JP2013224019A - 加飾成形用シート、加飾成形用プレフォーム成形体、加飾インサート成形体及びその製造方法 - Google Patents
加飾成形用シート、加飾成形用プレフォーム成形体、加飾インサート成形体及びその製造方法 Download PDFInfo
- Publication number
- JP2013224019A JP2013224019A JP2013053839A JP2013053839A JP2013224019A JP 2013224019 A JP2013224019 A JP 2013224019A JP 2013053839 A JP2013053839 A JP 2013053839A JP 2013053839 A JP2013053839 A JP 2013053839A JP 2013224019 A JP2013224019 A JP 2013224019A
- Authority
- JP
- Japan
- Prior art keywords
- molding
- decorative
- molded body
- preform
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】加飾インサート成形用プレフォーム成形体を成形するための加飾成形用シートであって、繊維絡合体の見かけ密度が0.45g/cm3以上であり、極細繊維の繊維絡合体と繊維絡合体に含浸された架橋された非発泡ポリウレタンとを含み、極細繊維は平均繊度0.9dtex以下の単繊維繊度を有し、且つ、ガラス転移温度(Tg)が100〜120℃のポリエステルからなり、架橋された非発泡ポリウレタンは、DMFに24時間浸漬して乾燥した後の、浸漬前の質量に対する質量減少率が5質量%以下である。
【選択図】図1
Description
質量減少率(%)=(1−DMF浸漬後の重量/DMF浸漬前の重量)×100、により算出される。
本工程においては、はじめに、溶融紡糸により海島型複合繊維からなる長繊維ウェブを製造する。長繊維ウェブは、例えば、いわゆるスパンボンド法を用いて、海島型複合繊維を溶融紡糸法を用いて紡糸し、これを切断せずにネット上に捕集してウェブを形成する方法が好ましく用いられる。
次に、得られた長繊維ウェブを4〜100枚程度重ねて絡合させることによりウェブ絡合シートを形成する。ウェブ絡合シートは、ニードルパンチや高圧水流処理等の公知の不織布製造方法を用いて長繊維ウェブに絡合処理を行うことにより形成される。以下に、ニードルパンチによる絡合処理について詳しく説明する。
次に、ウェブ絡合シートを熱収縮させることにより、ウェブ絡合シートの繊維密度および絡合度合を高める。なお、本工程においては、長繊維を含有するウェブ絡合シートを熱収縮させることにより、短繊維を含有するウェブ絡合シートを熱収縮させる場合に比べて、ウェブ絡合シートを大きく収縮させることができる。熱収縮処理されたウェブ絡合シートは、加熱ロールや加熱プレスすることにより、さらに、繊維密度が高められてもよい。
ウェブ絡合シートの形態安定性を高める目的で、ウェブ絡合シートの極細繊維化処理を行う前または後に、収縮処理されたウェブ絡合シートに非発泡ポリウレタンの水系エマルジョンを含浸させた後、ポリウレタンを凝固及び架橋させる。
ウェブ絡合シート中の海島型複合繊維は、海成分を水や溶剤等で抽出または分解除去することにより極細繊維に変換される。ポリビニルアルコール系樹脂等の水溶性樹脂を海成分に用いた海島型複合繊維の場合においては、水、アルカリ性水溶液、酸性水溶液等で熱水加熱処理することにより海成分が除去される。
海成分の熱可塑性樹脂としてエチレン変性ポリビニルアルコール(エチレン単位の含有量8.5モル%、重合度380、ケン化度98.7モル%)、島成分の熱可塑性樹脂としてTgが110℃である、イソフタル酸変性したポリエチレンテレフタレート(イソフタル酸単位の含有量6.0モル%)を、それぞれ個別に溶融させた。そして、海成分中に均一な断面積の島成分が25個分布した断面を形成しうるような、多数のノズル孔が並列状に配置された複数紡糸用口金に、それぞれの溶融樹脂を供給した。このとき、海成分と島成分との質量比が海成分/島成分=25/75となるように圧力調整しながら供給した。そして、口金温度260℃に設定されたノズル孔より吐出させた。
