CN112477451A - 适用于多种承印物的混合基热转印碳带 - Google Patents
适用于多种承印物的混合基热转印碳带 Download PDFInfo
- Publication number
- CN112477451A CN112477451A CN202011396287.6A CN202011396287A CN112477451A CN 112477451 A CN112477451 A CN 112477451A CN 202011396287 A CN202011396287 A CN 202011396287A CN 112477451 A CN112477451 A CN 112477451A
- Authority
- CN
- China
- Prior art keywords
- layer
- thermal transfer
- spraying
- mixed
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了适用于多种承印物的混合基热转印碳带,涉及打印材料技术领域,针对现有的不能很好的适应不同承应物的打印的问题,现提出如下方案,其包括基层,所述基层的背面涂布有润滑层,所述基层的正面依次涂布有离型层、油墨层、粘接层和保护层,本发明结构简单,可以适应不同位置的打印,同时配合着粘接层的工作可以增强油墨的粘接,保证打印的效果,适应多种承印物。
Description
技术领域
本发明涉及打印材料技术领域,尤其涉及适用于多种承印物的混合基热转印碳带。
背景技术
热转印色带是打印机耗材,就是在一面涂上蜡基、树脂基或混合的油墨的聚脂或其它高密度薄膜。在没有油墨的一面涂上润滑剂以防止打印头的磨损和损坏,碳带的轴芯常见的有纸质和塑料两种,主要要求是不能变形和在打印时不能滑动。
但是现有的碳带在使用过程中,根据基底的不同,对于要打印的承应物一般都具有一定的要求,使得在一定范围内使用受限,进而不能很好的适应打印的工作。
发明内容
本发明提出的适用于多种承印物的混合基热转印碳带,解决了不能很好的适应不同承应物的打印的问题。
为了实现上述目的,本发明采用了如下技术方案:
适用于多种承印物的混合基热转印碳带,包括基层,所述基层的背面涂布有润滑层,所述基层的正面依次涂布有离型层、油墨层、粘接层和保护层。
优选的,所述润滑层为滑石和有机硅,滑石和有机硅的重量比为1:11,保护层为油脂材料。
优选的,粘接层包括硫粉和磷粉,硫粉和磷粉的重量比为1:1。
优选的,离型层为硅树脂、聚酯树脂、蜡乳液和水性离型剂的混合物,硅树脂、聚酯树脂、蜡乳液和水性离型剂重量比为1:2.5:5.5:1.5:0.5,离型层的厚度为0.001~0.006mm。
优选的,油墨层为水性丙烯酸树脂、羟乙基纤维素、水、颜料、分散剂和棕榈蜡的混合物,水性丙烯酸树脂、羟乙基纤维素、水、颜料、分散剂和棕榈蜡的重量比为20:30:1:0.4:0.2:46,油墨层的厚度为0.002~0.004mm。
优选的,所述基层为聚酯材料,厚度为0.002~0.01mm。
优选的,包括以下生产步骤:
S1:将硫和磷在低温保护性气体的保护下,进行研磨,成极微的细粉;
S2:将硅树脂、聚酯树脂、蜡乳液和水性离型剂放置到混合搅拌机中混合搅拌一定时间,然后进行消泡处理;
S3:将水性丙烯酸树脂、羟乙基纤维素、水、颜料、分散剂和棕榈蜡放置到混合搅拌机中混合搅拌一定时间,然后进行消泡处理;
S4:将基带放置到绕卷机上,然后经过喷涂机,在喷涂机中依次喷涂一定厚度步骤S2和步骤S3中的成品,然后进行一定程度的低温烘干;
S5:将步骤S4生产好的成品放置到绕卷机上,然后经过喷涂机,在低温保护性气体中经过喷涂机,然后经过喷涂机喷涂一定厚度步骤S1中的成品,然后再喷涂一定的量的保护油膜;
