DE1521152A1 - Metallisierung von Kunststoffoberflaechen - Google Patents
Metallisierung von KunststoffoberflaechenInfo
- Publication number
- DE1521152A1 DE1521152A1 DE19651521152 DE1521152A DE1521152A1 DE 1521152 A1 DE1521152 A1 DE 1521152A1 DE 19651521152 DE19651521152 DE 19651521152 DE 1521152 A DE1521152 A DE 1521152A DE 1521152 A1 DE1521152 A1 DE 1521152A1
- Authority
- DE
- Germany
- Prior art keywords
- copper
- parts
- silver
- weight
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Badische Anilin- & Soda-Fabrik AG P 1521 152'6 Ludwigshafen, 1
o.z. 23 760 LS//pä ' 8. 11. 1968
• Metallisierung von Kunststoffoberflächen
Zur Herstellung von metallischen leitenden Schichten auf Kunststoffoberflächen ist es bekannt, Dispersionen von Metallpigmenten
in Bindemitteln auf die Kunststoffoberflächen aufzubringen und dort durch Trocknen, Auspolymerisieren oder
Auskondensieren zu verfestigen. Solche Leitlacke haben nur relativ geringe Leitwerte, da die dispergierten metallischen
Teilchen durch das Bindemittel keine zusammenhängende Leitschicht bilden. So erreichen die Leitwerte dieser Schichten
nicht diejenigen von Metallfolien vergleichbarer Dicke. Eine Erhöhung des Anteils an Metallpigmenten innerhalb der Schicht
ergibt zwar auch eine Erhöhung der Leitwerte, ist aber nicht immer anwendbar, da hierbei die Haftfestigkeit der leitenden
Schicht auf der Kunststoffoberfläche stark verringert wird.
Es ist ferner bekannt, zur Herstellung von metallischen leitenden Schichten auf Kunststoffen diese im Hochvakuum mit dem
Metall ai bedampfen. Dieses Verfahren ist Jedoch relativ aufwendig.
Es ist weiterhin bekannt (belgische Patentschrift 553 332) zur
Metallisierung von Oberflächen zu Schmuck- und Schutzzwecken als Bindemittel für Metallpulver Polyurethane zu verwenden, um
damit gegen die Einwirkung von Chemikalien beständige Überzüge zu erhalten.
309817/0668
(Art.7 n m.a Nr.ι st*a d«
- 2 - O.Z. 2? 7βΟ
Pur die Metallisierung von ABS-Kunststoffen ist in letzter
Zeit ein Verfahren bekanntgeworden, das darin besteht, daß man die gereinigten und entfetteten Kunststoffoberflächen
mit konzentrierter Schwefelsäure behandelt, wodurch die Oberfläche chemisch aufgerauht wird. Die Oberfläche
wird dann z.B. mit einer sauren Zinn(Il)-chloridlösung behandelt,
wobei auf ihr metallisches Zinn adsorbiert wird, φ Diese Schicht wird dann mit einer Edelmetallösung, z.B.
einer ammoniakalischen Silbersalzlösung, aktiviert und schließlich chemisch verkupfert. Abschließend wird die so
vorbehandelte Oberfläche in einem sauren Kupferelektrolyten verkupfert. Mit diesem Verfahren können jedoch nur auf '■
ABS-Kunststoffe metallische Schichten aufgebracht werden.
Gemäß einem weiteren bekannten Verfahren werden äiöcallische
Schichten dadurch auf eine Kunststoffoberfläche aufgebracht, daß man auf den Kunststoff in einem Binde- und/oder Lösungs-
W mittel fein dispergiertes Eisen nach einem beliebigen bekannten Beschichtungsverfahren aufbringt, trocknet, die erhaltene
disperse Eisenschicht in einem Tauchbad stromlos verkupfert und gegebenenfalls weitere metallische Leitschichten strom-
los oder galvanisch aufbringt. Mit diesem Verfahren können auf einfache Weise sehr haftfeste und gut leitende metallische
Schichten auf eine Kunststoffoberfläche aufgebracht werden.
