JP2007517947A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2007517947A5 JP2007517947A5 JP2006548221A JP2006548221A JP2007517947A5 JP 2007517947 A5 JP2007517947 A5 JP 2007517947A5 JP 2006548221 A JP2006548221 A JP 2006548221A JP 2006548221 A JP2006548221 A JP 2006548221A JP 2007517947 A5 JP2007517947 A5 JP 2007517947A5
- Authority
- JP
- Japan
- Prior art keywords
- component
- coating material
- dispersion
- coating
- prepolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
黄変値は、先行技術系(実施例5、6、9および10)と比較して、本発明の被覆材料(実施例7、8、11および12)は、ガラス上およびプラスチック(Makrofol(登録商標)、Bayer AG、レバークーゼン、独国)上の両方において熱暴露後、顕著に低い黄変値を示すこと表す。
さらに、実施例7、8、11および12からの本発明の被覆材料は、先行技術の例(実施例5、6、9および10)のものに匹敵する機械的特性および触質性を有する。
本発明の好適な実施態様には、以下のものが含まれる。
〔1〕 I)1以上の、ヒドロキシル非含有ポリウレタンおよび/またはポリウレタン-尿素の分散体(PU分散体)、
II)1以上の、成分I)の構成成分以外の、イオン的に変性されたヒドロキシル含有ポリウレタンおよび/またはポリウレタン-尿素の水性溶液または分散体、
III)少なくとも1つの架橋剤、および
IV)必要に応じて、さらなる被膜形成樹脂
を含んでなる被覆材料であって、
I)に使用されるPU分散体は、
A)最初に
A1)ポリイソシアネートと、
A2)400〜8000g/モルの数平均分子量を有するポリマーポリオールおよび/またはポリアミン、
A3)必要に応じて、モノおよびポリアルコール、モノおよびポリアミンならびにアミノアルコールからなる群から選択される17〜400g/モルの数平均分子量を有する低分子量化合物、
A4)イソシアネート反応性のイオン的にまたは潜在的にイオン的に親水性化する化合物、および/または
A5)イソシアネート反応性の非イオン的に親水性化する化合物
[ただし、成分A1)〜A5)のいずれも第1級または第2級アミノ基を含有しない]
を、
A6)必要に応じて、溶媒としての脂肪族ケトン中、
反応させることによってNCO含有ポリウレタンプレポリマーを製造し、
B)工程A)から得られるプレポリマーを脂肪族ケトン中に溶解するか、あるいは、上記製造が既にA6)の存在下で行われている場合、必要に応じて脂肪族ケトンをさらに添加することによってプレポリマー溶液を希釈し、そして
C)プレポリマーの残りの遊離NCO基と、
C1)ヒドラジンおよび/またはヒドラジン水和物、および
C2)必要に応じて、成分A2)、A3)、A4)および/またはA5)の定義を満たす化合物
[ただし、
・成分C2)の化合物は、第1級および/または第2級アミノ基を含有し、
・C1)およびC2)の合計量は、40〜200%の算術鎖延長度が達成されるような量であり、および
・C1)とC2)の割合は、少なくとも40%の遊離イソシアネート基が、成分C1)からのアミノ基によって、末端化および/または鎖延長されるような割合である]
を含んでなる鎖延長剤成分を反応させること
により得られることを特徴とする、被覆材料。
〔2〕 工程B)および必要に応じて工程A)におけるPU分散体の製造において、アセトンまたはブタノンを溶媒として使用することを特徴とする、上記〔1〕に記載の被覆材料。
