はなかった。これにC.I.Pigment Red 122(High Performance Colours Ltd社製、HPC Red 1220)を20部加え、サンドグラインダーで分散を行った。分散は1500rpmの条件下で15時間分散させて液を得た。得られた液にイオン交換水100部を滴下し、この液を濾過して分散用ビーズを取り除いた後、エバポレータで2−ブタノン及び水を減圧留去することにより、固形分15.1%の分散液を得た。これを「分散液5」とする。分散液5に含まれる顔料の平均粒子径は96nm、分散液5の25℃における粘度は6.0mPa・sであった。
国際公開第2013/115071号の合成例3を追試することにより得た高分子分散剤(ブロック共重合体A)を6部、2−ブタノン30部に溶解させ、均一な溶液とした。これに、0.45部の水酸化ナトリウムを42部のイオン交換水に溶解させた液を加え、1時間撹拌することで高分子分散剤が溶解した乳化溶液を調製した。このとき、結晶の析出はなかった。これにC.I.Pigment Red 122(High Performance Colours Ltd社製、HPC Red 1220)を20部加え、サンドグラインダーで分散を行った。分散は1500rpmの条件下で15時間分散させて液を得た。得られた液にイオン交換水100部を滴下し、この液を濾過して分散用ビーズを取り除いた後、エバポレータで2−ブタノン及び水を減圧留去することにより、固形分13.7%の分散液を得た。これを「分散液6」とする。分散液6に含まれる顔料の平均粒子径は80nm、分散液6の25℃における粘度は6.7mPa・sであった。
国際公開第2013/115071号の合成例5を追試することにより得た高分子分散剤(ブロック共重合体C)を6部、2−ブタノン30部に溶解させ、均一な溶液とした。これに、0.43部の水酸化ナトリウムを42部のイオン交換水に溶解させた液を加え、1時間撹拌することで高分子分散剤が溶解した乳化溶液を調製した。このとき、結晶の析出はなかった。これにC.I.Pigment Red 122(High Performance Colours Ltd社製、HPC Red 1220)を20部加え、サンドグラインダーで分散を行った。分散は1500rpmの条件下で15時間分散させて液を得た。得られた液にイオン交換水100部を滴下し、この液を濾過して分散用ビーズを取り除いた後、エバポレータで2−ブタノン及び水を減圧留去することにより、固形分13.9%の分散液を得た。これを「分散液7」とする。分散液7に含まれる顔料の平均粒子径は102nm、分散液7の25℃における粘度は7.4mPa・sであった。
国際公開第2013/115071号の合成例6を追試することにより得た高分子分散剤(ブロック共重合体D)を6部、2−ブタノン30部に溶解させ、均一な溶液とした。これに、0.44部の水酸化ナトリウムを41部のイオン交換水に溶解させた液を加え、1時間撹拌することで高分子分散剤が溶解した乳化溶液を調製した。このとき、結晶の析出はなかった。これにC.I.Pigment Red 122(High Performance Colours Ltd社製、HPC Red 1220)を20部加え、サンドグラインダーで分散を行った。分散は1500rpmの条件下で15時間分散させて液を得た。得られた液にイオン交換水100部を滴下し、この液を濾過して分散用ビーズを取り除いた後、エバポレータで2−ブタノン及び水を減圧留去することにより、固形分12.7%の分散液を得た。これを「分散液8」とする。分散液8に含まれる顔料の平均粒子径は102nm、分散液8の25℃における粘度は20.2mPa・sであった。
国際公開第2013/115071号の合成例7を追試することにより得た高分子分散剤(ブロック共重合体E)を6部、2−ブタノン30部に溶解させ、均一な溶液とした。これに、0.38部の水酸化ナトリウムを88部のイオン交換水に溶解させた液を加え、1時間撹拌することで高分子分散剤が溶解した乳化溶液を調製した。このとき、結晶の析出はなかった。これにC.I.Pigment Red 122(High Performance Colours Ltd社製、HPC Red 1220)を20部加え、サンドグラインダーで分散を行った。分散は1500rpmの条件下で15時間分散させて液を得た。得られた液にイオン交換水100部を滴下し、この液を濾過して分散用ビーズを取り除いた後、エバポレータで2−ブタノン及び水を減圧留去することにより、固形分11.7%の分散液を得た。これを「分散液9」とする。分散液9に含まれる顔料の平均粒子径は104nm、分散液9の25℃における粘度は3.0mPa・sであった。
国際公開第2013/115071号の合成例8を追試することにより得た高分子分散剤(ブロック共重合体F)を6部、2−ブタノン30部に溶解させ、均一な溶液とした。これに、0.51部の水酸化ナトリウムを41部のイオン交換水に溶解させた液を加え、1時間撹拌することで高分子分散剤が溶解した乳化溶液を調製した。このとき、結晶の析出はなかった。これにC.I.Pigment Red 122(High Performance Colours Ltd社製、HPC Red 1220)を20部加え、サンドグラインダーで分散を行った。分散は1500rpmの条件下で15時間分散させて液を得た。得られた液にイオン交換水100部を滴下し、この液を濾過して分散用ビーズを取り除いた後、エバポレータで2−ブタノン及び水を減圧留去することにより、固形分12.68%の分散液を得た。これを「分散液10」とする。分散液10に含まれる顔料の平均粒子径は110nm、分散液10の25℃における粘度は10.4mPa・sであった。