BAD ORIG>NAL 909817/0668
O.Z. 23 760
Gegenstand der vorliegenden Anmeldung ist die Verwendung
von Bindemitteln, die zu wenigstens 20 Gewichtsprozent aus Reaktionsprodukten polyfunktioneller Isooyanate mit polyfunktionellen
Hydroxylverbindungen bestehen, als Bindemittel (B) im Rahmen des Verfahrens zum Metallisieren von Oberflächen
von Kunststoff-Gegenständen, insbesondere von Kunststoff-Folien, bei dem man
a) auf die Oberflächen einen Leitlack aufbringt, der das Bindemittel (B) sowie feinverteiltes Eisen enthält,
b) das Bindemittel (B) verfestigt,
c) auf den Leitlack eine Schicht von Silber oder insbesondere
von Kupfer stromlos aufbringt und - gegebenenfalls -
d) auf die stromlos aufgebrachte Schicht von Silber oder Kupfer Weitere Metallsohiohten stromlos oder galvanisch aufbringt
.
Zu den als Bindemittel verwendeten Reaktionsprodukten polyfunktioneller
Isocyanate mit polyfunktionellen Hydroxylverbindungen ist im einzelnen folgendes auszuführen: Als polyfunktionelle
Isooyanate geeignet sind beispielsweise: Naphthalin-1,5-diisooyanat,
Benzol-1,4-diisooyanat und Diphenylmethan-4,41-diisooyanat
sowie Toluylen-diieocyanate, z. B. Toluylen-2,4-düsocyanat
und Toluylen-2,6-diiBocyanat oder dimerieiertes
Toluylen-2,4-diisooyanat. Ale polyfunktionelie Hydroxylver-
- ja -
909817/0668
, O.Z. 25 760
bindungen sind beispielsweise Polyäther oder Polyester mit endständigen Hydroxylgruppen geeignet. Besonders geeignete
Komponenten sind Polyäther aus polyoxpropyliertem Trimethylolpropan,
Polyester aus Adipinsäure, Hexantriol, Butylen-r .
glykol oder aus Adipinsäurediäthylenglykol und Butantriol.
Erfindungsgemäß kann man als Bindemittel die die Reaktionsprodukte
aus Polyisocyanaten und Polyhydroxyverbindungen w bildenden Komponenten allein anwenden oder einem -physikalisch
trocknenden Bindemittelgemisch zusetzen und auf der Kunststoffoberfläche aushärten lassen. Um eine gute Haftfestigkeit
der Metallschicht zu gewährleisten, müssen in dem verfestigten Lack mindestens 20 Gewichtsprozent eines Reaktionsproduktes
aus polyfunktionellen Isocyanaten und polyfunktionellen Hydroxylverbindungen enthalten sein.
909817/0668
ο.ζ. 25 760
Als weitere Bindemittel kommen z.B. Lösungen von gegebenenfalls
nachchloriertem Polyvinylchlorid, Viny!mischpolymerisate.
Polyvinylacetat -formal oder -butyral oder löslichen Polyamiden in Frage. Das Lösungsmittel sollte zweckmäßig so beschaffen
sein, daß es den jeweiligen Trägerwerkstoff anlöst oder anquellt. ■ . "
Diesen Gemischen werden 250 bis kkO Gewichtsprozent feinteiliges
Eisen zugesetzt, die dann z.B. mit Hilfe einer Kolloidmühle zu Dispersionen verarbeitet werden. Die verwendeten Eisenteilchen sollen eine Teilchengröße von etwa 0,1
bis 1/ü aufweisen. isv . ■-.
Die Dispersionen werden unmittelbar nach ihrer Herstellung auf den Trägerwerkstoff aufgebracht und dort verfestigt. Die
so hergestellten Schichten sollen eine Schichtdicke von 1 bis 6 zu. aufweisen. Die beschichteten Trägerwerkstoffe werden
dann in·ein Bad getaucht, das Silber- oder Kupfersalze enthält.
Je nach" der Konzentration dieser Bäder und ihrer Temperatur wird das in den Lackschichten befindliche Eisen durch
die Metalle der obengenannten Salze ersetzt. In Abhängigkeit von der Verweilzeit ist es möglich, das gesamte oder nur einen
Teil des in der Schicht enthaltenen Eisens zu entfernen und durch die genannten Metalle zu ersetzen. Bei dieser Behandlung
entstehen haftfeste und glänzende Überzüge aus Kupfer oder · Silber, die Wärme und Elektrizität gut leiten. Zur,Erhöhung
■;■ ■'. ' v- ■.■ · · · : · : ' ■ ;-■.-5-: ·■■·'■' ■
90ä817/0668
f - b °·ζ· 2^ 76°
der Haftfestigkeit ist es vorteilhaft, die mit den Eisendispersionen
beschichteten Trägerwerkstoffe vor ihrer stromlosen Verkupferung oder Versilberung einige Zeit bei erhöhten Temperaturen
von bis zu etwa 6O0C zu tempern. Eine deutliche Verbesserung
der Haftfestigkeit wird schon bei einstündiger Lagerung unter den genannten Bedingungen festgestellt. Zweckmäßig
werden die Gegenstände etwa 3 bis 6 Stunden getempert.
