JP2012500144A - モールドシーラーの調製方法、モールドシーラーアッセンブリおよびその組成物 - Google Patents
モールドシーラーの調製方法、モールドシーラーアッセンブリおよびその組成物 Download PDFInfo
- Publication number
- JP2012500144A JP2012500144A JP2011523955A JP2011523955A JP2012500144A JP 2012500144 A JP2012500144 A JP 2012500144A JP 2011523955 A JP2011523955 A JP 2011523955A JP 2011523955 A JP2011523955 A JP 2011523955A JP 2012500144 A JP2012500144 A JP 2012500144A
- Authority
- JP
- Japan
- Prior art keywords
- mold
- composition
- group
- alkyl
- mold sealer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、一般に熱可塑性部品を成形するのに有効なモールドシーラー組成物に関する。
高品質の平滑モールド表面、または高度に充填された熱可塑性複合物を使用するために半永久離型剤の効率が犠牲にされることが成形業者によって見出されることは、熱可塑性樹脂産業における共通の問題である。特にクロムまたはニッケル材料がモールド表面として用いられる場合は、とりわけ離型剤をモールド表面によく結合することができない。この離型剤はモールドから非常に簡単に剥がれてしまい、その結果、それらは複数回モールドから離型するにあたって充分に機能しない。この接着力の欠如は、硬化した離型剤をモールド表面から削ぎ取る際に証明されうる。
R1は、ヒドロキシおよびアルコキシから選択され;
R2は、アルキル、アルキレン、水素であり;
R3は、水素およびアルキルから選択され、ここで前記アルキルはアミノ基またはアルコキシシリル基によって任意に置換され;
Xは、C1−C6アルキレンであり;および
aは、0または1である。
(a)少なくとも1つの表面を有する部分を形成するためのモールドを提供するステップ;
(b)前記モールド形成部分の前記少なくとも1つの表面上にモールドシーラー組成物を塗布するステップであって、ここで前記モールドシーラー組成物は:
(i)式I:
本発明は、コーティングとして塗布される場合に耐久性を有し、コスト効率が良く、複数回の離型を可能にするモールドシーラー組成物を目的とする。また本発明は、本発明のモールドシーラー組成物で調製されたシールされたモールドアッセンブリも目的としている。そのような組成物を製造するための方法もまた開示する。
R1は、ヒドロキシおよびアルコキシから選択され;
R2は、アルキル、アルキレン、または水素であり;
R3は、水素およびアルキルから選択され、ここで前記アルキルは、任意にアミノ基またはアルコキシシリル基によって置換され;
Xは、C1−C6アルキレン(すなわち、C1、C2、C3、C4、C5、C6、望ましくはC3)であり;および
aは、0または1である。
(a)部分を形成するためのモールドを提供することであって、前記モールドは、少なくとも1つの表面を有し;
(b)モールドシーラー組成物を前記少なくとも1つの表面に塗布することであって、前記モールドシーラー組成物は、
(i)式I:
R1は、ヒドロキシおよびアルコキシから選択され;
R2は、アルキル、アルキレン、水素であり;
R3は、水素およびアルキルから選択され、ここで、前記アルキルは、任意にアミノ基またはアルコキシシリル基によって置換され;
Xは、C1−C6アルキレンであり;および
aは、0または1であり;
(ii)キャリア;を含み;および
(c)前記モールドシーラー組成物を少なくとも部分的な硬化を生じさせるのに充分な時間、硬化条件に曝し、それにより、耐久性シールを前記モールド上に形成する、
によって形成される、シールされたモールドを意図する。
表1は、5種の本発明による組成物の重量%を示す:
上記の手順に従って、本発明のモールドシーラー組成物(番号1、2、3および5)をステンレススチール上で試験し、比較を行った。
同じ手順に従って、本発明のモールドシーラー組成物(番号1、2、3および5)をクロムメッキされたモールド上で試験し、比較を行った。
保存寿命期間試験
腐食試験
モールドシーラーが金属モールドに腐食損傷を起こすかどうかを決定するために、簡単な試験を行った。なぜなら、これは水系配合物にとっては共通な問題であるからである。過剰量のモールドシーラーをスチールパネルに塗布し、室温で一夜、空気乾燥させた。また、それと同じパネル上で同じ試験を水およびFrekote R−150を用いて実施した。
任意の高度硬化による第2硬化
モールドシーラーの第1の硬化を325°Fで10分間行った。硬化後、モールドシーラーを600°Fに加熱し、その温度で1時間保持した。次いで、冷却して325°Fに戻し、Frekote−R150をモールドに塗布して、10分間硬化させた。このパネルのゴム離型を試験した結果、20回の自動的離型が可能であり、これは第2の硬化なしで達成できる12回の自動的離型と比較して顕著な改善であった。
シラン濃度
実施例6では、モールドシーラー組成物において使用するシランの最適量を決定するために実施された試験を記載する。
R1は、ヒドロキシおよびアルコキシから選択され;
