JP2011063272A - 外観特性の優れた多層プラスチック容器 - Google Patents
外観特性の優れた多層プラスチック容器 Download PDFInfo
- Publication number
- JP2011063272A JP2011063272A JP2009212908A JP2009212908A JP2011063272A JP 2011063272 A JP2011063272 A JP 2011063272A JP 2009212908 A JP2009212908 A JP 2009212908A JP 2009212908 A JP2009212908 A JP 2009212908A JP 2011063272 A JP2011063272 A JP 2011063272A
- Authority
- JP
- Japan
- Prior art keywords
- resin layer
- layer
- colored
- resin
- printed image
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】。顔料の配合により着色された着色樹脂層を備えた多層プラスチック容器において、該着色樹脂層よりも外面側が全て透明樹脂により形成されており、該着色樹脂層の外面側を形成している該透明樹脂の層の厚みが0.4乃至2.0mmであることを特徴とする。
【選択図】図1
Description
本発明の他の目的は、特に高級感を与える外観を有する多層プラスチック容器を提供することにある。
(1)前記透明樹脂の層の外表面に印刷像が形成されていること、
(2)前記顔料として無機顔料が使用されていること、
(3)前記着色樹脂層がシルバー色に着色されていること、
(4)前記着色樹脂層がスクラップ樹脂を含むリグラインド層中に顔料が分散されたものであり、該着色樹脂層の内面側には、バージンの樹脂から形成された最内層が形成されていること、
(5)前記透明樹脂の層が、最外層、接着樹脂層及び内側層から形成されていること、
が好適である。
例えば、着色樹脂層の外側の透明な層の厚みが上記範囲外であるときには、着色樹脂層の表面に印刷像の影が形成されず、この結果、印刷像の陰影が形成されず、印刷像が形成された状態での外観特性を向上させることはできない。
尚、共重合PETとは、ジオール成分としてエチレングリコール以外のもの、例えばプロピレングリコール、1,4−ブタンジオール、ネオペンチルグリコール、1,6−ヘキシレングリコール、シクロヘキサンジメタノール、ビスフェノールAのエチレンオキサイド付加物、ジエチレングリコール、トリエチレングリコール等のグリコール成分や、テレフタル酸以外のジカルボン酸成分、例えばイソフタル酸、p−β−オキシエトキシ安息香酸、ナフタレン2,6−ジカルボン酸、ジフェノキシエタン−4,4’−ジカルボン酸、5−ナトリウムスルホイソフタル酸、アジピン酸、セバシン酸及びこれらのアルキルエステル誘導体などを含むものであり、特にジオール成分として、エチレングリコール以外のものを、全ジオール成分当り20乃至60モル%で含む共重合PETが好ましく、特に、かかる量でシクロヘキサンジメタノールを共重合成分として含む共重合PETは、本発明における透明樹脂層3の形成には最適である。
即ち、図3において、着色樹脂層1の上の透明樹脂層3は、最外層3a、接着樹脂層3b及び内側層3cとから形成されており、着色樹脂層1の内側には、未着色樹脂からなる最内層6が形成されており、このような好適な層構成において、各層を形成する樹脂の組み合わせとしては、以下の例を挙げることができる。
透明樹脂層3(容器外面側から):
最外層3a;ポリエステル系樹脂層(特に共重合PET)
接着樹脂層3b;前記で例示したもの
内側層3c;オレフィン系樹脂、特にメタロセンLLDPE
着色樹脂層1:
オレフィン系樹脂(特にHDPE)に無機顔料(特に金属粉顔料)を分散した層
(スクラップ樹脂含有)
最内層6:
未着色オレフィン系樹脂(特にHDPE)
透明樹脂層3(容器外面側から):
最外層3a;ポリエステル系樹脂層(特に共重合PET)
接着樹脂層3b;前記で例示したもの
内側層3c;オレフィン系樹脂、特にランダムPP
着色樹脂層1:
オレフィン系樹脂(特にブロックPP)に無機顔料(特に金属粉顔料)を分散し
た層(スクラップ樹脂含有)
最内層6:
オレフィン系樹脂、特にブロックPP
本発明のプラスチック容器は、ボトル形状、カップ形状の容器或いは袋状容器として、種々の内容物を収容する容器として使用に供することができるが、中でも着色樹脂層1がシルバー色に着色されているものでは、印刷像5の陰影が極めて鮮明であり且つ高級感を与えることから、特にボトル形状の化粧品、シャンプー、リンスなどの容器として極めて好適である。
