JP2002526575A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2002526575A5 JP2002526575A5 JP2000574156A JP2000574156A JP2002526575A5 JP 2002526575 A5 JP2002526575 A5 JP 2002526575A5 JP 2000574156 A JP2000574156 A JP 2000574156A JP 2000574156 A JP2000574156 A JP 2000574156A JP 2002526575 A5 JP2002526575 A5 JP 2002526575A5
- Authority
- JP
- Japan
- Prior art keywords
- average molecular
- molecular weight
- weight average
- polyurethane
- glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
【特許請求の範囲】
【請求項１】
押出可能な熱可塑性エラストマー性尿素鎖延長ポリウレタンであって、
（ａ）4,4'-ジシクロヘキシルメタンジイソシアネートである少なくとも１の脂肪族ジイソシアネートと、650〜3000の重量平均分子量を有する少なくとも１のポリエーテルグリコールとの反応生成物を含むポリウレタンプレポリマーであって、ジイソシアネートに基づくＮＣＯ当量とポリエーテルグリコールに基づくＯＨ当量との比が２未満である、ポリウレタンプレポリマーと、
（ｂ）2,4-ジアミノ-3,5-ジエチルトルエン、2,6-ジアミノ-3,5-ジエチルトルエン、トリ-メチレングリコールジ-パラアミノベンゾエート及びこれらの混合物からなる群より選択される少なくとも１のジアミン硬化剤と、
の反応生成物を含み、上記ポリウレタンは、ショアーＡ硬度７２〜８４、DMA Tg -80℃（マイナス80℃）より大、TMA軟化点２０５〜２０８℃を有し、熱的安定性及び加水分解安定度、耐微生物分解性を有することを特徴とするポリウレタン。
【請求項２】
請求項１に記載のポリウレタンであって、少なくとも１のポリエーテルグリコールは、650〜3000の重量平均分子量を有するポリテトラメチレンエーテルグリコールであることを特徴とするポリウレタン。
【請求項３】
請求項２に記載のポリウレタンであって、1.6当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1.0当量の上記ポリテトラメチレンエーテルグリコールと反応することを特徴とするポリウレタン。
【請求項４】
請求項１に記載のポリウレタンであって、少なくとも１のポリエーテルグリコールは、1000の重量平均分子量を有するポリテトラメチレンエーテルグリコールと、2000の重量平均分子量を有するポリテトラメチレンエーテルグリコールとの混合物であることを特徴とするポリウレタン。
【請求項５】
請求項４に記載のポリウレタンであって、1.6当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1000の重量平均分子量を有するポリテトラメチレンエーテルグリコール0.9当量及び2000の重量平均分子量を有するポリテトラメチレンエーテルグリコール0.1当量と反応することを特徴とするポリウレタン。
【請求項６】
請求項１に記載のポリウレタンであって、少なくとも１のポリエーテルグリコールは、1000の重量平均分子量を有するポリテトラメチレンエーテルグリコールと、2900の重量平均分子量を有するポリテトラメチレンエーテルグリコールとの混合物であることを特徴とするポリウレタン。
【請求項７】
請求項６に記載のポリウレタンであって、1.8当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1000の重量平均分子量を有するポリテトラメチレンエーテルグリコール0.2当量及び2900の重量平均分子量を有するポリテトラメチレンエーテルグリコール0.8当量と反応することを特徴とするポリウレタン。
【請求項８】
生成物を形成する方法であって、
（ａ）4,4'-ジシクロヘキシルメタンジイソシアネートである少なくとも１の脂肪族ジイソシアネートと、650〜3000の重量平均分子量を有するポリエーテルグリコールである少なくとも１の水酸基含有中間体と、少なくとも１のジアミン硬化剤との反応生成物を含む熱可塑性エラストマー性尿素鎖延長ポリウレタン（ここでジイソシアネートに基づくＮＣＯ当量とポリエーテルグリコールに基づくＯＨ当量との比が２未満であり、ジアミン硬化剤が2,4-ジアミノ-3,5-ジエチルトルエン、2,6-ジアミノ-3,5-ジエチルトルエン、トリ-メチレングリコールジ-パラアミノベンゾエート及びこれらの混合物からなる群より選択される。）を加熱し、；
（ｂ）上記加熱されたポリウレタンを押出して、ショアーＡ硬度７２〜８４、DMA Tg -80℃より大、TMA軟化点２０５〜２０８℃を有し、熱的安定性及び加水分解安定度、耐微生物分解性を有する押出生成物を形成する各工程を備えることを特徴とする方法。
