JP2015053517A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2015053517A5 JP2015053517A5 JP2014234317A JP2014234317A JP2015053517A5 JP 2015053517 A5 JP2015053517 A5 JP 2015053517A5 JP 2014234317 A JP2014234317 A JP 2014234317A JP 2014234317 A JP2014234317 A JP 2014234317A JP 2015053517 A5 JP2015053517 A5 JP 2015053517A5
- Authority
- JP
- Japan
- Prior art keywords
- rare earth
- mass
- sintered magnet
- phase
- combination
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
従って、本発明は、下記のNd−Fe−B系希土類焼結磁石を提供する。
請求項1:
R(RはY及びScを含む希土類元素のうちの1種又は2種以上の組み合わせ)、T(TはFe、又はFe及びCo)、B、Ni、Si、Cu、及びM(MはGa、Zr、Nb、Hf、Ta、W、Mo、Al、V、Cr、Ti、Ag、Mn、Ge、Sn、Bi、Pb及びZnから選ばれる1種又は2種以上の組み合わせ)を含有し、
Rが26〜36質量%、Bが0.5〜1.3質量%、Niが0.1〜2.0質量%、Siが0.1〜3.0質量%、Cuが0.05〜1.0質量%、Mが0.05〜4.0質量%、残部がT及び不可避不純物である組成を有し、RがNdを含む焼結体からなり、該焼結体中にR2−T14−B1相を主相として含むことを特徴とするNd−Fe−B系希土類焼結磁石。
請求項2:
Rが、NdとDyとの組み合わせ、NdとPrとの組み合わせ、又はNdとPrとDyとの組み合わせを含むことを特徴とする請求項1記載のNd−Fe−B系希土類焼結磁石。
請求項3:
上記主相の平均結晶粒径が3.0〜10.0μmであることを特徴とする請求項1又は2記載のNd−Fe−B系希土類焼結磁石。
請求項4:
R、Co、Si、Ni及びCuを含む化合物の相が、焼結体中に析出していることを特徴とする請求項1乃至3のいずれか1項記載のNd−Fe−B系希土類焼結磁石。
請求項5:
焼結体が、上記不可避不純物として、O、C及びNから選ばれる1種又は2種以上を含み、上記化合物の相が、O、C及びNから選ばれる1種又は2種以上を含むことを特徴とする請求項4記載のNd−Fe−B系希土類焼結磁石。
請求項6:
焼結体中のO(酸素)量が8000ppm以下、C(炭素)量が2000ppm以下、N(窒素)量が1000ppm以下であることを特徴とする請求項5記載のNd−Fe−B系希土類焼結磁石。
請求項7:
R、Co、Si、Ni及びCuと、O、C及びNから選ばれる1種又は2種以上とを含む化合物の相が、焼結体中に析出していることを特徴とする請求項5又は6記載のNd−Fe−B系希土類焼結磁石。
請求項8:
PCT(プレッシャークッカー試験)における、120℃、2気圧、100時間後の試験前の表面積当たりの質量減が1.3g/cm 2 以下であることを特徴とする請求項1乃至7のいずれか1項記載のNd−Fe−B系希土類焼結磁石。
請求項9:
保磁力が18.11kOe以上であることを特徴とする請求項1乃至8のいずれか1項記載のNd−Fe−B系希土類焼結磁石。
更に、本発明は、下記のR−T−B系希土類焼結磁石が関連する。
