ES2553561T3 - Polimerización aniónica de lactamas mediante el uso de activadores especiales - Google Patents
Polimerización aniónica de lactamas mediante el uso de activadores especiales Download PDFInfo
- Publication number
- ES2553561T3 ES2553561T3 ES09153033.7T ES09153033T ES2553561T3 ES 2553561 T3 ES2553561 T3 ES 2553561T3 ES 09153033 T ES09153033 T ES 09153033T ES 2553561 T3 ES2553561 T3 ES 2553561T3
- Authority
- ES
- Spain
- Prior art keywords
- lactams
- anionic polymerization
- activator
- special activators
- activators
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Sistema que contiene a) al menos un catalizador para la polimerización aniónica de lactamas; y b) al menos un activador para la polimerización aniónica de lactamas, caracterizado por que como activador se emplea al menos una uretdiona como isocianato cíclico dimérico.
Description
5
15
25
35
45
55
65
Después de que se hayan preparado las mezclas precursoras se ponen las mezclas resultantes en general en el molde de la producción de poliamida de moldeo.
La adición de aditivos usados dado el caso se realiza en un momento adecuado antes del comienzo de la polimerización, por ejemplo en las mezclas precursoras.
En particular, en el marco de este uso se aplican las composiciones de acuerdo con la invención que se han descrito anteriormente. El uso de acuerdo con la invención de estas composiciones para la preparación de poliamidas mediante polimerización aniónica de lactamas comprende, por lo tanto, en particular el uso de la composición de acuerdo con la invención que se ha descrito anteriormente, dosificándose el activador y el catalizador habitualmente en primer lugar en cargas de lactama separadas y homogeneizándose con la lactama y agrupándose entonces en el molde.
La composición que se debe emplear de acuerdo con la invención se usa tanto para la producción de piezas terminadas de poliamida de moldeo como de semiproductos de poliamida de moldeo y materiales compuestos. A este respecto se pueden emplear procedimientos sin presión y de presión (por ejemplo, la técnica de inyecciónreacción). Otros procedimientos específicos son el procedimiento de colada vertical, colada de rotación y colada centrifugada. Además se pueden usar moldes abiertos o cerrados. A este respecto se aplican temperaturas de molde, duraciones de calentamiento y tiempos de colada habituales.
En el caso de las poliamidas preparadas según el procedimiento de acuerdo con la invención, las composiciones resultantes de poliamida resultantes presentan una cristalinidad excelente.
La presente invención se explica con más detalle mediante los siguientes ejemplos que, sin embargo, no limitan la presente invención:
Ejemplo 1: Aparatos y reactivos:
El conjunto de aparatos para la preparación de la masa fundida está compuesto de:
- •
- 2 matraces de tres bocas (500 ml) calentados en baño de aceite
- •
- 2 agitadores KPG con casquillo
- •
- 2 tapas de gas respectivamente 1 con y 1 sin grifo
- •
- 1 bomba de vacío con trampa de refrigeración, manómetro. El conjunto de aparatos para la medición de la temperatura está compuesto de:
- •
- Aparato de medición de temperatura por ejemplo Testo 175-T3 con IR-Serial Interface
- •
- Filamento de par termoeléctrico para la permanencia en la muestra endurecida
- •
- Vaso de precipitados 600 ml (forma alta)
- •
- Calentamiento para el vaso de precipitados (bloque de metal, baño de aceite)
- •
- Cronómetro de laboratorio (división 1 segundo)
- •
- caprolactama seca (PR > 69 ºC)
- •
- activador:
- ○
- TDI dimérico (de acuerdo con la invención, disponible en el mercado como Addolink® TT de Rhein Chemie Rheinau GmbH, Mannheim)
- ○
- solución de poliisocianato alifático
- •
- nitrógeno seco
- •
- catalizador NL-neu (RheinChemie -mezcla de caprolactama y lactamato sódico)
El matraz A se carga con 196,8 g de caprolactama y 3,2 g de activador, el matraz B con 192 g de caprolactama y 8 g de catalizador NL-Neu. Las masas fundidas se preparan a 122 ºC (± 2 ºC) en un baño de aceite al vacío (<15 mbar) 20 minutos. Después de la aireación con nitrógeno, ambos componentes se aúnan en un matraz de tres bocas, se agitan
7
Claims (1)
-
imagen1