【請求項９】
請求項８に記載の方法であって、少なくとも１のポリエーテルグリコールは重量平均分子量1000を有するポリテトラメチルエチレンエーテルグリコールであり、1.6当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1.0当量の上記ポリテトラメチルエチレンエーテルグリコールと反応することを特徴とする方法。
【請求項１０】
請求項８に記載の方法であって、少なくとも１の水酸基含有中間体が、重量平均分子量1000を有するポリテトラメチレンエーテルグリコールと重量平均分子量2000を有するポリテトラメチレンエーテルグリコールとの混合物であり、1.6当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1000の重量平均分子量を有するポリテトラメチルエチレンエーテルグリコール0.9当量及び2000の重量平均分子量を有するポリテトラメチルエチレンエーテルグリコール0.1当量と反応することを特徴とする方法。
【請求項１１】
請求項８に記載の方法であって、少なくとも１の水酸基含有中間体が、1000の重量平均分子量を有するポリテトラメチレンエーテルグリコールと、2900の重量平均分子量を有するポリテトラメチレンエーテルグリコールとの混合物であり、1.8当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1000の重量平均分子量を有するポリテトラメチルエチレンエーテルグリコール0.2当量及び2900の重量平均分子量を有するポリテトラメチルエチレンエーテルグリコール0.8当量と反応することを特徴とする方法。
【請求項１２】
請求項８〜１１のいずれかに記載の方法により形成される生成物であって、72mil厚のサンプルシートを80℃で30日間蒸留水中に浸すことによって加水分解老化し、その後25℃で7日間空気中で乾燥させた後のサンプルシートの引っ張り強さが少なくとも100％保持されることを特徴とする生成物。
【請求項１３】
請求項８〜１１のいずれかに記載の方法により形成される生成物であって、72mil厚のサンプルシートを105℃で30日間空気暴露により熱老化させ、その後室温で冷却した後のサンプルシートの引っ張り強さが少なくとも100％保持されることを特徴とする生成物。
【請求項１４】
請求項８〜１１のいずれかに記載の方法により形成される生成物であって、72mil厚のサンプルシートを80℃で30日間蒸留水中に浸すことによって加水分解老化し、その後、105℃で30日間空気暴露により熱老化させ、次いで室温で冷却した後のサンプルシートの引っ張り強さが少なくとも100％保持されることを特徴とする生成物。
【請求項１５】
請求項８〜１１のいずれかに記載の方法により形成される生成物であって、72mil厚のサンプルシートを105℃で30日間空気暴露により熱老化させ、その後、80℃で30日間蒸留水中に浸すことによって加水分解老化し、25℃で7日間空気中で乾燥させた後のサンプルシートの引っ張り強さが少なくとも100％保持されることを特徴とする生成物。
【請求項１】
押出可能な熱可塑性エラストマー性尿素鎖延長ポリウレタンであって、
（ａ）4,4'-ジシクロヘキシルメタンジイソシアネートである少なくとも１の脂肪族ジイソシアネートと、650〜3000の重量平均分子量を有する少なくとも１のポリエーテルグリコールとの反応生成物を含むポリウレタンプレポリマーであって、ジイソシアネートに基づくＮＣＯ当量とポリエーテルグリコールに基づくＯＨ当量との比が２未満である、ポリウレタンプレポリマーと、
（ｂ）2,4-ジアミノ-3,5-ジエチルトルエン、2,6-ジアミノ-3,5-ジエチルトルエン、トリ-メチレングリコールジ-パラアミノベンゾエート及びこれらの混合物からなる群より選択される少なくとも１のジアミン硬化剤と、
の反応生成物を含み、上記ポリウレタンは、ショアーＡ硬度７２〜８４、DMA Tg -80℃（マイナス80℃）より大、TMA軟化点２０５〜２０８℃を有し、熱的安定性及び加水分解安定度、耐微生物分解性を有することを特徴とするポリウレタン。
【請求項２】
請求項１に記載のポリウレタンであって、少なくとも１のポリエーテルグリコールは、650〜3000の重量平均分子量を有するポリテトラメチレンエーテルグリコールであることを特徴とするポリウレタン。
【請求項３】
請求項２に記載のポリウレタンであって、1.6当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1.0当量の上記ポリテトラメチレンエーテルグリコールと反応することを特徴とするポリウレタン。
【請求項４】
請求項１に記載のポリウレタンであって、少なくとも１のポリエーテルグリコールは、1000の重量平均分子量を有するポリテトラメチレンエーテルグリコールと、2000の重量平均分子量を有するポリテトラメチレンエーテルグリコールとの混合物であることを特徴とするポリウレタン。
【請求項５】
