JP2008520434A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2008520434A5 JP2008520434A5 JP2007543369A JP2007543369A JP2008520434A5 JP 2008520434 A5 JP2008520434 A5 JP 2008520434A5 JP 2007543369 A JP2007543369 A JP 2007543369A JP 2007543369 A JP2007543369 A JP 2007543369A JP 2008520434 A5 JP2008520434 A5 JP 2008520434A5
- Authority
- JP
- Japan
- Prior art keywords
- primer
- overcoat
- layer
- substrate
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
付着強さを沸騰水試験の前後に採点する。沸騰水試験のためにパネルを所定の時間にわたり沸騰水に浸漬させる。1〜4の採点システムにより付着破壊を定性的に採点する。4の評点は最善の粘着力評点である。非常に容易に剥離する膜をもたらした接着剤破壊を示すサンプルに1の評点を与える。膜を剥離するために著しい努力を必要とした接着剤破壊を示したサンプルに2の評点を与える。剥離によって破壊したが、膜の著しい伸びまたは膜の伸びの後に膜の緩やかな引裂をもたらしたサンプルに3の評点を与える。きれいな被膜破壊または伸びの後に破壊を示したサンプルに4の評点を与える。
以下に、本発明の好ましい態様を示す。
[1] 基材上に剥離表面を形成させる方法であって、
(a)プライマ粉末を前記基材に被着させてプライマ層を前記基材上に形成させる工程であって、前記プライマがテトラフルオロエチレン/パーフルオロオレフィンコポリマーおよびポリマー結合剤を含む工程と、
(b)オーバーコート粉末を前記プライマ層上に被着させて前記プライマ層上にオーバーコート層を形成させる工程であって、前記オーバーコートがテトラフルオロエチレン/パーフルオロ(アルキルビニルエーテル)コポリマーを含む工程と、
(c)前記プライマ層および前記オーバーコート層を焼付けて、前記剥離表面を形成させる工程と
を含むことを特徴とする方法。
[2] 前記パーフルオロオレフィンが3〜8個の炭素原子を含むことを特徴とする[1]に記載の方法。
[3] 前記パーフルオロオレフィンがヘキサフルオロプロピレンであることを特徴とする[2]に記載の方法。
[4] 前記パーフルオロ(アルキルビニルエーテル)のアルキル基が1〜5個の炭素原子を含むことを特徴とする[1]に記載の方法。
[5] 前記パーフルオロ(アルキルビニルエーテル)がパーフルオロ(プロピルビニルエーテル)であることを特徴とする[1]に記載の方法。
[6] 前記プライマ粉末を静電吹付けによって被着させることを特徴とする[1]に記載の方法。
[7] 前記オーバーコート粉末を静電吹付けによって被着させることを特徴とする[1]に記載の方法。
[8] 前記ポリマー結合剤がポリエーテルスルホン、ポリフェニレンスルフィドおよびポリアリーレンエーテルケトンからなる群から選択されることを特徴とする[1]に記載の方法。
[9] 前記ポリマー結合剤がポリフェニレンスルフィドを含むことを特徴とする[2]に記載の方法。
[10] 前記プライマ粉末が60重量%以下のテトラフルオロエチレン/パーフルオロ(アルキルビニルエーテル)を更に含むことを特徴とする[2]に記載の方法。
[11] 前記プライマ粉末が前記フルオロポリマーおよび前記ポリマー結合剤の総合重量を基準にして5〜90重量%のポリマー結合剤を含むことを特徴とする[1]に記載の方法。
[12] 前記プライマが、前記フルオロポリマー、前記ポリマー結合剤および充填剤の総合重量を基準にして10〜20重量%の無機充填剤を含むことを特徴とする[1]に記載の方法。
[13] 前記プライマ粉末の粉末が、前記フルオロポリマーおよび前記ポリマー結合剤の両方を含む粒子を含むことを特徴とする[1]に記載の方法。
[14] 前記プライマ粉末が噴霧乾燥によって形成されたことを特徴とする[1]に記載の方法。
[15] 前記基材が、炭素鋼、アルミニウムまたはアルミニウム被覆鋼からなる群から選択されることを特徴とする[1]に記載の方法。
[16] 工程(a)および(b)が行われるときに、前記基材が15〜25℃の温度であることを特徴とする[1]に記載の方法。
[17] 前記プライマ層上への前記オーバーコート粉末の前記被着を前記プライマ層を焼付ける前に行い、それによって前記オーバーコート層の前記焼付けが前記プライマ層も焼付けることを特徴とする[1]に記載の方法。
[18] 前記プライマ層上への前記オーバーコート粉末の前記被着を前記プライマ層を焼付けた後に行い、前記オーバーコート層を前記オーバーコート粉末の被着後に焼付けることを特徴とする[1]に記載の方法。
