HU212241B - Procedure for elastoform pressing of metal sheets by using silicone elastomers as flexible forming stamp - Google Patents
Procedure for elastoform pressing of metal sheets by using silicone elastomers as flexible forming stamp Download PDFInfo
- Publication number
- HU212241B HU212241B HU87496A HU49687A HU212241B HU 212241 B HU212241 B HU 212241B HU 87496 A HU87496 A HU 87496A HU 49687 A HU49687 A HU 49687A HU 212241 B HU212241 B HU 212241B
- Authority
- HU
- Hungary
- Prior art keywords
- weight
- parts
- groups
- silicone elastomer
- plasticizer
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K5/00—Use of organic ingredients
- C08K5/0008—Organic ingredients according to more than one of the "one dot" groups of C08K5/01 - C08K5/59
- C08K5/0016—Plasticisers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
- B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
- B21D22/00—Shaping without cutting, by stamping, spinning, or deep-drawing
- B21D22/10—Stamping using yieldable or resilient pads
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L83/00—Compositions of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon only; Compositions of derivatives of such polymers
- C08L83/04—Polysiloxanes
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G77/00—Macromolecular compounds obtained by reactions forming a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon in the main chain of the macromolecule
- C08G77/04—Polysiloxanes
- C08G77/12—Polysiloxanes containing silicon bound to hydrogen
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G77/00—Macromolecular compounds obtained by reactions forming a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon in the main chain of the macromolecule
- C08G77/04—Polysiloxanes
- C08G77/14—Polysiloxanes containing silicon bound to oxygen-containing groups
- C08G77/16—Polysiloxanes containing silicon bound to oxygen-containing groups to hydroxyl groups
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G77/00—Macromolecular compounds obtained by reactions forming a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon in the main chain of the macromolecule
- C08G77/04—Polysiloxanes
- C08G77/20—Polysiloxanes containing silicon bound to unsaturated aliphatic groups
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G77/00—Macromolecular compounds obtained by reactions forming a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon in the main chain of the macromolecule
- C08G77/04—Polysiloxanes
- C08G77/22—Polysiloxanes containing silicon bound to organic groups containing atoms other than carbon, hydrogen and oxygen
- C08G77/24—Polysiloxanes containing silicon bound to organic groups containing atoms other than carbon, hydrogen and oxygen halogen-containing groups
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T29/00—Metal working
- Y10T29/49—Method of mechanical manufacture
- Y10T29/49805—Shaping by direct application of fluent pressure
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Laminated Bodies (AREA)
- Processes Of Treating Macromolecular Substances (AREA)
- Shaping Metal By Deep-Drawing, Or The Like (AREA)
- Casting Or Compression Moulding Of Plastics Or The Like (AREA)
Claims (9)
- SZABADALMI IGÉNYPONTOK1. Eljárás fémlemezek elasztoform sajtolására rugalmas formázóbélyegként szilikon elasztomer felhasználásával, azzal jellemezve, hogy szilikon elasztomerként kisebb mint 40 Shore 00 keménységű, legalább egy, a sajtolás körülményei között stabil, nem migráló, szilikonnal kompatibilis, 100 tömegrész szilikon elasztomerre számolva 4-550 tömegrész a térhálóba beépült - önmagában ismert szerves vagy szervetlen - lágyítót tartalmazó folyékony önmagában ismert organopolisziloxánok térhálósításával nyert szilikon elasztomert alkalmazunk.
- 2. Az 1. igénypont szerinti eljárás, azzal jellemezve, hogy olyan szilikon elasztomert alkalmazunk, amely térhálóba beépülni képes - lágyítóként szerves vagy ásványi eredetű szénhidrogén olajokat, diorganopolisziloxán olajokat, szerves lágyítókat vagy szerves/diorganopolisziloxán polimer keverékét tartalmazza.
- 3. Az 1. vagy a 2. igénypont szerinti eljárás, azzal jellemezve, hogy olyan szilikon elasztomert alkalmazunk, amely lágyítóként 25 C-on előnyösen 5-3000 mPa s viszkozitású diorganopolisziloxán olajat tartalmaz.