[1]R(RはY及びScを含む希土類元素のうちの1種又は2種以上の組み合わせ)、T(TはFe、又はFe及びCo)、B、Ni、Si、Cu、及びM(MはGa、Zr、Nb、Hf、Ta、W、Mo、Al、V、Cr、Ti、Ag、Mn、Ge、Sn、Bi、Pb及びZnから選ばれる1種又は2種以上の組み合わせ)を含有し、
Rが26〜36質量%、Bが0.5〜1.5質量%、Niが0.1〜2.0質量%、Siが0.1〜3.0質量%、Cuが0.05〜1.0質量%、Mが0.05〜4.0質量%、残部がT及び不可避不純物である組成を有する焼結体からなることを特徴とするR−T−B系希土類焼結磁石。
[2]焼結体が、上記不可避不純物として、O、C及びNから選ばれる1種又は2種以上を含むことを特徴とする[1]記載のR−T−B系希土類焼結磁石。
[3]焼結体中のO(酸素)量が8000ppm以下、C(炭素)量が2000ppm以下、N(窒素)量が1000ppm以下であることを特徴とする[2]記載のR−T−B系希土類焼結磁石。
[4]焼結体中にR2−T14−B1相を主相として含み、該相の平均結晶粒径が3.0〜10.0μmであることを特徴とする[1]乃至[3]のいずれかに記載のR−T−B系希土類焼結磁石。
[5]R、Co、Si、Ni及びCuを含む化合物の相が、焼結体中に析出していることを特徴とする[1]乃至[4]のいずれかに記載のR−T−B系希土類焼結磁石。
請求項1:
R(RはY及びScを含む希土類元素のうちの1種又は2種以上の組み合わせ)、T(TはFe、又はFe及びCo)、B、Ni、Si、Cu、及びM(MはGa、Zr、Nb、Hf、Ta、W、Mo、Al、V、Cr、Ti、Ag、Mn、Ge、Sn、Bi、Pb及びZnから選ばれる1種又は2種以上の組み合わせ)を含有し、
Rが26〜36質量%、Bが0.5〜1.3質量%、Niが0.1〜2.0質量%、Siが0.1〜3.0質量%、Cuが0.05〜1.0質量%、Mが0.05〜4.0質量%、残部がT及び不可避不純物である組成を有し、RがNdを含む焼結体からなり、該焼結体中にR2−T14−B1相を主相として含むことを特徴とするNd−Fe−B系希土類焼結磁石。
請求項2:
Rが、NdとDyとの組み合わせ、NdとPrとの組み合わせ、又はNdとPrとDyとの組み合わせを含むことを特徴とする請求項1記載のNd−Fe−B系希土類焼結磁石。
請求項3:
上記主相の平均結晶粒径が3.0〜10.0μmであることを特徴とする請求項1又は2記載のNd−Fe−B系希土類焼結磁石。
請求項4:
R、Co、Si、Ni及びCuを含む化合物の相が、焼結体中に析出していることを特徴とする請求項1乃至3のいずれか1項記載のNd−Fe−B系希土類焼結磁石。
請求項5:
焼結体が、上記不可避不純物として、O、C及びNから選ばれる1種又は2種以上を含み、上記化合物の相が、O、C及びNから選ばれる1種又は2種以上を含むことを特徴とする請求項4記載のNd−Fe−B系希土類焼結磁石。
請求項6:
焼結体中のO(酸素)量が8000ppm以下、C(炭素)量が2000ppm以下、N(窒素)量が1000ppm以下であることを特徴とする請求項5記載のNd−Fe−B系希土類焼結磁石。
請求項7:
R、Co、Si、Ni及びCuと、O、C及びNから選ばれる1種又は2種以上とを含む化合物の相が、焼結体中に析出していることを特徴とする請求項5又は6記載のNd−Fe−B系希土類焼結磁石。
請求項8:
PCT(プレッシャークッカー試験)における、120℃、2気圧、100時間後の試験前の表面積当たりの質量減が1.3g/cm 2 以下であることを特徴とする請求項1乃至7のいずれか1項記載のNd−Fe−B系希土類焼結磁石。
請求項9:
保磁力が18.11kOe以上であることを特徴とする請求項1乃至8のいずれか1項記載のNd−Fe−B系希土類焼結磁石。
更に、本発明は、下記のR−T−B系希土類焼結磁石が関連する。