図9に示した部分を光学顕微鏡で側面から観察し写真を撮影した。そして、プレフォーム成形体の山の裾野の立ち上がり部分の角度θを測定し、賦形率(%)=(135/θ)×100 の式により金型の山の裾野の立ち上がり部分の角度に対するプレフォーム成形体の山の裾野の立ち上がり部分の角度の割合を算出した。
プレフォーム成形体の山の頂面の中央部の厚みを測定した。そして、加飾成形用シートの厚みに対する山の頂面の中央部の厚みを算出した。
プレフォーム成形体の表面状態を以下の基準で判定した。
5級:あらびがほとんど現れない。
3〜4級:少しあらびが現れる。
1〜2級:あらびが激しく現れる。
加飾インサート成形体の図9に示した部分を光学顕微鏡で側面から観察し写真を撮影した。そして、プレフォーム成形体の山の裾野の立ち上がり部分の角度θを測定し、賦形率(%)=(135/θ)×100 の式により金型の山の裾野の立ち上がり部分の角度に対するプレフォーム成形体の山の裾野の立ち上がり部分の角度の割合を算出し、形状の賦形性を以下の基準で判定した。
A:賦形率が95%以上であった。
B:賦形率が95%未満であった。
金型(i)で得られた加飾インサート成形体の銀面層の外観を観察し、以下の基準で評価した。
A:表面に高低差30μm以上の凹凸模様が残っていた。
B:表面の凹凸模様がほとんど押しつぶされて消失していた。
(金型(ii)の表面の凹凸模様)
金型(ii)で得られた加飾インサート成形体の銀面層の外観を観察し、以下の基準で評価した。
A:表面に高低差130μm以上の凹凸模様が残っていた。
B:表面に高低差130μm以上の凹凸模様が残らなかった。
実施例1において、島成分の熱可塑性樹脂としてTgが110℃である、イソフタル酸変性したポリエチレンテレフタレートを用いる代わりに、島成分の熱可塑性樹脂としてTgが120であるイソフタル酸変性したポリエチレンテレフタレートを用いた以外は実施例1と同様にして加飾成形用シートを得、また、プレフォーム成形体を得た。そして、同様にして評価した。結果を表1に示す。
実施例1において、島成分の熱可塑性樹脂としてTgが110℃である、イソフタル酸変性したポリエチレンテレフタレートを用いる代わりに、島成分の熱可塑性樹脂としてTgが100℃であるイソフタル酸変性したポリエチレンテレフタレートを用いた以外は実施例1と同様にして加飾成形用シートを得、また、プレフォーム成形体を得た。そして、同様にして評価した。結果を表1に示す。
実施例1において、繊維絡合体の見かけ密度を0.53g/cm3に調整する代わりに、非発泡ポリウレタン/繊維絡合体の質量比を29/71とすることにより繊維絡合体の見かけ密度を0.62g/cm3に調整した以外は実施例1と同様にして加飾成形用シートを得、また、プレフォーム成形体を得た。そして、同様にして評価した。結果を表1に示す。
実施例1において、緻密化された絡合ウェブに、DMF浸漬に対する質量減少率が0.5質量%である、架橋型の非発泡ポリウレタンを含浸させる代わりに、DMFに対する重量減少率が100質量%である、未架橋型の発泡ポリウレタンを形成するためのポリウレタンのDMF溶液(固形分20%)を含浸させ、湿式凝固させることにより、発泡ポリウレタン/絡合ウェブの質量比が18/82のポリウレタン絡合ウェブ複合体を形成した。上記変更以外は実施例1と同様にして加飾成形用シートを得、また、プレフォーム成形体を得た。そして、同様にして評価した。結果を表1に示す。
実施例1において、島成分の熱可塑性樹脂としてTgが110℃である、イソフタル酸変性したポリエチレンテレフタレートを用いる代わりに、島成分の熱可塑性樹脂としてTgが130℃であるポリエチレンテレフタレートを用いた以外は実施例1と同様にして加飾成形用シートを得、また、プレフォーム成形体を得た。そして、同様にして評価した。結果を表1に示す。