- 4. Az 1-3. igénypontok bármelyike szerinti eljárás, azzal jellemezve, hogy a következő összetételű organopolisziloxán keverék térhálósításával nyert szilikon elasztomert alkalmazzuk:A. 100 tömegrész vinilezett organopolisziloxán olaj, amelynek viszkozitása 25 °C-on 100-100 000 mPa s, amely molekulánként legalább 2 vinilcsoportot tartalmaz, a többi csoport pedig metil-, etil-, fenil- és3,3,3-trifluor-propil-csoport, mimellett a szerves csoportok legalább 60%-a metilcsoport;B. 0,1-10 tömegrész molekulánként legalább 3 =SiH csoportot tartalmazó, elágazó láncú organopolisziloxán vagy egy egyenes láncú diorganopolisziloxán;C. 0-10 tömegrész, molekulánként 2 =SiH csoportot tartalmazó egyenes láncú diorganopolisziloxán kapcsolószer, mimellett a (B+C) komponensben jelenlevő sSiH csoportok számának az A-ban jelenlévő vinilcsoportok számához viszonyított számaránya 0,7-2;D. 20-200 tömegrész stabilizáló vagy erősítő hatású, előnyösen részben előkezelt szervetlen töltőanyag;E. 0,0002-0,03 tömegrész egy plantiacsoportbeli fémkatalizátor;F. egy diorganopolisziloxán lágyító, amelynek viszkozitása 5 és 3000 mPas közötti, előnyösen 10 és 1500 mPa s közötti 25 ’C-on, amelyben a szerves csoport 1-10 szénatomos alkil-, fenil-, klór-fenil- vagy 3,3,3trifluor-propil-csoport, mimellett ezeknek a csoportoknak legalább 80%-a metilcsoport, és a lágyító mennyisége 5-400, előnyösen 20-200 tömegrész 100 tömegrész A+B+C+D+E keverékre vonatkoztatva.
- 5. Az 1-3. igénypontok bármelyike szerinti eljárás, azzal jellemezve, hogy a következő összetételű organopolisziloxán keverék térhálósításával nyert szilikon elasztomert alkalmazzuk:A’ 100 tömegrész, 25 ’C-on 20-500 000 mPa s viszkozitású legalább egy alfa,omega-dihidroxi-diorgano-polisziloxán-polimer, amelyben szerves csoportként metil-, vinil-, fenil- vagy 3,3,3-trifluor-propil-csoportok vannak jelen, mimellett a csoportok legalább 60%-a metilcsoport, maximum 20%-a fenilcsoport és maximum 2%-a vinilcsoport;B’ 25-200 tömegrész erősítő vagy az erősítést elősegítő szervetlen töltőanyag;C’ 0,5-15 tömegrész legalább egy térhálósító szer, mégpedig polialkoxi-szilán vagy polialkoxi-sziloxán;D’ 0,005-1 tömegrész (fém ónra számolva) ónkatalizátor, ésE’ 25 ’C-on 5-3000 mPa s, előnyösen 10-1500 mPas viszkozitású diorgano-polisziloxán lágyító, amelyben szerves csoportonként 1-10 szénatomos alkil-, fenil-, klór-fenil-, vinil- vagy 3,3,3-trifluor-propilcsoportokat alkalmazunk, mimellett ezeknek a csoportoknak legalább 80%-a metilcsoport, és a lágyító mennyisége 50-500, előnyösen 80-250 tömegrész 100 tömegrész A’+B’+C’+D’ keverékre számolva.
- 6. Az 1. igénypont szerinti eljárás, azzal jellemezve, hogy szilikon elasztomer formázóbélyegként a felületén vagy legalább a felülete egy részén 30-90, előnyösen 35-80 Shore A keménységű 0,5-25 mm vastag kemény elasztomer membrán-réteggel bevont szilikon elasztomert alkalmazunk.
- 7. A 6. igénypont szerinti eljárás azzal jellemezve, hogy kemény elasztomerként poliuretánt, polibutadiént vagy természetes gumit alkalmazunk.
- 8. A 6. vagy 7. igénypont szerinti eljárás, azzal jellemezve, hogy több rugalmas, a sajtolószerszámban egymás mellett vagy felett elhelyezett tagból álló szilikon elasztomer alátétet alkalmazunk.
- 9. Az 1-8. igénypontok bármelyike szerinti eljárás, azzal jellemezve, hogy fémlemezek elasztoform sajtolását egy kettős működési elven alapuló présben végezzük.