JP2019108169A - 断熱容器用積層体、断熱容器および断熱容器の製造方法 - Google Patents
断熱容器用積層体、断熱容器および断熱容器の製造方法 Download PDFInfo
- Publication number
- JP2019108169A JP2019108169A JP2019023614A JP2019023614A JP2019108169A JP 2019108169 A JP2019108169 A JP 2019108169A JP 2019023614 A JP2019023614 A JP 2019023614A JP 2019023614 A JP2019023614 A JP 2019023614A JP 2019108169 A JP2019108169 A JP 2019108169A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- heat insulation
- printing
- cover layer
- laminate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
発泡前のカバー層11Aは、少なくとも高圧法低密度ポリエチレンから構成されている。なお、以下の説明においては、カバー層11A(11)を構成する高圧法低密度ポリエチレンと、後述する表面層16を構成するポリエチレン系樹脂とを明確に区別するため、カバー層11A(11)を構成する高圧法低密度ポリエチレンについては、「高圧法低密度ポリエチレン(B)」と表記し、表面層16を構成するポリエチレン系樹脂については、「ポリエチレン系樹脂(A)」と表記する。
本実施形態にかかる断熱容器用積層体10A、10にあっては、前記カバー層11A、11上に、JIS K6922−2(2010年)により測定される融点が、前記カバー層11A、11を構成する高圧法低密度ポリエチレン(B)の融点よりも高いポリエチレン系樹脂(A)から構成されている表面層が設けられている点に特徴を有している。このような材質から構成される表面層16を設けることにより、カバー層11Aを、後述する印刷層15の影響を受けることなく、均一に発泡せしめることができる。より具体的には、例えば、後述する印刷層15が白インキ印刷部と色インキ印刷部とから構成される場合であっても、白インキ印刷部と色インキ印刷部との間の段差を200μm未満に抑えることが可能となる。
本発明の実施形態にかかる断熱容器用積層体10A、10にあっては、前記表面層16上に印刷層15が設けられており、当該印刷層15はバインダー樹脂としてウレタン樹脂を含み、かつ刷層層の全固形分の合計質量に対する当該ウレタン樹脂の割合が18質量%以上である点にも特徴を有している。このような特定のバインダーを含む印刷層15を用いることにより、印刷層15の追従性を向上せしめることができ、カバー層11Aが発泡状態となった際に当該カバー層11Aの発泡にうまく追従し、表面平滑性を担保でき、優れた意匠性を発揮することができる。なお、このような印刷層15は、必ずしも表面層16の全面に形成されている必要はなく、図1や図2に示すように、部分的に形成されていてもよい。
基材層12は紙から構成されている。この紙は、断熱容器を構成する基本素材となることから賦型性、耐屈曲性、剛性、腰、強度等を有するものを使用することができる。紙としては、例えば、主強度材であり、強サイズ性の晒または未晒の紙基材、あるいは、純白ロール紙、クラフト紙、板紙、加工紙、ミルク原紙等の各種の紙基材を使用することができる。基材層12は、これらの紙を複数層重ねたものであってもよい。また、紙は、坪量80〜600g/m2程度、好ましくは坪量100〜450g/m2程度であり、厚さ110〜860μm程度、好ましくは140〜640μm程度のものを使用することができる。
本実施形態にかかる断熱容器用積層体10A、10にあっては、基材層12の内面側に水蒸気遮断層13が設けられている。当該層は、基材層12を構成する紙から発生する水蒸気を遮断し、発生した水蒸気を効率良くカバー層11A側に送るために機能する層であり、したがって当該機能を有する層であれば、特に限定されることはない。
本実施形態にかかる断熱容器用積層体10A、10にあっては、上述した各層の他、種々の機能を発揮する層が含まれていてもよい。
以下に本願発明の実施形態にかかる断熱容器、および断熱容器の製造方法について説明する。
紙から構成される基材層の裏面に310℃の温度でTダイより押し出し、引き取り速度が100m/分、エアギャップ長さが140mmで40μmの厚さになるよう押出しラミネートを行うことで水蒸気遮断層を形成した。さらに、基材層の表面に引き取り速度が60m/分で表面層とカバー層を共押しすることで表面層とカバー層を形成した。ついでグラビア校正機により、表面層上に白インキを全面印刷した後、色インキをパターン状に印刷することで発泡前の断熱容器用積層体を得た。その後、当該断熱容器用積層体を裁断して円柱状にし、対流式オーブンを用いて120℃で5分間加熱することでカバー層を発泡させて発泡後の断熱容器用積層体を得た。
