JP2008019233A - 側鎖に硫黄原子を有するグラフトポリマー及びその製造方法 - Google Patents
側鎖に硫黄原子を有するグラフトポリマー及びその製造方法 Download PDFInfo
- Publication number
- JP2008019233A JP2008019233A JP2006221418A JP2006221418A JP2008019233A JP 2008019233 A JP2008019233 A JP 2008019233A JP 2006221418 A JP2006221418 A JP 2006221418A JP 2006221418 A JP2006221418 A JP 2006221418A JP 2008019233 A JP2008019233 A JP 2008019233A
- Authority
- JP
- Japan
- Prior art keywords
- group
- integer
- carbon atoms
- formula
- conh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明によれば、以下の化合物、グラフトポリマー及びその製造方法等が提供される。
1. 下記式(1)で表される化合物。
2.下記式(2)で表される化合物。
3.下記式(3)で表される化合物。
4.前記式(2)又は(3)のR2〜R8の少なくとも1つが重合性基を有する2又は3に記載の化合物。
5.R1が−CONH−C6H4−である1〜4のいずれに記載の化合物。
6.下記式(4)で表される高分子化合物。
7.R1が−CONH−C6H4−である6に記載の高分子化合物。
8.下記式(5)で表されるグラフトポリマー。
9.下記式(6)で表されるグラフトポリマー。
10.R1が−CONH−C6H4−である8又は9に記載のグラフトポリマー。
11.数平均分子量が400〜50,000の範囲内である2〜4のいずれかに記載の化合物。
12.数平均分子量が5,000〜500,000の範囲内である6に記載の高分子化合物。
13.数平均分子量が5,000〜500,000の範囲内である8又は9に記載のグラフトポリマー。
14.下記式で表される化合物に、R2−SH(R2−は式(1)と同じである。)を反応させる1に記載の化合物の製造方法。
15.上記1に記載の化合物に、下記式で示されるチイラン誘導体を反応させる請求項2に記載の化合物の製造方法。
16.上記2に記載の化合物に、下記式で示されるエポキシ化合物又はチイラン化合物を反応させる3に記載の化合物の製造方法。
17.上記2〜4のいずれかに記載の化合物を、単独でラジカル重合又は炭素数2〜50のアクリル系不飽和結合を有する単量体とラジカル共重合させる請求項8又は9に記載のグラフトポリマーの製造方法。
18.上記1に記載の化合物を、単独でラジカル重合又は炭素数2〜50のアクリル系不飽和結合を有する単量体とラジカル共重合させる請求項6に記載の高分子化合物の製造方法。
19.上記6に記載の高分子化合物に、下記式で示されるチイラン誘導体を反応させる請求項8に記載のグラフトポリマーの製造方法。
20.上記8に記載のグラフトポリマーに、下記式で示されるエポキシ化合物又はチイラン化合物を反応させる請求項9に記載のグラフトポリマーの製造方法。
21.重合性基を有する8〜10のいずれかに記載のグラフトポリマー。
22.上記21に記載のグラフトポリマーを硬化させて得られる3次元硬化物。
23.上記21に記載のグラフトポリマーに加熱又は活性エネルギー線照射を行って硬化させる3次元硬化物の製造方法。
24.上記6又は7に記載の高分子化合物、8〜10のいずれかに記載のグラフトポリマー、又は22に記載の3次元硬化物からなる光学用樹脂。
具体例としては、メチル、エチル、プロピル、ヘキシル、デシル等のアルキル基:シクロヘキシル、シクロオクチル、シクロドデシル等のシクロアルキル基:フェニル、ナフチル、それらの置換体(トリル、キシリル、ベンジルフェニル等)等のアリール基:チエニル基、フリル基、ピリジル基、ピロリル基等のヘテロアリール基:ベンジル、フェネチル、フェニルベンジル、ナフチルメチル等のアラルキル基が例示可能である。また、これらの基はメトキシ基、メトキシカルボニル基、シアノ基、ジメチルアミノ基、ハロゲン、ヒドロキシ基で置換されていてもよい。主鎖又は側鎖にハロゲン、硫黄、酸素又は窒素を含んでいてもよい。好ましくは、水素、ハロゲン、メチル基又は重水素である。尚、R3及びR4は同じでも異なっていてもよい。
好ましくは(メタ)アクリル酸アルキルエステル系単量体又は(メタ)アクリルアミド単量体である。さらに好ましくは(メタ)アクリルアミド単量体である。
そして式(I)で表される(メタ)アクリルアミド単量体としては、例えば、(メタ)アクリルアミド、N−フェニル(メタ)アクリルアミド、N,N−ジメチルアミノプロピル(メタ)アクリルアミド、N,N−ジメチル(メタ)アクリルアミド等が例示可能である。
式(3)、式(6)中のkは1〜1000の整数であり、好ましくは1〜500である。
に、R2−SH(R2−は式(1)と同じである。)を反応させることにより得ることができる。好ましくは縮合剤存在下で反応を行う。
