DE897671C - Zuendkerzenisolator und keramischer Koerper dafuer - Google Patents

Zuendkerzenisolator und keramischer Koerper dafuer

Info

Publication number
DE897671C
DE897671C DEG5012D DEG0005012D DE897671C DE 897671 C DE897671 C DE 897671C DE G5012 D DEG5012 D DE G5012D DE G0005012 D DEG0005012 D DE G0005012D DE 897671 C DE897671 C DE 897671C
Authority
DE
Germany
Prior art keywords
spark plug
ceramic body
plug insulator
mixture
alumina
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DEG5012D
Other languages
English (en)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Motors Liquidation Co
Original Assignee
Motors Liquidation Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Motors Liquidation Co filed Critical Motors Liquidation Co
Application granted granted Critical
Publication of DE897671C publication Critical patent/DE897671C/de
Expired legal-status Critical Current

Description

  • Zündkerzenisolator und keramischer Körper dafür Die Erfindung betrifft ein Verfahren zum Herstellen von Zündkerzenisolatoren nach Patent 763 264 durch Brennen eines Gemisches von Tonerde und Zirkonsilikat.
  • Es isst bekannt, zur Erzeugung hochfeuerfester Körper für bfenauskleidungen u. dgl. Gemische zu verwenden, die einen beträchtlichen Gehalt an Zirkon aufweisen und deren Bestandteile verhältnismäßig grob gemahlen sind. Diese feuerfesten Körper sind daher stark porös und infolge ihrer geringen Wärmeleitfähigkeit und Wärmeausidehnung zwar für Öfen, feuerfeste Gefäße u. dgl. geeignet, nicht jedoch für Zündkerzenisolato@ren. Es ist ferner bekannt, zur Herstellung von Zündkerzenisolatoren Gemische zu verwenden, die als Hauptbestandteile beträchtliche Mengen Zirkon neben Kaolin, Kugelton und ähnlichen Aluminiumsilikaten enthalten. Derartige .Körper zeigen aber Wärme- und Festigkeitseigenschaften, die@schlechter sind als die aus reiner geschmolzener Tonerde bestehenden Körper.
  • Demgegenüber besteht die Erfindung darin, daß ein, Gemisch aus Tonerde und i bis i5°/o Zirkonsilikat verwendet wird, und die daraus geformten Rohlinge bei Temperaturen von 16oo bis 175o° C gebrannt werden. Auf diese Weise hergestellte Zündkerzenisolatoren sind fast in jeder Beziehung sogar solchen aus reiner geschmolzener Tonerde überlegen. Sie sind praktisch porenfrei, haben eine ausreichende Wärmeausdehnung, großei mechanische Festigkeit, sind unempfindlich gegen plötzliche Temperaturschwankungen. und besitzen einen vorzüglichen elektrischen Widerstand bei hohen Temperaturen, insbesondere auch gegen Kriechströme und Hochfrequenzströme. Sie sind nicht nur für einen einwandfreien Betrieb, bei den heutigen Kraftfahrzeugmotoren gut geeignet, sondern auch denjenigen Beanspruchungen gewachsen, welchen die Zündkerzen voraussichtlich in Zukunft bei Steigerung der Kompresision und der Änderung der übrigen Betriebsverhältnisisie ausgesetzt sein werden.
  • Der Hauptvorteil des Zusatzes von Zirkon zu dem Tonerdegemisch besteht darin, daß dadurch die Brenntemperatur, d. h. diejenige Temperatur herabgesetzt wird, die man zur Erziehung eines dichten, porenfreien Körpers braucht, wie er für Zündkerzenisolatoren erforderlich eist. Beträgt die Brenntemperatur z. B,. für reine Tonerdekörper etwa 175o° C, so setzt ein Zusatz von 5 °/a Zirkon die Brenntemperatur auf ungefähr 1675° C herab. Bei so 1/o Zirkon Zusatz ist sogar nur eine Brenntemperatur von 1625° C erforderlich. Dieser Umstand ist wirtschaftlich insofern von Bedeutung, als damit auch die Schwierigkeiten beim Bau und Betrieb von Öfen zur Herstellung der Isolatoren weitgehend verringert werden.
  • Die Herstellung der Isolatoren geschieht nach dem im Patent 763 264 angegebenen Verfahren; bei dem man die Bestandteile mit einem zeitweiligen Bindemittel, insbesondere organischer Natur, wie Bakeliite, mischt, die Isolatoren unter Erwärmung bei hohem Druck formt und darauf bei den angegebenen Temperaturen brennt, wobei die zeitweiligen Bindemittel entfernt werden. Die Rohstoffe werden vorher etwa durch Behandlung mit Borsäure zweckmäßig möglichst von Alkali befreit.
  • Die nach der Erfindung hergestellten Körper besitzen eine seidige, glasartige Oberfläche, selbst wenn. sie nach einem Gußverfahren hergestellt sind. Sie bedürfen daher keiner Glasur. Das Gefüge deir gebrannten Körper besteht im wesentlichen aus Ko@rund mit eingelagerter Zirkonerde und Zirkonaluminiumsiidikatglas. Die Korundkristalle sind im wesentlichen frei von Lunkern, da das Zirkon die Größe und das Wachstum der Korundkristalle zu vermindern scheint. Die Zwischenräume sind durch das Glas, ausgefüllt, wodurch die Festigkeit des Körpers weiter gesteigert wird.
  • Für die wirtschaftliche Herstellung von Zündkerzenisolatoren gemäß der Erfindung wird man vorzugsweise 21/z bis, 5 o/a Zirkou verwenden. Dieser Gehalt ergibt wünschenswerte physikalische Eigenschaften in solchem Grade, daß die praktischen Erfordernisse mit- dem geringsten Koistenaufwand befriedigt werden.

Claims (2)

  1. PATENTANSPRÜCHE: 1. Verfahren zum Herstellen von Zündkerzenisolatoren nach Patent 763 264 durch . Brennen eines Gemisches aus Tonerde und Zirkonsilikat, dadurch gekennzeichnet, daß man ein, Gemisch mit 1 bis 15 o/a, Zirkonsilikat verwendet, und die darausi geformten Rohlinge bei Temperaturen von 16oo bis 175o° C gebrannt werden.
  2. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß der Alkaligehalt in dem Germisch möglichst niedrig gehalten wird.
DEG5012D 1935-11-08 1935-12-13 Zuendkerzenisolator und keramischer Koerper dafuer Expired DE897671C (de)