DE55711C - Verfahren zur Bereitung von Stahl - Google Patents
Verfahren zur Bereitung von StahlInfo
- Publication number
- DE55711C DE55711C DENDAT55711D DE55711DA DE55711C DE 55711 C DE55711 C DE 55711C DE NDAT55711 D DENDAT55711 D DE NDAT55711D DE 55711D A DE55711D A DE 55711DA DE 55711 C DE55711 C DE 55711C
- Authority
- DE
- Germany
- Prior art keywords
- sugar
- steel
- acids
- acid series
- white
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
KAISERLICHES
PATENTAMT.
KLASSE 18: Eisenerzeugung.
Die vorliegende Neuerung bei der Erzeugung von Stahl aus schmiedbarem Gufseisen
und schwach gekohltem Stahl bezweckt, die Kohlung der genannten Materialien bis zur
Erzeugung von Stahl bezw. hochgekohltem Stahl billig und zugleich rasch zu erzielen,
und besteht zu dem Zwecke darin, das schmiedbare Gufseisen bezw. den schwach gekohlten
Stahl im weifsglühenden Zustande in ein Bad zu tauchen und darin der Abkühlung zu überlassen,
welches aus einer wässerigen Lösung von Säuren der Milchsäurereihe oder Säuren der Oxalsäurereihe oder deren Alkalisalzen,
insbesondere Oxalsäure, Weinsäure oder deren Alkalisalzen besteht.
Bringt man das weifsglühende Metall in das. Bad, so erleidet letzteres eine Zersetzung derart,
dafs der Wasserstoff und Sauerstoff der organischen Substanz zu Wasser zusammentreten,
während der Kohlenstoff an das Eisen geht und von diesem gebunden wird.
Die anzuwendende Menge des Carburirmittels richtet sich danach, ob das Metall in seiner
Masse durchaus oder nur an seiner Oberfläche . und bis zu einer bestimmten Tiefe gekohlt
werden soll. Nur oberflächlich gestähltes Metall kann dadurch tiefer oder durch seine
ganze Masse hindurch gekohlt werden, dafs man es nochmals auf Weifsglut erhitzt und in
ein frisches Carburirbad bringt.
An Stelle der genannten Säuren kann man auch ein Gemisch aus Honig bezw. Zucker
aller Art, Syrupen, Melassen und sonstigen Abfällen der Zuckerfabriken in Gegenwart von
Alkalien (kaustischen oder kohlensauren) oder Mineralsäuren anwenden. Hierbei wird der
Zucker zunächst in andere, Kohlenstoff, Wasserstoff und Sauerstoff enthaltende Verbindungen
umgewandelt und zersetzen sich dann diese bei weiterer Erhitzung unter Abgabe von
Kohlenstoff. Z. B. beim Erhitzen von Zucker mit Salpetersäure oder kaustischem Alkali findet
zunächst eine Zerlegung des ersteren zu Zuckersäure, Oxalsäure, Weinsäure u. a. m, statt,
welche sich dann ihrerseits unter Abgabe von Kohlenstoff an das Eisen weiter zersetzen.
Wenn für zweckmä'fsig erachtet, kann man das Carburirbad auch vor dem Einbringen des
weifsglühenden Metalles bis nahe an die Zersetzungstemperatur erhitzen.
Ferner kann man die genannten organischen Stoffe entweder je einzeln oder mehrere im
Gemisch anwenden.
Nach den Versuchen des Erfinders haben sich insbesondere die folgenden Kohlungsbäder
als sehr vortheilhaft erwiesen:
ι. Zucker bezw. Melasse 0,5 kg, kaustisches Kali oder Natron 28 g, Wasser 5 1.
2. Doppelweinsaures Kali 113 g, oxalsaures
Kali 113 g, Wasser 4,5 1.
Wo es der Preis gestattet, empfiehlt sich die Oxalsäure als wirksamstes Carburirmittel.
Claims (1)
- Patent-Ansprüch:Verfahren zur Bereitung von Stahl aus schmiedbarem Gufseisen und schwach gekohltem Stahl durch Abkühlenlassen des auf Weifsglut erhitzten Metalles in einem Bade, welches aus einer wässerigen Lösung von Säuren der ■Milchsäurereihe oder der Oxalsäurereihe bezw. deren Alkalisalzen, oder aus solcher Lösung von Zucker (Syrupen, Melassen, Abfällen der Zuckerfabriken, Honig), versetzt mit kaustischen bezw. kohlensauren Alkalien oder mit Mineralsäuren, zusammengesetzt ist.