実施例1において、繊維絡合体の見かけ密度を0.53g/cm3に調整する代わりに、非発泡ポリウレタン/繊維絡合体の質量比を8/92とすることにより繊維絡合体の見かけ密度を0.43g/cm3に調整した以外は実施例1と同様にして加飾成形用シートを得、また、プレフォーム成形体を得た。そして、同様にして評価した。結果を表1に示す。
1a 極細単繊維
1b 繊維束
2 非発泡ポリウレタン
3 基材
4 銀面層
5 プレフォーム用金型
5a 上金型
5b 下金型
7 樹脂フィルム
10,60 加飾成形用シート
15,25 射出成形金型
15a,25a 可動側金型
15b,25b 固定側金型
15c,25c スペーサープレート
15d,25dキャビティ
15f,25f スプルーブッシュ
15g,15h,25g,25h ゲート
16 ノズル
20,40 プレフォーム成形体
21,41 成形体本体
21' 溶融樹脂
22,42 スプルーランナー
30,50 インサート成形体
E 端面
S' キャビティ表面の凹凸模様
S 銀面層表面の凹凸模様
W 皺
WL ウエルドライン形成部
Claims (10)
- 加飾インサート成形用プレフォーム成形体を成形するための加飾成形用シートであって、
極細繊維の繊維絡合体と前記繊維絡合体に含浸された架橋された非発泡ポリウレタンとを含む基材を備え、
前記繊維絡合体の見かけ密度が0.45g/cm3以上であり、
前記極細繊維は平均繊度0.9dtex以下の単繊維繊度を有し、且つ、ガラス転移温度(Tg)が100〜120℃のポリエステルからなり、
前記架橋された非発泡ポリウレタンは、N,N−ジメチルホルムアミドに24時間浸漬して乾燥した後の、浸漬前の質量に対する質量減少率が5質量%以下であることを特徴とする加飾成形用シート。 - 前記架橋された非発泡ポリウレタンが水系ポリウレタンエマルジョンに由来する請求項1に記載の加飾成形用シート。
- 150℃における30%伸長応力が50N/25mm以下である請求項1または2に記載の加飾成形用シート。
- 見かけ密度が0.50〜0.75g/cm3である請求項1〜3の何れか1項に記載の加飾成形用シート。
- 前記基材の表層に高分子弾性体を含む銀面層が積層形成されている請求項1〜4の何れか1項に記載の加飾成形用シート。
- ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリカーボネート、ABS系樹脂からなる群から選ばれる樹脂を含む樹脂フィルムに積層された請求項1〜5の何れか1項に記載の加飾成形用シート。
- 請求項1〜6の何れか1項に記載の加飾成形用シートを三次元形状に成形したことを特徴とする加飾インサート成形用プレフォーム成形体。
- インサート射出成形により成形され、樹脂成形体本体と、前記樹脂成形体の表層に配置された請求項7に記載のプレフォーム成形体とを備えることを特徴とする加飾インサート成形体。
- インサート射出成形により成形された、樹脂成形体本体と、前記樹脂成形体の表層に配置されたプレフォーム成形体とを備える加飾インサート成形体であって、
前記プレフォーム成形体が、請求項5に記載の加飾成形用シートを三次元形状に成形したプレフォーム成形体であり、その表面の前記銀面層に高低差100μm以上の凹凸模様が形成されていることを特徴とする加飾インサート成形体。 - 加飾インサート成形体の製造方法であって、
請求項5に記載の加飾成形用シートを三次元形状に成形した加飾インサート成形用プレフォーム成形体をインサート成形用金型のキャビティに配置する工程と、
前記成形用プレフォーム成形体が配置された金型を型締めし、溶融樹脂を射出することにより加飾インサート成形体を成形する工程とを備え、
前記キャビティの前記加飾インサート成形用プレフォーム成形体と接する面に凹凸模様が形成されていることを特徴とする加飾インサート成形体の製造方法。