尚、以下の例で、作成された容器(ボトル)の評価は、印刷像の立体感を以下の方法で評価することにより行った。
得られたボトルの外面印刷像正面から蛍光灯で光りを照射し、ボトル表面に対し45度の角度から視覚で、印刷像の立体感を、以下の基準で評点を付与して評価した。
○:印刷像の影が明確に立体的にみえる。
△:印刷像の影がやや立体的にみえる。
×:印刷像の影が立体的にはみえない。
(○と△が許容範囲である。)
図3に示す層構造のボトルを、各層形成用樹脂として、以下のものを用いて成形した。
透明樹脂層(最外層)3a:
非晶性共重合PETである透明ポリエステル系樹脂
(イーストマンPETG DryStar 0601、ヘイズ:0.3%)
透明樹脂層(接着樹脂層)3b:
MFR1.5g/10min(JIS K7210 190℃)の粘着性LDPEであるポリエチレン
系接着剤樹脂(三菱化学モディックF512A)に0.02WT%の滑剤(東洋インキエ
クセフローEX-LD)を混合した樹脂
透明樹脂層(内側層)3c:
MFR2.1g/10min(JIS K7210 210℃)のメタロセンLLDPE樹脂(プライ
ムポリマー社SP1020、ヘイズ:44%)
着色樹脂層1:
MFR0.36g/10min(JIS K7210 210℃)のHDPE樹脂(プライムポリマー
社6008B)にアルミ顔料(平均粒径5μm)を2重量%の割合で混合した樹脂
(顔料の平均粒径は顕微鏡写真により測定した算術平均値)
最内層(未着色樹脂層)6:
MFR0.36g/10min(JIS K7210 210℃)のHDPE樹脂(プライムポリマー
社6008B)
透明樹脂層3cの側壁厚みを0.2mmにし透明樹脂層3のトータル厚みを0.4mmとした以外は実施例1と同様にして円筒形ボトルを成形し、印刷し、評価した。
得られた容器胴部樹脂種類と印刷部での各層の平均肉厚及び評価結果を表1に示す。
透明樹脂層3cの側壁厚みを1.8mmにし透明樹脂層3のトータル厚みを2.0mmとし、着色樹脂層1の側壁厚みを1.6mmにし、最内層6の側壁厚みを0.4mmにした以外は実施例1と同様にして円筒形ボトルを成形し、印刷し、評価した。
得られた容器胴部樹脂種類と印刷部での各層の平均肉厚及び評価結果を表1に示す。
着色樹脂層1を、パール顔料(平均粒径15μm)が1.5重量%の割合で混合されたHDPEに変更して形成した以外は実施例1と同様にして円筒形ボトルを成形し、印刷し、評価した。
得られた容器胴部樹脂種類と印刷部での各層の平均肉厚及び評価結果を表1に示す。
着色樹脂層1を、銀蒸着にて着色されたガラス顔料(平均粒径20μm)が2重量%の割合で混合されたHDPEに変更して形成した以外は実施例1と同様にして円筒形ボトルを成形し、印刷し、評価した。
得られた容器胴部樹脂種類と印刷部での各層の平均肉厚及び評価結果を表1に示す。
透明樹脂層3cをランダムPP樹脂(プライムポリマー社B251VT、ヘイズ:15%)に変更し、且つ着色樹脂層1及び最内層6をブロックPP樹脂(プライムポリマー社B511QA)に変更した以外は実施例1と同様にして円筒形ボトルを成形し、印刷し、評価した。
得られた容器胴部樹脂種類と印刷部での各層の平均肉厚及び評価結果を表1に示す。
透明樹脂層3a、3b、3cをランダムPP樹脂(プライムポリマー社B251VT)により形成された単層(厚み1.1mm)とした以外は実施例6と同様にして円筒形ボトルを成形し、印刷し、評価した。
得られた容器胴部樹脂種類と印刷部での各層の平均肉厚及び評価結果を表1に示す。
透明樹脂層3cの側壁厚みを0.1mmとし、透明樹脂層3のトータル厚みを0.3mmとした以外は実施例1と同様にして円筒形ボトルを成形し、印刷し、評価した。
得られた容器胴部樹脂種類と印刷部での各層の平均肉厚及び評価結果を表1に示す。
3:透明樹脂層
5:印刷像
5’:印刷像の影
Claims (6)
- 顔料の配合により着色された着色樹脂層を備えた多層プラスチック容器において、該着色樹脂層よりも外面側が全て透明樹脂により形成されており、該着色樹脂層の外面側を形成している該透明樹脂の層の厚みが0.4乃至2.0mmであることを特徴とする多層プラスチック容器。
- 前記透明樹脂の層の外表面に印刷像が形成されている請求項1に記載の多層プラスチック容器。
- 前記顔料として無機顔料が使用されている請求項1又は2に記載の多層プラスチック容器。
- 前記着色樹脂層がシルバー色に着色されている請求項1乃至3の何れかに記載の多層プラスチック容器。
- 前記着色樹脂層がスクラップ樹脂を含むリグラインド層中に顔料が分散されたものであり、該着色樹脂層の内面側には、バージンの樹脂から形成された最内層が形成されている請求項1乃至4の何れかに記載の多層プラスチック容器。
- 前記透明樹脂の層が、最外層、接着樹脂層及び内側層から形成されている請求項1乃至5の何れかに記載の多層プラスチック容器。