〔3〕 PU分散体の製造において、工程A)〜C)中、8〜27重量%の成分A1)、65〜85重量%の成分A2)、0〜8重量%の成分A3)、0〜10重量%の成分A4)、0〜15重量%の成分A5)、1.0〜2.5重量%のC1)(純ヒドラジン(N 2 H 4 )に基づく)および0〜8重量%のC2)を、
A4)とA5)の合計が0.1〜25重量%であり、および成分の合計が100重量%となるように使用することを特徴とする、上記〔1〕または〔2〕に記載の被覆材料。
〔4〕 PU分散体の製造において、C1)およびC2)の量は、101〜150%の算術鎖延長度が生じるような量であることを特徴とする、上記〔1〕〜〔3〕のいずれかに記載の被覆材料。
〔5〕 III)において、ポリイソシアネートを架橋剤として使用することを特徴とする、上記〔1〕〜〔4〕のいずれかに記載の被覆材料。
〔6〕 成分III)のNCO基と、成分II)およびIV)のOH基との比は、1.0:1.0〜2.5:1.0であることを特徴とする、上記〔5〕に記載の被覆材料。
〔7〕 成分I)、II)およびIV)の混合物は、25〜75重量%の成分II)を含有し、およびI)およびIV)の量は、I)、II)およびIV)の合計量が100重量%になるように選択されることを特徴とする、上記〔1〕〜〔6〕のいずれかに記載の被覆材料。
〔8〕 被覆物の製造における、上記〔1〕〜〔7〕のいずれかに記載の被覆材料の使用。
〔9〕 上記〔1〕〜〔7〕のいずれかに記載の被覆材料を使用して製造された被覆物。
〔10〕 上記〔9〕に記載の被覆物で被覆された基材。
さらに、実施例7、8、11および12からの本発明の被覆材料は、先行技術の例(実施例5、6、9および10)のものに匹敵する機械的特性および触質性を有する。
本発明の好適な実施態様には、以下のものが含まれる。
〔1〕 I)1以上の、ヒドロキシル非含有ポリウレタンおよび/またはポリウレタン-尿素の分散体(PU分散体)、
II)1以上の、成分I)の構成成分以外の、イオン的に変性されたヒドロキシル含有ポリウレタンおよび/またはポリウレタン-尿素の水性溶液または分散体、
III)少なくとも1つの架橋剤、および
IV)必要に応じて、さらなる被膜形成樹脂
を含んでなる被覆材料であって、
I)に使用されるPU分散体は、
A)最初に
A1)ポリイソシアネートと、
A2)400〜8000g/モルの数平均分子量を有するポリマーポリオールおよび/またはポリアミン、
A3)必要に応じて、モノおよびポリアルコール、モノおよびポリアミンならびにアミノアルコールからなる群から選択される17〜400g/モルの数平均分子量を有する低分子量化合物、
A4)イソシアネート反応性のイオン的にまたは潜在的にイオン的に親水性化する化合物、および/または
A5)イソシアネート反応性の非イオン的に親水性化する化合物
[ただし、成分A1)〜A5)のいずれも第1級または第2級アミノ基を含有しない]
を、
A6)必要に応じて、溶媒としての脂肪族ケトン中、
反応させることによってNCO含有ポリウレタンプレポリマーを製造し、
B)工程A)から得られるプレポリマーを脂肪族ケトン中に溶解するか、あるいは、上記製造が既にA6)の存在下で行われている場合、必要に応じて脂肪族ケトンをさらに添加することによってプレポリマー溶液を希釈し、そして
C)プレポリマーの残りの遊離NCO基と、
C1)ヒドラジンおよび/またはヒドラジン水和物、および
C2)必要に応じて、成分A2)、A3)、A4)および/またはA5)の定義を満たす化合物
[ただし、
・成分C2)の化合物は、第1級および/または第2級アミノ基を含有し、
・C1)およびC2)の合計量は、40〜200%の算術鎖延長度が達成されるような量であり、および
・C1)とC2)の割合は、少なくとも40%の遊離イソシアネート基が、成分C1)からのアミノ基によって、末端化および/または鎖延長されるような割合である]
を含んでなる鎖延長剤成分を反応させること
により得られることを特徴とする、被覆材料。
〔2〕 工程B)および必要に応じて工程A)におけるPU分散体の製造において、アセトンまたはブタノンを溶媒として使用することを特徴とする、上記〔1〕に記載の被覆材料。
