DE1924991B2 - Wasserloesliche salzkerne - Google Patents
Wasserloesliche salzkerneInfo
- Publication number
- DE1924991B2 DE1924991B2 DE19691924991 DE1924991A DE1924991B2 DE 1924991 B2 DE1924991 B2 DE 1924991B2 DE 19691924991 DE19691924991 DE 19691924991 DE 1924991 A DE1924991 A DE 1924991A DE 1924991 B2 DE1924991 B2 DE 1924991B2
- Authority
- DE
- Germany
- Prior art keywords
- water
- salt
- soluble salt
- cores
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
15
Die Erfindung betrifft wasserlösliche Salzkerne, die bis zu 10% Borax, Magnesium oder Talkum einzeln
oder als Gemisch enthalten und durch Verdichten der Salze unter Druck und anschließendem Sintern
hergestellt werden nach Patent 14 83 641.
Aus der US-PS 33 56 129 ist es bekannt, aus wasserlöslichen
Salzen, wie NaQ oder KCl, Kerne für Gießereizwecke zu pressen, die anschließend bei Temperaturen
zwischen 500 bis 750' C gesintert werden. Diese Kerne werden in ein Gußstück eingegossen und nach
dessen Erkalten im allgemeinen wieder mit Wasser herausgespült. Dieses Verfahren hat sich bei Gußstücken
mit einfachen Konturen ausgezeichnet bewährt. Werden jedoch die Konturen des Gußstückes
zum Beispiel durch schroffe Querschnittsübergänge kompliziert, so sind auch die gepreßten und gesinterten
Salzkerne infolge Temperaturwechsel und mechanischen Beanspruchungen höheren Belastungen
ausgesetzt, die zu einer Zerstörung der Salzkerne an den gefährdeten Stellen führen können.
Es ist deshalb in der DT-PS 14 83 641 vorgesehen, die thermische und mechanische Beanspruchbarkeit
der wasserlöslichen Salzkerne dadurch zu erhöhen, daß dem wasserlöslichen Salz bis zu 10% Borax, Magnesium
oder Talkum einzeln oder im Gemisch zugesetzt sind, um die Sinterung zu fördern und damit die
Druck- und Biegefestigkeit der Salzkerne zu verbessern.
Es ist die Aufgabe der vorliegenden Erfindung, eine weitere Erhöhung der Druck- und Biegefestigkeit der
Salzkerne gemäß der eingangs genannten Zusammen-Setzung
zu erzielen.
Die Lösung dieser Aufgabe erfolgt in der Weise, daß die wasserlöslichen Salzkerne noch einen Zusatz
von 0,5 bis 2 % Wasserglas enthalten.
Aus der FR-PS 13 39 372 und der FR-PS 1:5 26465 ist zwar die Verwendung von Wasserglas als Zusatz
zu wasserlöslichen Salzkernen bekannt, doch dient das Wasserglas in beiden Fällen als Bindemittel für
das jeweils benutzte Salz, so daß daraus nicht geschlossen werden kann, daß bei einem wasserlöslichen
Salzkern gemäß der DT-PS 14 83 641, der eines Bindemittels nicht bedarf, eine erhebliche Steigerung der
Druck- und Biegefestigkeit durch den Zusatz von Wasserglas erzeugt wird.
Die Mischung zur Herstellung des Salzkernes wird im alleemeinen bei einem Preßdruck von 1 bis
lOkp/mnr etwa 1,5 bis 2,5 Minuten lang in einer Presse verdichtet. Anschließend wird der gepreßte
Salzkern bei einer Temperatur vun 500 bis 750 C dreißig Minuten bis zwei Stunden lang einem Sintcrglühprozeß
unterworfen.
Besonders vorteilhaft ist es, das Pressen und Sintern des Salzkerns in einem Arbeitsschritt mit Hilfe des
Heißpreßverfahrens durchzuführen.
Um die mit dem erfindungsgemüß zusammengesetzten
wasserlöslichen Salzkern erzielten Vorteile hinsichtlich erhöhter Werte für die Druck- und Biegefestigkeit
gegenüber dem nach der DT-PS 14 83 641 zusammengesetzten wasserlöslichen Salzkern zu verdeutlichen,
ist im folgenden je ein Ausführungsbeispiel für einen Salzkern gemäß DT-PS 14 83 641 und
einen nach der vorliegenden Erfindung zusammengesetzten Salzkern wiedergegeben:
Ein Gemisch aus
92,5 % Kochsalz
5,0% Borax
1,5% Magnesiumoxid
1,0% Talkum
5,0% Borax
1,5% Magnesiumoxid
1,0% Talkum
wurde in ein Preßgesenk eingefüllt und bei einem Preßdruck von 7,5kp/mnr zwei Minuten lang verdichtet.
Anschließend wurde derauf diese Weise hergestellte Salzkern eine Stunde lang bei 200 C getrocknet
und dann bei 700 C eine Stunde lang gesintert. Nach der Abkühlung auf Raumtemperatur
wurden die Druck- und Biegefestigkeit des hergestellten Salzkerns auf einer bekannten Prüfmaschine
zu 450 kp/cnr bzw. 120 kp/cnr ermittelt.
Ein Gemisch aus
92,0% Kochsalz
5,0 % Borax
1,5% Magnesiumoxid
1,0% Talkum
und 0,5 % Wasserglas
5,0 % Borax
1,5% Magnesiumoxid
1,0% Talkum
und 0,5 % Wasserglas
wurde nach dem Einfüllen in ein Preßgesenk bei einem Druck von 7,5 kp/mm2 zwei Minuten lang verdichtet.
Der auf diese Weise hergestellte Salzkern wurde eine Stunde lang bei 200 C getrocknet und
anschließend in einem Glühofen einer Sinterung von 60 Minuten Dauer bei einer Temperatur von 700' C
unterworfen. Nach der Abkühlung auf Raumtemperatur wurden die Druck- und Biegefestigkeit des gesinterten
Salzkerns auf einer bekannten Prüfmaschine zu 540 kp/cnr bzw. 170 kp/cnr ermittelt.
Eine vergleichende Gegenüberstellung der Versuchsergebnisse der beiden vorstehenden Ausführungsbeispiele
zeigt eindeutig, daß es mit Hilfe der erfindungsgemäßen Salzkemmischup.g gelingt, die Druckfestigkeit
der Salzkerne um 20 % und die Biegefestigkeit um 40% gegenüber den mit einem nach der DT-PS
14 83 641 zusammengesetzten Salzkern erzielten Werten zu steigern.
Claims (1)
- Patentanspruch:Wasserlösliche Salzkerne, die bis zu 10% Borax, Magnesiumoxid oder Talkum einzeln oder als Gemisch enthalten und durch Verdichten der Salze unter Druck und anschließendem Sintern hergestellt werden nach Patent 1483641, gekennzeichnet durch einen Zusatz von 0,5 bis 2% Wasserglas.