DE3215777A1 - Zement-fliessmoertel - Google Patents
Zement-fliessmoertelInfo
- Publication number
- DE3215777A1 DE3215777A1 DE19823215777 DE3215777A DE3215777A1 DE 3215777 A1 DE3215777 A1 DE 3215777A1 DE 19823215777 DE19823215777 DE 19823215777 DE 3215777 A DE3215777 A DE 3215777A DE 3215777 A1 DE3215777 A1 DE 3215777A1
- Authority
- DE
- Germany
- Prior art keywords
- cement
- weight
- portland cement
- self
- screeds
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
- Zement - FließmbIei
- Die Erfindung bezieht sich auf die Zusammensetzung eines Mörtels, der mit Wasser angemacht und maschinell oder manuell angemischt und aufgegossen wird. Die Masse verläuft, verdichtet und glättet sich selbst und härtet dann spannungs- und rissefrei.
- Die klassische Methode Zenient-Estrich zu verlegen ist sehr zeitraubend, weil die einzelnen Arbeitsgänge mühsames Verteilen, Verdichten, Abziehen und Glätten bedeuten. Die selbstfließenden und sich selbst ausnivellierenden Zement-Fließestriche sparen alle diese Arbeitsgänge ein, durch einfaches Gießen oder Pumpen. Die auf dem Markt befindlichen Zement-Fließestriche sind mit Polymerstoffen angereichert, weil es notwendig ist hauptsächlich die Zugfestigkeit von gegossenen Belägen zu erhöhen, da sonst bei der Erstarrung und Erhärtung der gegossenen Beläge durch die Schrumpfung eine Rissbildung statt finden würde. Durch den Zusatz von Polymerstoffen sind aber diese Zement-Fließestriche hauptsächlich bei höheren Estrichstärken (20-50 mm), kostspielig und deshalb unwirtschaftlich.
- Die Aufgabe der Erfindung besteht darin, einen Zement-Fließmörtel genannter Art zu schaffen, aber ohne Polymerstoffe, unter Verwendung von besonders preiswerten Zusätzen, die die Herstellung von spannungs- und rissefreien Massen ermöglichen.
- Diese Aufgabe ist gemäß der Erfindung dadurch gelöst, daß bei der Erstarrung und Erhärtung der stark schrumpfende Portlandzement durch ein leicht aus= dehnendes Bindemittel gemisch ersetzt worden ist. Das Bindemittelgemisch enthält außer dem Portlandzement noch Tonerdezement, Kalziumsulfat, Kalk= hydrat und hydraulische Zugaben. Das Gemisch enthält also durch-den Ton= erdezement eine zusätzliche Menge Kalziumaluminat. Hydrationsfähiger Tonerdezement zusammen mit Kalziumaluminat aus dem Portlandzement reagiert während der Erstarrung und der Erhärtung der Masse mit dem Kalziumsulfat unter Entstehung von stark expandierbaren Kalziumhydrosulfraluminaten so daß die gesamte Mischung eine leichte Ausdehnung hat. Die hydraulische Zugabe verringert in der Lösung die Konzentration von Kalziumoxid, ermöglicht eine schnelle Auflösung von Kalziumaluminaten und eine bessere Kristallisation von Kalziumhydrosulfvaluminaten. Unter hydraulischen Zugaben sind natürliche oder kunstliche Puzzolane gemeint.
- Zu den natürlichen Puzzolanen zählen vorwiegend Aschen und Gesteine vulkanischen Ursprungs wie Bims, Tuffstein (Traß), Santorinerde sowie der SiO2 - reichste Vertreter Kieselgur oder Molererde (Ablagerung von Radiolarien- und Diatomeen - Skelettresten). Künstliche Puzzolane sind z. B. das bereits aus der Römerzeit bekannte Ziegelmehl, sowie der größte Teil der Steinkohle - Kraftwerkaschen.
- Die aus dem B-indemittelgemisch gegossene Standard-Mörtel -PrUfkörper 40 X 40 X 160 mm haben folgende Eigenschaften: Erstarrungszeit - Beginn (h) = 0,5 Erstarrungszeit - Ende (h) = 12,0 Schwindmaß - Wasserlagerung nach 24 Std. = - + 0,15% Zuwachs nach 28 Tg. = - + 0,3-1,0% Zuwachs - Feuchtigkeitlagerung nach 28 Tg. = - + 0;1% Zuwachs Mischungsbeispiel: 41,9 Gew.-% Sand einer Korngröße von 0,05 bis 3,0 mm 20,0 Gew.-% hydraulische Zugabe 22,0 Gew.-% Portlandzement 45 2,0 Gew.-% Kalkhydrat 6,0 Gew.-% Tonerdezement 8,0 Gew.-% Kalziumsulfat 0,1 Gew.-% Superverflüssiger wurden vermischt. Die so gewonnene trockene Arbeitsmasse wurde durch Zugabe von 24 Gew.-% Wasser pumpfähig und selbstverlaufend.
- Aus dieser Masse gegossene Prüfkörper 40 X 40-X 160 mm haben folgende Druckfestigkeit: nach 3 Tagen nach 28 Tagen N/mm. 18,0 40,0
Claims (4)
- Patentansprüche: 1. Der Zement-Fließmörtel, dadurch gekennzeichnet, daß die Masse aus: Mineralischen Füllstoffen 50,0 bis 85,0 Gew.-% Portlandzement 15,0 bis 50,0 Gew.-% Kalkhydrat 0,5 bis 10,0 Gew.-% Tonerdezement 0,1 bis 10,0 Gew.-% Kalziumsulfat 0,1 bis 15,0 Gew.-% Hydraulische Zugabe 1,0 bis 30,0 Gew.-% und Superverflüssiger 0,01 bis 1,0 Gew.-% zusammen gesetzt ist.
- 2. Der Zement-Fließmörtel nach Anspruch 1. dadurch gekennzeichnet, daß anstatt des Portlandzements die Zemente mit Zumahistoffen verwendet werden.
- 3. Der Zement-Fließmörtel nach Anspruch 1 und 2, dadurch gekennzeichnet, daß hydraulische Zugaben natürliche oder künstliche Puzzolanen sind.
- 4. Der Zement-Fließmörtel nach Anspruch 1 , dadurch gekennzeichnet, daß Superverflüssiger ein sulfonierter Polykondensat des Formaldehyds mit dem Phenol, Naphthalen, Melamin oder Harnstoff sit.