JP2017105986A - ステンレス鋼板用潤滑塗料および潤滑ステンレス鋼板 - Google Patents
ステンレス鋼板用潤滑塗料および潤滑ステンレス鋼板 Download PDFInfo
- Publication number
- JP2017105986A JP2017105986A JP2016216584A JP2016216584A JP2017105986A JP 2017105986 A JP2017105986 A JP 2017105986A JP 2016216584 A JP2016216584 A JP 2016216584A JP 2016216584 A JP2016216584 A JP 2016216584A JP 2017105986 A JP2017105986 A JP 2017105986A
- Authority
- JP
- Japan
- Prior art keywords
- stainless steel
- mass
- parts
- polyethylene wax
- lubricating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】アクリル系樹脂およびポリエチレンワックスを含み、前記ポリエチレンワックスの融点が115℃以上であり前記アクリル系樹脂100質量部に対して20質量部超〜50質量部の前記ポリエチレンワックスを含有する、ステンレス鋼板用潤滑塗料。
【選択図】なし
Description
加工時に潤滑性を得るために一般的には潤滑油が広く用いられているが、潤滑油は垂れ落ちたり、また揮発性があり空気中に拡散するなど、作業環境を低下させる場合があった。
ワックスは潤滑剤として広く用いられており、特に低融点のものは摩擦係数が低いために良く用いられている。しかし一方で、ワックスは固化しにくい欠点があり、ワックスを多く添加して潤滑性を向上させようとした場合、焼付け炉等で塗料を乾燥させようとしてもワックスが固化せずに皮膜にベタツキが残ってしまう問題があった。
特許文献2の発明は、潤滑ステンレス鋼板としての効果が得られたが、ステンレス鋼における連続プレス時や激しい深絞り成形時にはまだ改良の必要があった。
(1) アクリル系樹脂およびポリエチレンワックスを含み、前記ポリエチレンワックスの融点が115℃以上であり、前記アクリル系樹脂100質量部に対して20質量部超〜50質量部のポリエチレンワックスを含有する、ステンレス鋼板用潤滑塗料。
(2) さらに、有機カルシウム化合物を、前記アクリル系樹脂100質量部に対して、1質量部〜10質量部含有する(1)に記載のステンレス鋼板用潤滑塗料。
(3) 水系溶媒を用い、前記ポリエチレンワックスをエマルション化して添加する、(1)または(2)に記載のステンレス鋼板用潤滑塗料の製造方法。
(4) ステンレス鋼板上に、(1)または(2)のいずれか1に記載のステンレス鋼板用潤滑塗料を塗布し、熱風乾燥して、乾燥後の質量で片面当たり0.5〜2.5g/m2の潤滑皮膜を形成する潤滑ステンレス鋼板の製造方法。
(5) 上記(1)または(2)に記載のステンレス鋼板用潤滑塗料を、乾燥後の質量で片面当たり0.5〜2.5g/m2有する潤滑ステンレス鋼板。
本発明のステンレス鋼板用潤滑塗料は、アクリル系樹脂含有水性塗料であって、融点が115℃以上のポリエチレンワックスを、アクリル系樹脂100質量部に対して20質量部超〜50質量部含有するステンレス鋼板用潤滑塗料である。