上記の作製方法により、以下の構成からなる実施例1の断熱容器用積層体を得た。
・層構成:
印刷層/表面層/カバー層/基材層/水蒸気遮断層
・印刷層:
乾燥後の印刷層の全固形分の合計質量に対するウレタン樹脂の割合35質量%
・表面層:
LLDPE(東ソー(株)製ニポロン−L M72)
密度925kg/m3
MFR20g/10分
溶融温度121℃
厚さ10μm
・カバー層:
LDPE(東ソー(株)製ペトロセン 212)
密度919kg/m3
MFR13g/10分
溶融温度107℃
発泡前の厚さ60μm
発泡後の厚さ700μm(表面層を含む)
・基材層:
日本製紙(株)製コップ原紙
坪量280g/m2
・水蒸気遮断層:
MDPE(東ソー(株)製ペトロセン LW04−1)
密度940kg/m3
MFR7g/10分
溶融温度133℃
厚さ40μm
上記の作製方法により、以下の構成からなる実施例2の断熱容器用積層体を得た。
・層構成:
印刷層/表面層/カバー層/基材層/水蒸気遮断層
・印刷層:
乾燥後の印刷層の全固形分の合計質量に対するウレタン樹脂の割合35質量%
・表面層:
LLDPE(東ソー(株)製ニポロン−L M72)
密度925kg/m3
MFR20g/10分
溶融温度121℃
厚さ5μm
・カバー層:
LDPE(東ソー(株)製ペトロセン 212)
密度919kg/m3
MFR13g/10分
溶融温度107℃
発泡前の厚さ60μm
発泡後の厚さ700μm(表面層を含む)
・基材層:
日本製紙(株)製コップ原紙
坪量280g/m2
・水蒸気遮断層:
MDPE(東ソー(株)製ペトロセン LW04−1)
密度940kg/m3
MFR7g/10分
溶融温度133℃
厚さ40μm
上記の作製方法により、以下の構成からなる実施例3の断熱容器用積層体を得た。
・層構成:
印刷層/表面層/カバー層/基材層/水蒸気遮断層
・印刷層:
乾燥後の印刷層の全固形分の合計質量に対するウレタン樹脂の割合35質量%
・表面層:
LLDPE(東ソー(株)製ニポロン−L M72)
密度925kg/m3
MFR20g/10分
溶融温度121℃
厚さ2.5μm
・カバー層:
LDPE(東ソー(株)製ペトロセン 212)
密度919kg/m3
溶融温度107℃
MFR13g/10分
発泡前の厚さ70μm
発泡後の厚さ750μm(表面層を含む)
・基材層:
日本製紙(株)製コップ原紙
坪量280g/m2
・水蒸気遮断層:
MDPE(東ソー(株)製ペトロセン LW04−1)
密度940kg/m3
MFR7g/10分
溶融温度133℃
厚さ40μm
上記の作製方法により、以下の構成からなる実施例4の断熱容器用積層体を得た。
・層構成:
印刷層/表面層/カバー層/基材層/水蒸気遮断層
・印刷層:
乾燥後の印刷層の全固形分の合計質量に対するウレタン樹脂の割合35質量%
・表面層:
LLDPE(東ソー(株)製ニポロン−L M65)
密度920kg/m3
MFR20g/10分
溶融温度120℃
厚さ10μm
・カバー層:
LDPE(東ソー(株)製ペトロセン 212)
密度919kg/m3
溶融温度107℃
MFR13g/10分
発泡前の厚さ60μm
発泡後の厚さ700μm(表面層を含む)
・基材層:
日本製紙(株)製コップ原紙
坪量280g/m2
・水蒸気遮断層:
MDPE(東ソー(株)製ペトロセン LW04−1)
密度940kg/m3
MFR7g/10分
溶融温度133℃
厚さ40μm
上記の作製方法により、以下の構成からなる実施例5の断熱容器用積層体を得た。
・層構成:
印刷層/表面層/カバー層/基材層/水蒸気遮断層
・印刷層:
乾燥後の印刷層の全固形分の合計質量に対するウレタン樹脂の割合25質量%
・表面層:
LLDPE(東ソー(株)製ニポロン−L M72)
密度925kg/m3
MFR20g/10分
溶融温度121℃
厚さ5μm
・カバー層:
LDPE(東ソー(株)製ペトロセン 212)
密度919kg/m3
MFR13g/10分
溶融温度107℃
発泡前の厚さ60μm
発泡後の厚さ600μm(表面層を含む)
・基材層:
日本製紙(株)製コップ原紙
坪量280g/m2
・水蒸気遮断層:
MDPE(東ソー(株)製ペトロセン LW04−1)
密度940kg/m3
MFR7g/10分
溶融温度133℃
厚さ40μm
上記の作製方法により、以下の構成からなる実施例6の断熱容器用積層体を得た。
・層構成:
印刷層/表面層/カバー層/基材層/水蒸気遮断層
・印刷層:
乾燥後の印刷層の全固形分の合計質量に対するウレタン樹脂の割合18質量%
・表面層:
LLDPE(東ソー(株)製ニポロン−L M72)
密度925kg/m3
MFR20g/10分
溶融温度121℃
厚さ5μm
・カバー層:
LDPE(東ソー(株)製ペトロセン 212)
密度919kg/m3
MFR13g/10分
溶融温度107℃
発泡前の厚さ60μm