C.I.Pigment Red 122の代わりに、C.I.Pigment Black 7を用いる以外は上記調製例6と同様にして、固形分12.9%の分散液を得た。これを「分散液11」とする。分散液11に含まれる顔料の平均粒子径は88nm、分散液11の25℃における粘度は4.6mPa・sであった。
C.I.Pigment Red 122の代わりに、C.I.Pigment Blue 15:3を用いる以外は上記調製例6と同様にして、固形分12.4%の分散液を得た。これを「分散液12」とする。分散液12に含まれる顔料の平均粒子径は102nm、分散液12の25℃における粘度は6.2mPa・sであった。
C.I.Pigment Red 122の代わりに、C.I.Pigment Yellow 155を用いる以外は上記調製例6と同様にして、固形分14.1%の分散液を得た。これを「分散液13」とする。分散液13に含まれる顔料の平均粒子径は82nm、分散液13の25℃における粘度は2.4mPa・sであった。
国際公開第2013/115071号の合成例3を追試することにより得た高分子分散剤(ブロック共重合体A)を4部、2−ブタノン25部に溶解させ、均一な溶液とした。これに、0.45部の水酸化ナトリウムを42部のイオン交換水に溶解させた液を加え、1時間撹拌することで高分子分散剤が溶解した乳化溶液を調製した。このとき、結晶の析出はなかった。これにタイペークCR−50−2(石原産業株式会社製)を40部加え、サンドグラインダーで分散を行った。分散は1500rpmの条件下で15時間分散させて液を得た。得られた液にイオン交換水100部を滴下し、この液を濾過して分散用ビーズを取り除いた後、エバポレータで2−ブタノン及び水を減圧留去することにより、固形分30.0%の分散液を得た。これを「分散液14」とする。分散液14に含まれる顔料の平均粒子径は266nm、分散液14の25℃における粘度は4.0mPa・sであった。
上記分散液6及び分散液11〜13と下記表3に記載の各成分とを混合し、5μmのメンブランフィルタで夾雑物を濾別することにより、評価試験に用いる実施例17〜21のインク組成物を得た。いずれのインク組成物も、顔料の含有量が6%になるように調整した。
下記表3中の略号等及び空欄は、上記表1及び表2と同じ意味を有する。また、「0850Z」は、JSR株式会社製のグレード0850Zのラテックスを意味する。
Claims (9)
- 顔料、水、下記式(1)で表されるモノマーA、モノマーB、及びモノマーCよりなる群から選択される少なくとも2種類のモノマーからなるポリマーD、スチレン−ブタジエン樹脂、水溶性有機溶剤、及びノニオン界面活性剤を含有する、インクジェット捺染に用いるインク組成物(但し、染料を含有した樹脂からなる着色微粒子、染料を被覆した樹脂からなる着色微粒子、及び染料を含有した樹脂の表面を更に樹脂で被覆した着色微粒子から選ばれる少なくとも1種の着色微粒子を含有するインク組成物を除く。)。
モノマーA:下記式(1)中、Rが水素原子であるモノマー。
モノマーB:下記式(1)中、RがC1−C4アルキル基であるモノマー。
モノマーC:下記式(1)中、Rがアリール基又はアリールC1−C4アルキル基であるモノマー。
- インク組成物の総質量に対する各成分の含有量が、
前記顔料:1〜15質量%、
前記ポリマーD:0.1〜15質量%、
前記スチレン−ブタジエン樹脂:1〜20質量%、
前記水溶性有機溶剤:10〜45質量%、
前記ノニオン界面活性剤:0.01〜5質量%であり、
残部が水である、請求項1に記載のインク組成物。 - 前記スチレン−ブタジエン樹脂がカルボキシ変性スチレン−ブタジエン樹脂である、請求項1又は2に記載のインク組成物。
- 前記水溶性有機溶剤がポリグリセリルエーテル及びC2−C6ジオールを含む、請求項1〜3のいずれか一項に記載のインク組成物。
- 25℃において、表面張力が20〜40mN/m、粘度が2〜10mPa・sである、請求項1〜4のいずれか一項に記載のインク組成物。
- 請求項1〜5のいずれか一項に記載のインク組成物の液滴を、記録信号に応じて吐出させ、被記録材に付着させることにより捺染を行うインクジェット捺染方法。
- 前記被記録材が、ポリエステル、セルロース、ポリアミド、及び天然繊維よりなる群から選択される繊維、これらの繊維を含有する混紡繊維、又はこれらの繊維を含有する布帛である、請求項6に記載のインクジェット捺染方法。
- 請求項6又は7に記載のインクジェット捺染方法を用いて被記録材に付着させたインク組成物が含有する顔料を、スチーミング又はベーキング処理により前記被記録材に染着させ、染色を行うインクジェット染色方法。
- 前記スチーミング又はベーキング処理の処理温度が80〜250℃であり、処理時間が10秒から30分の範囲である、請求項8に記載のインクジェット染色方法。