本発明に用いるアクリル系樹脂は、特に限定されない。好ましくは1.アクリル酸、メタクリル酸、マレイン酸、無水マレイン酸、イタコン酸、フマル酸等の脂肪酸、2.上記1.の脂肪酸をメチル化、エチル化、イソプロピル化、ブチル化、2-エチルヘキシル化等をしたエステル、3.上記1.の脂肪酸とアンモニア等のアミド、4.スチレン、5.上記1.の脂肪酸にポリオキシエチレンを付加したもの、の上記1.から5.からなる群から選ばれる1種類または2種類以上をモノマーとして重合または共重合したものを使用する。重合または共重合する方法としては、溶液重合法、エマルション重合法または懸濁重合法などが例示できる。アクリル系樹脂に添加する添加剤としては、一般的に塗料に広く用いられている界面活性剤、防錆剤、極圧剤、pH調整剤等を合計で前記アクリル系樹脂100質量部に対して10質量部以下含有することができる。潤滑塗料の溶媒は、水系あるいは有機溶剤のいずれでも良いが水系溶媒が好ましい。
用いるポリエチレンワックスは、融点115℃以上のポリエチレンワックスであれば限定されない。好ましくは中密度〜高密度ポリエチレンワックス(密度0.930g/cm3以上)を使用する。融点が115℃未満であると、前記アクリル系樹脂100質量部に対して20質量部超えて添加した場合に、塗料乾燥後に容易に固化せずにベタツキが発生するため、融点115℃以上のポリエチレンワックスとする。特に融点が120℃以上の高密度ポリエチレンワックス(密度0.942g/cm3以上)が好ましく、さらに融点が130℃以上のポリエチレンワックスがより好ましい。融点は145℃以下であることが好ましい。融点が高くなりすぎると硬くなり、プレス加工時の金型との接触で皮膜の剥離が大きくなることがある。
融点115℃以上のポリエチレンワックスは、エマルション化したものをアクリル系樹脂含有水性塗料に添加するとアクリル系樹脂含有水性塗料に均一に混ざり、得られる潤滑塗料の特性が優れるので好ましい。
エマルション化されたポリエチレンワックスの平均粒径は1.0μm未満が好ましい。平均粒径が小さいほうがポリエチレンワックスが皮膜に均一に分散するためである。さらに均一に分散するためには、平均粒径が0.2μm以下であればより好ましい。
一般的に塗料に広く用いられている界面活性剤、防錆剤、極圧剤、pH調整剤などを合計で前記アクリル系樹脂100質量部に対して10質量部以下含有することができる。水性塗料の溶媒は、水を主体とする溶媒で、少量の有機溶媒を含んでも良いが潤滑塗料中の揮発性有機溶剤発生量を極力低減できるので水系溶媒が好ましい。
1)特許文献2の基本的技術思想として、摩擦係数の小さい低融点ワックスを所定量使用する潤滑塗料では、ステンレス鋼板の高面圧のプレス加工では、前記アクリル系樹脂100質量部に対して20質量部以下のワックスの添加では、十分な耐型かじり性が得られない場合があり、ステンレス鋼板の高面圧のプレス加工ではより耐型かじり性を上げる必要がある。
融点115℃以上の高融点ポリエチレンワックスはそれ自体の摩擦係数が低融点ポリエチレンワックスよりも高いため、低融点ポリエチレンワックスと同量程度添加したのでは摩擦抵抗が十分に低下しないという懸念があったが、高融点ポリエチレンワックスを用いる場合は前記アクリル系樹脂100質量部に対して20質量部を超えて添加すると、アクリル樹脂の比率が低くなるため摩擦係数の高いアクリル樹脂の寄与が下がるとともに、高融点ポリエチレンワックス摩擦係数低減効果が現れるので従来得られなかった優れた潤滑性が得られる。
この理由は不明であるが以下のことが考えられる。
高融点のワックスは、低融点のワックスと比較して粘度が高く、金型と鋼板との接触摺動時にその隙間に残存しやすいため、深絞り性および型かじりに対して効果があると推定される。
2)本願の型かじり性の評価は、実施例で説明するように特許文献1,2とは異なる評価方法である。特許文献1では角筒絞りの型カジリを観察し、特許文献2ではエリクセンカップ(円筒絞り)の型カジリで評価している。評価の段階(金型と板との接触面圧)としてはおよそ、本願>特許文献1>特許文献2であり、本願の「同じ供試材に対して高面圧(約200MPa)で20回連続して摺動しても摩擦係数が上昇しない」評価は、ステンレス鋼にとって好適な評価方法である。この理由はステンレス鋼では一回のプレスでは成形加工が完了せず複数回のプレス成型が行われる場合があるため、過酷なプレス成型の評価方法で初めてステンレス鋼の耐型かじり性を適切に評価できる。このような過酷なプレス成型の評価を行った従来技術はない。