発泡後の厚さ400μm(表面層を含む)
・基材層:
日本製紙(株)製コップ原紙
坪量280g/m2
・水蒸気遮断層:
MDPE(東ソー(株)製ペトロセン LW04−1)
密度940kg/m3
MFR7g/10分
溶融温度133℃
厚さ40μm
上記の作製方法により、以下の構成からなる比較例1の断熱容器用積層体を得た。
・層構成:
印刷層/表面層/カバー層/基材層/水蒸気遮断層
・印刷層:
乾燥後の印刷層の全固形分の合計質量に対するウレタン樹脂の割合35質量%
・表面層:
LDPE(東ソー(株)製ペトロセン 213)
密度918kg/m3
溶融温度102℃
MFR8g/10分
厚さ10μm
・カバー層:
LDPE(東ソー(株)製ペトロセン 212)
密度919kg/m3
MFR13g/10分
溶融温度107℃
発泡前の厚さ60μm
発泡後の厚さ650μm(表面層を含む)
・基材層:
日本製紙(株)製コップ原紙
坪量280g/m2
・水蒸気遮断層:
MDPE(東ソー(株)製ペトロセン LW04−1)
密度940kg/m3
MFR7g/10分
溶融温度133℃
厚さ40μm
上記の作製方法により、以下の構成からなる実施例2の断熱容器用積層体を得た。
・層構成:
印刷層/表面層/カバー層/基材層/水蒸気遮断層
・印刷層:
乾燥後の印刷層の全固形分の合計質量に対するウレタン樹脂の割合10質量%
・表面層:
LLDPE(東ソー(株)製ニポロン−L M72)
密度925kg/m3
MFR20g/10分
溶融温度121℃
厚さ5μm
・カバー層:
LDPE(東ソー(株)製ペトロセン 212)
密度919kg/m3
MFR13g/10分
溶融温度107℃
発泡前の厚さ60μm
発泡後の厚さ250μm(表面層を含む)
・基材層:
日本製紙(株)製コップ原紙
坪量280g/m2
・水蒸気遮断層:
MDPE(東ソー(株)製ペトロセン LW04−1)
密度940kg/m3
MFR7g/10分
溶融温度133℃
厚さ40μm
上記の作製方法により、以下の構成からなる比較例3の断熱容器用積層体を得た。
・層構成:
印刷層/カバー層/基材層/水蒸気遮断層
・印刷層:
乾燥後の印刷層の全固形分の合計質量に対するウレタン樹脂の割合35質量%
・カバー層:
LDPE(東ソー(株)製ペトロセン 212)
密度919kg/m3
MFR13g/10分
溶融温度107℃
発泡前の厚さ60μm
発泡後の厚さ700μm(表面層を含む)
・基材層:
日本製紙(株)製コップ原紙
坪量280g/m2
・水蒸気遮断層:
MDPE(東ソー(株)製ペトロセン LW04−1)
密度940kg/m3
MFR7g/10分
溶融温度133℃
厚さ40μm
発泡前後の厚みは、厚み計(ダイヤルシックネスゲージG:(株)尾崎製作所製)を用いて測定し、差分から白インキと色インキを積層した部位の表面層とカバー層の厚みの和を算出し、以下の基準に従って評価した。
A:450μm以上
B:300μm以上450μm未満
C:300μm未満
発泡後の印刷層の表面について、白インキ印刷部の厚みと、この白インキ印刷部に積層された色インキ印刷部の厚みを厚み計(ダイヤルシックネスゲージG:(株)尾崎製作所製)を用いて測定し、その差分を段差とした。そして、この段差について以下の基準に従って評価した。
A:白インキ印刷部と色インキ部分の段差が100μm未満
B:白インキ印刷部と色インキ部分の段差が100μm以上200μm未満
C:白インキ印刷部と色インキ部分の段差が200μm以上
発泡後の色インキ印刷部の外観状態を目視による観察と指触を行ない、表面の滑らかさを以下の基準に従って評価した。
A:表面が滑らかで、凹凸を感じない。
B:わずかに凹凸を感じる。
C:かなり凹凸があり、ざらつきを感じる。
上記発泡厚み、発泡追随性、および発泡外観のそれぞれについての評価結果を表1に示す。
10A…断熱容器用積層体(発泡前)
11…カバー層(発泡後)
11A…カバー層(発泡前)
12…基材層
13…水蒸気遮断層
15…印刷層
16…表面層
Claims (1)
- 外面側から、印刷層、表面層、カバー層、紙から構成される基材層、前記基材層を構成する紙から発生する水蒸気を遮断する水蒸気遮断層、を少なくとも有する断熱容器用積層体であって、
前記カバー層は、少なくとも高圧法低密度ポリエチレンから構成されており、
前記表面層は、JIS K6922−2(2010年)により測定される融点が、前記カバー層を構成する高圧法低密度ポリエチレンの融点よりも高いポリエチレン系樹脂から構成されており、
前記印刷層は、バインダーとしてウレタン樹脂を含み、かつ印刷層の全固形分の合計質量に対する当該ウレタン樹脂の割合が18質量%以上であり、さらに、
前記カバー層は、発泡しており、その厚さが300〜900μmであり、
前記印刷層が、白インキを印刷した白インキ印刷部と、当該白インキ印刷部上に色インキを印刷した色インキ印刷部との積層構造を有しており、
前記白インキ印刷部と色インキ部の段差が200μm未満である
ことを特徴とする断熱容器用積層体。