請求項４に記載のポリウレタンであって、1.6当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1000の重量平均分子量を有するポリテトラメチレンエーテルグリコール0.9当量及び2000の重量平均分子量を有するポリテトラメチレンエーテルグリコール0.1当量と反応することを特徴とするポリウレタン。
【請求項６】
請求項１に記載のポリウレタンであって、少なくとも１のポリエーテルグリコールは、1000の重量平均分子量を有するポリテトラメチレンエーテルグリコールと、2900の重量平均分子量を有するポリテトラメチレンエーテルグリコールとの混合物であることを特徴とするポリウレタン。
【請求項７】
請求項６に記載のポリウレタンであって、1.8当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1000の重量平均分子量を有するポリテトラメチレンエーテルグリコール0.2当量及び2900の重量平均分子量を有するポリテトラメチレンエーテルグリコール0.8当量と反応することを特徴とするポリウレタン。
【請求項８】
生成物を形成する方法であって、
（ａ）4,4'-ジシクロヘキシルメタンジイソシアネートである少なくとも１の脂肪族ジイソシアネートと、650〜3000の重量平均分子量を有するポリエーテルグリコールである少なくとも１の水酸基含有中間体と、少なくとも１のジアミン硬化剤との反応生成物を含む熱可塑性エラストマー性尿素鎖延長ポリウレタン（ここでジイソシアネートに基づくＮＣＯ当量とポリエーテルグリコールに基づくＯＨ当量との比が２未満であり、ジアミン硬化剤が2,4-ジアミノ-3,5-ジエチルトルエン、2,6-ジアミノ-3,5-ジエチルトルエン、トリ-メチレングリコールジ-パラアミノベンゾエート及びこれらの混合物からなる群より選択される。）を加熱し、；
（ｂ）上記加熱されたポリウレタンを押出して、ショアーＡ硬度７２〜８４、DMA Tg -80℃より大、TMA軟化点２０５〜２０８℃を有し、熱的安定性及び加水分解安定度、耐微生物分解性を有する押出生成物を形成する各工程を備えることを特徴とする方法。
【請求項９】
請求項８に記載の方法であって、少なくとも１のポリエーテルグリコールは重量平均分子量1000を有するポリテトラメチルエチレンエーテルグリコールであり、1.6当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1.0当量の上記ポリテトラメチルエチレンエーテルグリコールと反応することを特徴とする方法。
【請求項１０】
請求項８に記載の方法であって、少なくとも１の水酸基含有中間体が、重量平均分子量1000を有するポリテトラメチレンエーテルグリコールと重量平均分子量2000を有するポリテトラメチレンエーテルグリコールとの混合物であり、1.6当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1000の重量平均分子量を有するポリテトラメチルエチレンエーテルグリコール0.9当量及び2000の重量平均分子量を有するポリテトラメチルエチレンエーテルグリコール0.1当量と反応することを特徴とする方法。
【請求項１１】
請求項８に記載の方法であって、少なくとも１の水酸基含有中間体が、1000の重量平均分子量を有するポリテトラメチレンエーテルグリコールと、2900の重量平均分子量を有するポリテトラメチレンエーテルグリコールとの混合物であり、1.8当量の4,4'-ジシクロヘキシルメタンジイソシアネートが、1000の重量平均分子量を有するポリテトラメチルエチレンエーテルグリコール0.2当量及び2900の重量平均分子量を有するポリテトラメチルエチレンエーテルグリコール0.8当量と反応することを特徴とする方法。
【請求項１２】
請求項８〜１１のいずれかに記載の方法により形成される生成物であって、72mil厚のサンプルシートを80℃で30日間蒸留水中に浸すことによって加水分解老化し、その後25℃で7日間空気中で乾燥させた後のサンプルシートの引っ張り強さが少なくとも100％保持されることを特徴とする生成物。
【請求項１３】
請求項８〜１１のいずれかに記載の方法により形成される生成物であって、72mil厚のサンプルシートを105℃で30日間空気暴露により熱老化させ、その後室温で冷却した後のサンプルシートの引っ張り強さが少なくとも100％保持されることを特徴とする生成物。
【請求項１４】
請求項８〜１１のいずれかに記載の方法により形成される生成物であって、72mil厚のサンプルシートを80℃で30日間蒸留水中に浸すことによって加水分解老化し、その後、105℃で30日間空気暴露により熱老化させ、次いで室温で冷却した後のサンプルシートの引っ張り強さが少なくとも100％保持されることを特徴とする生成物。
【請求項１５】
請求項８〜１１のいずれかに記載の方法により形成される生成物であって、72mil厚のサンプルシートを105℃で30日間空気暴露により熱老化させ、その後、80℃で30日間蒸留水中に浸すことによって加水分解老化し、25℃で7日間空気中で乾燥させた後のサンプルシートの引っ張り強さが少なくとも100％保持されることを特徴とする生成物。