ステンレス鋼板のプレス成形の際には、1回のプレスでは完了せずに、複数回のプレスで成形が行われる場合がある。その際に初期のプレスで塗装が損傷を受け、その後摩擦係数が上昇して行く型かじりという現象がある。耐型かじり性を向上させるために、必要により有機カルシウム化合物を添加する。
有機カルシウム化合物は、カルシウムを6質量%以上含有しているものを使用する。例えば、ステアリン酸カルシウム、オレイン酸カルシウム,ラウリン酸カルシウム等、脂肪酸がC12〜C18の脂肪酸カルシウム。あるいは、過塩基性アルキルベンゼンスルフォン酸カルシウム、過塩基性アルキルナフタレンスルフォン酸カルシウム,過塩基性アルキルアリールスルフォン酸カルシウム等の過塩基性石油スルフォン酸カルシウムを使用する。
有機カルシウム化合物は、前記アクリル系樹脂100質量部に対して1〜10質量部添加すると型かじり性改善効果が得られるため、必要に応じて添加する。1質量部未満であると、型かじり性改善効果が得られない。10質量部超えて添加しても効果は飽和する。
本発明のステンレス鋼板用潤滑塗料は、ステンレスの種類によらず全てのステンレス鋼板に適用でき深絞り加工性と耐型かじり性に優れる潤滑ステンレス鋼板が得られる。特に絞り加工が用いられるフェライト系ステンレス鋼板のプレス加工に適している。
本発明のステンレス鋼板用潤滑塗料をステンレス鋼板表面に塗布して乾燥する。塗布方法は、限定されないが、スプレー塗布、ロールコーター塗布、浸漬塗布、刷毛塗塗布等の方法が例示できる。本発明塗料の固形分(アクリル系樹脂+ポリエチレンワックス+カルシウム化合物)濃度は、用いられる塗布方法や乾燥方法に合わせて調製することができる。好ましくは1質量%〜50質量%である。塗料の乾燥方法は、一般的な焼付け炉等を使用することが出来るが、本発明の潤滑塗料は固化しやすいため、簡易的な熱風乾燥で十分に固化させることが出来る。塗装は、鋼板の使用用途により鋼板の片面または両面に行うが、乾燥後の付着量は、片面当り0.5〜2.5g/m2が好ましい。
乾燥後の付着量が0.5g/m2〜2.5g/m2であると皮膜の損傷が起こりにくく、耐型かじり性が優れ、潤滑効果が十分で、摺動時の皮膜の剥がれが少なく、剥がれたものがプレス金型に堆積してプレス加工に悪影響を及ぼすことがない。より好ましくは0.8g/m2以上、2.0g/m2以下、さらに好ましくは1.5g/m2以下とする。
摩擦係数は測定方法による違いがあり、本発明で得られる潤滑皮膜の同一サンプルでも測定方法により絶対値が異なるため、絶対値では評価できないが、一般的には相対比較で高いとすべりが悪くなるため、プレス性は低下する。一方で低すぎると、鋼帯をコイルにした場合、コイルが自重でつぶれる場合があり、また滑りすぎて板のハンドリングに支障をきたす場合もある。
表1の組成のアクリル樹脂含有水性塗料を作製し、ステンレス鋼板(SUS444の(19mass%Cr-2mass%Mo-0.4mass%Nb)2D仕上げ)に、スプレーで均一に塗布し、ドライヤーの熱風で乾燥させる塗装を板の両面に実施し、その特性を評価した。なお、各塗料とも固形分(アクリル樹脂+ポリエチレンワックス+カルシウム化合物)濃度を10質量%に調整した。その結果を表1に示す。ポリエチレンワックスはエマルション化したものを水性塗料に混合して用いた。
1.摩擦係数は、図1に示す装置、すなわち曲率5がR20の上下の金型の間に、厚さ1.5mm×長さ200mm×幅20mmの供試材を挟み、押し付け荷重方向6で押し付けた状態で引抜荷重方向8に引抜き、引抜荷重を測定する摺動試験機で引抜荷重を測定した。摩擦係数は、引抜荷重/押し付け荷重、により求めた。試験条件は、金型:材質SKD11、曲率R20、サンプル幅20mm、摺動距離:100mm、引抜速度:20mm/s、押し付け荷重:3920Nで行った。金型と供試材の接触面積は約20mm2(20mm幅×約1mm)であり、面圧は約200MPa(=3920N/20mm2)となる。