R2は、アルキル、アルケン、水素であり;
R3は、水素およびアルキルから選択され、ここで前記アルキルはアミノ基またはアルコキシシリル基によって任意に置換され;
Xは、C1−C6アルキレンであり;および
aは、0または1である。
R1は、ヒドロキシおよびアルコキシから選択され;
R2は、アルキル、アルケン、水素であり;
R3は、水素およびアルキルから選択され、ここで前記アルキルは、任意にアミノ基またはアルコキシシリル基によって置換され;
Xは、C1−C6アルキレンであり;および
aは、0または1であり;
(ii)キャリア;を含み;および
(c)前記モールドシーラー組成物を、少なくとも部分的な硬化を達成するのに充分な時間、硬化条件に曝すステップであって、それによりモールド上に耐久性シールを形成する、
を含む。
R1は、ヒドロキシおよびアルコキシから選択され;
R2は、アルキル、アルケン、または水素であり;
R3は、水素およびアルキルから選択され、ここで前記アルキルは、任意にアミノ基またはアルコキシシリル基によって置換され;
Xは、C1−C6アルキレン(すなわち、C1、C2、C3、C4、C5、C6、望ましくはC3)であり;および
aは、0または1である。
Claims (20)
- さらにスリップ剤を含み、前記スリップ剤が官能性または非官能性シロキサンからなる群より選択される、請求項1に記載の組成物。
- 前記組成物が、10.5−10.8のpHを有する、請求項1に記載の組成物。
- 前記キャリアが、エマルジョン、水系溶液および有機溶液からなる群より選択される、請求項1に記載の組成物。
- さらに架橋剤を含み、前記架橋剤がアルコキシ官能基化シランおよびヒドロキシ官能基化シランからなる群より選択される、請求項1に記載の組成物。
- さらに乳化剤を含み、前記乳化剤が3−25のHLBを有する非イオン性およびイオン性界面活性剤の使用からなる群より選択される、請求項1に記載の組成物。
- 前記pH調整剤が、トリエチルアミンもしくは7より高いpHを有する同等物、ならびに酢酸もしくは7より低いpHを有する同等物からなる群より選択される、請求項1に記載の組成物。
- Xが、C3アルキレンである、請求項1に記載の組成物。
- 前記式Iで表されるシランが、3−アミノプロピルトリエトキシシランである、請求項1に記載の組成物。
- 前記式Iで表されるシランが、n−(2−アミノエチル)−3−アミノプロピルメチルジメトキシシラン、4−アミノブチルトリエトキシシラン、3−アミノプロピルメチルジメトキシシラン、n−(2−アミノエチル)−3−アミノプロピルトリメトキシシラン、ビス(3−トリメトキシシリルプロピル)アミン、3−アミノプロピルシラントリオール、および上記モノマーから上記の事前に形成されたまたはイン・サイチュで形成されたオリゴマーからなる群より選択される、請求項1に記載の組成物。
- さらに塩基を含み、前記塩基がトリエチルアミンである、請求項1に記載の組成物。
- さらに、有機チタン化合物および有機錫化合物からなる群より選択される触媒を含む、請求項1に記載の組成物。
- さらに殺生物剤を含む、請求項1に記載の組成物。
- (a)部品を形成するためのモールドであって、前記モールドは少なくとも1つの表面を有し;
(b)請求項1に記載のモールドシーラー組成物を含む前記少なくとも1つの表面上のコーティング;
を含む、シールされたモールドアッセンブリ。 - 前記モールドシーラー組成物が、前記少なくとも1つの表面に化学的に結合している、請求項14に記載のアッセンブリ。
- 前記モールドが、スチール、ステンレススチール、クロム、鋳鉄、アルミニウム、およびニッケルからなる群より選択される金属から構成される、請求項14に記載のアッセンブリ。
- 耐久性シールをモールド上に製造するための方法であり、以下のステップ:
(a)部品を形成するためのモールドを提供するステップであって、前記モールドは少なくとも1つの表面を有し;
(b)前記少なくとも1つの表面にモールドシーラー組成物を塗布するステップであって、前記モールドシーラー組成物は:
(i)式I:
R1は、ヒドロキシおよびアルコキシからなる群より選択され;
R2は、アルキル、アルキレン、水素であり;
R3は、水素およびアルキルからなる群より選択され、ここで前記アルキルは、任意にアミノ基またはアルコキシシリル基によって置換され;
XはC1−C6アルキレンであり;および
aは、0または1であり;
(ii)キャリア;を含み;および
(c)前記モールドシーラー組成物を少なくとも部分的な硬化を生じさせるのに充分な時間、硬化条件に曝すステップであって、それにより、前記モールド上に耐久性シールを形成する、
を含む方法。 - 前記硬化条件が、400°Fで5分間または200°Fで30分間である、請求項17に記載の方法。
- さらに、前記組成物がより高い温度の第2の硬化を受ける、請求項17に記載の方法。
- モールドシーラー組成物を調製するための方法であり、以下のステップ:
(a)キャリアと式I:
R1は、ヒドロキシおよびアルコキシからなる群より選択され;
R2は、アルキル、アルキレン、水素であり;
R3は、水素およびアルキルからなる群より選択され、ここで前記アルキルは、任意にアミノ基またはアルコキシシリル基によって置換され;
XはC1−C6アルキレンであり;および
aは、0または1であり;および
(b)任意に1種以上の架橋剤、乳化剤、pH調整剤、塩基、触媒および殺生物剤を前記エマルジョンまたは溶液に添加してモールドシーラー組成物を形成するステップ、
を含む方法。