DK2244976T3 - LSX-zeolit med kontrolleret partikelstørrelse - Google Patents
LSX-zeolit med kontrolleret partikelstørrelse Download PDFInfo
- Publication number
- DK2244976T3 DK2244976T3 DK08865114.6T DK08865114T DK2244976T3 DK 2244976 T3 DK2244976 T3 DK 2244976T3 DK 08865114 T DK08865114 T DK 08865114T DK 2244976 T3 DK2244976 T3 DK 2244976T3
- Authority
- DK
- Denmark
- Prior art keywords
- stirring
- less
- hours
- zeolite
- maturation
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B39/00—Compounds having molecular sieve and base-exchange properties, e.g. crystalline zeolites; Their preparation; After-treatment, e.g. ion-exchange or dealumination
- C01B39/02—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof; Direct preparation thereof; Preparation thereof starting from a reaction mixture containing a crystalline zeolite of another type, or from preformed reactants; After-treatment thereof
- C01B39/20—Faujasite type, e.g. type X or Y
- C01B39/22—Type X
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
- B01J20/10—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising silica or silicate
- B01J20/16—Alumino-silicates
- B01J20/18—Synthetic zeolitic molecular sieves
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/01—Particle morphology depicted by an image
- C01P2004/03—Particle morphology depicted by an image obtained by SEM
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
- C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
- C01P2004/62—Submicrometer sized, i.e. from 0.1-1 micrometer
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
- Y10T428/2982—Particulate matter [e.g., sphere, flake, etc.]
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Inorganic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Life Sciences & Earth Sciences (AREA)
- General Life Sciences & Earth Sciences (AREA)
- Geology (AREA)
- Analytical Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Silicates, Zeolites, And Molecular Sieves (AREA)
- Catalysts (AREA)
Claims (12)
1. Zeolit af LSX- typen med et Si/AI-atomforhold på mindre end eller lig med 1,15, fortrinsvis lig med 1 ± 0,05, i krystallinsk form, hvorhos: - partikelstørrelsesfordelingen bestemt ved SEM-tælling er monomodal, med en topbredde (2σ) på mindre end 8, fortrinsvis mindre end 6, endnu mere fortrinsvis mindre end 4, og helst mindre end 2; og - gennemsnitsdiameteren efter antal målt ved scanningelektronmikroskopi er større end 0,1 pm og mindre end 10 pm, fortrinsvis mindre end 4 pm, endnu mere fortrinsvis mindre end 3 pm.
2. Zeolit ifølge krav 1, hvoraf krystallinitetsgraden er større end 88%, fortrinsvis større end 93%, endnu mere fortrinsvis større end 95%.
3. Fremgangsmåde til fremstilling af en zeolit af LSX-typen ifølge et hvilket som helst af kravene 1 og 2, hvorhos krystallerne har en gennemsnitsdiameter efter antal målt ved scanningelektronmikroskopi på mere end 0,1 pm og mindre end 10 pm, fortrinsvis mindre end 4 pm, endnu mere fortrinsvis mindre end 3 pm, med et Si/AI-atomforhold på mindre end eller lig med 1,15, fortrinsvis lig med 1 ± 0,05, omfattende mindst et modningstrin med omrøring, og et krystalliseringstrin eventuelt med omrøring af en gel, hvis molsammensætning opfylder følgende betingelser: • et forhold Na20/(Na20+K20) på 0,75 til 1, fortrinsvis 0,75 til 0,8; • et forhold H2O/AI2O3 på 60 til 85, fortrinsvis 65 til 80, og endnu mere fortrinsvis 70 til 80; • et forhold S1O2/AI2O3 på 1,8 til 2,2; • et forhold (Na20+K20)/Al203, på 4,8 til 6, fortrinsvis 5 til 5,5.
4. Fremgangsmåde ifølge krav 3 til syntese af LSX-zeolit med en krystallinitetsgrad på mere end 88%, fortrinsvis mere end 93%, endnu mere fortrinsvis mere end 95%.
5. Fremgangsmåde ifølge krav 3, kendetegnet ved at gelen modnes under omrøring med en forskydningshastighed på mere end 25 s'1, fortrinsvis mere end 50 s-1, endnu mere fortrinsvis mere end 100 s-1, og helst mere end 125 s-1.
6. Fremgangsmåde ifølge et hvilket som helst af kravene 3 til 5, hvor omrøringen tilvejebringes ved hjælp af en aksial og/eller radial omrører fortrinsvis valgt blandt en skrueomrører, et skovlhjul og en Archimedes-skrue, fortrinsvis under anvendelse af en Archimedes-skrue.
7. Fremgangsmåde ifølge et hvilket som helst af kravene 3 til 6, hvor modningen udføres ved en temperatur på mellem 0°C og 80°C, fortrinsvis på mellem 30°C og 70°C.
8. Fremgangsmåde ifølge et hvilket som helst af kravene 3 til 7, omfattende følgende trin: a) at blande en opløsning af alkalialuminat(er), med en silicakilde, fortrinsvis et kolloidt silica eller en opløsning af alkalisilicat(er), og natrumhydroxid og kaliumhydroxid, indtil geldannelse af den resulterende blanding, b) modning af gelen under omrøring, ved en temperatur på mellem 0°C og 80°C, fortrinsvis på mellem 30°C og 70°C, i et tidsrum på mellem 0,5 time og 40 timer, fortrinsvis på mellem 5 timer og 30 timer, og endnu mere fortrinsvis på mellem 10 timer og 24 timer; c) krystallisering, eventuelt under omrøring, ved en temperatur på mellem 50°C og 100°C, i et tidsrum på mellem 0,5 time og 10 timer, fortrinsvis på mellem 1 time og 5 timer.
9. Fremgangsmåde ifølge krav 8, hvor krystalliseringen udføres under omrøring, fortrinsvis med en forskydningshastighed på mere end 25 s-1, fortrinsvis på mere end 50 s-1, endnu mere fortrinsvis på mere end 100 s-1, og helst på mere end 125 S"1.
10. Fremgangsmåde ifølge et hvilket som helst af kravene 8 eller 9, hvor krystalliseringen udføres under de samme omrøringsbetingelser som dem i modningen ifølge krav 6.
11. Fremgangsmåde ifølge et hvilket som helst af kravene 8 til 10, i hvilken podemateriale, i en mængde på mellem 0,01 vægtprocent og 1,5 vægtprocent af vægten af udgangsblandingen, tilsættes, delvist eller fuldstændigt, i et eller flere af af følgende trin af fremgangsmåden: - i blandingen i trin a);- under geldannelsen; og/eller- ved starten af modningen.
12. Fremgangsmåde ifølge et hvilket som helst af kravene 8 til 11, hvor podematerialet er valgt blandt zeolitter, ler og nukleringsopløsninger baseret på silica og alumina.