[1]R(RはY及びScを含む希土類元素のうちの1種又は2種以上の組み合わせ)、T(TはFe、又はFe及びCo)、B、Ni、Si、Cu、及びM(MはGa、Zr、Nb、Hf、Ta、W、Mo、Al、V、Cr、Ti、Ag、Mn、Ge、Sn、Bi、Pb及びZnから選ばれる1種又は2種以上の組み合わせ)を含有し、
Rが26〜36質量%、Bが0.5〜1.5質量%、Niが0.1〜2.0質量%、Siが0.1〜3.0質量%、Cuが0.05〜1.0質量%、Mが0.05〜4.0質量%、残部がT及び不可避不純物である組成を有する焼結体からなることを特徴とするR−T−B系希土類焼結磁石。
[2]焼結体が、上記不可避不純物として、O、C及びNから選ばれる1種又は2種以上を含むことを特徴とする[1]記載のR−T−B系希土類焼結磁石。
[3]焼結体中のO(酸素)量が8000ppm以下、C(炭素)量が2000ppm以下、N(窒素)量が1000ppm以下であることを特徴とする[2]記載のR−T−B系希土類焼結磁石。
[4]焼結体中にR2−T14−B1相を主相として含み、該相の平均結晶粒径が3.0〜10.0μmであることを特徴とする[1]乃至[3]のいずれかに記載のR−T−B系希土類焼結磁石。
[5]R、Co、Si、Ni及びCuを含む化合物の相が、焼結体中に析出していることを特徴とする[1]乃至[4]のいずれかに記載のR−T−B系希土類焼結磁石。
Claims (9)
- R(RはY及びScを含む希土類元素のうちの1種又は2種以上の組み合わせ)、T(TはFe、又はFe及びCo)、B、Ni、Si、Cu、及びM(MはGa、Zr、Nb、Hf、Ta、W、Mo、Al、V、Cr、Ti、Ag、Mn、Ge、Sn、Bi、Pb及びZnから選ばれる1種又は2種以上の組み合わせ)を含有し、
Rが26〜36質量%、Bが0.5〜1.3質量%、Niが0.1〜2.0質量%、Siが0.1〜3.0質量%、Cuが0.05〜1.0質量%、Mが0.05〜4.0質量%、残部がT及び不可避不純物である組成を有し、RがNdを含む焼結体からなり、該焼結体中にR2−T14−B1相を主相として含むことを特徴とするNd−Fe−B系希土類焼結磁石。 - Rが、NdとDyとの組み合わせ、NdとPrとの組み合わせ、又はNdとPrとDyとの組み合わせを含むことを特徴とする請求項1記載のNd−Fe−B系希土類焼結磁石。
- 上記主相の平均結晶粒径が3.0〜10.0μmであることを特徴とする請求項1又は2記載のNd−Fe−B系希土類焼結磁石。
- R、Co、Si、Ni及びCuを含む化合物の相が、焼結体中に析出していることを特徴とする請求項1乃至3のいずれか1項記載のNd−Fe−B系希土類焼結磁石。
- 焼結体が、上記不可避不純物として、O、C及びNから選ばれる1種又は2種以上を含み、上記化合物の相が、O、C及びNから選ばれる1種又は2種以上を含むことを特徴とする請求項4記載のNd−Fe−B系希土類焼結磁石。
- 焼結体中のO(酸素)量が8000ppm以下、C(炭素)量が2000ppm以下、N(窒素)量が1000ppm以下であることを特徴とする請求項5記載のNd−Fe−B系希土類焼結磁石。
- R、Co、Si、Ni及びCuと、O、C及びNから選ばれる1種又は2種以上とを含む化合物の相が、焼結体中に析出していることを特徴とする請求項5又は6記載のNd−Fe−B系希土類焼結磁石。
- PCT(プレッシャークッカー試験)における、120℃、2気圧、100時間後の試験前の表面積当たりの質量減が1.3g/cm 2 以下であることを特徴とする請求項1乃至7のいずれか1項記載のNd−Fe−B系希土類焼結磁石。
- 保磁力が18.11kOe以上であることを特徴とする請求項1乃至8のいずれか1項記載のNd−Fe−B系希土類焼結磁石。