Es ist möglich, auf die stromlos aufgebrachten metallischen Grundschichten weitere Metallschichten stromlos oder auf
galvanischem Wege aufzubringen.
Die erfindungsgemäß metallisierten Kunststoffoberflächen eignen sich gut zur Ableitung statischer Elektrizität sowie
zur Herstellung elektrischer Abschirmungen gegen hochfrequente elektrische Wechselfelder. Aus erfindungsgemäß beschichteten
Folien lassen sich Kondensatoren kleinster Abmessungen herstellen. Solche Folien sind auch vorzüglich als
Trägerfolien für die Herstellung von Magnetogrammträgern mit oxydischen magnetisierbaren Teilchen geeignet. Ferner
lassen sie sich als Schaltbänder einsetzen. Verwendet man bei der nachfolgenden Galvanisierung Salze von feruomagnetischen
Materialien, z. B. Salze des Eisens, Nickels oder Kobalts, oder Gemische dieser Salze, so lassen sich auf den
verkupferten oder versilberten Oberflächen sehr häft- und abriebfeste, magnetische Oberzüge herstellen, so daß die so
90981^70668
ο.ζ. 23 760
beschichteten Körper direkt als Magnetspeicher eingesetzt werden können. Bereits bei Schichtdicken von 1/U erhält mc
Speicher mit hervorragenden magnetischen Eigenschaften*
Nach dem erfindungsgemäßen Verfahren lassen sich auf einfache Weise gedruckte Schaltungen herstellen. Hierzu wird der
für die Grundbeschichtung verwendete Leitlack mit Hilfe von Schablonen auf die Kunststoffoberfläche gedruckt und diese
auf stromlosem Wege mit Kupfer oder Silber Überzogen.
. " . Beispiel 1 ■
Aus 72 Gewichtstellen Eisenpulver mit einer Teilchengröße,
'von bis zu 1/U1 20,9 Gewichtsteilen nachchloriertem Polyvinylchlorid, 5*1 Gewichtsteilen eines Gemisches aus gleichen
Teilen Adipinsäurediäthylenglykol und Toluylen-2,6-diiso-.cyanat, 2 Gewichtsteilen Stearinsäure und 60 Gewichtsteilen
eines LUsungsmittelgemisehes aus 5 Teilen Tetrahydrofuran und f
2 Teilen Toluol wird durch 5- bis 6stündiges Behandeln in
: einer Rührwerksmühle eine Dispersion hergestellt. Die Dispersion wird bei einem I^.^ck von etwa 2 atü durch Watte fil-·
■;* triert und dann mittels einer Gießvorrichtung auf eine Folie
aus Polyvinylchlorid aufgebracht und dort verfestigt. Die so beschichtete Folie wird durch ein Bad geführt, das Je
Liter Wasser 150 g Kupfersulfat, 4o g Triäthanolamin und
27 g konzentrierte Schwefelsäure enthält. Naoh 5 Minuten ist
■■'- r ■ . ' J-·"/: ''■- '■■ : ■ '; '■■■:.-7- '■
909817/066 8 eAD
1524152
-\- Ο.Ζ. 23 760
bereits bei Raumtemperatur die Eisenäohioht unter Entwicklung
von Wasserstoff so weit abgebaut, daß die Oberfläche mit einem zusammenhängenden überzug aus Kupfer (0,8 mg Cu/em ) .
versehen ist. Nach dem Trocknen wird dieser überzug poliert, weist einen schönen Metallglanz auf und besitzt eine gute
Haftfestigkeit auf der Kunststoffoberfläche.
2
Stromdichte von 0,2 bis 0,8 Amp/dm können in dem gleichen
Stromdichte von 0,2 bis 0,8 Amp/dm können in dem gleichen
Auf die so aufgebrachte Kupferschicht kann eine Silberschicht
auf stromlosem Wege aufgebracht werden, wenn man die ver- ';■;'"
kupierte Folie durch ein Bad leitet, das pro Liter Wasser ; 1/5 g Silbernitrat, 5 g Ä'thylendiamlnotetraessigsKure, Jg
Natrlumthiosulfat und 2 g Weinsäure enthält. Innerhalb von ·
3 Minuten können auf diese Welse 0,08 mg/cm Silber auf der, .
Folie abgeschieden werden. ; .