S6:将步骤S5中生产好的成品放置到喷涂绕卷机上,然后经过喷涂机,在基带的背面喷涂一定量的滑石粉或者有机硅;
S6:对步骤S6中的成品进行真空包装。
8、根据权利要求6所述的适用于多种承印物的混合基热转印碳带,其特征在于,步骤S1和S5的保护性气体为氮气,处理温度为0~10摄氏度。
优选的,步骤S4中烘干温度为40~50摄氏度,烘干时间为2~5h。
优选的,硫、磷、滑石粉或者有机硅的粒度为10000~15000目。
本发明的有益效果:
1、通过多种材料说组成的离型层和油墨层可以适应不同位置的打印,同时配合着粘接层的工作可以增强油墨的粘接,保证打印的效果,适应多种承印物。
2、通过多种工艺的生产,可以快速稳定的进行生产的需要,同时经过的多种步骤的生产,保证产品的质量,太高产能的同时,提高产品的质量。
具体实施方式
下面将本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。
适用于多种承印物的混合基热转印碳带,包括基层,所述基层的背面涂布有润滑层,所述基层的正面依次涂布有离型层、油墨层和粘接层,润滑层可以减少摩擦,减少打印头的磨损,离型层保证后续的工作,油墨层保证的显示以及颜色的突出,粘接层可以增强油墨的粘接,保证打印的效果,适应多种承印物。
润滑层为滑石和有机硅,滑石和有机硅的重量比为1:1,两者的配合可以保证润滑的进行,保护层为油脂材料,保护硫粉和磷粉直接与空气的接触。
粘接层包括硫粉和磷粉,硫粉和磷粉的重量比为1:1,硫和磷在后续打印过程中,由于在打印后保护油膜的损坏,使得其与外界空气接触,磷氧化放热,同时带动硫的氧化,再一定温度下空气中的水以及氧反应,在金属或者其他部分物件上,形成酸性物质,进行微量的腐蚀,形成粗糙的表面,增加粘附的力度,在磷氧化放热时,也可对塑料等不耐高温的表面加热凹陷成极微的凹陷或者变形,进而增加粘附力度,保证打印的进行,适应多样化的承印物。
离型层为硅树脂、聚酯树脂、蜡乳液和水性离型剂的混合物,硅树脂、聚酯树脂、蜡乳液和水性离型剂重量比为1:2.5:5.5:1.5:0.5,离型层的厚度为0.001~0.006mm,通过混合的多种离型层可以很好让油墨与基层脱离,保证打印的需要。
油墨层为水性丙烯酸树脂、羟乙基纤维素、水、颜料、分散剂和棕榈蜡的混合物,水性丙烯酸树脂、羟乙基纤维素、水、颜料、分散剂和棕榈蜡的重量比为20:30:1:0.4:0.2:46,油墨层的厚度为0.002~0.004mm,通过多个材料的组合,形成的油墨可以在多种复合的场景下进行存储,保证打印的要求以及对存储的要求,配合着粘贴层的作用,保证稳定的打印。
基层为聚酯材料,厚度为0.002~0.01mm。
包括以下生产步骤:
S1:将硫和磷在低温保护性气体的保护下,进行研磨,成极微的细粉,细粉可以进行保证后续反应的接触面积,同时可以均匀分散,保证后续的腐蚀的稳定。
S2:将硅树脂、聚酯树脂、蜡乳液和水性离型剂放置到混合搅拌机中混合搅拌一定时间,然后进行消泡处理;
S3:将水性丙烯酸树脂、羟乙基纤维素、水、颜料、分散剂和棕榈蜡放置到混合搅拌机中混合搅拌一定时间,然后进行消泡处理,混合处理后,各个材料均匀分布,每种材料的性能有一定的差异,进而适应不同的材料打印工作,保证打印的需要。
S4:将基带放置到绕卷机上,然后经过喷涂机,在喷涂机中依次喷涂一定厚度步骤S2和步骤S3中的成品,然后进行一定程度的低温烘干,混合处理后,各个材料均匀分布,每种材料的性能有一定的差异,进而适应不同的材料打印工作,保证打印对油墨的不同的需要,同时烘干可以对油墨进行一定的稳定作用,避免后续空气对油墨可能造成的影响。