〔3〕 PU分散体の製造において、工程A)〜C)中、8〜27重量%の成分A1)、65〜85重量%の成分A2)、0〜8重量%の成分A3)、0〜10重量%の成分A4)、0〜15重量%の成分A5)、1.0〜2.5重量%のC1)(純ヒドラジン(N 2 H 4 )に基づく)および0〜8重量%のC2)を、
A4)とA5)の合計が0.1〜25重量%であり、および成分の合計が100重量%となるように使用することを特徴とする、上記〔1〕または〔2〕に記載の被覆材料。
〔4〕 PU分散体の製造において、C1)およびC2)の量は、101〜150%の算術鎖延長度が生じるような量であることを特徴とする、上記〔1〕〜〔3〕のいずれかに記載の被覆材料。
〔5〕 III)において、ポリイソシアネートを架橋剤として使用することを特徴とする、上記〔1〕〜〔4〕のいずれかに記載の被覆材料。
〔6〕 成分III)のNCO基と、成分II)およびIV)のOH基との比は、1.0:1.0〜2.5:1.0であることを特徴とする、上記〔5〕に記載の被覆材料。
〔7〕 成分I)、II)およびIV)の混合物は、25〜75重量%の成分II)を含有し、およびI)およびIV)の量は、I)、II)およびIV)の合計量が100重量%になるように選択されることを特徴とする、上記〔1〕〜〔6〕のいずれかに記載の被覆材料。
〔8〕 被覆物の製造における、上記〔1〕〜〔7〕のいずれかに記載の被覆材料の使用。
〔9〕 上記〔1〕〜〔7〕のいずれかに記載の被覆材料を使用して製造された被覆物。
〔10〕 上記〔9〕に記載の被覆物で被覆された基材。
Claims (4)
- I)1以上の、ヒドロキシル非含有ポリウレタンおよび/またはポリウレタン-尿素の分散体(PU分散体)、
II)1以上の、成分I)の構成成分以外の、イオン的に変性されたヒドロキシル含有ポリウレタンおよび/またはポリウレタン-尿素の水性溶液または分散体、
III)少なくとも1つの架橋剤、および
IV)必要に応じて、さらなる被膜形成樹脂
を含んでなる被覆材料であって、
I)に使用されるPU分散体は、
A)最初に
A1)ポリイソシアネートと、
A2)400〜8000g/モルの数平均分子量を有するポリマーポリオールおよび/またはポリアミン、
A3)必要に応じて、モノおよびポリアルコール、モノおよびポリアミンならびにアミノアルコールからなる群から選択される17〜400g/モルの数平均分子量を有する低分子量化合物、
A4)イソシアネート反応性のイオン的にまたは潜在的にイオン的に親水性化する化合物、および/または
A5)イソシアネート反応性の非イオン的に親水性化する化合物
[ただし、成分A1)〜A5)のいずれも第1級または第2級アミノ基を含有しない]
を、
A6)必要に応じて、溶媒としての脂肪族ケトン中、
反応させることによってNCO含有ポリウレタンプレポリマーを製造し、
B)工程A)から得られるプレポリマーを脂肪族ケトン中に溶解するか、あるいは、上記製造が既にA6)の存在下で行われている場合、必要に応じて脂肪族ケトンをさらに添加することによってプレポリマー溶液を希釈し、そして
C)プレポリマーの残りの遊離NCO基と、
C1)ヒドラジンおよび/またはヒドラジン水和物、および
C2)必要に応じて、成分A2)、A3)、A4)および/またはA5)の定義を満たす化合物
[ただし、
・成分C2)の化合物は、第1級および/または第2級アミノ基を含有し、
・C1)およびC2)の合計量は、40〜200%の算術鎖延長度が達成されるような量であり、および
・C1)とC2)の割合は、少なくとも40%の遊離イソシアネート基が、成分C1)からのアミノ基によって、末端化および/または鎖延長されるような割合である]
を含んでなる鎖延長剤成分を反応させること
により得られることを特徴とする、被覆材料。 - 被覆物の製造における、請求項1に記載の被覆材料の使用。
- 請求項1に記載の被覆材料を使用して製造された被覆物。
- 請求項3に記載の被覆物で被覆された基材。