反応は、アンプル封管等、水分を除去できる状態で行うのが望ましい。
を反応させることによって得ることができる。好ましくは塩触媒存在下で反応を行う。
反応はアンプル封管等、水分を除去できる状態で行うのが望ましい。
反応は、アンプル封管等、水分を除去できる状態で行うのが望ましい。
反応はアンプル封管等、水分を除去できる状態で行うのが望ましい。
さらに、3次元硬化物の特性を高める目的で、シリカや酸化チタン等無機フィラーや有機フィラーを任意の割合で加えてもよい。
実施例1
下記式(7)で示される化合物(以下(7)と略す)を下記の方法で合成した。
得られた化合物の分析結果を以下に示す。
IR(cm−1):3315、1675、1655、1625
1H−NMR(500MHz、DMSO−d6):
δ(ppm)2.02〜2.45(m、3H)、5.64(s、1H)、5.88(s、1H)、7.51〜7.53(m、3H)、7.94(d、2H)、10.02(s、1H)
下記式(9)で示される化合物(以下(9)と略す)を下記の方法で合成した。
得られた化合物の分子量をGPC法で測定したところ、数平均分子量0.8×103、分散度1.8であった。
GPC法の測定条件は以下の通りであった。
(a)ゲルパーミエーションクロマトグラフィー(SEC):東ソー株式会社製、ゲル浸透クロマトグラフィー(SEC)HLC−8220型
(b)カラム:TSKgelG1000H
(c)展開溶媒:N,N’−ジメチルホルムアミド
(d)標準物質:ポリスチレン
また、得られた化合物のIR結果を以下に示す。
・IR(cm−1):3340、3058、2668、1676、1658、1629
また、スルフィドAの量を変えて検討を行った。得られた生成物の屈折率、分子量、分子量分布、硫黄含有量を表1に示す。
下記式(10)で示されるグラフトポリマーを(以下(10)と略す)を下記の方法で合成した。
得られた化合物の分子量をSEC法で、実施例2と同じ条件で測定したところ、数平均分子量1.9×104、分散度3.1であった。
得られた化合物のIR結果を以下に示す。
IR(cm−1):3328、3060、2867、1685、1658
また、スルフィドAの量を変えて検討を行った。得られた生成物の屈折率、分子量、分子量分布を表2に示す。
下記式(11)で示されるグラフトポリマー(以下(11)と略す)を下記の方法で合成した。
反応終了後、反応溶媒を貧溶媒としてメタノールを用いて再沈精製を行い、(11)を白色の粘性液体として0.456g(収率:95.0%)得た。得られたポリマーの分子量をGPC法で実施例2と同じ条件で測定したところ、数平均分子量は4.6×104、分散度は2.9、屈折率は1.637であった。
得られた高分子化合物の分析結果を以下に示す。
IR(cm−1):3351、3058、2869、1656
また、スルフィドAの重合度の異なる(9)を用いて同様の条件でPMAとのラジカル共重合を行い、得られたグラフトポリマーについて実施例2と同じ条件で屈折率を測定した。結果を表3に示す。
下記式(12)で示されるグラフトポリマー(以下(12)と略す)を下記の方法で合成した。
得られた高分子化合物の分析結果を以下に示す。
IR(cm−1):3328、3060、2867、1685、1658
また、スルフィドAの重合度の異なる(9)を用いて同様の条件でMAとのラジカル共重合を行い、得られたグラフトポリマーについて実施例2と同じ条件で屈折率を測定した。結果を表4に示す。
Claims (24)
- 下記式(3)で表される化合物。
- 前記式(2)又は(3)のR2〜R8の少なくとも1つが重合性基を有する請求項2又は3に記載の化合物。
- R1が−CONH−C6H4−である請求項1〜4のいずれ一項に記載の化合物。
- R1が−CONH−C6H4−である請求項6に記載の高分子化合物。
- 下記式(5)で表されるグラフトポリマー。
- 下記式(6)で表されるグラフトポリマー。
- R1が−CONH−C6H4−である請求項8又は9に記載のグラフトポリマー。
- 数平均分子量が400〜50,000の範囲内である請求項2〜4のいずれか一項に記載の化合物。
- 数平均分子量が5,000〜500,000の範囲内である請求項6に記載の高分子化合物。
- 数平均分子量が5,000〜500,000の範囲内である請求項8又は9に記載のグラフトポリマー。
- 請求項2〜4のいずれか一項に記載の化合物を、単独でラジカル重合又は炭素数2〜50のアクリル系不飽和結合を有する単量体とラジカル共重合させる請求項8又は9に記載のグラフトポリマーの製造方法。
- 請求項1に記載の化合物を、単独でラジカル重合又は炭素数2〜50のアクリル系不飽和結合を有する単量体とラジカル共重合させる請求項6に記載の高分子化合物の製造方法。
- 重合性基を有する請求項8〜10のいずれか一項に記載のグラフトポリマー。
- 請求項21に記載のグラフトポリマーを硬化させて得られる3次元硬化物。
- 請求項21に記載のグラフトポリマーに加熱又は活性エネルギー線照射を行って硬化させる3次元硬化物の製造方法。
- 請求項6又は7に記載の高分子化合物、請求項8〜10のいずれか一項に記載のグラフトポリマー、又は請求項22に記載の3次元硬化物からなる光学用樹脂。