2.ベタツキ有無、潤滑皮膜形成後のステンレス鋼板に、皮膜無しのステンレス鋼を面圧0.01MPaで押し付け、剥がしたのちに皮膜無しのステンレス鋼板の表面に潤滑皮膜が転写されていないかを、蛍光X線でCカウント量を測定することにより評価した。C量の増加は見られない場合、ベタツキ無しとした。皮膜無しのステンレス鋼板の表面にC量の増加があった場合をベタツキ有り、と評価した。
3.深絞り性は、限界深絞り比(LDR(=Limiting Drawing Ratio))測定により評価した。円板形の試験片に、円筒形のポンチ(直径d=33mm)を押し込み、破断することなく、絞り抜けする最大の試験片直径(D(mm))を求め、D/dの計算式で求めた。ポンチの肩Rは3mm、ポンチ送り速度1mm/秒、しわ押さえ荷重10kN、しわ押さえ肩R3mmで行った。
4.耐型かじり性は、図1に記載する摺動試験機を用い、1つの供試材を途中金型研磨なしで20回連続して摺動し、摩擦係数が上昇しない場合を耐型かじり性良好と評価した。摩擦係数が上昇しないとは、「同じ供試材に対して高面圧(約200MPa)で20回連続して摺動しても20回目の摩擦係数が0.15未満である」とし、この場合を耐型かじり性良好とし、「0.15以上」を不可と評価した。
A:ステアリン酸カルシウム
B:過塩基性石油スルフォン酸カルシウム
表1の樹脂の種類、
アクリル1:スチレン+メタクリル酸ブチル+メタクリル酸+エチレン性不飽和カルボン酸 の共重合物(質量比25:30:24:21)
アクリル2:スチレン+メタクリル酸ブチル+メタクリル酸 の共重合物(質量比25:51:24)
表1のP系添加剤、
*)オレイルアシッドホスフェイト(極圧剤)
表1の結果から、実施例1〜18では、高融点のポリエチレンワックスを前記アクリル系樹脂100質量部に対して従来の量より多い特定量添加すると、ステンレス鋼板に対して優れた加工性を有する潤滑塗料が得られることがわかる。表1の実施例1、3、5、6、15、17では有機カルシウム化合物を無添加としても耐型かじり性に優れるが、有機カルシウム化合物を添加するとさらに耐型かじり性が向上した。比較例1、4、6では高融点のポリエチレンワックスの量が樹脂に対して少ないと耐型かじり性が劣る。比較例5では低融点のポリエチレンワックスが前記アクリル系樹脂100質量部に対して多量に添加されると潤滑塗料がベタツクことがわかる。比較例2,3では、低融点ワックスを使用すると、摩擦係数は低くなるがステンレス鋼用の潤滑塗料としては耐型かじり性が低いことがわかる。また、比較例1、2、3、4、6のポリエチレンワックスの添加量が低い場合、LDR値が実施例より低く、深絞り性が劣る結果となっている。
8:引抜荷重方向
Claims (5)
- アクリル系樹脂およびポリエチレンワックスを含み、前記ポリエチレンワックスの融点が115℃以上であり前記アクリル系樹脂100質量部に対して20質量部超〜50質量部の前記ポリエチレンワックスを含有する、ステンレス鋼板用潤滑塗料。
- さらに、有機カルシウム化合物を、前記アクリル系樹脂100質量部に対して、1質量部〜10質量部含有する請求項1に記載のステンレス鋼板用潤滑塗料。
- 水系溶媒を用い、前記ポリエチレンワックスをエマルション化して添加する、請求項1または2に記載のステンレス鋼板用潤滑塗料の製造方法。
- ステンレス鋼板上に、請求項1または2に記載のステンレス鋼板用潤滑塗料を塗布し、熱風乾燥して、乾燥後の質量で片面当たり0.5〜2.5g/m2の潤滑皮膜を形成する潤滑ステンレス鋼板の製造方法。
- 請求項1または2に記載のステンレス鋼板用潤滑塗料を、乾燥後の質量で片面当たり0.5〜2.5g/m2有する潤滑ステンレス鋼板。