S5:将步骤S4生产好的成品放置到绕卷机上,然后经过喷涂机,在低温保护性气体中经过喷涂机,然后经过喷涂机喷涂一定厚度步骤S1中的成品,然后再喷涂一定的量的保护油膜,油膜对粉末进行保护,避免在不打印时,材料与空气的接触实效,保证后续的打印。
S6:将步骤S5中生产好的成品放置到喷涂绕卷机上,然后经过喷涂机,在基带的背面喷涂一定量的滑石粉或者有机硅。
S6:对步骤S6中的成品进行真空包装,真空包装保证后续的存储和产品的质量。
步骤S1和S5的保护性气体为氮气,处理温度为0~10摄氏度,低温充氮保证加工过程中的安全,避免不必要的损耗,保证产品的质量。
步骤S4中烘干温度为40~50摄氏度,烘干时间为2~5h,低温烘干,保证油墨的稳定。
硫、磷、滑石粉或者有机硅的粒度为10000~15000目。
以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,根据本发明的技术方案及其发明构思加以等同替换或改变,都应涵盖在本发明的保护范围之内。
Claims (10)
1.适用于多种承印物的混合基热转印碳带,包括基层,其特征在于,所述基层的背面涂布有润滑层,所述基层的正面依次涂布有离型层、油墨层、粘接层和保护层。
2.根据权利要求1所述的适用于多种承印物的混合基热转印碳带,其特征在于,所述润滑层为滑石和有机硅,滑石和有机硅的重量比为1:1,保护层为油脂材料。
3.根据权利要求1所述的适用于多种承印物的混合基热转印碳带,其特征在于,粘接层包括硫粉和磷粉,硫粉和磷粉的重量比为1:1。
4.根据权利要求1所述的适用于多种承印物的混合基热转印碳带,其特征在于,离型层为硅树脂、聚酯树脂、蜡乳液和水性离型剂的混合物,硅树脂、聚酯树脂、蜡乳液和水性离型剂重量比为1:2.5:5.5:1.5:0.5,离型层的厚度为0.001~0.006mm。
5.根据权利要求1所述的适用于多种承印物的混合基热转印碳带,其特征在于,油墨层为水性丙烯酸树脂、羟乙基纤维素、水、颜料、分散剂和棕榈蜡的混合物,水性丙烯酸树脂、羟乙基纤维素、水、颜料、分散剂和棕榈蜡的重量比为20:30:1:0.4:0.2:46,油墨层的厚度为0.002~0.004mm。
6.根据权利要求1所述的适用于多种承印物的混合基热转印碳带,其特征在于,所述基层为聚酯材料,厚度为0.002~0.01mm。
7.根据权利要求1所述的适用于多种承印物的混合基热转印碳带,其特征在于,包括以下生产步骤:
S1:将硫和磷在低温保护性气体的保护下,进行研磨,成极微的细粉;
S2:将硅树脂、聚酯树脂、蜡乳液和水性离型剂放置到混合搅拌机中混合搅拌一定时间,然后进行消泡处理;
S3:将水性丙烯酸树脂、羟乙基纤维素、水、颜料、分散剂和棕榈蜡放置到混合搅拌机中混合搅拌一定时间,然后进行消泡处理;
S4:将基带放置到绕卷机上,然后经过喷涂机,在喷涂机中依次喷涂一定厚度步骤S2和步骤S3中的成品,然后进行一定程度的低温烘干;
S5:将步骤S4生产好的成品放置到绕卷机上,然后经过喷涂机,在低温保护性气体中经过喷涂机,然后经过喷涂机喷涂一定厚度步骤S1中的成品,然后再喷涂一定的量的保护油膜;
S6:将步骤S5中生产好的成品放置到喷涂绕卷机上,然后经过喷涂机,在基带的背面喷涂一定量的滑石粉或者有机硅;
S6:对步骤S6中的成品进行真空包装。
8.根据权利要求6所述的适用于多种承印物的混合基热转印碳带,其特征在于,步骤S1和S5的保护性气体为氮气,处理温度为0~10摄氏度。
9.根据权利要求6所述的适用于多种承印物的混合基热转印碳带,其特征在于,步骤S4中烘干温度为40~50摄氏度,烘干时间为2~5h。
10.根据权利要求6所述的适用于多种承印物的混合基热转印碳带,其特征在于,硫、磷、滑石粉或者有机硅的粒度为10000~15000目。