Die verkupferten oder versilberten Folien können z.B. als Schaltbänder fUr Magnetogrammträger eingesetzt werden. Sie
zeigen gegenüber den bisher als Schaltbänder verwendeten Alumlniumfolien oder mit einer Silberdisperslon beschichteten
Kunststoffolien eine um den Faktor 7 erhöhte Lebensdauer. .
-8-
BAD ORIGiNAL
9Ö981 7/06 6 8
9 | 1521 | 152 |
-V- | O.Z. 23 | 760 |
Beispiel 2 |
In einer Rührwerksmühle wird durch 4stündiges Rühren eine
Dispersion hergestellt, die aus 54,7 Gewichtsteilen feinteiligem
Eisen, 15,7 Gewichtsteilen eines Polyäthers aus polyoxpropyliertem Trimethylolpropan, 1,6 Gewichtsteilen
Stearinsäure und 30 Gewichtsteilen eines Lösungsraittelgemisches aus 2 Teilen Ä'thylacetat und 1 Teil Toluol besteht. Die Dis- %
persion wird unter Druck durch eine Papierfilterkerze filtriert und anschließend mit 50 Gewichtsteilen Cyclohexanon
und 11 Gewichtsteilen eines Urethans aus 3 Molen Toluylendiisocyanat
und 1 Mol Trimethylolpropan intensiv verrührt. Die erhaltene Mischung wird innerhalb von 2 Stunden auf die
Oberfläche eines Formteiles aus einem Mischpolymerisat aus Acrylnitril, Butadien und Styrol aufgesprüht. Hierauf wird
der Formteil etwa 5 Stunden bei 60°C getempert und anschliessend poliert. Durch Behandlung des Formteiles in einer
Lösung, die pro Liter Wasser 150 g Kupfersulfat, 40 g Tri- "
äthanolamin und 27 g konzentrierte Schwefelsäure enthält,
entsteht innerhalb von 30 Minuten ein haftfester glänzender
Überzug aus metallischem Kupfer in einer Schichtdicke von .etwa, 1/U. Diese Kupferschicht kann anschließend bei Stromstärken
von 1 bis 3 Amp/dm im gleichen Bad beliebig verstärkt
werden.
Die so hergestellte Kupferoberfläche kann mit anderen Metallen,
z.B. Chrom, Nickel, Kobalt oder Rhodium, galvanisch abgedeckt werden.
-9-
909817/0668
AO -Y-
O.Z.. 2? 760
Die so hergestellten, anschließend noch 15 Stunden gelagerten
glänzenden Metallüberzüge weisen eine ausgezeichnete Haft« '-festigkeit auf, deren Abreißkraft gegenüber der Kunststoffoberfläche, gemessen an einem 2,5 cm breiten und 5 cm
langen Probestück, etwa 3 kp beträgt.
Verwendet man anstelle eines Formteiles aus einem Mischpolymerisat aus Acrylnitril, Butadien und Styrol solche aus ■
Polyvinylchlorid oder aus einem Polyester aus Phthalsäure, Maleinsäure und Propylenglykol, der mit Styrol versetzt ist,
und bringt auf diese Formteile einen metallischen überzug
wie oben beschrieben auf, so werden unter gleichen Bedingungen
AbreiSkräfte von 4,5 bzw. 2,5 kp gemessen.
-10-
909817/0668
8AD ORfälNÄU■
Claims (1)
- AA.fifl ffitttt JE» ft»Yon Biüäeaittoln» ut* m venicttane Sd Otviobta·-alt FOlyfunztionellcn. Hydrotylvortindua^on toetohon» alo BIn-(B). lia Bulmen doe Yorfahrens stm Kctallloiortn vonvon Eunstotofi-Gesonotünden» itxebaüotvlere von Kimstetoff-Tollett, toi dem nau .ft) ftuf dl» Oterriäciien einen !,eltXack aufbringt, d«r da« (B) «owie felnvertelltea ΐ:ΐ·βαde* BlTideaUtol (B) verfestigtf '"c) «nf -4«a LeitXttQJr «in« Schicht iron SllVoy oder yon. tuyttv »tr«aloe »ufbringt und · gtg»t«nenfalle -von Silhsr od«r Kup· odor4i« etrossloe aufgolirfichta fer weitere H«tellechlohteaBiDISCH]S /JILH- A ßOBA-PAKllE909817/0668