[19] 前記プライマ層が厚さ2ミル(50マイクロメートル)未満であり、前記オーバーコート層が25ミル(650マイクロメートル)以下であることを特徴とする[1]に記載の方法。
[20] 前記プライマ層が厚さ1.5ミル未満であることを特徴とする[17]に記載の方法。
[21] 前記オーバーコート層が厚さ1.5〜3ミル(38マイクロメートル〜76マイクロメートル)であることを特徴とする[17]に記載の方法。
[22] [1]に記載の方法に製造された剥離被膜をその上に有する基材。
以下に、本発明の好ましい態様を示す。
[1] 基材上に剥離表面を形成させる方法であって、
(a)プライマ粉末を前記基材に被着させてプライマ層を前記基材上に形成させる工程であって、前記プライマがテトラフルオロエチレン/パーフルオロオレフィンコポリマーおよびポリマー結合剤を含む工程と、
(b)オーバーコート粉末を前記プライマ層上に被着させて前記プライマ層上にオーバーコート層を形成させる工程であって、前記オーバーコートがテトラフルオロエチレン/パーフルオロ(アルキルビニルエーテル)コポリマーを含む工程と、
(c)前記プライマ層および前記オーバーコート層を焼付けて、前記剥離表面を形成させる工程と
を含むことを特徴とする方法。
[2] 前記パーフルオロオレフィンが3〜8個の炭素原子を含むことを特徴とする[1]に記載の方法。
[3] 前記パーフルオロオレフィンがヘキサフルオロプロピレンであることを特徴とする[2]に記載の方法。
[4] 前記パーフルオロ(アルキルビニルエーテル)のアルキル基が1〜5個の炭素原子を含むことを特徴とする[1]に記載の方法。
[5] 前記パーフルオロ(アルキルビニルエーテル)がパーフルオロ(プロピルビニルエーテル)であることを特徴とする[1]に記載の方法。
[6] 前記プライマ粉末を静電吹付けによって被着させることを特徴とする[1]に記載の方法。
[7] 前記オーバーコート粉末を静電吹付けによって被着させることを特徴とする[1]に記載の方法。
[8] 前記ポリマー結合剤がポリエーテルスルホン、ポリフェニレンスルフィドおよびポリアリーレンエーテルケトンからなる群から選択されることを特徴とする[1]に記載の方法。
[9] 前記ポリマー結合剤がポリフェニレンスルフィドを含むことを特徴とする[2]に記載の方法。
[10] 前記プライマ粉末が60重量%以下のテトラフルオロエチレン/パーフルオロ(アルキルビニルエーテル)を更に含むことを特徴とする[2]に記載の方法。
[11] 前記プライマ粉末が前記フルオロポリマーおよび前記ポリマー結合剤の総合重量を基準にして5〜90重量%のポリマー結合剤を含むことを特徴とする[1]に記載の方法。
[12] 前記プライマが、前記フルオロポリマー、前記ポリマー結合剤および充填剤の総合重量を基準にして10〜20重量%の無機充填剤を含むことを特徴とする[1]に記載の方法。
[13] 前記プライマ粉末の粉末が、前記フルオロポリマーおよび前記ポリマー結合剤の両方を含む粒子を含むことを特徴とする[1]に記載の方法。
[14] 前記プライマ粉末が噴霧乾燥によって形成されたことを特徴とする[1]に記載の方法。
[15] 前記基材が、炭素鋼、アルミニウムまたはアルミニウム被覆鋼からなる群から選択されることを特徴とする[1]に記載の方法。
[16] 工程(a)および(b)が行われるときに、前記基材が15〜25℃の温度であることを特徴とする[1]に記載の方法。
[17] 前記プライマ層上への前記オーバーコート粉末の前記被着を前記プライマ層を焼付ける前に行い、それによって前記オーバーコート層の前記焼付けが前記プライマ層も焼付けることを特徴とする[1]に記載の方法。
[18] 前記プライマ層上への前記オーバーコート粉末の前記被着を前記プライマ層を焼付けた後に行い、前記オーバーコート層を前記オーバーコート粉末の被着後に焼付けることを特徴とする[1]に記載の方法。
[19] 前記プライマ層が厚さ2ミル(50マイクロメートル)未満であり、前記オーバーコート層が25ミル(650マイクロメートル)以下であることを特徴とする[1]に記載の方法。
[20] 前記プライマ層が厚さ1.5ミル未満であることを特徴とする[17]に記載の方法。
[21] 前記オーバーコート層が厚さ1.5〜3ミル(38マイクロメートル〜76マイクロメートル)であることを特徴とする[17]に記載の方法。
[22] [1]に記載の方法に製造された剥離被膜をその上に有する基材。
Claims (2)
- 基材上に剥離表面を形成させる方法であって、
(a)プライマ粉末を前記基材に被着させてプライマ層を前記基材上に形成させる工程であって、前記プライマがテトラフルオロエチレン/パーフルオロオレフィンコポリマーおよびポリマー結合剤を含む工程と、
(b)オーバーコート粉末を前記プライマ層上に被着させて前記プライマ層上にオーバーコート層を形成させる工程であって、前記オーバーコートがテトラフルオロエチレン/パーフルオロ(アルキルビニルエーテル)コポリマーを含む工程と、
(c)前記プライマ層および前記オーバーコート層を焼付けて、前記剥離表面を形成させる工程と
を含むことを特徴とする方法。 - 請求項1に記載の方法に製造された剥離被膜をその上に有する基材。